CN103436037A - 一种汽车高压点火线用氟硅/硅橡胶并用胶的制备方法 - Google Patents
一种汽车高压点火线用氟硅/硅橡胶并用胶的制备方法 Download PDFInfo
- Publication number
- CN103436037A CN103436037A CN2013104229852A CN201310422985A CN103436037A CN 103436037 A CN103436037 A CN 103436037A CN 2013104229852 A CN2013104229852 A CN 2013104229852A CN 201310422985 A CN201310422985 A CN 201310422985A CN 103436037 A CN103436037 A CN 103436037A
- Authority
- CN
- China
- Prior art keywords
- rubber
- silicon
- silicon rubber
- parts
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
邵氏硬度 | 拉伸强度/MPa | 扯断伸长率/% | 耐电击穿性/ kV/mm | |
实施例1 | 71 | 8.2 | 389 | 21 |
实施例2 | 72 | 8.4 | 391 | 21 |
实施例3 | 73 | 7.5 | 356 | 23 |
实施例4 | 72 | 7.9 | 363 | 20 |
对比例1 | 71 | 7.4 | 349 | 16 |
对比例2 | 75 | 5.1 | 232 | 22 |
Claims (9)