CN110468625A - A kind of fire-retardant production method and system from saturating body paper for tobacco-use tipping paper - Google Patents
A kind of fire-retardant production method and system from saturating body paper for tobacco-use tipping paper Download PDFInfo
- Publication number
- CN110468625A CN110468625A CN201910811395.6A CN201910811395A CN110468625A CN 110468625 A CN110468625 A CN 110468625A CN 201910811395 A CN201910811395 A CN 201910811395A CN 110468625 A CN110468625 A CN 110468625A
- Authority
- CN
- China
- Prior art keywords
- paper
- fire
- tobacco
- retardant
- detection device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-retardant production methods and system from saturating body paper for tobacco-use tipping paper, wherein production method includes the following steps: S100, mashing: needle slurry is ground through double plate and is beaten, beating consistency 65-750SR, weight in wet base 7-9g, and eucalyptus pulp is discongested through double plate mill, beating consistency 15-200The needle handled well slurry and eucalyptus pulp are mixed according to the proportion of weight ratio 30-35%:65-70%, joint slurry are made, the calcium carbonate of its total weight 30-50% and the wet strength agent of 1-1.4% is added in joint slurry, is made and is mixed with beating material by SR, weight in wet base 1-2g；S200, copy paper: it is manufactured paper with pulp forming by cylinder mould machine, to form the natural hole of uniform interleaving；S300, drying: being dried into multiple groups drying cylinder, applies the compound mixture that agent machine is coated with oxidized starch and acrylic resin by surface when drying, handles page surface performance；S400, press polish: ornamenting is carried out by paper surface of the soft press-polishing machine to drying；S500, printing: using intaglio press paper back face printing fire retardant.Using the production method and system of the invention from saturating body paper for tobacco-use tipping paper, the product of preparation has both high-air-permeability and flame-retarding characteristic simultaneously, the air permeability coefficient of variation≤7%, and automatic distinguishing rate is up to 100%.
Description
Technical field
The present invention relates to technology for making paper fields, specifically, being to be related to a kind of fire-retardant life from saturating body paper for tobacco-use tipping paper
Production method and production system.
Background technique
Smoking is behavior extremely common in daily life, after smoker sucks cigarette, since cigarette butt not being extinguished in time,
Cause the accident that fire occurs commonplace.More attention with people to fire prevention and control safety problem, people's self-protection
Awareness of safety be also continuously improved, promote the safety for requiring tobacco leaf production industry that must reinforce cigarette product itself, improve volume
The technology of preparing of smoke product reduces the fire safety evaluating hidden danger of cigarette product, meets society to the exploitation need of safe and environment-friendly product
It asks.The fire-retardant body paper for tobacco-use tipping paper of research and development energy is a hot technology, because having unique benefit, such as when smoker inhales
Complete cigarette does not in time extinguish cigarette butt, and cigarette tipping paper can prevent cigarette from burning away, and cigarette is promoted to extinguish, to play anti-
The effect of fire only occurs.
In addition, considering for health, cigarette filter air permeability with higher is also required, main flume can be diluted
In pernicious gas, achieve the purpose that reducing tar and reducing harm, while being also equipped with flame retarding function, automatic extinguishing when cigarette being enable to be burned to stub
It goes out, improves the safety of cigarette.
However, at present in the prior art, preparing the technology of body paper for tobacco-use tipping paper, at least there is following several point defects:
(1) prior art cannot achieve product and both have high-air-permeability but also with flame retardant property；
(2) air permeability is lower, can not dilute the pernicious gas in main flume, cannot achieve the purpose that reducing tar and reducing harm；
(3) cigarette automatic distinguishing rate is lower；
(4) the printing applicable performance of paper is poor；
(5) ventilation of Yao Shixian filter tip needs to carry out laser boring on cigarette tipping paper, and the aperture of laser boring is larger, Bu Nengjun
Even dilution main flume, sense organ when smoker being caused to smoke is deteriorated, and causes filter ventilation rates to make a variation since aperture is larger
Coefficient is larger, and stability is poor.
Therefore, find it is a kind of it is fire-retardant from the production method and system of saturating body paper for tobacco-use tipping paper be the task of top priority.
Summary of the invention
The purpose of the present invention is to provide a kind of fire-retardant production methods and system from saturating body paper for tobacco-use tipping paper, to solve
Such as above-mentioned prior art problem.
In one aspect, the invention discloses a kind of fire-retardant production method from saturating body paper for tobacco-use tipping paper, this method packets
Include following steps:
S100, mashing: needle slurry being ground through double plate and is beaten, beating consistency 65-750SR, weight in wet base 7-9g, and eucalyptus pulp is passed through
Double plate mill is discongested, beating consistency 15-200SR, weight in wet base 1-2g,
The needle handled well slurry and the eucalyptus pulp are mixed according to the proportion of weight ratio 30-35%:65-70%, connection is made
Slurry is closed,
The wet strength agent of the calcium carbonate and 1-1.4% of its total weight 30-50% is added in the joint slurry, is made and is mixed with beating
Material；
S200, copy paper: the material that is mixed with beating is diluted with water to the online concentration that weight ratio is 0.5-1.0%, is sequentially added
The AKD of the dispersing agent of 0.2-0.6% weight ratio, 1-2% weight ratio is manufactured paper with pulp forming by cylinder mould machine, to form uniform interleaving
Natural hole；
S300, drying: it after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, when drying passes through
The compound mixture of agent machine coating oxidized starch and acrylic resin is applied on surface, is handled page surface performance,
Wherein, the weight ratio of oxidized starch and acrylic resin in the compound mixture is respectively 5-9% and 0.2-0.4%；
S400, press polish: ornamenting, paper smoothness 100-200s, paper are carried out by paper surface of the soft press-polishing machine to drying
The smooth exquisiteness in surface；And
S500, printing: paper longitudinal direction is parallel to, in the anti-of paper using intaglio press according to tipping paper printing surface specification
Fire retardant is printed in face, and the fire retardant is the mixture of Arabic gum, aluminium hydroxide, calcium carbonate, ethyl alcohol and propylene glycol.
Optionally, in step s 200, it manufactures paper with pulp when shaping, using spacer screen be 12-14 mesh, veil is the double circles of 90-100 purpose
Net paper machine composite molding；
60 μm of the aperture < of the nature hole, average pore size are 15-20 μm.
Optionally, in step S300, the coating dosage of the compound mixture is 0.5-1.5g/m2。
Optionally, in step S500, Arabic gum in the fire retardant: aluminium hydroxide: calcium carbonate: ethyl alcohol: propylene glycol
Weight ratio be 10:5:5:14:1；
When printing fire retardant, there are ventilative blank areas for tipping paper；And
The fire retardant is 5-10mm in the width that reverse side of paper is printed.
On the other hand, the invention also discloses one kind suitable for above-mentioned fire-retardant from saturating body paper for tobacco-use tipping paper producer
The production system of method, the system include: refining system (100), copy paper system (200), drying system (300), calendaring system
(400) and print system (500)；
The refining system (100) is provided with double plate mill；
The copy paper system (200) is provided with that spacer screen is 12-14 mesh, veil is the double cylinder mould machines of 90-100 purpose, for copying
Cause shape；
The drying system (300) is provided with drying cylinder；
The calendaring system (400) is provided with soft press-polishing machine；And
The print system (500) is provided with intaglio press, and the intaglio press is provided with the carving of the laser with U-shaped depression
It cuts blocks for printing roller.
Optionally, the refining system (100) is provided with 4 double plate mills, and preceding two double plates mill is to cut off mill, and rear two
Platform is brooming mill；
The double plate mill is that TF20 type double plate is ground.
Optionally, the line number of the laser carving plate roller is 25 lines, and depth is 60 μm.
Optionally, preceding dry drying cylinder is Flying Dutchman, and outer diameter φ 3000mm, temperature is 85-100 DEG C, and rear dry drying cylinder is outer by 4
The multiple groups drying cylinder of diameter φ 1500mm forms, and temperature is 100-115 DEG C；And
MSP film transfer, which is provided with, between preceding dry drying cylinder and rear dry drying cylinder applies agent machine；
Optionally, the outer diameter of the soft press-polishing machine is φ 680mm, and upper roller is steel rider, contact paper wire side, and lower roll is rubber roller, connects
Touch the non-wire side of paper；
The temperature of the steel rider is 120-130 DEG C, pressure 0.28-0.30MPa.
It optionally, further include detection system (600) and packaging system (700)；
The detection system (600) includes quantitative detection equipment (610), thickness detecting equipment (620), air permeability detection device
(630), tensile strength detection device (640), smoothness detection device (650), opacity detection device (660) and water suction
Property detection device (670)；
The quantitative detection equipment (610) is provided with proportional sampling device and electronic balance；
The thickness detecting equipment (620) is provided with thickness measuring instrument；
The air permeability detection device (630) is provided with air permeability instrument；
The tensile strength detection device (640) is provided with tensile strength tester；
The smoothness detection device (650) is provided with bekk smoothness instrument；
The opacity detection device (660) is provided with whiteness and colure meter；
The water imbibition detection device (670) is provided with can vigorous absorbability analyzer；And
The packaging system (700) is provided with thin film winding machine.
Related technical personnel are it is understood that be previously with regard to fire-retardant be retouched from the production method of saturating body paper for tobacco-use tipping paper
The feature and effect stated, are also applied for the system of course, repeat no more.
Of the invention is at least as described below from the production method of saturating body paper for tobacco-use tipping paper and the beneficial effect of system:
1, the product prepared has both high-air-permeability and flame-retarding characteristic simultaneously；
2, the product prepared has high-air-permeability, can effectively dilute the pernicious gas in main flume, reach reducing tar and reducing harm
Purpose.In addition, the product of preparation has stable air permeability, the air permeability coefficient of variation≤7%.
3, the product prepared has good flame retardant property, and automatic distinguishing rate is up to 100%.
4, laser boring process is saved, existing punching product can be replaced, the hole of the product of preparation is uniformly distributed, no
It can only achieve the effect that reduce tar, CO and nicotine, and more be able to satisfy smoker to the mouthfeel demand of smoking.In addition, also
Automatic distinguishing when cigarette being enable to be burned to stub improves the safety of cigarette.
5, the smooth exquisiteness of paper surface, may be implemented good printing effect, and the printing applicable performance of paper is preferable.
Additional aspect and advantage of the invention will be set forth in part in the description, and will partially become from the following description
Obviously, or practice through the invention is recognized.
Detailed description of the invention
Above-mentioned and/or additional aspect of the invention and advantage will become from the description of the embodiment in conjunction with the following figures
Obviously and it is readily appreciated that, in which:
Fig. 1 be according to an embodiment of the present invention in the process flow of the fire-retardant production method from saturating body paper for tobacco-use tipping paper show
It is intended to；
Fig. 2 be according to an embodiment of the present invention in the fire-retardant production system from saturating body paper for tobacco-use tipping paper structural representation
Figure；
Fig. 3 be according to a different embodiment in the structure of the fire-retardant production system from saturating body paper for tobacco-use tipping paper show
It is intended to；
Fig. 4 be according to an embodiment of the present invention in the fire-retardant production system from saturating body paper for tobacco-use tipping paper detection system
Structural schematic diagram.
Appended drawing reference:
100- refining system, 200- copy paper system, 300- drying system, 400- calendaring system, 500- print system, 600- detection
System, 610- quantitative detection equipment, 620- thickness detecting equipment, 630- air permeability detection device, the detection of 640- tensile strength are set
Standby, 650- smoothness detection device, 660- opacity detection device, 670- water imbibition detection device, 700- packaging system.
Specific embodiment
The present invention is described in further detail below by specific embodiment, and in conjunction with attached drawing.It needs to illustrate
It is that in the absence of conflict, the features in the embodiments and the embodiments of the present application can be combined with each other.In addition, embodiment
It is exemplary, for explaining only the invention, and is not considered as limiting the invention.
In one aspect, the invention discloses a kind of fire-retardant production methods from saturating body paper for tobacco-use tipping paper, according to this hair
Bright embodiment, as shown in Figure 1, the production method the following steps are included:
S100, mashing:
Needle slurry is ground through double plate and is beaten, beating consistency 65-750SR, weight in wet base 7-9g, and eucalyptus pulp is ground through double plate and is dredged
Solution, beating consistency 15-200SR, weight in wet base 1-2g,
The needle handled well slurry and the eucalyptus pulp are mixed according to the proportion of weight ratio 30-35%:65-70%, connection is made
Slurry is closed,
The wet strength agent of the calcium carbonate and 1-1.4% of its total weight 30-50% is added in the joint slurry, is made and is mixed with beating
Material；
S200, copy paper:
The material that is mixed with beating is diluted with water to the online concentration that weight ratio is 0.5-1.0%, sequentially adds 0.2-0.6% weight
The AKD of the dispersing agent of ratio, 1-2% weight ratio is manufactured paper with pulp forming by cylinder mould machine, to form the natural hole of uniform interleaving.
According to an embodiment of the invention, manufacturing paper with pulp when shaping, using spacer screen be 12-14 mesh, veil is the double circles of 90-100 purpose
Net paper machine composite molding, make nature hole 60 μm of aperture <, 15-20 μm of average pore size, so that paper fibre be made uniformly to hand over
It knits, forms natural permeable degree.
, it is dry:
It after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, agent machine is applied by surface when drying
It is coated with the compound mixture of oxidized starch and acrylic resin, page surface performance is handled,
Wherein, the weight ratio of oxidized starch and acrylic resin in the compound mixture is respectively 5-9% and 0.2-0.4%.
, press polish:
Paper surface progress ornamenting by soft press-polishing machine to drying, paper smoothness 100-200s, paper surface are smooth thin
It is greasy.
, printing:
It is parallel to paper longitudinal direction using intaglio press according to tipping paper printing surface specification, it is fire-retardant in the back face printing of paper
Agent.
In the present invention, when printing fire retardant, there are 4 Particular crafts as described below:
1, fire retardant when printing includes at least one of Arabic gum, aluminium hydroxide, calcium carbonate, ethyl alcohol and propylene glycol, example
Such as, it is preferred that Arabic gum: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight ratio of propylene glycol is 10:5:5:14:1.
2, intaglio press setting has the laser carving plate roller of U-shaped depression, and the line number of laser carving plate roller is 25 lines, deep
Degree is 60 μm.
3, when printing fire retardant, there are ventilative blank areas for tipping paper.
4, fire retardant is 5-10mm in the width that reverse side of paper is printed.
Such unique design makes the present invention that can obtain 4 advantageous effects as described below:
One, the natural permeable degree characteristic that product is remained while realize flame-retarded technology purpose, in reducing tar and reducing harm and raising
Be conducive to the mouthfeel demand for meeting smoker to smoking while stability, increase selling point；
Secondly, the U-shaped depression of gravure printing machine can store more fire retardants, to realize more good flame retardant effect；
Thirdly, fire-retardant bandwidth it is adjustable, with printing surface perfect combination, do not influence product appearance；
Four, product realizes the technical purpose of meeting automatic distinguishing when cigarette is burned to stub, is beneficial to prevent and causes fire thing
Therefore with conservation of nature environment.
According to an embodiment of the invention, the fire-retardant technical solution from saturating body paper for tobacco-use tipping paper production method of the invention exists
On the basis of above-mentioned, further improvement as described below can also be done:
(1) in step s 200, it manufactures paper with pulp when shaping, using spacer screen be 12-14 mesh, veil is that the double cylinder mould machines of 90-100 purpose are multiple
Synthesis type；
60 μm of the aperture < of the nature hole, average pore size are 15-20 μm.
(2) in step S300, the coating dosage of the compound mixture is 0.5-1.5g/m2。
(3) in step S500, Arabic gum in the fire retardant: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight of propylene glycol
Amount is than being 10:5:5:14:1；
When printing fire retardant, there are ventilative blank areas for tipping paper；And
The fire retardant is 5-10mm in the width that reverse side of paper is printed.
Certainly, the present invention also can be by all utilizable prior arts, these variations all fall within guarantor of the invention
Within the scope of shield.
In a further aspect, the invention discloses a kind of suitable for the above-mentioned fire-retardant production from saturating body paper for tobacco-use tipping paper
The production system of method.According to an embodiment of the invention, as shown in Fig. 2, the system includes: refining system (100), copy paper system
(200), drying system (300), calendaring system (400) and print system (500)；
The refining system (100) is provided with double plate mill；
The copy paper system (200) is provided with that spacer screen is 12-14 mesh, veil is the double cylinder mould machines of 90-100 purpose, for copying
Cause shape；
The drying system (300) is provided with drying cylinder；
The calendaring system (400) is provided with soft press-polishing machine；And
The print system (500) is provided with intaglio press, and the intaglio press is provided with the carving of the laser with U-shaped depression
It cuts blocks for printing roller.
About the implementation method of the fire-retardant production system from saturating body paper for tobacco-use tipping paper of the invention, above section has been done
It illustrates, and will be further elaborated in following part, therefore not repeat to illustrate herein.
According to an embodiment of the invention, the technical solution of the fire-retardant production system from saturating body paper for tobacco-use tipping paper of the invention
On the basis of the above, further improvement as described below can also be done:
(1) according to an embodiment of the invention, as shown in Fig. 2, the refining system (100) is provided with 4 double plate mills, and first two
Double plate mill is cutting mill, and latter two are brooming mill.
(2) according to an embodiment of the invention, as shown in Fig. 2, double plate mill is that TF20 type double plate is ground.
(3) according to an embodiment of the invention, as shown in Fig. 2, the line number of the laser carving plate roller is 25 lines, depth 60
μm。
(4) according to an embodiment of the invention, as shown in Fig. 2, preceding dry drying cylinder is Flying Dutchman, outer diameter φ 3000mm, temperature
It is 85-100 DEG C；
Dry drying cylinder is made of the multiple groups drying cylinder of 4 outer diameter φ 1500mm afterwards, and temperature is 100-115 DEG C.
(5) according to an embodiment of the invention, as shown in Fig. 2, being provided with MSP film transfer between preceding dry drying cylinder and rear dry drying cylinder
Apply agent machine.
(6) according to an embodiment of the invention, upper roller is steel as shown in Fig. 2, the outer diameter of the soft press-polishing machine is φ 680mm
Roller, contact paper wire side, lower roll are rubber roller, the contact non-wire side of paper；
The temperature of the steel rider is 120-130 DEG C, pressure 0.28-0.30MPa.
(7) according to an embodiment of the invention, as shown in figure 3, further including detection system (600), as shown in figure 4, the inspection
Examining system (600) includes that quantitative detection equipment (610), thickness detecting equipment (620), air permeability detection device (630), anti-tensile are strong
Spend detection device (640), smoothness detection device (650), opacity detection device (660) and water imbibition detection device
(670).
(8) according to an embodiment of the invention, as shown in figure 4, the quantitative detection equipment (610) is provided with proportional sampling device
And electronic balance；
The thickness detecting equipment (620) is provided with thickness measuring instrument；
The air permeability detection device (630) is provided with air permeability instrument；
The tensile strength detection device (640) is provided with tensile strength tester；
The smoothness detection device (650) is provided with bekk smoothness instrument；
The opacity detection device (660) is provided with whiteness and colure meter；
The water imbibition detection device (670) is provided with can vigorous absorbability analyzer.
(9) according to an embodiment of the invention, as shown in figure 3, further include packaging system (700), the packaging system (700)
It is provided with thin film winding machine.
Related technical personnel are it is understood that be previously with regard to fire-retardant be retouched from the production method of saturating body paper for tobacco-use tipping paper
The feature and effect stated, are also applied for the system of course, repeat no more.
1-4 with reference to the accompanying drawing, by specific embodiment, the present invention is described further, it should be noted that
These embodiments are merely to illustrate that purpose, and cannot be construed to limitation of the present invention in any way.In addition, following
In embodiment if not otherwise specified, then used equipment and material are commercially available.
Embodiment 1: air permeability 150CU body paper for tobacco-use tipping paper is prepared
1, it is beaten:
Needle slurry is ground into mashing through double plate, it is 4 TF20 type double plate mills that double plate, which is ground, and preceding two double plates mill is to cut off mill, rear two
Platform is brooming mill, beating consistency 750SR, weight in wet base 7g, and eucalyptus pulp is discongested through double plate mill, beating consistency 200It is SR, wet
Weight is 1g；
The needle handled well slurry and eucalyptus pulp are mixed according to the proportion of weight ratio 35%:65%, joint slurry is made；
The calcium carbonate of its total weight 30% and 1.4% wet strength agent is added in joint slurry, is made and is mixed with beating material.
2, copy paper:
Will be mixed with beating material be diluted with water to weight ratio be 0.9% online concentration, sequentially add 0.5% weight ratio dispersing agent,
The AKD of 1.5% weight ratio, by spacer screen be 12-14 mesh, veil is that the double cylinder mould machines of 90-100 purpose carry out forming of manufacturing paper with pulp, with shape
At the natural hole of uniform interleaving, 60 μm of the aperture < of natural hole, average pore size are 15-20 μm.
3, dry:
It after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, agent machine is applied by surface when drying
It is coated with the compound mixture of oxidized starch and acrylic resin, page surface performance is handled, wherein oxidized starch and third
Weight ratio of the olefin(e) acid resin in the compound mixture is respectively 6% and 0.3%；
When dry, preceding dry drying cylinder is Flying Dutchman, and outer diameter φ 3000mm, temperature is 85-100 DEG C, and rear dry drying cylinder is by 4 outer diameters
The multiple groups drying cylinder of φ 1500mm forms, and temperature is 100-115 DEG C；And MSP film is provided between preceding dry drying cylinder and rear dry drying cylinder
Agent machine is applied in transfer.
4, press polish:
Ornamenting carried out to the paper surface of drying by soft press-polishing machine, the outer diameter of soft press-polishing machine is φ 680mm, upper roller be steel rider,
Paper wire side is contacted, lower roll is rubber roller, the contact non-wire side of paper, and the temperature of steel rider is 120-130 DEG C, pressure 0.28-
0.30MPa, paper smoothness 100-200s meet printing requirement.
5, it prints:
It is printed using intaglio press, which is provided with the laser carving plate roller with U-shaped depression, laser carving
The line number of roller of cutting blocks for printing is 25 lines, and depth is 60 μm, in the reverse side of above-mentioned base paper for tipping paper, is parallel to paper longitudinal direction, prints fire-retardant
Agent, fire retardant are Arabic gum: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight ratio of propylene glycol is 10:5:5:14:1, printing resistance
The width for firing agent is respectively 5mm and 10mm.
Product testing
Product inspection method and detection project are detailed in lower section embodiment 4.
Properties of product
Prepare the quantitative 35g/m of body paper for tobacco-use tipping paper2, air permeability 150CU, automatic distinguishing rate is 100% after cigarette.
Product packaging
Packaging facilities is thin film winding machine, by plastic winding films with certain tension, is uniformly wrapped on the outside of product, rises simultaneously
To fixed and protective action.
Embodiment 2: air permeability 200CU body paper for tobacco-use tipping paper is prepared
1, it is beaten:
Needle slurry is ground into mashing through double plate, it is 4 TF20 type double plate mills that double plate, which is ground, and preceding two double plates mill is to cut off mill, rear two
Platform is brooming mill, beating consistency 700SR, weight in wet base 8g, and eucalyptus pulp is discongested through double plate mill, beating consistency 180It is SR, wet
Weight is 1g；
The needle handled well slurry and eucalyptus pulp are mixed according to the proportion of weight ratio 32%:68%, joint slurry is made；
The calcium carbonate of its total weight 40% and 1.4% wet strength agent is added in joint slurry, is made and is mixed with beating material.
2, copy paper:
Will be mixed with beating material be diluted with water to weight ratio be 0.9% online concentration, sequentially add 0.5% weight ratio dispersing agent,
The AKD of 1.5% weight ratio, by spacer screen be 12-14 mesh, veil is that the double cylinder mould machines of 90-100 purpose carry out forming of manufacturing paper with pulp, with shape
At the natural hole of uniform interleaving, 60 μm of the aperture < of natural hole, average pore size are 15-20 μm.
3, dry:
It after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, agent machine is applied by surface when drying
It is coated with the compound mixture of oxidized starch and acrylic resin, page surface performance is handled, wherein oxidized starch and third
Weight ratio of the olefin(e) acid resin in the compound mixture is respectively 6% and 0.3%；
When dry, preceding dry drying cylinder is Flying Dutchman, and outer diameter φ 3000mm, temperature is 85-100 DEG C, and rear dry drying cylinder is by 4 outer diameters
The multiple groups drying cylinder of φ 1500mm forms, and temperature is 100-115 DEG C；And MSP film is provided between preceding dry drying cylinder and rear dry drying cylinder
Agent machine is applied in transfer.
4, press polish:
Ornamenting carried out to the paper surface of drying by soft press-polishing machine, the outer diameter of soft press-polishing machine is φ 680mm, upper roller be steel rider,
Paper wire side is contacted, lower roll is rubber roller, the contact non-wire side of paper, and the temperature of steel rider is 120-130 DEG C, pressure 0.28-
0.30MPa, paper smoothness 100-200s meet printing requirement.
5, it prints:
It is printed using intaglio press, intaglio press setting has the laser carving plate roller of U-shaped depression, laser engraving
The line number of roller is 25 lines, and depth is 60 μm, in the reverse side of above-mentioned base paper for tipping paper, is parallel to paper longitudinal direction, prints fire retardant,
Fire retardant is Arabic gum: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight ratio of propylene glycol is 10:5:5:14:1, prints fire retardant
Width be respectively 5mm and 10mm.
Product testing
Product inspection method and detection project are detailed in lower section embodiment 4.
Properties of product
Prepare the quantitative 35g/m of body paper for tobacco-use tipping paper2, air permeability 200CU, automatic distinguishing rate is 100% after cigarette.
Product packaging
Packaging facilities is thin film winding machine, by plastic winding films with certain tension, is uniformly wrapped on the outside of product, rises simultaneously
To fixed and protective action.
Embodiment 3: air permeability 250CU body paper for tobacco-use tipping paper is prepared
1, it is beaten:
Needle slurry is ground into mashing through double plate, it is 4 TF20 type double plate mills that double plate, which is ground, and preceding two double plates mill is to cut off mill, rear two
Platform is brooming mill, beating consistency 650SR, weight in wet base 8g, and eucalyptus pulp is discongested through double plate mill, beating consistency 150It is SR, wet
Weight is 1g；
The needle handled well slurry and eucalyptus pulp are mixed according to the proportion of weight ratio 30%:70%, joint slurry is made；
The calcium carbonate of its total weight 50% and 1.4% wet strength agent is added in joint slurry, is made and is mixed with beating material.
2, copy paper:
Will be mixed with beating material be diluted with water to weight ratio be 0.9% online concentration, sequentially add 0.5% weight ratio dispersing agent,
The AKD of 1.5% weight ratio, by spacer screen be 12-14 mesh, veil is that the double cylinder mould machines of 90-100 purpose carry out forming of manufacturing paper with pulp, with shape
At the natural hole of uniform interleaving, 60 μm of the aperture < of natural hole, average pore size are 15-20 μm.
3, dry:
It after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, agent machine is applied by surface when drying
It is coated with the compound mixture of oxidized starch and acrylic resin, page surface performance is handled, wherein oxidized starch and third
Weight ratio of the olefin(e) acid resin in the compound mixture is respectively 6% and 0.3%；
When dry, preceding dry drying cylinder is Flying Dutchman, and outer diameter φ 3000mm, temperature is 85-100 DEG C, and rear dry drying cylinder is by 4 outer diameters
The multiple groups drying cylinder of φ 1500mm forms, and temperature is 100-115 DEG C；And MSP film is provided between preceding dry drying cylinder and rear dry drying cylinder
Agent machine is applied in transfer.
4, press polish:
Ornamenting carried out to the paper surface of drying by soft press-polishing machine, the outer diameter of soft press-polishing machine is φ 680mm, upper roller be steel rider,
Paper wire side is contacted, lower roll is rubber roller, the contact non-wire side of paper, and the temperature of steel rider is 120-130 DEG C, pressure 0.28-
0.30MPa, paper smoothness 100-200s meet printing requirement.
5, it prints:
It is printed using intaglio press, which is provided with the laser carving plate roller with U-shaped depression, laser carving
The line number of roller of cutting blocks for printing is 25 lines, and depth is 60 μm, in the reverse side of above-mentioned base paper for tipping paper, is parallel to paper longitudinal direction, prints fire-retardant
Agent, fire retardant are Arabic gum: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight ratio of propylene glycol is 10:5:5:14:1, printing resistance
The width for firing agent is respectively 5mm and 10mm.
Product testing
Product inspection method and detection project are detailed in lower section embodiment 4.
Properties of product
Prepare the quantitative 35g/m of body paper for tobacco-use tipping paper2, air permeability 250CU, automatic distinguishing rate is 100% after cigarette.
Product packaging
Packaging facilities is thin film winding machine, by plastic winding films with certain tension, is uniformly wrapped on the outside of product, rises simultaneously
To fixed and protective action.
Product testing project table
Embodiment 4: product inspection method and detection project
According to shown in top " product testing project table ", properties of product are detected, specific detecting step is not superfluous herein
It states.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, and the present invention can have respectively
Kind change and variation.All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should all wrap
Containing within protection scope of the present invention.
Claims (9)
1. a kind of fire-retardant production method from saturating body paper for tobacco-use tipping paper, which is characterized in that this method comprises the following steps:
S100, mashing: needle slurry being ground through double plate and is beaten, beating consistency 65-750SR, weight in wet base 7-9g, and eucalyptus pulp is passed through
Double plate mill is discongested, beating consistency 15-200SR, weight in wet base 1-2g,
The needle handled well slurry and the eucalyptus pulp are mixed according to the proportion of weight ratio 30-35%:65-70%, connection is made
Slurry is closed,
The wet strength agent of the calcium carbonate and 1-1.4% of its total weight 30-50% is added in the joint slurry, is made and is mixed with beating
Material；
S200, copy paper: the material that is mixed with beating is diluted with water to the online concentration that weight ratio is 0.5-1.0%, is sequentially added
The AKD of the dispersing agent of 0.2-0.6% weight ratio, 1-2% weight ratio is manufactured paper with pulp forming by cylinder mould machine, to form uniform interleaving
Natural hole；
S300, drying: it after the page of forming is by squeezing further dehydration, is dried into multiple groups drying cylinder, when drying passes through
The compound mixture of agent machine coating oxidized starch and acrylic resin is applied on surface, is handled page surface performance,
Wherein, the weight ratio of oxidized starch and acrylic resin in the compound mixture is respectively 5-9% and 0.2-0.4%；
S400, press polish: ornamenting, paper smoothness 100-200s, paper are carried out by paper surface of the soft press-polishing machine to drying
The smooth exquisiteness in surface；And
S500, printing: paper longitudinal direction is parallel to, in the anti-of paper using intaglio press according to tipping paper printing surface specification
Fire retardant is printed in face, and the fire retardant is the mixture of Arabic gum, aluminium hydroxide, calcium carbonate, ethyl alcohol and propylene glycol.
2. the fire-retardant production method from saturating body paper for tobacco-use tipping paper according to claim 1, which is characterized in that in step
It in S200, manufactures paper with pulp when shaping, using spacer screen be 12-14 mesh, veil is the double cylinder mould machine composite moldings of 90-100 purpose；
60 μm of the aperture < of the nature hole, average pore size are 15-20 μm.
3. the fire-retardant production method from saturating body paper for tobacco-use tipping paper according to claim 1, which is characterized in that in step
In S300, the coating dosage of the compound mixture is 0.5-1.5g/m2。
4. the fire-retardant production method from saturating body paper for tobacco-use tipping paper according to claim 1, which is characterized in that in step
In S500, Arabic gum in the fire retardant: aluminium hydroxide: calcium carbonate: ethyl alcohol: the weight ratio of propylene glycol is 10:5:5:14:
1；
When printing fire retardant, there are ventilative blank areas for tipping paper；And
The fire retardant is 5-10mm in the width that reverse side of paper is printed.
5. a kind of suitable for the fire-retardant production system from saturating body paper for tobacco-use tipping paper production method described in any one of claim 1-4
System, which is characterized in that the system includes: refining system (100), copy paper system (200), drying system (300), calendaring system
(400) and print system (500)；
The refining system (100) is provided with double plate mill；
The copy paper system (200) is provided with that spacer screen is 12-14 mesh, veil is the double cylinder mould machines of 90-100 purpose, for copying
Cause shape；
The drying system (300) is provided with drying cylinder；
The calendaring system (400) is provided with soft press-polishing machine；And
The print system (500) is provided with intaglio press, and the intaglio press is provided with the carving of the laser with U-shaped depression
It cuts blocks for printing roller.
6. the fire-retardant production system from saturating body paper for tobacco-use tipping paper according to claim 5, which is characterized in that the mashing
System (100) is provided with 4 double plate mills, and preceding two double plates mill is cutting mill, and latter two are brooming mill；
The double plate mill is that TF20 type double plate is ground.
7. the fire-retardant production system from saturating body paper for tobacco-use tipping paper according to claim 5, which is characterized in that the laser
The line number for carving roller is 25 lines, and depth is 60 μm.
8. the fire-retardant production system from saturating body paper for tobacco-use tipping paper according to claim 5, which is characterized in that preceding dry drying cylinder
For Flying Dutchman, outer diameter φ 3000mm, temperature is 85-100 DEG C, rear dry drying cylinder by 4 outer diameter φ 1500mm multiple groups cylinder group
At temperature is 100-115 DEG C；And
MSP film transfer, which is provided with, between preceding dry drying cylinder and rear dry drying cylinder applies agent machine；
The fire-retardant production system from saturating body paper for tobacco-use tipping paper according to claim 5, which is characterized in that the soft calendaring
The outer diameter of machine is φ 680mm, and upper roller is steel rider, contact paper wire side, and lower roll is rubber roller, the contact non-wire side of paper；
The temperature of the steel rider is 120-130 DEG C, pressure 0.28-0.30MPa.
9. the fire-retardant production system from saturating body paper for tobacco-use tipping paper, feature according to any one of claim 5-9 exist
In further including detection system (600) and packaging system (700)；
The detection system (600) includes quantitative detection equipment (610), thickness detecting equipment (620), air permeability detection device
(630), tensile strength detection device (640), smoothness detection device (650), opacity detection device (660) and water suction
Property detection device (670)；
The quantitative detection equipment (610) is provided with proportional sampling device and electronic balance；
The thickness detecting equipment (620) is provided with thickness measuring instrument；
The air permeability detection device (630) is provided with air permeability instrument；
The tensile strength detection device (640) is provided with tensile strength tester；
The smoothness detection device (650) is provided with bekk smoothness instrument；
The opacity detection device (660) is provided with whiteness and colure meter；
The water imbibition detection device (670) is provided with can vigorous absorbability analyzer；And
The packaging system (700) is provided with thin film winding machine.