CN114231038A - 一种复方硅橡胶雄黄驱鸟型材及其制备方法 - Google Patents
一种复方硅橡胶雄黄驱鸟型材及其制备方法 Download PDFInfo
- Publication number
- CN114231038A CN114231038A CN202111591543.1A CN202111591543A CN114231038A CN 114231038 A CN114231038 A CN 114231038A CN 202111591543 A CN202111591543 A CN 202111591543A CN 114231038 A CN114231038 A CN 114231038A
- Authority
- CN
- China
- Prior art keywords
- realgar
- parts
- bird
- silicon rubber
- section bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于硅橡胶技术领域，具体涉及一种复方硅橡胶雄黄驱鸟型材及其制备方法，以生胶为基础料，按照重量份数计，每1000份生胶中添加有30份雄黄矿粉。本发明制备得到的复方硅橡胶雄黄驱鸟型材，具有高柔韧性，绝缘性能良好，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃‑380℃，材料耐紫外线照射、憎水性好、耐老化，适应户外严酷环境使用。利用其独特的配方气味，驱防各种鸟类等小动物，远离被复方硅橡胶雄黄驱鸟型材保护的电气设备，进而实现电力设备安全运行，避免发生因鸟类等小动物造成的故障。
Description
技术领域
本发明属于硅橡胶技术领域，具体涉及一种复方硅橡胶雄黄驱鸟型材及其制备方法。
背景技术
鸟类等小动物给电力系统造成的威害，一年四季困扰影响着供用电设备安全运行，依据人类世界和动物多样性共存原则，成为整个电力系统安全运行的技术难题，难点主要是鸟具有鲜明的低级和高级生命特点所不具备生存特点。鸟可以展翅飞翔，生存空间无限广阔，鸟类不以时空，鸟为食忘，鸟为繁衍，展现自己的生命规律。其它小动物如蛇，它会季节性休眠，爬行是做拿手的无腿无手功夫，几十米，甚至几百米外，它能嗅到温度的变化，嗅到食物的存在，即便是在有电场存在，有一定高度的杆塔上，有鸟巢和鸟蛋存在，也能爬行将其吞下，能够顺着杆塔拉线和杆身爬行上去，也能顺着导线绝缘子高超爬行，也时常因此电气设备经常造成设备故障，再如老鼠，虽然老鼠身小，天生的打洞本领，牙齿尖利，经常钻到变压器室内，开关柜内，也时常出没的电缆沟内，经常造成故障发生。
目前，主流的防鸟装置如防鸟刺、防鸟挡板、防鸟风车等装置从材料意义上讲，已无法适应现阶段鸟害和动物防护要求。在杆塔强电场及环境严酷恶劣的条件下，现有的防鸟材料和装置存在材料运行的时间短、维护成本高等难题。
发明内容
本发明的目的在于提供一种复方硅橡胶雄黄驱鸟型材及其制备方法，利用其独特的配方气味，驱防各种鸟类等小动物，远离被复方硅橡胶雄黄驱鸟型材保护的电气设备，进而实现电力设备安全运行，避免发生因鸟类等小动物造成的故障。
本发明所述的一种复方硅橡胶雄黄驱鸟型材，以生胶为基础料，按照重量份数计，每1000份生胶中添加有30份雄黄矿粉。
本发明中，雄黄矿粉应用其作为添加剂使用。雄黄，四硫化四砷，是砷的硫化物，化学式AS4S4，粉末状质软，性脆，当加热到一定温度后在空气中被氧化，本发明作为添加剂掺入到生胶中，由于雄黄不容于水，也不溶于生胶。合成出新的型材利用其独特的配方气味，驱防各种鸟类等小动物，实现人与动物和谐共存。
作为优选方案，一种复方硅橡胶雄黄驱鸟型材，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料200～300份、低收缩树脂300～500份、引发剂50～100份、色浆50～100份、雄黄矿粉30份、硫化剂150～200份。
其中，作为优选方案，所述的生胶为乙烯基封端或甲基封端线性聚有机硅氧烷，其分子量为400000-800000g/mol，乙烯基含量为0.03-5mol％。
作为优选方案，所述的补强填料为沉淀法白炭黑、气相法白炭黑、硅藻土、超细硅微粉、纳米碳酸钙、石英粉、硅酸锆、钛白粉、高岭土中的一种或几种。
作为优选方案，所述的低收缩树脂为聚醋酸乙烯酯。
作为优选方案，所述的引发剂为纳米级光引发剂，具体为光引发剂819、光引发剂369、光引发剂500中的一种或多种。
作为优选方案，所述的硫化剂为过氧化苯甲酰、过苯甲酸叔丁酯及过氧化二异丙苯的中的一种或几种。
本发明还提供了一种复方硅橡胶雄黄驱鸟型材的制备方法，按照以下步骤制备而成：
1)将生胶、补强填料、低收缩树脂、引发剂、色浆、雄黄矿粉和硫化剂进行混炼，再将混炼料在金属模具中加压加热成型和硫化，其压力为50公斤/cm2，温度为120～130℃，时间为10～30分钟；
2)将硅橡皮从金属模具中取出后，放入烘箱内，于200～250℃下烘烤3至24小时，使橡皮进一步硫化，同时使有机过氧化物分解挥发。
本发明所具有的优点是：
(1)本发明制备得到的复方硅橡胶雄黄驱鸟型材，具有高柔韧性，绝缘性能良好，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃-380℃，材料耐紫外线照射、憎水性好、耐老化，适应户外严酷环境使用。
(2)其优良的绝缘特性，加压成型各种各类电压等级的绝缘子串用的防鸟罩、防鸟伞裙、防鸟护套，满足杆塔不同横担形式的防鸟挡板。加压成型满足中低压变压器出线及开关、刀闸侧护罩，防止因小动物诱发的短路。加压成型满足各种杆塔、拉线护管护套防治蛇类攀爬杆塔。
(3)满足电力行业特高压线路、输配电及中低压线路，不同电压等级线路，户外设备各种形式的防鸟、防小动物的型材，通过材料本身的专有特性，有效的实现满足生物多样性的环境要求。
具体实施方式
下面将结合实施例对本发明做进一步说明。
实施例1：
一种复方硅橡胶雄黄驱鸟型材，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料200份、低收缩树脂300份、引发剂50份、黑色色浆50份、雄黄矿粉30份、硫化剂150份。
其中，所述的生胶为乙烯基封端线性聚有机硅氧烷，其分子量为500000g/mol，乙烯基含量为1mol％。
所述的补强填料为纳米碳酸钙和石英粉按照1：1的混合物。
所述的低收缩树脂为聚醋酸乙烯酯。
所述的引发剂为纳米级光引发剂，具体为光引发剂819。
所述的硫化剂为过氧化苯甲酰。
制备时，按照以下步骤制备而成：
1)将生胶、补强填料、低收缩树脂、引发剂、色浆、雄黄矿粉和硫化剂进行混炼，再将混炼料在金属模具中加压加热成型和硫化，其压力为50公斤/cm2，温度为120℃，时间为20分钟；
2)将硅橡皮从金属模具中取出后，放入烘箱内，于220℃下烘烤24小时，使橡皮进一步硫化，同时使有机过氧化物分解挥发。
本实施例中制备的复方硅橡胶雄黄驱鸟型材物质地均匀，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃-380℃。该型材加工成杆塔用防鸟挡板，摄像机观测周期7天，未发现有鸟类等小动物停留。
实施例2：
一种复方硅橡胶雄黄驱鸟型材，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料250份、低收缩树脂400份、引发剂60份、黑色色浆60份、雄黄矿粉30份、硫化剂180份。
其中，所述的生胶为乙烯基封端线性聚有机硅氧烷，其分子量为500000g/mol，乙烯基含量为1mol％。
所述的补强填料为沉淀法白炭黑。
所述的低收缩树脂为聚醋酸乙烯酯。
所述的引发剂为纳米级光引发剂，具体为光引发剂369。
所述的硫化剂为过苯甲酸叔丁酯。
制备方法同实施例1。
本实施例中制备的复方硅橡胶雄黄驱鸟型材物质地均匀，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃-380℃。该型材加工成杆塔用防鸟挡板，摄像机观测周期7天，未发现有鸟类等小动物停留。
实施例3：
一种复方硅橡胶雄黄驱鸟型材，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料300份、低收缩树脂500份、引发剂90份、黑色色浆80份、雄黄矿粉30份、硫化剂200份。
其中，所述的生胶为乙烯基封端线性聚有机硅氧烷，其分子量为500000g/mol，乙烯基含量为1mol％。
所述的补强填料为超细硅微粉。
所述的低收缩树脂为聚醋酸乙烯酯。
所述的引发剂为纳米级光引发剂，具体为光引发剂819。
所述的硫化剂为过氧化苯甲酰。
制备方法同实施例1。
本实施例中制备的复方硅橡胶雄黄驱鸟型材物质地均匀，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃-380℃。该型材加工成杆塔用防鸟挡板，摄像机观测周期7天，未发现有鸟类等小动物停留。
对比例1：
一种复方硅橡胶型材，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料200份、低收缩树脂300份、引发剂50份、黑色色浆50份、硫化剂150份。
其中，所述的生胶为乙烯基封端线性聚有机硅氧烷，其分子量为500000g/mol，乙烯基含量为1mol％。
所述的补强填料为纳米碳酸钙和石英粉按照1：1的混合物。
所述的低收缩树脂为聚醋酸乙烯酯。
所述的引发剂为纳米级光引发剂，具体为光引发剂819。
所述的硫化剂为过氧化苯甲酰。
制备方法同实施例1。
本实施例中制备的复方硅橡胶雄黄驱鸟型材物质地均匀，绝缘强度大于20kV/㎜，绝缘电阻大于1000ΜΩ，阻燃性LO1>35％，材料耐高温环境适应50℃-380℃。该型材加工成杆塔用防鸟挡板，由于该挡板中未添加有雄黄矿粉，不具备驱鸟特性，摄像机观测周期7天，发现有鸟类等小动物停留172次。
Claims (8)
1.一种复方硅橡胶雄黄驱鸟型材，其特征在于，以生胶为基础料，按照重量份数计，每1000份生胶中添加有30份雄黄矿粉。
2.根据权利要求1所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，按照重量份数计，由以下原料制备而成：生胶1000份、补强填料200～300份、低收缩树脂300～500份、引发剂50～100份、色浆50～100份、雄黄矿粉30份、硫化剂150～200份。
3.根据权利要求2所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，所述的生胶为乙烯基封端或甲基封端线性聚有机硅氧烷，其分子量为400000-800000g/mol，乙烯基含量为0.03-5mol％。
4.根据权利要求2所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，所述的补强填料为沉淀法白炭黑、气相法白炭黑、硅藻土、超细硅微粉、纳米碳酸钙、石英粉、硅酸锆、钛白粉、高岭土中的一种或几种。
5.根据权利要求2所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，所述的低收缩树脂为聚醋酸乙烯酯。
6.根据权利要求2所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，所述的引发剂为纳米级光引发剂，具体为光引发剂819、光引发剂369、光引发剂500中的一种或多种。
7.根据权利要求2所述的一种复方硅橡胶雄黄驱鸟型材，其特征在于，所述的硫化剂为过氧化苯甲酰、过苯甲酸叔丁酯及过氧化二异丙苯的中的一种或几种。
8.一种权利要求1所述的复方硅橡胶雄黄驱鸟型材的制备方法，其特征在于，按照以下步骤制备而成：
1)将生胶、补强填料、低收缩树脂、引发剂、色浆、雄黄矿粉和硫化剂进行混炼，再将混炼料在金属模具中加压加热成型和硫化，其压力为50公斤/cm2，温度为120～130℃，时间为10～30分钟；
2)将硅橡皮从金属模具中取出后，放入烘箱内，于200～250℃下烘烤3至24小时，使橡皮进一步硫化，同时使有机过氧化物分解挥发。