CN103290721A - Production method of tipping base paper for flame-retardant cigarettes - Google Patents
Production method of tipping base paper for flame-retardant cigarettes Download PDFInfo
- Publication number
- CN103290721A CN103290721A CN2013101889210A CN201310188921A CN103290721A CN 103290721 A CN103290721 A CN 103290721A CN 2013101889210 A CN2013101889210 A CN 2013101889210A CN 201310188921 A CN201310188921 A CN 201310188921A CN 103290721 A CN103290721 A CN 103290721A
- Authority
- CN
- China
- Prior art keywords
- pulp
- slurry
- mixing
- paper
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a production method of tipping base paper for flame-retardant cigarettes. The production method of tipping base paper for flame-retardant cigarettes comprises the following steps of: continuously beating softwood pulp and hardwood pulp by using a double disc refiner, wherein the beating concentration of the softwood pulp is 3.4-4.4% and the beating degree is 65-750SR, the beating concentration of the hardwood pulp is 3.8-4.2% and the beating degree is 60-700SR; mixing the pulped softwood pulp and the pulped hardwood pulp in a weight ratio of 40-65% to 35-60% as mixed pulp for future use. The raw materials, filling substances, various additives and the surface additives during producing the products are innocuous and non-poisonous products, so that the tipping base paper for flame-retardant cigarettes is low in heavy metal content, free of fluorescent whitening agent and good in flame retardant property. The tipping base paper is coiled on the cigarettes, so that the cigarettes can be automatically extinguished when the cigarettes are combusted to the position of the tipping base paper for the flame-retardant cigarettes.
Description
Technical field
The present invention relates to a kind of production method of fire-retardant body paper for tobacco-use tipping paper.
Background technology
After people suck cigarette, owing to do not extinguish cigarette end timely, cause fire easily, along with the attention of country to the fire safety evaluating problem, the raising of people's inherently safe consciousness requires tobacco business to strengthen the security of cigarette product self, reduces the fire safety evaluating hidden danger of cigarette product, satisfy the interior development requirement to safety, environment-friendly products of industry, the body paper for tobacco-use tipping paper that the market demand research and development can be fire-retardant.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, the production method of fire-retardant body paper for tobacco-use tipping paper is provided, the anti-flammability by tipping body paper self has reaches cigarette and props up when being burned to stub and can extinguish automatically, has improved the problem of security preferably.
Fire-retardant body paper for tobacco-use tipping paper basic material mainly contains various strings and constitutes, and string carries out wire-dividing broom purification by the double plate mill, makes it have certain beating degree, guarantees can reach the combination that well is interweaved between fiber, constitutes the basic framework of paper; Packing material such as talcum powder, titanium dioxide etc. can play the opacity of improving paper printing characteristic, improving paper, make paper have high temperature resistant, heat conductivility not preferably, increase fire resistance; And the adding of each analog assistant such as cationic starch, polyacrylamide etc. can improve keeping of fiber fines and filler, guarantees paper formation and intensity, further improves the paper fire resistance simultaneously.
Fire-retardant body paper for tobacco-use tipping paper mainly is made up of following several constituents:
Basic material: mainly contain softwood pulp, hardwood pulp, straw pulp, bamboo pulp, reed pulp (or other non-wood materials) etc., basic material accounts for the 70-95% of total composition.
Packing material: mainly comprise grinding calcium carbonate, mineral fibres, talcum powder, kaolin, titanium dioxide, magnesia, magnesium hydroxide, aluminium hydroxide etc.Packing material accounts for the 5-30% of total composition.
Each analog assistant: mainly comprise bactericide, defoamer, polyamide epoxy polyamine chloropropane resin (or other wet strength agents), cationic starch, polymine, polyacrylamide, alkyl ketene dimer (or other neutral sizing agents) etc.Each analog assistant accounts for total composition 5%-10%.
Table is coated with auxiliary agent: fire retardant, water repellent agent, polyvinyl alcohol, alginate, carboxymethyl cellulose (or other cellulose derivatives), styrene-butadiene latex (or other adhesives), thickener, printability agent, oxidized starch (or other converted starches) etc.Each analog assistant accounts for total composition 10%-30%.
Above-mentioned purpose realizes by following technical scheme:
1, a kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0Between the SR; The hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0Between the SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
Described hardwood pulp replaces with hardwood pulp and mixes slurry with bamboo pulp, and wherein hardwood pulp and bamboo pulp part by weight are 2:1.
Described hardwood pulp replaces with straw pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
Described machine hand's section replaces with: in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3-5g/m
2, proceed oven dry again after table is coated with;
Described talcum powder replaces with grinding calcium carbonate.
Described talcum powder replaces with and grinds mountain range soil.
Described oxidized starch replaces with carboxymethyl cellulose.
Described oxidized starch replaces with polyvinyl alcohol.
Beneficial effect:
The invention belongs to fire-retardant body paper for tobacco-use tipping paper production technology, its fire resistance is mainly by attaching filler, each analog assistant, also realizing by the coating of surface size press light weight in starching.Sizing material in the coating is dispersed emulsion with water, selects suspension is good, content of beary metal is low fire retardant, water repellent agent to be equipped with table such as oxidized starch simultaneously and is coated with auxiliary agent and disperses wherein, realizes the coating good uniformity by coating method.Selected raw material, filler, each analog assistant and table are coated with auxiliary agent and are nontoxic product during production, content of beary metal is low, do not contain the fluorescence optical brightener, its fire resistance is good, twisting in cigarette with it props up, when cigarette props up when being burned to fire-retardant body paper for tobacco-use tipping paper position, can extinguish automatically, the rate of putting out certainly reaches 100%.
The flame-retardant tipping paper body paper is compared with common tipping paper body paper, has stronger fire resistance and not sticking lip performance.Selected raw material, auxiliary material, auxiliary agent and table are coated with auxiliary agent and are nontoxic product during production, content of beary metal is low, do not contain the fluorescence optical brightener, its fire resistance is good, twists in cigarette with it and props up, when cigarette props up when being burned to the flame-retardant tipping paper position, can extinguish automatically, reach 100% from the rate of putting out, do not extinguish when effectively having prevented because of cigarette combustion to stub and cause fire, strengthened security of products greatly.Product has higher WATER RESISTANCE and opacity in addition, and good binding intensity can satisfy the high-speed press requirement.
The production method of above-mentioned a kind of fire-retardant body paper for tobacco-use tipping paper all can reach fire resistance, satisfy the client to the requirement of fire resistance, technical scheme is except hardwood pulp slurry kind of difference, the main difference point is that table is coated with the technology difference, wherein example 1-6 carries out the light weight coating, composite mixture viscosity is low, and coating weight is at 0.3-1.0g/m
2, example 7-12 table coated compounding compound component is many, and viscosity is big, and coating weight is at 3-5g/m
2, the tipping paper body paper produced surface film-formation result is splendid, has better heat-resisting, airtight, heat conductivility not, and outline is better than example 1-6 on flame retardant effect.
The specific embodiment
Embodiment 1
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0SR; The hardwood pulp beating consistency is 3.8%, beating degree guarantees 60
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40%:60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 40% of slurry gross weight, the titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, the cationic starch dosage is for mixing 1.0% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 7% of oxidized starch and fire retardant is coated with composite mixture weight at 0.3g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 7% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 0.3g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 2
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0SR; The hardwood pulp beating consistency is 4.2%, beating degree guarantees 70
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 65%:35% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 80% of slurry gross weight, the titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 9% of oxidized starch and fire retardant is coated with composite mixture weight at 1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 9% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 3
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 4%, beating degree guarantees 70
0SR; The hardwood pulp beating consistency is 4%, beating degree guarantees 65
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 50%:50% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 60% of slurry gross weight, the titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, the cationic starch dosage is for mixing 1.1% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 8% of oxidized starch and fire retardant is coated with composite mixture weight at 0.8g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 8% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 0.8g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 4
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 3.8%, beating degree guarantees 60
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 40%:60% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 40% of slurry gross weight, the titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, the cationic starch dosage is for mixing 1.0% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 7% of oxidized starch and fire retardant is coated with composite mixture weight at 0.3g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 7% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 0.3g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 5
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 4.2%, beating degree guarantees 70
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 65%:35% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 80% of slurry gross weight, the titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 9% of oxidized starch and fire retardant is coated with composite mixture weight at 1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 9% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 6
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 4%, beating degree guarantees 70
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 4%, beating degree guarantees 65
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 50%:50% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 60% of slurry gross weight, the titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, the cationic starch dosage is for mixing 1.1% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration 8% of oxidized starch and fire retardant is coated with composite mixture weight at 0.8g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration 8% of water, oxidized starch and water repellent agent is coated with composite mixture weight at 0.8g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 7
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0SR; The hardwood pulp beating consistency is 3.8%, beating degree guarantees 60
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40%:60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 40% of slurry gross weight, the titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, the cationic starch dosage is for mixing 1.0% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 8
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0SR; The hardwood pulp beating consistency is 4.2%, beating degree guarantees 70
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 65%:35% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 80% of slurry gross weight, the titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 5g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 9
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 4%, beating degree guarantees 70
0SR; The hardwood pulp beating consistency is 4%, beating degree guarantees 65
0SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 50%:50% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing 60% of slurry gross weight, the titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, the cationic starch dosage is for mixing 1.1% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 4g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
Embodiment 10
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 3.8%, beating degree guarantees 60
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 40%:60% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder, titanium dioxide is filler, wherein the talcum powder dosage is for mixing 40% of slurry gross weight, the titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, the cationic starch dosage is for mixing 1.0% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 11
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 4.2%, beating degree guarantees 70
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 65%:35% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder, titanium dioxide is filler, wherein the talcum powder dosage is for mixing 80% of slurry gross weight, the titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 5g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 12
A kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 4%, beating degree guarantees 70
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 4%, beating degree guarantees 65
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 50%:50% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder, titanium dioxide is filler, wherein the talcum powder dosage is for mixing 60% of slurry gross weight, the titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, the cationic starch dosage is for mixing 1.1% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 4g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 13
1, a kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0Between the SR; The hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0Between the SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
Embodiment 14
1, a kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 3.8～4.2%, beating degree guarantees 60～70
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 40～65%:35～60% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp with bamboo pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
Embodiment 15
1, a kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0Between the SR; The hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0Between the SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3-5g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
Embodiment 16
1, a kind of production method of fire-retardant body paper for tobacco-use tipping paper comprises the steps:
(1), beater floor, hardwood pulp is mixed slurry, softwood pulp adopt two disks mill continuous beatings with bamboo pulp, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0SR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency are 3.8～4.2%, beating degree guarantees 60～70
0SR; Mix slurry with bamboo pulp and be made into the ratio of weight 40～65%:35～60% that to mix slurry stand-by accomplishing fluently the softwood pulp of slurry and hardwood pulp;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3-5g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind mountain range soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp with bamboo pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
Claims (9)
1. the production method of a fire-retardant body paper for tobacco-use tipping paper is characterized in that comprising the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted two disks mill continuous beatings, the softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0Between the SR; The hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0Between the SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), machine hand's section, in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing page one side surface of agent machine after to preceding do, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight is 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, the opposite side table is coated with the composite mixture of water, oxidized starch and water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight is 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9% is coated with composite mixture weight at 0.3-1.0g/m
2, proceed oven dry again after table is coated with;
(3), press polish workshop section, page after adopting calender to oven dry carries out press polish, make product have the good characteristic of glossiness, can make tipping paper obtain splendid levelling effect, make paper have certain smoothness, produce and satisfy the printing performance requirement, and have the body paper for tobacco-use tipping paper of fire resistance.
2. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1 is characterized in that described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
3. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1, it is characterized in that: described hardwood pulp replaces with hardwood pulp and mixes slurry with bamboo pulp, and wherein hardwood pulp and bamboo pulp part by weight are 2:1.
4. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1, it is characterized in that: described hardwood pulp replaces with straw pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
5. as the production method of each described a kind of fire-retardant body paper for tobacco-use tipping paper of claim 1-4, it is characterized in that: described machine hand's section replaces with: in the mixing that in beater floor, the prepares slurry with talcum powder
,Titanium dioxide is filler, wherein the talcum powder dosage is for mixing the 40-80% of slurry gross weight, the titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode that attaches continuously to attach the neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry for preparing, attach the double base retention agent of forming with cationic polyacrylamide and cationic starch again, make body paper have certain anti-current body permeance property, improve into dimensional stability, the cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, the cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, make then and mix slurry after wet end and press section dehydration shaping, the stage of doing before the l Water Paper page or leaf enters dries, show to be coated with water through executing the page both side surface of agent machine after to preceding do, oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the composite mixture that aluminium hydroxide is formed; water in the composite mixture; oxidized starch; styrene-butadiene latex; thickener; fire retardant; water repellent agent; magnesium hydroxide; the aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5% is coated with composite mixture weight at 3-5g/m
2, proceed oven dry again after table is coated with.
6. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 5 is characterized in that: described talcum powder replaces with grinding calcium carbonate or grinds mountain range soil.
7. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 5, it is characterized in that: described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.
8. as the production method of each described a kind of fire-retardant body paper for tobacco-use tipping paper of claim 1-4, it is characterized in that: described talcum powder replaces with grinding calcium carbonate or grinds mountain range soil.
9. as the production method of each described a kind of fire-retardant body paper for tobacco-use tipping paper of claim 1-4, it is characterized in that: described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.