CN103666047A - 一种紫外光固化胶印油墨及其制备方法 - Google Patents

一种紫外光固化胶印油墨及其制备方法 Download PDF

Info

Publication number
CN103666047A
CN103666047A CN201310600555.5A CN201310600555A CN103666047A CN 103666047 A CN103666047 A CN 103666047A CN 201310600555 A CN201310600555 A CN 201310600555A CN 103666047 A CN103666047 A CN 103666047A
Authority
CN
China
Prior art keywords
parts
ink
tripropylene glycol
offset printing
printing ink
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310600555.5A
Other languages
English (en)
Other versions
CN103666047B (zh
Inventor
陈可夏
陈可亮
潮建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Founder Plastics Technology Co Ltd
Original Assignee
Tongling Founder Plastics Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Founder Plastics Technology Co Ltd filed Critical Tongling Founder Plastics Technology Co Ltd
Priority to CN201310600555.5A priority Critical patent/CN103666047B/zh
Publication of CN103666047A publication Critical patent/CN103666047A/zh
Application granted granted Critical
Publication of CN103666047B publication Critical patent/CN103666047B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种紫外光固化胶印油墨,其特征在于,由下列重量份的原料制备制成:有机颜料1-3、E-12环氧树脂12-15、对二甲胺基苯甲酸乙酯4-6、二缩三丙二醇双丙烯酸酯12-15、碳酸钙粉3-5、4-异丙基硫杂蒽酮1-2、环氧丙烯酸酯12-15、纳米三氧化钨1-2、四丁基氯化膦1-2、硫氰酸钠2-3、二乙胺1-2、二缩三丙二醇二丙烯酸酯10-12、三丙二醇二丙烯酸酯6-9、安息香双甲醚5-7、助剂4-5;本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明油墨具有高光泽,耐磨、耐折、耐老化等高性能的特点。

Description

一种紫外光固化胶印油墨及其制备方法
技术领域
本发明涉及一种油墨及其制备方法,特别是一种紫外光固化胶印油墨及其制备方法。
背景技术
紫外光固化(UV)油墨是指在紫外线照射下,利用不同波长和能量的紫外光使油墨成膜和干燥的油墨。利用不同紫外光谱,可产生不同能量,将不同油墨连结料中的单体聚合成聚合物,所以UV油墨的色膜具有良好的机械和化学性能。UV油墨的主要优点有:(1)不用溶剂;(2)干燥速度快,耗能少;(3)光泽好,色彩鲜艳;(4)耐水、耐溶剂,耐磨性能好。UV油墨中光引发剂是一种易受光激发的化合物,在吸收光照后激发成自由基,能量转移给感光性分子或光交联剂,使UV墨发生光固化反应。目前UV墨已成为一种较成熟的油墨技术,其污染物排放几乎为零。除了不含溶剂,UV墨还有如不易糊版,网点清晰,墨色鲜艳光亮,耐化学性能优异,用量省等优点。紫外光固化油墨广泛应用于包装行业,但现有紫外光固化油墨性能单一,印品光泽度较差,油墨墨性不易调整,较难适应复杂的印刷工艺,成为影响高档包装品印刷质量的重要因素。
发明内容
本发明的目的是提供一种紫外光固化胶印油墨及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种紫外光固化胶印油墨,由下列重量份的原料制备制成:有机颜料1-3、E-12环氧树脂12-15、对二甲胺基苯甲酸乙酯4-6、二缩三丙二醇双丙烯酸酯12-15、碳酸钙粉3-5、4-异丙基硫杂蒽酮1-2、环氧丙烯酸酯12-15、纳米三氧化钨1-2、四丁基氯化膦1-2、硫氰酸钠2-3、二乙胺1-2、二缩三丙二醇二丙烯酸酯10-12、三丙二醇二丙烯酸酯6-9、安息香双甲醚5-7、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-550 2-3、甲基丙烯酸-2- 羟基乙酯2-3、新戊二醇5-8、醋酸乙烯酯12-15、交联剂TAC2-3、抗氧剂1035 2-3、N-羟甲基丙烯酰胺1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述紫外光固化胶印油墨,由以下具体步骤制成:首先加入有机颜料、E-12环氧树脂、对二甲胺基苯甲酸乙酯、二缩三丙二醇双丙烯酸酯、碳酸钙粉、环氧丙烯酸酯、纳米三氧化钨、四丁基氯化膦、硫氰酸钠、二乙胺搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除4-异丙基硫杂蒽酮之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入4-异丙基硫杂蒽酮,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
本发明的有益效果是:本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明油墨具有高光泽,耐磨、耐折、耐老化等高性能的特点。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种紫外光固化胶印油墨,由下列重量份(公斤)的原料制备制成:有机颜料1、E-12环氧树脂12、对二甲胺基苯甲酸乙酯4、二缩三丙二醇双丙烯酸酯12、碳酸钙粉3、4-异丙基硫杂蒽酮1、环氧丙烯酸酯12、纳米三氧化钨1、四丁基氯化膦1、硫氰酸钠2、二乙胺1、二缩三丙二醇二丙烯酸酯10、三丙二醇二丙烯酸酯6、安息香双甲醚5、助剂4;
所述助剂由下列重量份(公斤)的原料制备而成:纳米硅藻土粉0.2、纳米云母粉0.2、硅烷偶联剂KH-550 2、甲基丙烯酸-2- 羟基乙酯2、新戊二醇5、醋酸乙烯酯12、交联剂TAC2、抗氧剂1035 2、N-羟甲基丙烯酰胺1、没食子酸丙酯2、薏仁油1;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述紫外光固化胶印油墨,由以下具体步骤制成:首先加入有机颜料、E-12环氧树脂、对二甲胺基苯甲酸乙酯、二缩三丙二醇双丙烯酸酯、碳酸钙粉、环氧丙烯酸酯、纳米三氧化钨、四丁基氯化膦、硫氰酸钠、二乙胺搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除4-异丙基硫杂蒽酮之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入4-异丙基硫杂蒽酮,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
所得的油墨,使用划格法牛皮胶带剥离,划格间距1mm,100%附着;使用浸有酒精的棉球,300克压力擦拭50次,无异状;浸泡于色拉油中(常温)8小时,无异状;使用浸有盐水的棉球,300克压力擦拭50次,无异状。

Claims (2)

1.一种紫外光固化胶印油墨,其特征在于,由下列重量份的原料制备制成:有机颜料1-3、E-12环氧树脂12-15、对二甲胺基苯甲酸乙酯4-6、二缩三丙二醇双丙烯酸酯12-15、碳酸钙粉3-5、4-异丙基硫杂蒽酮1-2、环氧丙烯酸酯12-15、纳米三氧化钨1-2、四丁基氯化膦1-2、硫氰酸钠2-3、二乙胺1-2、二缩三丙二醇二丙烯酸酯10-12、三丙二醇二丙烯酸酯6-9、安息香双甲醚5-7、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-550 2-3、甲基丙烯酸-2- 羟基乙酯2-3、新戊二醇5-8、醋酸乙烯酯12-15、交联剂TAC2-3、抗氧剂1035 2-3、N-羟甲基丙烯酰胺1-2、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
2.根据权利要求1所述紫外光固化胶印油墨,其特征在于,由以下具体步骤制成:首先加入有机颜料、E-12环氧树脂、对二甲胺基苯甲酸乙酯、二缩三丙二醇双丙烯酸酯、碳酸钙粉、环氧丙烯酸酯、纳米三氧化钨、四丁基氯化膦、硫氰酸钠、二乙胺搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除4-异丙基硫杂蒽酮之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入4-异丙基硫杂蒽酮,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
CN201310600555.5A 2013-11-25 2013-11-25 一种紫外光固化胶印油墨及其制备方法 Active CN103666047B (zh)