CN103612031A - 一种光伏焊带用预涂助焊剂 - Google Patents
一种光伏焊带用预涂助焊剂 Download PDFInfo
- Publication number
- CN103612031A CN103612031A CN201310565022.8A CN201310565022A CN103612031A CN 103612031 A CN103612031 A CN 103612031A CN 201310565022 A CN201310565022 A CN 201310565022A CN 103612031 A CN103612031 A CN 103612031A
- Authority
- CN
- China
- Prior art keywords
- parts
- flux
- coated
- tin
- soldering flux
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种光伏焊带用预涂助焊剂,属于光伏发电技术领域。其包括异丙醇60-85份、二甲基甲酰胺10-20份、松香2-5份、苯酐聚酯多元醇1-10份,添加剂1-10份和活性剂0.1-5份。本发明提供了一种光伏焊带用预涂助焊剂,通过这种预涂助焊剂生产的涂锡铜带,该助焊剂只要在原有涂锡铜带生产时增加一道预涂工序,将此助焊剂通过预涂的方式均匀的涂在涂锡铜带正反面和两侧边使其呈均匀状包裹整个涂锡铜带,在使用时无需助焊剂浸泡、烘干,可以直接使用无需等待,从而节省物料降低成本,缩短生产周期提高生产效率。
Description
技术领域
本发明涉及一种光伏焊带用预涂助焊剂,属于光伏发电技术领域。
背景技术
为了普及光伏发电在全世界的运用,降低光伏发电成本是普及的一个重要前提。现在光伏发电的成本很高,大概是煤发电成本的一倍到到四倍之间,是风电项目的两倍到四倍之间。但是,光伏发电的资源是取之不尽的,降低光伏发电的成本是普及光伏发电的唯一途径,也是发展低碳经济的重要法宝之一。而降低光伏组件生产的成本是降低光伏发电成本的重要途径之一。
现有技术中,光伏组件需用涂锡铜带在使用前需提前30分钟将涂锡焊带浸泡在助焊剂池中15分钟,再取出晾晒5分钟,然后再60度烘干15分钟才能使用,如此长时间的等待和助焊剂的大量使用,使得客户成本高高不下生产周期过长无法缩短。
随着市场的要求,降低光伏组件的发电成本越来越重要。光伏组件厂家都想尽一切办法降低生产成本。如能解决客户在焊带使用中浪费大量辅料助焊剂和时间等待的问题,将能给客户带来助焊剂100%的收益和效率、工时的收益。
发明内容
本发明的目的在于克服上述不足之处,提供一种无需在等待和烘干焊带的光伏焊带用预涂助焊剂。
按照本发明提供的技术方案,一种光伏焊带用预涂助焊剂,配方比例按重量份计如下:异丙醇60-85份、二甲基甲酰胺10-20份、松香2-5份、苯酐聚酯多元醇1-10份,添加剂1-10份和活性剂0.1-5份。
所述添加剂为聚硫醇、多异氰酸酯中的一种。
所述活性剂为阴离子表面活性剂类的脂肪盐酸、硫酸盐酸、磷酸酯盐中的任意两种。
光伏焊带用预涂助焊剂在预涂涂锡铜带生产过程中,将按照上述配方配合混匀得到的预涂助焊剂加入涂布机或其它辅助设备内,涂锡铜带在涂完锡后直接从涂布设备或其它辅助设备内经过,预涂助焊剂通过喷淋、喷涂、刷涂或浸泡方式附在涂锡铜带表面,再经过可以调节高低控制厚度的挤压辊,使其均匀的包裹整个涂锡铜带,涂好的涂锡铜带在50-80℃低温下烘烤10-90s,使其表面的助焊剂固化形成单边厚度为0.005-0.02mm的固化层,再经过小于40℃的冷风冷却10-120s,使涂锡铜带表面温度达到常温完成作业。
本发明的有益效果:本发明提供了一种光伏焊带用预涂助焊剂,通过这种预涂助焊剂生产的涂锡铜带,该助焊剂只要在原有涂锡铜带生产时增加一道预涂工序,将此助焊剂通过预涂的方式均匀的涂在涂锡铜带正反面和两侧边使其呈均匀状包裹整个涂锡铜带,在使用时无需助焊剂浸泡、烘干,可以直接使用无需等待,从而节省物料降低成本,缩短生产周期提高生产效率。
具体实施方式
实施例1
一种光伏焊带用预涂助焊剂,配方比例按重量份计如下:异丙醇60份、二甲基甲酰胺10份、松香2份、苯酐聚酯多元醇1份,添加剂1份和活性剂0.1份。
所述添加剂为聚硫醇。所述活性剂为阴离子表面活性剂类的脂肪盐酸、硫酸盐酸。
实施例2
一种光伏焊带用预涂助焊剂,配方比例按重量份计如下:异丙醇85份、二甲基甲酰胺20份、松香5份、苯酐聚酯多元醇10份,添加剂10份和活性剂5份。
所述添加剂为聚硫醇、多异氰酸酯中的一种。
所述活性剂为阴离子表面活性剂类的脂肪盐酸、硫酸盐酸、磷酸酯盐中的任意两种。
实施例3
一种光伏焊带用预涂助焊剂,配方比例按重量份计如下:异丙醇70份、二甲基甲酰胺15份、松香4份、苯酐聚酯多元醇6份,添加剂6份和活性剂3份。
所述添加剂为聚硫醇、多异氰酸酯中的一种。
所述活性剂为阴离子表面活性剂类的脂肪盐酸、硫酸盐酸、磷酸酯盐中的任意两种。
按照实施例1-3的配方制备得到的光伏焊带用预涂助焊剂在预涂涂锡铜带生产过程中,将预涂助焊剂加入涂布机或其它辅助设备内,涂锡铜带在涂完锡后直接从涂布设备或其它辅助设备内经过,预涂助焊剂通过喷淋、喷涂、刷涂或浸泡方式附在涂锡铜带表面,再经过可以调节高低控制厚度的挤压辊,使其均匀的包裹整个涂锡铜带,涂好的涂锡铜带在50-80℃低温下烘烤10-90s,使其表面的助焊剂固化形成单边厚度为0.005-0.02mm的固化层,再经过小于40℃的冷风冷却10-120s,使涂锡铜带表面温度达到常温完成作业。
所述光伏焊带用预涂助焊剂参数如表1所示
表1成品预涂助焊剂其它主要参数
闪点 | 16℃~25℃ |
沸点 | 80℃~95℃ |
自燃温度 | 360℃~400℃ |
比重 | 0.75~0.9 |
固体含量 | 2~6 |
外观 | 微黄色 |
这样的预涂助焊剂可以有效附着于涂锡铜带,并在干燥后形成长期有效和不易脱落的预涂层,此预涂助焊剂用于产品表面可形成保护层在后续焊接中可以随时焊接。
Claims (3)
1. 一种光伏焊带用预涂助焊剂,其特征是:配方比例按重量份计如下:异丙醇60-85份、二甲基甲酰胺10-20份、松香2-5份、苯酐聚酯多元醇1-10份,添加剂1-10份和活性剂0.1-5份。
2.如权利要求1所述光伏焊带用预涂助焊剂,其特征是:所述添加剂为聚硫醇、多异氰酸酯中的一种。
3.如权利要求1所述光伏焊带用预涂助焊剂,其特征是:所述活性剂为阴离子表面活性剂类的脂肪盐酸、硫酸盐酸、磷酸酯盐中的任意两种。