CN103466688A - 一种制备ZnS纳米片的方法 - Google Patents

一种制备ZnS纳米片的方法 Download PDF

Info

Publication number
CN103466688A
CN103466688A CN2013104258094A CN201310425809A CN103466688A CN 103466688 A CN103466688 A CN 103466688A CN 2013104258094 A CN2013104258094 A CN 2013104258094A CN 201310425809 A CN201310425809 A CN 201310425809A CN 103466688 A CN103466688 A CN 103466688A
Authority
CN
China
Prior art keywords
zns
preparation
mixture
product
fused salt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013104258094A
Other languages
English (en)
Other versions
CN103466688B (zh
Inventor
林璋
李冬松
黄丰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Institute of Research on the Structure of Matter of CAS
Original Assignee
Fujian Institute of Research on the Structure of Matter of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Institute of Research on the Structure of Matter of CAS filed Critical Fujian Institute of Research on the Structure of Matter of CAS
Priority to CN201310425809.4A priority Critical patent/CN103466688B/zh
Publication of CN103466688A publication Critical patent/CN103466688A/zh
Application granted granted Critical
Publication of CN103466688B publication Critical patent/CN103466688B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种ZnS纳米片的制备方法。该方法将ZnS前体和熔盐混合，经高温加热处理后获得ZnS纳米片。本方法反应条件温和，工艺简单，节省时间，成本低廉，所得纳米片产物厚度均匀，表面积大，可宏量生产具有潜在的工业化前景。

Description

一种制备ZnS纳米片的方法
技术领域
本发明涉及一种二维半导体纳米材料的制备方法，特别涉及一种ZnS纳米片材料的制备方法。
背景技术
ZnS是一种具有重要应用价值的宽禁带半导体材料,具有优良的荧光效应及电致发光功能，在电学、磁学、光学、力学和催化等领域呈现出许多优异的性能。由于这些优异的性质和广泛的应用,人们探索了许多的方法和技术来合成这种重要的材料。目前合成ZnS微纳米材料的方法主要有：气相沉积法、模板法和水热法等,这些方法往往存在着尺寸形貌难于控制，产率不高，高温反应条件苛刻，制备工艺技术复杂、成本高等缺点，这些潜在的困难和阻碍使硫化锌的大规模实用前景令人堪忧。
相比以上合成方法,熔盐合成法具有转化率高、工艺简单、少污染、低能耗等优点。并且,熔盐体系能够提供一个液相的环境,在较高的反应温度下各反应物的扩散系数提高，可以使反应物迅速发生反应。同时,熔盐法制备硫化物时,晶体在整个生长过程中可以在液相条件下进行,晶体生长形态容易控制,产品纯度也较高。而且所用的熔盐易溶于水等溶液中,易于筛洗。因此,熔盐法已经成为控制合成不同形貌微纳米材料的优选方法之一,为研究其形貌及物性关联,最终设计功能微纳米材料奠定基础。
发明内容
本发明的目的在于针对现有技术的不足，提供一种制备ZnS纳米片的材料方法。本发明的方法反应条件温和、工艺简单，节省时间，成本低廉，是一种制备ZnS纳米片材料的理想方法。
本发明中的目的通过以下技术方案实现，一种ZnS纳米片的制备方法，该方法按如下步骤进行：
1）ZnS前体和熔盐均匀混合后，经高温热处理制备出ZnS纳米片。
2）在步骤1）中所述的熔盐为强碱和卤化物的混合物。
3）在步骤1）中所述的ZnS前体可以为：ZnS粉末，ZnCl2和Na2S·9H2O的混合物，ZnSO4·7H2O和Na2S·9H2O的混合物，Zn(NO3)2·6H2O和Na2S·9H2O的混合物。
4）在步骤2）中所述强碱为NaOH、KOH、CsOH中的一种或其组合。
5）在步骤2）中所述卤化物可以选用碘化物、溴化物或氯化物。
6）在步骤1）中所述熔盐和卤化物反应的温度为180-300℃。
7）在步骤1）中所述熔盐和卤化物的反应时间为5-24小时。
附图说明
图1为实施例1中产物的扫描电镜图，其中标尺为500nm。
图2为实施例2中产物的扫描电镜图，其中标尺为500nm。
图3为实施例3中产物的扫描电镜图，其中标尺为500nm。
图4为实施例1中产物的X射线衍射谱图。
图5为实施例2中产物的X射线衍射谱图。
图6为实施例3中产物的X射线衍射谱图。
具体实施方式
下面通过具体实施例的阐述，进一步阐明本发明的实质性特点和显著的进步。
实施例1
取3nm ZnS粉末0.3g，NaOH3.24g，NaI2.85g，将这三种化合物均匀混合，置于聚四氟乙烯烧杯中。然后将混合物置于250℃马弗炉中，加热12小时。将产物取出后冷却至室温，用去离子水将熔盐溶解后，再用去离子水和无水乙醇将产物反复洗涤，然后将产物在室温下干燥获得片状ZnS纳米材料。
实施例2
取100nm ZnS粉末0.3g，NaOH3.24g，KOH2.25g，将这三种化合物均匀混合，置于聚四氟乙烯烧杯中。然后将混合物置于180℃马弗炉中，加热24小时。将产物取出后冷却至室温，用去离子水将熔盐溶解后，再用去离子水和无水乙醇将产物反复洗涤，然后将产物在室温下干燥获得片状ZnS纳米材料。
实施例3
取ZnCl20.41g，Na2S·9H2O0.72g，NaOH3.24g，NaCl8.76g，将这四种化合物均匀混合，置于聚四氟乙烯烧杯中。然后将混合物置于200℃马弗炉中，加热12小时。将产物取出后冷却至室温，用去离子水将熔盐溶解后，再用去离子水和无水乙醇将产物反复洗涤，然后将产物在室温下干燥获得片状ZnS纳米材料。
应当指出的是，以上所述的实施实例只是用3个例子来说明本发明，它不应是对本发明的限制，对本领域普通技术人员来说，对本发明可以根据上述说明加以改进和变换，而所有这些改进和变换都应属于本发明所附权利要求保护范围。

Claims (7)

1.一种ZnS纳米片的制备方法，包括以下步骤：将ZnS前体和熔盐均匀混合后，经高温热处理制备出ZnS纳米片。
2.根据权利要求1所述的制备方法，其特征在于：所用熔盐为强碱和卤化物的混合物。
3.根据权利要求1所述的制备方法，其特征在于：所用ZnS前体为：ZnS粉末、ZnCl2和Na2S·9H2O的混合物，ZnSO4·7H2O和Na2S·9H2O的混合物，Zn(NO3)2·6H2O和Na2S·9H2O的混合物。
4.根据权利要求1所述的制备方法，其特征在于：加热的温度为180-300。℃
5.根据权利要求1所述的制备方法，其特征在于：加热的时间为5-24小时。
6.根据权利要求2所述的制备方法，其特征在于：所述强碱为NaOH、KOH、CsOH中的一种或其组合。
7.根据权利要求2所述的制备方法，其特征在于：所述卤化物选用碘化物、溴化物、氯化物。
CN201310425809.4A 2013-09-17 2013-09-17 一种制备ZnS纳米片的方法 Active CN103466688B (zh)