CN103541232A - 一种锦纶迷彩织物的制作工艺 - Google Patents
一种锦纶迷彩织物的制作工艺 Download PDFInfo
- Publication number
- CN103541232A CN103541232A CN201310477476.XA CN201310477476A CN103541232A CN 103541232 A CN103541232 A CN 103541232A CN 201310477476 A CN201310477476 A CN 201310477476A CN 103541232 A CN103541232 A CN 103541232A
- Authority
- CN
- China
- Prior art keywords
- soren
- coating
- nhf
- temperature
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种纺织印染工艺,尤其是一种锦纶迷彩织物的制作工艺。其工艺为:原布缝接→前处理→定型→染底→印花→焙烘→蒸化→后整理拉幅→验收。其印花配方:每100kg色浆中含分散料0.6-1.8kg,酸性料0.01-5.0kg,涂料0.02—0.5kg同浆印花;焙烘:车速35±1米/分,温度165—170℃,蒸化:车速10±1米/分,温度101-105℃,时间:30分钟。后整理用不同助剂具有防水、透气、拒油、抗静电等功能的兼容性,本发明的优点在于生产工序短,色相一致性好,色牢度优良,色泽鲜艳,成本低,以环保染料为主,它非常适合防红外迷彩产品织物面料中较高档次的产品使用。
Description
(一)技术领域
本发明涉及一种纺织印染工艺,具体的说是一种锦纶迷彩织物的制作工艺。
(二)背景技术
目前国内锦纶迷彩织物印制采用分散、酸性、中性、涂料其中的一种染料印制,且存在问题:锦纶用分散染料印花能够印制出均匀性良好的花纹,印花方法简便,也易于拼色,但色泽鲜艳度不够、易偏蓝或偏暗。因湿牢度差而不适应印制深浓色泽,否则沾色严重,湿牢度更差;锦纶用酸性染料印花能够印制出色泽鲜艳、牢度较高、但匀染性差;锦纶用中性染料日晒牢度好,色泽不够鲜艳,遮盖性差,匀染性也差;锦纶用涂料印花能够印制出花纹轮廓清晰,但手感硬,干湿摩牢度差。
(三)发明内容
本发明的目的在于提供一种分散.酸性.涂料三种染料同浆印花.生产工序短,色相一致性好,色牢度优良.色泽丰满,成本低的一种锦纶迷彩织物的制作工艺。
为实现上述目的本发明是这样来实现的,本发明的制作工艺为取原布缝接经以下处理:(1)前处理:车速25±1米/分,轧槽常温,轧槽含量为烧碱40-45g/L,双氧水8±1g/L,履带温度95—100℃,堆置时间45分,水洗第1—4格65-70℃,第5格60-65℃,全部活流水;(2)定型:车速50±1米/分,温度1-8室185-190℃,落布幅宽155—155.5cm,落布温度低于45℃;(3)染底:车速25±1米/分,多浸一轧染液→两组红外线→两组预烘→烘干落布;(4)印花:车速25±1米/分,烘干温度120—130℃,其中(a)浅斑:150%分散黄棕S-4RL:0.6kg,100%色派伦绿S—GLN:0.42kg,100%依索伦黄NHF—S:0.57kg,100%依索伦红NHF—S:0.01kg,100%涂料绿FFB:0.03kg,100%涂料黑FBRN:0.02kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg;(b)绿斑:150%分散黄棕S-4RL:1.6kg,100%天龙藏青AMF:0.42kg,100%天龙绿M—BW:4.2kg,100%依索伦黄NHF-S:2.1kg,涂料绿FFB:0.05kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg;(c)棕斑:200%分散黑P—G:0.8kg,100%依索伦黄NHF—S:1.2kg,100%依索伦棕NHF—S:2.0kg,100%依索伦红NHF—S:0.45kg,100%依索伦黑2S—LD:0.22kg,100%涂料红棕HF—G:0.03kg,100%涂料黑FBRN:0.13kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg;(d)黑斑:100%依索伦黑2S—LD:5.0kg,200%分散黑P-G:1.8kg,100%色派伦绿S—GLN:3.5kg,100%依索伦黄NHF—S:0.5kg,100%涂料黄FG:0.5kg,粘合剂WH:10kg,硫酸铵;2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg;(5)焙烘:车速35±1米/分,温度165-170℃;(6)蒸化:车速10±1米/分,温度101-105℃,时间30分钟;(6)皂洗:车速25±1米/分,温度皂煮80—90℃,水洗75—80℃,最后一格60—65℃,全部活流水;(10)后整理拉幅:车速20—25米/分,温度180—185℃,落布幅宽153—153.5cm。
本发明的优点在于解决了锦纶织物目前采用分散.酸性.涂料单独一种染料印花存在的色泽.牢度.匀染性.手感等问题,本发明采用的酸性染料+涂料+分散染料的同浆印花,为色相一致性好,色牢度优良,色泽丰满,成本低的一种迷彩织物的制作工艺。它非常适合迷彩产品织物面料中较高档次的产品使用。
(四)具体实施例
下面结合实施例对本发明作进一步祥细的说明:
本发明是将具体的一个产品如何制作出来需分别进行详细的描述-注意这里的描述为制作工艺。
1000D锦纶林地迷彩牛津纺(63“)
该产品在700-1200nm波长范围内具有防红外功能.
工艺流程:原布缝接→前处理→定型→染底→印花→焙烘→蒸化→后整理拉幅→验收。
1、原布缝接:针距密度:24—26针/10cm,缝接平、直、齐。
2、前处理:车速25±1米/分,轧槽常温,轧槽含量:烧碱40—45g/L,双氧水8±1g/L,履带温度95-100℃,堆置时间45分,水洗:第1-4格65—70℃,第5格60—65℃,全部活流水。
3、定型:车速:50±1米/分,温度1-8室185-190℃,落布幅宽155—155.5cm,落布温度低于45℃。
4、染底:车速25±1米/分,多浸一轧染液→两组红外线→两组预烘→烘干落布。(配方:天龙藏青AMF:1.0kg;依索伦黄NHF-S:3.0kg,依索伦红NHF-S:0.1kg/5001)。
5、印花:车速:25±1米/分,烘干温度:120—130℃。(a)浅斑:150%分散黄棕S-4RL:0.6kg,100%色派伦绿S-GLN:0.42kg,100%依索伦黄NHF-S:0.57kg,100%依索伦红NHF—S:0.01kg,100%涂料绿FFB:0.03kg,100%涂料黑FBRN:0.02kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg。(b)绿斑:150%分散黄棕S-4RL:1.6kg,100%天龙藏青AMF:0.42kg,100%天龙绿M—BW:4.2kg,100%依索伦黄NHF—S:2.1kg,100%涂料绿FFB:0.05kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg。(c)棕斑:200%分散黑P—G:0.8kg,100%依索伦黄NHF—S:1.2kg,100%依索伦棕NHF—S:2.0kg,100%依索伦红NHF—S:0.45kg,100%依索伦黑2S—LD:0.22kg,100%涂料红棕HF—G:0.03kg,100%涂料黑FBRN:0.13kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg。(d)黑斑:100%依索伦黑2S—LD:5.0kg,200%分散黑P—G:1.8kg,100%色派伦绿S—GLN:3.5kg,100%依索伦黄NHF—S:0.5kg,100%涂料黄FG:0.5kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg。
6、焙烘:车速35±1米/分,温度165-170℃。
7、蒸化:车速10±1米/分,温度101-105℃,时间:30分钟。
8、皂洗:车速25±1米/分,温度:皂煮:80-90℃,水洗:75—80℃,最后一格60—65℃,全部活流水。
10、后整理拉幅:车速20-25米/分,温度180—185℃,落布幅宽153—153.5cm。(配方:防水、拒油、抗静电剂XQ-608A:50g/L)。
Claims (3)
1.一种锦纶迷彩织物的制作工艺,其特征在于取原布缝接经以下处理:(1)前处理:车速25±1米/分,轧槽常温,轧槽含量为烧碱40—45g/L,双氧水8±1g/L,履带温度95—100℃,堆置时间45分,水洗第1—4格65—70℃,第5格60-65℃,全部活流水;(2)定型:车速50±1米/分,温度1-8室185—190℃,落布幅宽155—155.5cm,落布温度低于45℃;(3)染底:车速25±1米/分,多浸一轧染液→两组红外线→两组预烘→烘干落布;(4)印花:车速25±1米/分,烘干温度120—130℃;(5)焙烘:车速35±1米/分,温度165—170℃;(6)蒸化:车速10±1米/分,温度101-105℃,时间30分钟;(6)皂洗:车速25±1米/分,温度皂煮80—90℃,水洗75—80℃,最后一格60—65℃,全部活流水;(10)后整理拉幅:车速20—25米/分,温度180—185℃,落布幅宽153-153.5cm。
2.根据权利要求1所示的一种锦纶迷彩织物的制作工艺,其特征在于所述的印花为同浆印花,即:酸性染料+涂料+分散染料;其酸性染料为:每100kg色浆中含依索伦黄NHF—S:0.5—2.1kg,依索伦红NHF—S:0.01-0.45kg,依索伦黑2S—LD:0.22—5.0kg,索伦棕NHF-S:0—2.0kg,色派伦绿S—GLN:0.42—3.5kg,天龙藏青AMF:0—0.42kg,天龙绿M—BW:0—4.2kg。涂料为:每100kg色浆中含涂料黑FBRN:0.02—0.13kg,涂料绿FFB:0.03—0.05kg,涂料红棕HF—G:0—0.03kg,涂料黄FG:0—0.05kg;分散染料为:每100kg色浆中含分散黄棕S-4R:0.6—1.6kg、分散黑P-G:0.8-1.8kg。
3.根据权利要求1或2所示的一种锦纶迷彩织物的制作工艺,其特征在于所述的印花有(a)浅斑:150%分散黄棕S-4RL:0.6kg,100%色派伦绿S-GLN:0.42kg,100%依索伦黄NHF—S:0.57kg,100%依索伦红NHF—S:0.01kg,100%涂料绿FFB:0.03kg,100%涂料黑FBRN:0.02kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg;(b)绿斑:150%分散黄棕S-4RL:1.6kg,100%天龙藏青AMF:0.42kg,100%天龙绿M—BW:4.2kg,100%依索伦黄NHF—S:2.1kg,100%涂料绿FFB:0.05kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,剩余加水配置至100kg;(c)棕斑:200%分散黑P—G:0.8kg,100%依索伦黄NHF—S:12kg,100%依索伦棕NHF-S:2.0kg,100%依索伦红NHF—S:0.45kg,100%依索伦黑2S—LD:0.22kg,100%涂料红棕HF—G:0.03kg,100%涂料黑FBRN:0.13kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg;(d)黑斑:,100%依索伦黑2S—LD:5.0kg,200%分散黑P—G:1.8kg,100%色派伦绿S—GLN:3.5kg,100%依索伦黄NHF—S:0.5kg,100%涂料黄FG:0.5kg,粘合剂WH:10kg,硫酸铵:2.0kg,尿素:5.0kg,增稠剂FS-80E:4kg,加水配置至100kg。