CN103655211A - 应用于二次印模室温加成硅橡胶超轻体口腔印模材料 - Google Patents
应用于二次印模室温加成硅橡胶超轻体口腔印模材料 Download PDFInfo
- Publication number
- CN103655211A CN103655211A CN201310551894.9A CN201310551894A CN103655211A CN 103655211 A CN103655211 A CN 103655211A CN 201310551894 A CN201310551894 A CN 201310551894A CN 103655211 A CN103655211 A CN 103655211A
- Authority
- CN
- China
- Prior art keywords
- silicone oil
- impression
- agent
- impression material
- vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种应用于二次印模室温加成硅橡胶超轻体口腔印模材料,为双组分材料,其双组分为基质组分和催化组分,其中基质组分由含有两个乙烯基的乙烯基硅油、含有三个或三个以上的Si-H基团的含氢硅油、增容剂、增强剂、抑制剂等组成。催化组分含有两个乙烯基的聚硅氧烷、增容剂、增强剂、亲水改性剂、铂催化剂等组成。本发明操作简单,工艺简便,固化时间,弹性回复,撕裂强度,邵氏硬度,细微复制等都达到了要求,提高印模材料的永久亲水性,降低印模材料的体积收缩率,提高材料的尺寸稳定性,材料复制精确度高,印模细微复制清晰。
Description
技术领域
本发明属于医用材料领域,涉及口腔印模材料。
背景技术
印模材料是口腔临床治疗修复中制取口腔印膜的材料,目前我国临床普遍使用藻酸盐类印模材料、琼脂类印模材料、聚硫橡胶印模材料。但是纯净的藻酸盐类印模材料还不能满足印模材料的性能要求,必须加入相关辅料,琼脂类印模材料材料凝胶很脆很难不能抵抗印模取出时的应力,聚硫橡胶印模材料不足之处是质地较软,永久变形偏大,硬化较慢,如时间不足取出印模易变形。由于室温加成型硅橡胶具有固化时间短在口腔凝固快,凝固后尺寸稳定,细微复制清晰,弹性回复优越,良好的操作性能等优点。目前我国市场上使用的印模材料主要依靠进口,国外生产硅橡胶印模材料的公司有登士柏公司、3M公司、贺利氏公司、意大利Virtual等,为了打破他们的垄断性,国内也致力于开发室温加成型硅橡胶口腔印模材料。
发明内容
本发明的目的是提供一种应用于二次印模室温加成硅橡胶超轻体口腔印模材料,以克服传统印模材料亲水性差、易收缩、尺寸稳定性差的不足,这种材料具有良好的弹性、韧性和强度,并且流动性良好,可塑性高,体积收缩率小,复制精确度高,化学稳定性好,有良好的亲水性,操作简单容易脱模等优点。
本发明所述的室温加成硅橡胶超轻体口腔印模材料以乙烯基硅油为基础聚合物,以含氢硅油为交联剂,以铂络合物为催化剂,添加增强剂和增容剂,增容剂可以扩充胶料的体积,增加胶料的质量,增强剂可以提高印模材的物理机械性能。本发明所述的室温加成硅橡胶超轻体口腔印模材料为双组分材料,双组分分为基质组分和催化组分,基质组分内含基础聚合物、交联剂和抑制剂,催化组分内含基础聚合物、催化剂和亲水改性剂,同时在两组分中添加适量的增强剂、增容剂、色浆等,交联剂为含氢硅油,含氢硅油为氢基聚硅氧烷,本发明是通过以下技术方案实现的。
本发明所述的室温加成硅橡胶超轻体口腔印模材料由基质组分和催化组分两个组分组成,并分别由以下几种原料按质量百分比经电动搅拌机搅拌、抽真空脱泡而成:
基质组分由30%-60%一种或多种至少每个分子含有两个乙烯基的乙烯基硅油;1%-5%一种或多种至少每个大分子应含有三个或三个以上的Si-H基团的含氢硅油;25%-55%的增容剂;5%-8%的增强剂;0.5%-1.5%的抑制剂;1.5%-3.5%的其他助剂所组成。
催化组分由30%-65%一种或多种至少每个分子含有两个乙烯基的乙烯基硅油;25%-55%的增容剂;5%-8%的增强剂;1%-2%的亲水改性剂;0.1%-0.5%的铂催化剂;2%-5%的其他助剂所组成。
所述的乙烯基硅油的乙烯基含量在0.22-1.9 mol%,粘度在200-60000 mPa·s范围,且该乙烯基硅油为双键封端或双键为支链的乙烯基硅油,其结构式如Ⅰ或Ⅱ所示。
所述的含氢硅油分子量为740-3800,粘度在25℃时为5-300 mm2/s,含Si-H键量为0.5-1.3%,其结构式如Ⅲ所示。
所述的亲水改性剂为聚醚表面活性剂,亲水改性剂使材料具有更良好的亲水性能,具备了一定的永久亲水性。
所述的增强剂为气相白炭黑,其比表面积为10 m2/g。
所述的增容剂为石英粉。
所述的抑制剂为四甲基二乙烯基二硅氧烷,其质量百分比为0.5%-1.5%,延长了临床医生的操作时间,便于更好的操作,保证材料固化后的质量。
所述的其他助剂为薄荷香精油、色浆以及脱模剂。
所述的脱模剂为甲基硅油。
本发明基质组分和催化组分分别用电动搅拌机混合均匀,并且抽真空脱泡30 min后制得。
本发明脱泡后的各组分胶料由双组分灌装机注入2×50 ml双组分胶管中待用,用室温加成硅橡胶超轻体口腔印模材料制取二次印模时,可以使用混合枪自动混合也可以手调混合。使用混合枪自动混合时能够将双组分胶管中的双组份按体积比1∶1自动混合搅拌均匀并输出,手调混合时在室温下取等量的基质组分和催化组分,用塑料调伴刀搅拌30秒至混合物的颜色一致,表示已混合均匀,即可使用。本发明超轻体口腔印模材料与室温加成硅橡胶腻子型印模材料制备的初次印模配合使用,其可操作时间约为1.5 min,口腔固化时间为2-3 min,阴模的物理性能如表1所示。
表1
本发明的材料于临床使用中应避免乳胶手套与印模材料及口腔组织的接触,即避免催化剂中毒,引起材料不硫化。
本发明的反应机理为硅氢加成反应,印模材中的乙烯基硅油的封端乙烯基与含氢硅油的硅氢键发生硅氢加成反应,即硅氢键同碳碳双键加成,形成交联网状结构,其反应方程式如公式(1)所示。
本发明所述的催化剂为铂化合物溶于甲基乙烯基硅氧烷配合的化合物,铂含量为1000ppm-3000ppm,该催化剂催化剂机理如公式(2)所示。
Ⅰ
Ⅱ
其中R=CnH2n+1。
Ⅲ
其中R=CnH2n+1。
下式为本发明的硅氢加成反应机理方程式:
下式为本发明的催化剂的催化机理:
本发明的优点在于开发了一种超轻体型在口腔内使用的室温加成硅橡胶印模材料,该材料固化时间3min,操作时间1-2min,取出时间为3min,邵氏硬度53左右,细微复制0.02mm清晰可见,亲水接触角小于65°,弹性回复99.8%,尺寸稳定性良好。
本发明操作简单,工艺简便,固化时间,弹性回复,撕裂强度,邵氏硬度,细微复制等都达到了要求。与现有技术相比,本发明的有益效果是提高印模材料的永久亲水性,降低印模材料的体积收缩率,提高材料的尺寸稳定性,材料复制精确度高,印模细微复制清晰。
具体实施方式
本发明将通过以下实施例作进一步说明。
实施例1。
本实施例的室温加成硅橡胶超轻体口腔印模材料的配方如下表所示:
实施例2。
本实施例的室温加成硅橡胶超轻体口腔印模材的配方如下表所示:
实施例3。
本实施例的室温加成硅橡胶超轻体口腔印模材的配方如下表所示:
实施例4。
本实施例的室温加成硅橡胶超轻体口腔印模材的配方如下表所示:
本实施例中所述的乙烯基硅油的粘度为200-60000 mPa·s且该乙烯基硅油为双键封端或双键为支链的乙烯基硅油,其结构式如Ⅰ或Ⅱ所示,所述的含氢硅油含Si-H键量为0.75%,所述的铂催化剂为氯铂酸与乙烯基硅油络合催化剂,所述的增容剂为超细石英粉,所述的增强剂为比表面积为10 m2/g的气相白炭黑,所述的脱模剂为低粘度甲基硅油,所述的抑制剂为四甲基二乙烯基二硅氧烷,所述的亲水改性剂为聚醚表面活性剂。
按照配方加料后将基质组分和催化组分分别用电动搅拌机混合均匀,并且抽真空脱泡30 min,脱泡后的各组分胶料由双组分灌装机注入2×50 ml双组分胶管中待用,用室温加成硅橡胶超轻体口腔印模材制备二次印模时,可以使用混合枪自动混合也可以手调混合。使用混合枪自动混合能够将药筒中的双组份按体积比1∶1自动混合搅拌均匀并输出,手调混合时在室温下取等量的基质和催化剂,用塑料调刀搅拌30秒,直至混合物的颜色一致,表示已混合均匀,即可使用。
本发明的室温加成硅橡胶超轻体口腔印模材满足牙科各种精细印模的要求,与室温加成硅橡胶腻子型口腔印模材配合使用,用于牙科取得精确印模,能被广泛应用于冠桥印模,嵌体和高嵌体印模,功能印模,种植体印模,义齿印模和口腔组织印模。
Claims (1)
1.一种应用于二次印模室温加成硅橡胶超轻体口腔印模材料,其特征是由基质组分和催化组分两个组分组成,其中:
基质组分(质量百分比):30%-60%一种或多种至少每个分子含有两个乙烯基的乙烯基硅油;1%-5%一种或多种至少每个大分子应含有三个或三个以上的Si-H基团的含氢硅油;25%-55%的增容剂;5%-8%的增强剂;0.5%-1.5%的抑制剂;1.5%-3.5%的其他助剂;
催化组分(质量百分比):30%-65%一种或多种至少每个分子含有两个乙烯基的聚硅氧烷;25%-55%的增容剂;5%-8%的增强剂;1%-2%的亲水改性剂;0.1%-0.5%的铂催化剂;2%-5%的其他助剂;
所述的乙烯基硅油的乙烯基含量在0.22-1.9 mol%,粘度在200-60000 mPa·s范围,且该乙烯基硅油为双键封端或双键为支链的乙烯基硅油;
所述的含氢硅油分子量为740-3800,粘度在25℃时为5-300 mm2/s,含Si-H键量为0.5-1.3%;
所述的亲水改性剂为聚醚表面活性剂;
所述的增强剂为气相白炭黑,其比表面积为10 m2/g;
所述的增容剂为石英粉;
所述的抑制剂为四甲基二乙烯基二硅氧烷,其质量百分比为0.5%-1.5%;
所述的其他助剂为薄荷香精油、色浆以及脱模剂;
所述的脱模剂为甲基硅油。