CN101593584A - 一种防鸟害氟硅绝缘护套的生产方法 - Google Patents

一种防鸟害氟硅绝缘护套的生产方法 Download PDF

Info

Publication number
CN101593584A
CN101593584A CNA2009100748204A CN200910074820A CN101593584A CN 101593584 A CN101593584 A CN 101593584A CN A2009100748204 A CNA2009100748204 A CN A2009100748204A CN 200910074820 A CN200910074820 A CN 200910074820A CN 101593584 A CN101593584 A CN 101593584A
Authority
CN
China
Prior art keywords
production method
fluorine
bird damage
damage resistant
insulated sleeve
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100748204A
Other languages
English (en)
Other versions
CN101593584B (zh
Inventor
陈原
卢毅
陈泓
张跃男
宋志强
宋福如
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEBEI GUIGU CHEMICAL RESEARCH INSTITUTE
NINGXIA ELECTRIC POWER Co
North China Electric Power Research Institute Co Ltd
Original Assignee
HEBEI GUIGU CHEMICAL RESEARCH INSTITUTE
NINGXIA ELECTRIC POWER Co
North China Electric Power Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEBEI GUIGU CHEMICAL RESEARCH INSTITUTE, NINGXIA ELECTRIC POWER Co, North China Electric Power Research Institute Co Ltd filed Critical HEBEI GUIGU CHEMICAL RESEARCH INSTITUTE
Priority to CN2009100748204A priority Critical patent/CN101593584B/zh
Publication of CN101593584A publication Critical patent/CN101593584A/zh
Application granted granted Critical
Publication of CN101593584B publication Critical patent/CN101593584B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种防鸟害氟硅绝缘护套的生产方法，其生产方法为：将10－30％的含氟的聚二甲基硅氧烷、40－50％的含乙烯基的聚二甲基硅氧烷、20－40％的增强填料二氧化硅、耐电蚀损填料氢氧化铝和1－5％的颜料的混合物在70－120℃、压力≤0.2Mpa的密炼机中辊炼1小时，在经密炼机辊炼过的混合物中加入1－3％的硫化剂并混合均匀，再置于开炼机上辊炼1小时进行混炼，然后将经开炼机混炼过的含硫化剂的混合物返炼，经挤压成型机压延挤压成型，最后在180℃的硫化炉中二段硫化2小时，即得氟硅绝缘护套，将氟硅绝缘护套切割成一定长度，使用时用粘合胶密封榫扣。它是一种高绝缘的防鸟害氟硅绝缘护套的生产方法。

Description

一种防鸟害氟硅绝缘护套的生产方法
技术领域
本发明涉及一种硅氟橡胶绝缘护套，尤其是一种用在高压输电线路防鸟害闪络跳闸的氟硅绝缘护套的生产方法。
背景技术
目前，输变电线路因鸟害造成的跳闸停电事故发生频繁，近年随国家电力工业的大发展，输电线路大幅度增加。华北电网、西北电网鸟害跳闸事故已占非正常停电的8-12％，造成巨大损失。现行使用的防鸟刺、驱鸟器等技术措施不能完全解决，复杂生活区异物相间搭接等潜在危害也需要一种高绝缘的技术措施。
发明内容
本发明所要解决的技术问题是提供一种防鸟害氟硅绝缘护套的生产方法。
本发明解决其技术问题的技术方案是：
一种防鸟害氟硅绝缘护套的生产方法，其组成成分为：含氟的聚二甲基硅氧烷10-30％，含乙烯基的聚二甲基硅氧烷40-50％，二氧化硅增强填料20-40％，耐电蚀损填料氢氧化铝20-40％，硫化剂1-3％，防老化剂0.5-1％，颜料1-5％，其制备方法为：将10-30％的含氟的聚二甲基硅氧烷、40-50％的含乙烯基的聚二甲基硅氧烷、20-40％的增强填料二氧化硅、耐电蚀损填料氢氧化铝和1-5％的颜料的混合物在70-120℃、压力≤0.2Mpa的密炼机中辊炼1小时，在经密炼机辊炼过的混合物中加入1-3％的硫化剂并混合均匀，再置于开炼机上辊炼1小时进行混炼，然后将经开炼机混炼过的含硫化剂的混合物返炼，经挤压成型机压延挤压成型，最后在180℃的硫化炉中二段硫化2小时，即得氟硅绝缘护套，将氟硅绝缘护套切割成一定长度，使用时用粘合胶密封榫扣。
本发明解决其技术问题的技术方案还可以是：
本发明所述的硫化剂的商品名为双-25，化学名称为2.5-二甲基-2.5-二(叔丁基过氧基)己烷。
本发明所述的颜料为三氧化二铁。
本发明所述的防老化剂为氟硅聚合物。
本发明所述的二氧化硅增强填料的商品名为白碳黑。
本发明所述的粘合胶为室温硫化氟硅橡胶。
本发明所述的氟硅绝缘护套的长度为1.5M。
本发明的有益效果是：
①、优异的绝缘性能，介电强度达到20KV/mm以上，耐电蚀损性TMA4.5级，阻燃性达FV-0级，持久的憎水迁移性，耐污闪电压高、抗电弧。在异常情况下能有效保护输电线路不拉弧、放电；②、机械强度高达4.0Mpa，耐侯性强、耐臭氧、耐酸、碱、盐和化学腐蚀，使用寿命达20年；③适用的榫扣式粘合橡胶软管结构，应用方便、安装快捷，不影响运行维护，满足输变电线路防鸟害的要求。
具体实施方式
一种防鸟害氟硅绝缘护套的生产方法，其组成成分为：含氟的聚二甲基硅氧烷10-30％，含乙烯基的聚二甲基硅氧烷40-50％，二氧化硅增强填料20-40％，耐电蚀损填料氢氧化铝20-40％，硫化剂1-3％，防老化剂0.5-1％，颜料1-5％，其制备方法为：将10-30％的含氟的聚二甲基硅氧烷、40-50％的含乙烯基的聚二甲基硅氧烷、20-40％的增强填料二氧化硅、耐电蚀损填料氢氧化铝和1-5％的颜料的混合物在70-120℃、压力≤0.2Mpa的密炼机中辊炼1小时，在经密炼机辊炼过的混合物中加入1-3％的硫化剂并混合均匀，再置于开炼机上辊炼1小时进行混炼，然后将经开炼机混炼过的含硫化剂的混合物返炼，经挤压成型机压延挤压成型，最后在180℃的硫化炉中二段硫化2小时，即得氟硅绝缘护套，将氟硅绝缘护套切割成一定长度，使用时用粘合胶密封榫扣。
所述的硫化剂的商品名为双-25，化学名称为2.5-二甲基-2.5-二(叔丁基过氧基)己烷。
所述的颜料为三氧化二铁。
所述的防老化剂为氟硅聚合物。
所述的二氧化硅增强填料的商品名为白碳黑。
所述的粘合胶为室温硫化氟硅橡胶。
所述的氟硅绝缘护套的长度为1.5M。

Claims (7)

1、一种防鸟害氟硅绝缘护套的生产方法，其特征在于：其组成成分为：含氟的聚二甲基硅氧烷10-30％，含乙烯基的聚二甲基硅氧烷40-50％，二氧化硅增强填料20-40％，耐电蚀损填料氢氧化铝20-40％，硫化剂1-3％，防老化剂0.5-1％，颜料1-5％，其制备方法为：将10-30％的含氟的聚二甲基硅氧烷、40-50％的含乙烯基的聚二甲基硅氧烷、20-40％的增强填料二氧化硅、耐电蚀损填料氢氧化铝和1-5％的颜料的混合物在70-120℃、压力≤0.2Mpa的密炼机中辊炼1小时，在经密炼机辊炼过的混合物中加入1-3％的硫化剂并混合均匀，再置于开炼机上辊炼1小时进行混炼，然后将经开炼机混炼过的含硫化剂的混合物返炼，经挤压成型机压延挤压成型，最后在180℃的硫化炉中二段硫化2小时，即得氟硅绝缘护套，将氟硅绝缘护套切割成一定长度，使用时用粘合胶密封榫扣。
2、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的硫化剂的商品名为双-25，化学名称为2.5-二甲基-2.5-二(叔丁基过氧基)己烷。
3、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的颜料为三氧化二铁。
4、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的防老化剂为氟硅聚合物。
5、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的二氧化硅增强填料的商品名为白碳黑。
6、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的粘合胶为室温硫化氟硅橡胶。
7、根据权利要求1所述的一种防鸟害氟硅绝缘护套的生产方法，其特征在于：所述的氟硅绝缘护套的长度为1.5M。
CN2009100748204A 2009-07-03 2009-07-03 一种防鸟害氟硅绝缘护套的生产方法 Active CN101593584B (zh)