CN101935832B - 一种常温下可循环使用的锌铁系金属表面磷化液 - Google Patents

一种常温下可循环使用的锌铁系金属表面磷化液 Download PDF

Info

Publication number
CN101935832B
CN101935832B CN201010515980A CN201010515980A CN101935832B CN 101935832 B CN101935832 B CN 101935832B CN 201010515980 A CN201010515980 A CN 201010515980A CN 201010515980 A CN201010515980 A CN 201010515980A CN 101935832 B CN101935832 B CN 101935832B
Authority
CN
China
Prior art keywords
zinc
normal temperature
molybdate
liquid
water
Prior art date
Application number
CN201010515980A
Other languages
English (en)
Other versions
CN101935832A (zh
Inventor
陈兆林
雷忠祥
陈吉武
Original Assignee
南京有为化工有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南京有为化工有限公司 filed Critical 南京有为化工有限公司
Priority to CN201010515980A priority Critical patent/CN101935832B/zh
Publication of CN101935832A publication Critical patent/CN101935832A/zh
Application granted granted Critical
Publication of CN101935832B publication Critical patent/CN101935832B/zh

Abstract

本发明涉及一种常温下可循环使用的锌铁系金属表面磷化液,其特征在于由以下原料按重量百分比配置而成:磷酸14%~28%,氧化锌3.5%~7%,硝酸锌12.6%~17.5%,柠檬酸0.14%~0.56%,酒石酸0.14%~0.7%,钼酸盐0.14%~0.84%,余量的水。本发明磷化在除油除锈后,采用一道工序进行,免去了中和、表调、钝化、水洗等过程,能够有效快速地在黑色金属表面形成一层致密均匀、附着力强的磷化膜;此工序大大减少了操作流程,本磷化过程不排渣,减少了对环境的污染,大幅度提高了材料的利用率,常温下进行更降低了能耗节水,并且有使用范围广、投资少、效益高、安全性等优点,而且槽液稳定性好,不变质、无挥发、易维护,利于后续喷涂工艺。

Description

一种常温下可循环使用的锌铁系金属表面磷化液
技术领域
[0001] 本发明涉及钢铁等黑色金属表面处理的环保磷化液,特别涉及一种常温下可循环使用的锌铁系金属表面磷化液。
背景技术
[0002] 金属在含有磷酸盐的溶液中进行处理,在其表面形成的磷酸盐化学转化膜,称之为磷化膜。100多年来,磷化技术广泛应用于汽车、军工、电器、机械等领域,其主要用途是防锈、耐磨减摩、润滑、涂漆底层等。
[0003] 现有传统磷化工艺是在高温下使用磷化液对金属材料和金属制品的表面进行磷化处理进行,这种方式存在耗能大、处理时间长、磷化质量不稳定、有废渣废液要排放、维护繁杂、对环境有污染等缺点,而且成本高。随着国内磷化技术的发展,目前市场上也出现常温磷化液,但在使用过程中,处理时间过长,其酸性物质对钢铁表面有着较大的腐蚀,影响磷化质量,而且使用有毒促进剂亚硝酸钠、氟化物、重铬酸盐,磷化后有沉渣及废液排放。
发明内容
[0004] 本发明的目的是提供一种高效、经济、环保的常温下可循环使用的金属表面磷化液,以克服传统磷化工艺工序繁杂、高温下进行、工作环境恶劣、磷化有沉渣有排放需水洗以及磷化后易返锈、槽液不稳定、成膜不均勻、维护难、对环境有污染等问题;适用在钢铁制造行业中各种黑色金属工件涂装前表面处理。
[0005] 本发明所述锌铁系金属表面磷化液由下列组分按重量百分比配制而成:
[0006]
磷酸 14%〜28%氧化锌 3.5%~7%硝酸锌 12.6%~17.5%柠檬酸 0.14%〜0.56%酒石酸 0.14%〜0.7%钼酸盐 0.14%~0.84%水 余量
[0007]
[0008] 上述磷酸为85wt%工业级或食用级磷酸;柠檬酸为的99. 5wt%的柠檬酸;酒石酸为99. 5wt%的酒石酸;钼酸盐可以为钼酸钠、钼酸锌或钼酸铵。
[0009] 本发明的制备方法如下:
[0010] ①先将氯化锌加入10%的水调成糊状,在缓慢加入磷酸至全部反应结束。
[0011] ②将硝酸锌、柠檬酸、酒石酸、钼酸盐溶于剩余水中
[0012] ③将①和②混合即可[0013] 本发明的使用方法如下:
[0014] 常温下使用时将本发明与水按1 : 6重量比稀释后再使用,根据黑色金属工件成膜厚度要求,可在6〜15分钟磷化处理,操作方式为浸渍处理。
[0015] 采用本发明常温下可在黑色金属表面形成锌铁复合盐膜,且根据处理时间的长短来调整膜的厚度,磷化后金属表面呈彩膜。
[0016] 本发明具有如下优点:
[0017] 1、本发明配槽浸泡,投资成本低,常温下进行,低能耗,适用于各种黑色金属工件。
[0018] 2、本发明磷化在除油除锈后,采用一道工序进行,免去了中和、表调、钝化、水洗等过程,此工序大大减少了操作流程,本磷化过程不排渣,减少了对环境的污染,大幅度提高了材料的利用率,常温下进行更降低了能耗节水
[0019] 3、磷化过程在常温下即可进行、无需加温,不使用有毒物质亚硝酸钠作为促进剂、 磷化过程中无结渣无金属盐外泄,磷化后不水洗,气相液相二次成膜,风干或自干即可。
[0020] 4、根据不同大小的工件可以浸泡、涂刷或喷淋,并根据成膜要求适当调整时间,磷化过程能够有效快速地在黑色金属表面形成一层致密均勻、附着力强的磷化膜,该膜经检测达到国家涂装行业一级标准,为后续喷涂工艺做好强有力的保障。
[0021] 5、本发明磷化面积是传统磷化的五倍以上,并且槽液稳定性好,不变质、无挥发、 安全高效。
[0022] 6、使用过程中可根据其PH和比重值的变化及时添加相应组份,易维护,并可实现循环使用。
[0023] 按一个涂装厂要对15000平方的黑色金属工件进行磷化处理,传统每公斤磷化液能磷化大约30平方,每公斤费用在6元左右,实际磷化液消耗费用约3000元;如用本发明, 每公斤磷化150平方以上,每公斤费用在22元,实际磷化液消耗费用不超过2200元,直接节省了 27%的生产成本,还不包含用水排放的成本,具有极高的经济价值和社会价值。
具体实施方式
[0024] 实施例1 :
[0025] 本实施例由下列组分按重量比配制而成:
[0026]
磷酸 14%氧化锌 5.6%硝酸锌 13.3%柠檬酸 0.56%酒石酸 0.56%钼酸盐 0.35%水 余量
[0027] 本实施例适用于常温下各种黑色金属工件表面喷涂前的磷化处理,处理时间6〜 15分钟,其中钼酸盐选用钼酸钠。[0028]
[0029]
[0030]
实施例2 :
本实施例由下列组分按重量比配制而成:
磷酸 21%
氧化锌 4.9%
硝酸锌 15.4%
柠檬酸 0.42%
酒石酸 0.35%
钼酸盐 036%
水 余量本实施例适用于常温下各种黑色金属工件表面喷涂前的磷化处理,处理时间6 其中钼酸盐选用钼酸锌。。
[0031]
15分钟,
[0032] 实施例3
[0033]
磷酸
氧化锌
硝酸锌
柠檬酸
酒石酸
钼酸盐
28% 4.2% 17.5% 0.28% 0.14% 0.7% 余量
本实施例适用于常温下各种黑色金属工件表面喷涂前的磷化处理,处理时间6 其中钼酸盐选用钼酸胺。
[0034]
15分钟,
[0035] 下表是本发明与传统磷化液各项指标特点对比如下
[0036]
Figure CN101935832BD00051
Figure CN101935832BD00061

Claims (5)

1. 一种常温下可循环使用的锌铁系金属表面磷化液,其特征在于由以下原料按重量百分比配置而成:磷酸14°Γ28%,氧化锌3. 5%〜7%,硝酸锌12. 6%〜17· 5%,柠檬酸0. 14%〜0· 56%,酒石酸 0. 14%〜0· 7%,钼酸盐0. 14%〜0· 84%,余量的水。
2.根据权利要求1所述的金属表面磷化液,其特征在于所述的钼酸盐选自钼酸钠、钼酸锌或钼酸铵。
3.根据权利要求1或2所述的金属表面磷化液,其特征在于各原料的重量百分比为: 磷酸14%,氧化锌5. 6%,硝酸锌13. 3%,柠檬酸0. 56%,酒石酸0. 56%,钼酸盐0. 35%,余量的水。
4.根据权利要求1或2所述的金属表面磷化液,其特征在于各原料的重量百分比为: 磷酸21%,氧化锌4. 9%,硝酸锌15. 4%,柠檬酸0. 42%,酒石酸0. 35%,钼酸盐0. 56%和余量的水。
5.根据权利要求1或2所述的金属表面磷化液,其特征在于各原料的重量百分比为: 磷酸28%,氧化锌4. 2%,硝酸锌17. 5%,柠檬酸0. 28%,酒石酸0. 14%,钼酸盐0. 7%和余量的水。
CN201010515980A 2010-10-22 2010-10-22 一种常温下可循环使用的锌铁系金属表面磷化液 CN101935832B (zh)