CN103572276A - 一种新型除油除锈磷化钝化综合处理剂的制备方法 - Google Patents

一种新型除油除锈磷化钝化综合处理剂的制备方法 Download PDF

Info

Publication number
CN103572276A
CN103572276A CN201210257927.4A CN201210257927A CN103572276A CN 103572276 A CN103572276 A CN 103572276A CN 201210257927 A CN201210257927 A CN 201210257927A CN 103572276 A CN103572276 A CN 103572276A
Authority
CN
China
Prior art keywords
treating agent
comprehensive
citric acid
zinc oxide
comprehensive treating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210257927.4A
Other languages
English (en)
Inventor
王力
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN JIANFA PRECISION MACHINERY MANUFACTURING Co Ltd
Original Assignee
TIANJIN JIANFA PRECISION MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN JIANFA PRECISION MACHINERY MANUFACTURING Co Ltd filed Critical TIANJIN JIANFA PRECISION MACHINERY MANUFACTURING Co Ltd
Priority to CN201210257927.4A priority Critical patent/CN103572276A/zh
Publication of CN103572276A publication Critical patent/CN103572276A/zh
Pending legal-status Critical Current

Abstract

本发明研制了一种只需10~20min就可以完成除油、除锈、磷化、钝化的“四合一”综合处理剂，本发明的技术方案是：综合处理剂由氧化锌、磷酸二氢锌、硫脲、钼酸钠、氯酸钾、三乙醇胺、OP-10、柠檬酸和水构成。其优越性：研制的综合处理液适用于钢铁表面涂装前处理，室温下使钢铁工件表面涂油、除锈、磷化、钝化一步完成，用后不产生沉渣，可循环使用，节省工时，节约电源。本综合处理液具有高效节能、适应性强等特点，适合于局部和户外大型部件得处理，也可作短期存放的防锈处理。本综合处理液不含亚硝酸盐，铬酸盐，铅盐等有害物质，不污染环境。

Description

一种新型除油除锈磷化钝化综合处理剂的制备方法
技术领域
本发明涉及一种用于钢铁及其制品表面处理的药剂，尤其涉及一种新型除油除锈磷化钝化综合处理剂的制备方法。 
背景技术
根据国家标准，钢铁表面在进行涂漆、喷塑或电镀之前，都要对钢铁表面进行磷化、钝化的预处理，以提高钢铁表面的防锈性和附和力。目前，磷酸盐转化膜处理广泛应用于汽车、轮船、机械制造航空航天及家用电器等产品上。 
保证质量的前提下，尽量减少处理步骤，缩短处理时间，降低处理成本以及减少处理危害，已成为当前钢铁表面处理领域中急待解决的重要课题。同时，推行清洁上产已成为世界各国实现经济、社会可持续发展的必然选择。我们研究了一种新的磷化方法，所得磷化膜有较好的防锈性和吸附性。只需10~20min就可以完成除油、除锈、磷化、钝化的“四合一”综合处理液，此种处理液具有工序少，操作简单，投资省，能大量节约人力物理和财力，对大型工件也可进行处理等优越性，并且不含亚硝酸盐、重铬酸盐及氟化物的“绿色”综合处理液。该处理液性能稳定，成膜耐蚀性及附着力均佳。 
发明内容
本发明研制了一种只需10~20min就可以完成除油、除锈、磷化、钝化的“四合一”综合处理剂，本发明的技术方案是：综合处理剂由氧化锌、磷酸二氢锌、硫脲、钼酸钠、氯酸钾、三乙醇胺、OP- 10、柠檬酸和水构成。适宜配方为：270g/L磷酸(85%)、8-20g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、4-23g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水 。包括如下步骤：先将称量好的水加入烧杯中，在搅拌下依次加入按照比例称量完的氧化锌、磷酸二氢锌、硫脲、钼酸钠、氯酸钾、三乙醇胺、OP- 10、柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的磷酸,加毕后继续搅拌30min，即可得综合处理液。 
如要配制得5倍浓缩液，则只需降水量降至配方量的20%即可，其配方和工艺均不变，便可制得综合处理液的5倍浓缩液，使用时只需将浓缩液兑5倍水便可直接使用。 
本发明的优越性：研制的综合处理液适用于钢铁表面涂装前处理，室温下使钢铁工件表面涂油、除锈、磷化、钝化一步完成，用后不产生沉渣，可循环使用，节省工时，节约电源。本综合处理液具有高效节能、适应性强等特点，适合于局部和户外大型部件得处理，也可作短期存放的防锈处理。本综合处理液不含亚硝酸盐，铬酸盐，铅盐等有害物质，不污染环境。 
具体实施方式
下面的实施例可以使本专业技术人员更全面地理解本发明，但不以任何方式限制本发明。 
实施例1：
配方为：270g/L磷酸(85%)、8g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、4g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水 。包括如下步骤：先将称量好的625L水加入烧杯中，在搅拌下依次加入按照比例称量完的8g氧化锌、53g磷酸二氢锌、1g硫脲、3g钼酸钠、6g氯酸钾、4g三乙醇胺、12g OP- 10、10g柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的270磷酸,加毕后继续搅拌30min，即可得综合处理液。
实施例2：配方为：270g/L磷酸(85%)、12g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、10g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水 。包括如下步骤：先将称量好的625L水加入烧杯中，在搅拌下依次加入按照比例称量完的12g氧化锌、53g磷酸二氢锌、1g硫脲、3g钼酸钠、6g氯酸钾、10g三乙醇胺、12g OP- 10、10g柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的270磷酸,加毕后继续搅拌30min，即可得综合处理液。 
实施例3：配方为：270g/L磷酸(85%)、16g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、16g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水 。包括如下步骤：先将称量好的625L水加入烧杯中，在搅拌下依次加入按照比例称量完的16g氧化锌、53g磷酸二氢锌、1g硫脲、3g钼酸钠、6g氯酸钾、16g三乙醇胺、12g OP- 10、10g柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的270磷酸,加毕后继续搅拌30min，即可得综合处理液。 
实施例4：
配方为：270g/L磷酸(85%)、20g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、23g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水 。包括如下步骤：先将称量好的625L水加入烧杯中，在搅拌下依次加入按照比例称量完的20g氧化锌、53g磷酸二氢锌、1g硫脲、3g钼酸钠、6g氯酸钾、23g三乙醇胺、12g OP- 10、10g柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的270磷酸,加毕后继续搅拌30min，即可得综合处理液。

Claims (1)

1.一种新型除油除锈磷化钝化综合处理剂的制备方法，其特征在于：综合处理剂的制备由氧化锌、磷酸二氢锌、硫脲、钼酸钠、氯酸钾、三乙醇胺、OP- 10、柠檬酸和水构成，适宜配方为：270g/L磷酸(85%)、8-20g/L氧化锌、3g/L钼酸钠、53g/L磷酸二氢锌、6g/L氯酸钾、12g/LOP- 10、4-23g/L三乙醇胺、10g/L柠檬酸、1g/L硫脲、625g/L水，包括如下步骤：先将称量好的水加入烧杯中，在搅拌下依次加入按照比例称量完的氧化锌、磷酸二氢锌、硫脲、钼酸钠、氯酸钾、三乙醇胺、OP- 10、柠檬酸，加毕后在常温下搅拌10min,再在搅拌下加入称量完的磷酸,加毕后继续搅拌30min，即可得综合处理液。
CN201210257927.4A 2012-07-25 2012-07-25 一种新型除油除锈磷化钝化综合处理剂的制备方法 Pending CN103572276A (zh)