CN103640352B - 一种镭射转移膜的生产工艺 - Google Patents

一种镭射转移膜的生产工艺 Download PDF

Info

Publication number
CN103640352B
CN103640352B CN201310615774.0A CN201310615774A CN103640352B CN 103640352 B CN103640352 B CN 103640352B CN 201310615774 A CN201310615774 A CN 201310615774A CN 103640352 B CN103640352 B CN 103640352B
Authority
CN
China
Prior art keywords
laser
mold pressing
basement membrane
membrane
laser transfer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310615774.0A
Other languages
English (en)
Other versions
CN103640352A (zh
Inventor
汪名海
刘兵
华晓东
程军明
柴鑫
潘四兵
王晓磊
李志伟
余国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Taili Hengyou Technology Development Co ltd
Original Assignee
ZHEJIANG YAXIN PACKAGE MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG YAXIN PACKAGE MATERIAL Co Ltd filed Critical ZHEJIANG YAXIN PACKAGE MATERIAL Co Ltd
Priority to CN201310615774.0A priority Critical patent/CN103640352B/zh
Publication of CN103640352A publication Critical patent/CN103640352A/zh
Application granted granted Critical
Publication of CN103640352B publication Critical patent/CN103640352B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种镭射转移膜的生产工艺，依次包括以下步骤：基膜涂布、第一次模压、第二次模压、镀铝、分切；本发明的优点：依次通过基膜涂布、第一次模压、第二次模压、镀铝、分切生产制成的镭射转移膜，具有光洁度好，平滑度高，色泽鲜艳，外观亮丽，视觉冲击力强，能很好提升产品包装档次，具有优良的阻隔性，防潮、抗氧化效果显著。

Description

一种镭射转移膜的生产工艺
技术领域
本发明涉及一种镭射转移膜的生产工艺。
背景技术
镭射转移纸已经成为中；高档烟包；酒包的首选；它是根据防伪要求；将特种制版；计算机光刻；精密电铸；激光全息模压；进行化工和高精度玻离等多项高新技术有机结合的一种新型防伪；环保；包装材料；由镭射转移膜与纸进行转移复合而成；然而由于生产工艺的限制；镭射转移膜表面不可避免形成版缝；根据具体生产工艺要求；缝宽通常控制在0.1～0.5mm这种带有版缝的镭射转移膜会给后续生产带来一些不必要的麻烦；而且工序较多；如一道工序出问题将会报废处理；每道工序必须环环相扣；不仅导致烟包废品率上升；而且还会浪费大量的原辅材料。
发明内容
本发明要解决的技术问题是现有镭射转移膜表面存在版缝，易对后续生产带来麻烦，导致了产品废品率上升，提高了生产成本，从而提供一种镭射转移膜的生产工艺。
为了解决上述技术问题，本发明是通过以下技术方案实现的：一种镭射转移膜的生产工艺，依次包括以下步骤：
a）基膜涂布：通过涂布机的陶瓷网纹辊均匀的将涂料涂布在基膜上，并通过五节烘箱进行烘烤，从第一节烘箱到第五节烘箱所述五节烘箱的烘烤温度依次为：83～87℃、112～116℃、143～146℃、150～165℃、98～102℃；
b）第一次模压：通过模压机将镭射模压版材上的镭射图案压制在步骤a）处理后的基膜上，模压温度为160～170℃，所述镭射模压版材采用无版缝的镭射图案；
c）第二次模压：特步骤b）处理后的基膜上的镭射图案烘干后进行第二次模压处理，模压温度为165～175℃，所述镭射模压版材采用有版缝的镭射图案；
d）镀铝：将步骤c）处理后的基膜上通过真空镀铝在基膜表面涂覆一层铝层；镀覆时的真空度为1.3×10-2～1.3×10-3Pa，镀覆时的温度为1200～1400℃；
e）分切：根据生产要求将步骤d）处理后基膜通过分切机进行分切。
优选的，步骤a）中所述涂料由以下重量份的组分组成：30～40重量份的丙烯酸树脂、10～15重量份的醋酸纤维素，丙烯酸树脂具有良好的保光保色性、耐水耐化学性、干燥快，醋酸纤维素与丙烯酸树脂具有良好的吸附性。
优选的，步骤d）中的铝层厚度为380～420埃，实用性能好，便于后续工序中铝层的清洗及保护，当铝层厚度小于380埃时，铝层容易被损坏，可靠性能差，当铝层厚度大于420埃时，铝层不易不清洗，易影响后续工艺，实用性能差。
优选的，步骤e）的分切机连接PLC控制装置，PLC控制可以根据分切要求进行设置参数，控制效果好，实用性能好，便于操作，可靠性能好。
综上所述，本发明的优点：依次通过基膜涂布、第一次模压、第二次模压、镀铝、分切生产制成的镭射转移膜，具有光洁度好，平滑度高，色泽鲜艳，外观亮丽，视觉冲击力强，能很好提升产品包装档次，具有优良的阻隔性，防潮、抗氧化效果显著。
具体实施方式
一种镭射转移膜的生产工艺，依次包括以下步骤：
a）基膜涂布：通过涂布机的陶瓷网纹辊均匀的将涂料涂布在基膜上，并通过五节烘箱进行烘烤，从第一节烘箱到第五节烘箱所述五节烘箱的烘烤温度依次为：83～87℃、112～116℃、143～146℃、150～165℃、98～102℃；
b）第一次模压：通过模压机将镭射模压版材上的镭射图案压制在步骤a）处理后的基膜上，模压温度为160～170℃，所述镭射模压版材采用无版缝的镭射图案；
c）第二次模压：特步骤b）处理后的基膜上的镭射图案烘干后进行第二次模压处理，模压温度为165～175℃，所述镭射模压版材采用有版缝的镭射图案；
d）镀铝：将步骤c）处理后的基膜上通过真空镀铝在基膜表面涂覆一层铝层；镀覆时的真空度为1.3×10-2～1.3×10-3Pa，镀覆时的温度为1200～1400℃；
e）分切：根据生产要求将步骤d）处理后基膜通过分切机进行分切。
步骤a）中所述涂料由以下重量份的组分组成：30～40重量份的丙烯酸树脂、10～15重量份的醋酸纤维素，丙烯酸树脂具有良好的保光保色性、耐水耐化学性、干燥快，醋酸纤维素与丙烯酸树脂具有良好的吸附性，步骤d）中的铝层厚度为380～420埃，实用性能好，便于后续工序中铝层的清洗及保护，当铝层厚度小于380埃时，铝层容易被损坏，可靠性能差，当铝层厚度大于420埃时，铝层不易不清洗，易影响后续工艺，实用性能差，步骤e）的分切机连接PLC控制装置，PLC控制可以根据分切要求进行设置参数，控制效果好，实用性能好，便于操作，可靠性能好。
依次通过基膜涂布、第一次模压、第二次模压、镀铝、分切生产制成的镭射转移膜，具有光洁度好，平滑度高，色泽鲜艳，外观亮丽，视觉冲击力强，能很好提升产品包装档次，具有优良的阻隔性，防潮、抗氧化效果显著。

Claims (3)

1.一种镭射转移膜的生产工艺，其特征在于：依次包括以下步骤：
a)基膜涂布：通过涂布机的陶瓷网纹辊均匀的将涂料涂布在基膜上，并通过五节烘箱进行烘烤，从第一节烘箱到第五节烘箱所述五节烘箱的烘烤温度依次为：83～87℃、112～116℃、143～146℃、150～165℃、98～102℃；
b)第一次模压：通过模压机将镭射模压版材上的镭射图案压制在步骤a)处理后的基膜上，模压温度为160～170℃，所述镭射模压版材采用无版缝的镭射图案；
c)第二次模压：将步骤b)处理后的基膜上的镭射图案烘干后进行第二次模压处理，模压温度为165～175℃，镭射模压版材采用有版缝的镭射图案；
d)镀铝：在步骤c)处理后的基膜上通过真空镀铝在基膜表面涂覆一层铝层；镀铝时的真空度为1.3×10-2～1.3×10-3Pa，镀铝时的温度为1200～1400℃；
e)分切：根据生产要求将步骤d)处理后基膜通过分切机进行分切；
步骤a)中所述涂料包括以下重量份的组分：30～40重量份的丙烯酸树脂、10～15重量份的醋酸纤维素。
2.根据权利要求1所述的一种镭射转移膜的生产工艺，其特征在于：步骤d)中的铝层厚度为380～420A。
3.根据权利要求1所述的一种镭射转移膜的生产工艺，其特征在于：步骤e)的分切机连接PLC控制装置。
CN201310615774.0A 2013-11-26 2013-11-26 一种镭射转移膜的生产工艺 Active CN103640352B (zh)