CN103434067A - 单体经编布汽车顶蓬的制造工艺 - Google Patents
单体经编布汽车顶蓬的制造工艺 Download PDFInfo
- Publication number
- CN103434067A CN103434067A CN2013103452735A CN201310345273A CN103434067A CN 103434067 A CN103434067 A CN 103434067A CN 2013103452735 A CN2013103452735 A CN 2013103452735A CN 201310345273 A CN201310345273 A CN 201310345273A CN 103434067 A CN103434067 A CN 103434067A
- Authority
- CN
- China
- Prior art keywords
- warp knitting
- knitting cloth
- automobile ceiling
- manufacturing process
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种单体经编布汽车顶蓬的制造工艺,特征是,包括以下工艺步骤:(1)材料铺放:将经编布面料在面料铺放台上铺平;(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为150~300℃,烘温时间为30~90秒;(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的经编布面料输送到聚氨酯复合板上方,压制成型得到汽车顶蓬半成品;成型压力为4~6MPa,成型时间为40~80秒;(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为40000~50000psi,切割气压为0.4~0.7MPa。本发明产品质地轻,符合现代汽车轻量化,高性能的要求。
Description
技术领域
本发明涉及一种汽车顶蓬的制造工艺,尤其是一种单体经编布汽车顶蓬的制造工艺,属于汽车内饰件技术领域。
背景技术
汽车顶蓬具有装饰、吸音、隔音、隔热等特点,在越来越追求高性能,环保型,轻量化的时代,汽车内饰成为人们选车的一个重要因素,因此对汽车内饰件的要求越来越高。目前顶蓬面料主要包括针织复合面料及无纺复合面料。现有复合面料主要存在以下问题:1、易脏污;2、产品重量大,不利于整车轻量化;3、面料延伸率较差,导致加工成型时行腔较深处面料贴不牢,产生起泡等现象;4、单体面料通过火焰或者胶水与PU复合成型,易引起VOC不合格,不能满足主机厂技术要求;5、对于无纺复合面料,外观性较差;6、成本高。
而经编布是通过一种经编纺织工艺针织或编织而成,具有延伸率高、外观性好、价格低廉等有点。
发明内容
本发明的目的是克服现有技术中存在的不足,提供一种单体经编布汽车顶蓬的制造工艺,产品质地轻,符合现代汽车轻量化,高性能的要求。
按照本发明提供的技术方案,一种单体经编布汽车顶蓬的制造工艺,其特征是,包括以下工艺步骤:
(1)材料铺放:将经编布面料在面料铺放台上铺平;
(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为150~300℃,烘温时间为30~90秒;
(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的经编布面料输送到聚氨酯复合板上方,压制成型得到汽车顶蓬半成品;成型压力为4~6MPa,成型时间为40~80秒;
(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为40000~50000psi,切割气压为0.4~0.7MPa。
所述聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜。
步骤(3)中,经编布面料与聚氨酯复合板的PE膜一侧接触。
所述经编布面料的克重为100~300g/㎡。
所述聚氨酯复合板的克重为700~1000g/㎡。
所述经编布面料采用涤纶经编布面料。
本发明与已有技术相比具有以下优点:(1)本发明生产的汽车顶蓬,重量轻,成型加工容易,采用经编布面料解决了现有汽车顶篷面料的不耐脏污及VOC不合格问题;(2)外观性好,能够很好地满足主机厂的技术要求和客户使用要求,符合现代汽车轻量化、高性能的要求;(3)本发明采用的经编布面料不需要经过火焰或者胶水复合成型,减少了中间环节一次成型,减少了对环境的污染,符合环保要求。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
本发明中所使用的聚氨酯复合板为市售的汽车顶棚用PU复合板材,在本发明实施例中所采用的为无锡吉兴木桥高分子材料科技有限公司生产的汽车顶棚PU复合板材;该聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜。
实施例一:一种单体经编布汽车顶蓬的制造工艺,包括以下工艺步骤:
(1)材料铺放:将涤纶经编布面料在面料铺放台上铺平,涤纶经编布面料的克重为100g/㎡;
(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为150℃,烘温时间为90秒;所述聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜;所述聚氨酯复合板的克重为700g/㎡;
(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的涤纶经编布面料输送到聚氨酯复合板上方,涤纶经编布面料与聚氨酯复合板的PE膜一侧接触,压制成型得到汽车顶蓬半成品;成型压力为4MPa,成型时间为80秒;
(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为40000psi,切割气压为0.4MPa。
实施例二:一种单体经编布汽车顶蓬的制造工艺,包括以下工艺步骤:
(1)材料铺放:将涤纶经编布面料在面料铺放台上铺平,涤纶经编布面料的克重为300g/㎡;
(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为300℃,烘温时间为90秒;所述聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜;所述聚氨酯复合板的克重为1000g/㎡;
(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的涤纶经编布面料输送到聚氨酯复合板上方,涤纶经编布面料与聚氨酯复合板的PE膜一侧接触,压制成型得到汽车顶蓬半成品;成型压力为6MPa,成型时间为40秒;
(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为50000psi,切割气压为0.7MPa。
实施例三:一种单体经编布汽车顶蓬的制造工艺,包括以下工艺步骤:
(1)材料铺放:将涤纶经编布面料在面料铺放台上铺平,涤纶经编布面料的克重为200g/㎡;
(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为200℃,烘温时间为60秒;所述聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜;所述聚氨酯复合板的克重为800g/㎡;
(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的涤纶经编布面料输送到聚氨酯复合板上方,涤纶经编布面料与聚氨酯复合板的PE膜一侧接触,压制成型得到汽车顶蓬半成品;成型压力为5MPa,成型时间为60秒;
(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为45000psi,切割气压为0.5MPa。
本发明生产的汽车顶蓬重量轻,材料之间相容性好,耐洗可回收,成型加工容易,环保,产生的边角料很容易回收再利用,还解决了现有汽车顶篷面料的不耐脏污及气味不合格问题,能够很好地满足客户使用要求,符合现代汽车轻量化、环保化的要求。
Claims (6)
1.一种单体经编布汽车顶蓬的制造工艺,其特征是,包括以下工艺步骤:
(1)材料铺放:将经编布面料在面料铺放台上铺平;
(2)烘温软化:将聚氨酯复合板送入烘箱内进行烘温软化,温度为150~300℃,烘温时间为30~90秒;
(3)模压成型:将烘温软化后的聚氨酯复合板送入汽车顶蓬模具型腔内,将步骤(1)的经编布面料输送到聚氨酯复合板上方,压制成型得到汽车顶蓬半成品;成型压力为4~6MPa,成型时间为40~80秒;
(4)水刀切割:将模压成型得到的汽车顶蓬半成品从汽车顶蓬模具内取出,转移到切割治具上,切割成所需尺寸,即得到所述的汽车顶蓬;切割水压为40000~50000psi,切割气压为0.4~0.7MPa。
2.如权利要求1所述的单体经编布汽车顶蓬的制造工艺,其特征是:所述聚氨酯复合板的材料从下至上依次为无纺布、玻璃纤维毡、聚氨酯泡沫、玻璃纤维毡、PE膜。
3.如权利要求2所述的单体经编布汽车顶蓬的制造工艺,其特征是:步骤(3)中,经编布面料与聚氨酯复合板的PE膜一侧接触。
4.如权利要求1所述的单体经编布汽车顶蓬的制造工艺,其特征是:所述经编布面料的克重为100~300g/㎡。
5.如权利要求1所述的单体经编布汽车顶蓬的制造工艺,其特征是:所述聚氨酯复合板的克重为700~1000g/㎡。
6.如权利要求1所述的单体经编布汽车顶蓬的制造工艺,其特征是:所述经编布面料采用涤纶经编布面料。