CN106368069A - Heating non-combustible cigarette paper and preparation method thereof - Google Patents
Heating non-combustible cigarette paper and preparation method thereof Download PDFInfo
- Publication number
- CN106368069A CN106368069A CN201610913140.7A CN201610913140A CN106368069A CN 106368069 A CN106368069 A CN 106368069A CN 201610913140 A CN201610913140 A CN 201610913140A CN 106368069 A CN106368069 A CN 106368069A
- Authority
- CN
- China
- Prior art keywords
- cigarette paper
- heating non
- preparation
- burning
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses heating non-combustible cigarette paper and a preparation method thereof. The preparation method of the heating non-burning cigarette paper comprises the following steps: 1) pulping the plant fiber with the length of 0.5 to 4mm, or adding the appropriate proportion of inorganic fiber; 2) adding the inorganic filler in the process of dilution of the pulp, wherein the addition ratio of the inorganic filler is 5 to 50% of the mass of the pulp; 3) sizing the paper to improve water and oil resistance, and cigarette paper is quantified at 50 to 120 g/m<2>. Compared with the existing heated non-combustible cigarette paper that is heated at 350 DEG C, the non-combustible cigarette paper of the present invention has very few yellow stitches, and no tar spots and carbonization, while the entire surface of the existing non-combustible cigarette paper turns yellow, with large tar penetrating and carbonized. In addition, the non-combustible cigarette paper of the present invention is rarely present broken in actual production, and there is almost no deformation and wrinkling after being sucked as the heated cigarette paper.
Description
Technical field
The present invention relates to a kind of heating non-burning cigarette paper and preparation method thereof, particularly to a kind of heating non-burning Nicotiana tabacum L.
Non-burning cigarette paper used by product.
Background technology
Step with international Tobacco Control campaign is more accelerated, the limit to smoking especially smoking in public places for the Chinese government
System is further strict, and has gradually formed social consensus.Under increasingly strict Tobacco Control environment, Partial Tobacco article consumer may
New non-traditional tobacco product can be selected, and this variation tendency is day by day clear.Show according to statistical data in 2015, in the world
While scope inner wrap strip volume of production and marketing has declined, other types tobacco product assumes rapid growth trend, World tobacco market
Constantly there is profound change in product structure, positive Development of Novel tobacco product is increasingly becoming the strategy of each transnational tobacco company
Orientation.
Traditional cigarette produces multiple harmful components due to result of combustion of tobacco and thermal cracking, and heating non-combustion-type Medicated cigarette produces
Flue gas is closer to traditional cigarette, and avoids because of 900 DEG C of high temperature above cracking substantial amounts of harmful components of generation, side-stream smoke
Substantially reduce with part harmful components, decrease the harm to body while consumer obtains gratification, and reduce
The pollution of environment flue gas.In addition, heating non-burning Medicated cigarette as most potential replacement traditional cigarette novel tobacco product, closely
The sales volume growth rate of 2 years is very swift and violent.And cigarette paper, as one of Medicated cigarette emphasis material, is heating non-burning Medicated cigarette
In research and development essential it is necessary to there be the cigarette paper complete sets of Techniques that can meet it head-on, could power-assisted Chinese-style cigarette product upgrading wound
Newly.
Existing heating non-burning cigarette paper technology is also disclosed, and such as " a kind of low-temperature heat type Medicated cigarette is not with for Chinese patent
Combustion cigarette paper and preparation method thereof ", application number cn201410437696.4.This patented technology pass through slurry in be filled with magnesium hydroxide,
Aluminium hydroxide and be coated with phosphorus flame retardant to reach the purpose do not fired when cigarette paper uses on paper substrate surface.Its disclosed embodiment
Testing result show, can accomplish that 350 DEG C do not fire (carbonization when 450 DEG C), but whole turn to be yellow.
Applicant is tested according to the cigarette paper that do not fire that the method that patent cn201410437696.4 provides obtains, and finds
There is during actually used blackened appearance, tar stain, Folding Deformation；Further, since quantitative low, low intensity, shape are steady
Property difference the problems such as easily cause during production processing curly course in frequently break paper problem.Obviously, existing do not fire cigarette paper skill
Art index is far from the actually used demand meeting heating non-burning Medicated cigarette.
Content of the invention
The purpose of the present invention solves the existing cigarette paper that do not fire to be existed when being applied to and heating non-burning Medicated cigarette
Drawbacks described above, provides a kind of Novel heating non-burning cigarette paper and preparation method thereof.
For reaching above-mentioned purpose, the technical scheme that the present invention takes is as follows:
A kind of preparation method of heating non-burning cigarette paper, comprises the steps:
1) choose Plant fiber's making beating that length is 0.5～4mm, or the inorfil mixing proper proportion；
2) add inorganic filler after grinding during thick stock dilution, the adding proportion of inorganic filler be stock quality 5～
50%；
3) applying glue after copy paper, improves water resistant, the grease resistance of body paper；
Quantification of 50～the 120g/ of cigarette paper.
Further, above-mentioned step 1), to length be 0.5～1.5mm, 3～4mm Plant fiber beating degree be 20～
40 ° of sr, fibre length is the beating degree of 1.5～3mm Plant fiber is 40～90 ° of sr.Described Plant fiber can be wood pulp,
The mixing slurry of one or more of jute pulp, straw pulp, described wood pulp include but are not limited to birch, Eucalyptus, Zelkova schneideriana Hand.-Mazz., Lignum seu Ramulus Cunninghamiae Lanceolatae or
Masson Pine, described ramie pulp fiber includes Fructus Cannabiss or Caulis et Folium Lini, and described straw pulp fiber includes but are not limited to Caulis et Folium Oryzae, straw or dragon
Grass.
Further, above-mentioned step 1), described inorfil includes but are not limited to alumina silicate fibre, shepardite fibre
Dimension, Calcium Carbonate fiber etc., further, the inorfil Particle size requirements 0.1～4mm of interpolation.Using Plant fiber and inorganic fibre
During the mixed slurry of dimension, the mass mixing ratio preferably 0.5～4:1 of Plant fiber and inorfil.
Further, above-mentioned step 2), described inorganic filler includes caco3, Pulvis Talci, caso4、al(oh)3.3h2o、
al2o3、mg(oh)2Deng one or more of mixture, preferably ca co3Or mg (oh)2；Inorganic filler Particle size requirements 0.3～
20 microns.The adding proportion of inorganic filler is preferably the 15～20% of stock quality.
Further, above-mentioned step 3), the sizing agent that applying glue adopts is stearic acid, calcium stearate, styrene-acrylate
Polymer, alkyl ketene dimer (akd), styrene acrylic polymers, styrene maleic anhydride copolymer, carboxymethyl cellulose
The single sizing agent such as element, polyvinyl alcohol, polyacrylamide, polyurethane or the mixture of multiple sizing agent, preferably alkyl alkene
Ketone dimer (akd) or styrene-acrylate polymers.
Further, in order to optimize follow-up papermaking properties, in step 2) add reinforcing agent afterwards, described reinforcing agent is oxidation
Starch, phosphate ester starch, hydroxyalkyl starch, acetate starch, cationic starch, guar gum, xanthan gum, casein, polyethylene
One of alcohol, polyacrylamide etc. or multiple mixture.The consumption of reinforcing agent is 5～30kg paper per ton, specifically can be
Add before pressurized screen.
Further, in order to optimize follow-up papermaking properties, in step 2) also can add a small amount of general cigarette paper afterwards with helping
Stay the process assistants such as agent, such as cationic starch etc., the ratio of interpolation is 1～5kg paper per ton.Specifically can add after pressurized screen.
Beneficial effects of the present invention:
The present invention is manufactured paper with pulp body paper using the fiber through making beating, after being filled with, then through glue-applying technique, body paper is changed in slurry
Property, reduce the cracking of cigarette paper and hydrophilic, reach that raising cigarette paper is heat-resisting, anti-deformation, the purpose of impermeabilisation ability.
The present invention is not burnt with existing heating compared with cigarette paper, with 350 DEG C heat when, the non-burning Medicated cigarette of the present invention
The stitching of the only few jaundice of paper, existing cigarette paper whole surface of not firing all is turned to be yellow；The non-burning cigarette paper of the present invention does not have
There is tar stain and start carbonization phenomenon, and the existing cigarette paper that do not fire has the infiltration of bulk tar and starts carbonization.In addition, the present invention
Non-burning cigarette paper disconnected paper phenomenon also seldom occurs in actual production, almost do not have as after the cigarette paper suction of hot type
There are deformation and gauffer.
Below in conjunction with drawings and Examples, the specific implementation method of the present invention is elaborated.
Brief description
Fig. 1 is that the prepared heating non-burning cigarette paper of embodiment 1 heats the outward appearance after 6 mouthfuls of suction in 350 DEG C of heaters
Picture.Heating non-burning cigarette paper whiteness conservation rate is 90%, and the problems such as tar stain, deformation.
Fig. 2 heats the outward appearance picture after 6 mouthfuls of suction for cigarette paper prepared by comparative example 1 in 350 DEG C of heaters.Cigarette paper
Whiteness conservation rate is 44%, and the problems such as serious tar stain, deformation.
Specific embodiment
Embodiment 1: prepare quantification of 90g/m2Heating non-burning cigarette paper
Using fibrous raw material, inorganic filler, reinforcing agent, sizing agent and, retention agent and some processes index see table 1,
Inorfil Particle size requirements 0.1～4mm, 0.3～20 micron of inorganic filler Particle size requirements.
Table 1
Other slurrying and copy paper technique are carried out according to the production technology of general cigarette paper.
By the quantification of 90g/m obtaining2Heating non-burning cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of suction, the whiteness taking out photographic analysis cigarette paper is 80%, and whiteness conservation rate is 90%；Additionally,
After 6 mouthfuls of continuous sucking, the problems such as tar stain, deformation in outward appearance.Illustrate using adding that the inventive method prepares
Hot non-burning cigarette paper can be actually used in 350 DEG C of heating non-burning Medicated cigarette.
Embodiment 2: prepare quantification of 120g/m2Heating non-burning cigarette paper
Using fibrous raw material, inorganic filler, reinforcing agent, sizing agent and, retention agent and some processes index see table 2,
Inorfil Particle size requirements 0.1～4mm, 0.3～20 micron of inorganic filler Particle size requirements.
Table 2
Other slurrying and copy paper technique are carried out according to the production technology of general cigarette paper.
By the quantification of 120g/m obtaining2Heating non-burning cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of suction, the whiteness taking out photographic analysis cigarette paper is 88%, and whiteness conservation rate is 98%；Additionally,
After 6 mouthfuls of continuous sucking, the problems such as tar stain, deformation in outward appearance.The heating being prepared using inventive method is described
Non-burning cigarette paper can be actually used in 350 DEG C of heating non-burning Medicated cigarette, and indices are excellent.
Embodiment 3: prepare quantification of 90g/m2Heating non-burning cigarette paper
Using fibrous raw material, inorganic filler, reinforcing agent, sizing agent and, retention agent and some processes index see table 3,
Inorfil Particle size requirements 0.1～4mm, 0.3～20 micron of inorganic filler Particle size requirements.
Table 3
Other slurrying and copy paper technique are carried out according to the production technology of general cigarette paper.
By the quantification of 90g/m obtaining2Heating non-burning cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of suction, the whiteness taking out photographic analysis cigarette paper is 86%, and whiteness conservation rate is 96%；Additionally,
After 6 mouthfuls of continuous sucking, the problems such as tar stain, deformation in outward appearance.Illustrate using adding that the inventive method prepares
Hot non-burning cigarette paper successfully can use in 350 DEG C of heating non-burning Medicated cigarette, and effect is fine.
Embodiment 4: prepare quantification of 100g/m2Heating non-burning cigarette paper
Using fibrous raw material, inorganic filler, reinforcing agent, sizing agent and, retention agent and some processes index see table 4,
Inorfil Particle size requirements 0.1～4mm, 0.3～20 micron of inorganic filler Particle size requirements.
Table 4
Other slurrying and copy paper technique are carried out according to the production technology of general cigarette paper.
By the quantification of 100g/m obtaining2Heating non-burning cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of suction, the whiteness taking out photographic analysis cigarette paper is 86%, and whiteness conservation rate is 96%；Additionally,
After 6 mouthfuls of continuous sucking, the problems such as tar stain, deformation in outward appearance.Heating non-burning using this method preparation is described
Cigarette paper can heat at 350 DEG C can practical application in non-burning Medicated cigarette.
Embodiment 5: prepare quantification of 50g/m2Heating non-burning cigarette paper
Using fibrous raw material, inorganic filler, reinforcing agent, sizing agent and, retention agent and some processes index see table 5,
Inorfil Particle size requirements 0.1～4mm, 0.3～20 micron of inorganic filler Particle size requirements.
Table 5
Other slurrying and copy paper technique are carried out according to the production technology of general cigarette paper.
By the quantification of 50g/m obtaining2Heating non-burning cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of suction, the whiteness taking out photographic analysis cigarette paper is 80%, and whiteness conservation rate is 90%；Additionally,
After 6 mouthfuls of continuous sucking, the problems such as tar stain, deformation in outward appearance.Heating non-burning using this method preparation is described
Cigarette paper successfully can use in 350 DEG C of heating non-burning Medicated cigarette.
Comparative example 1:
Table 6 does not fire cigarette paper composition
Quantification of 32g/m prepared by comparative example 12Do not fire cigarette paper, with 350 DEG C heating non-burning cigarette heater enter
Row heats and aspirates, and after 6 mouthfuls of continuous sucking, the whiteness taking out photographic analysis cigarette paper is 40%, and whiteness conservation rate is 44%, and
And by accompanying drawing as can be seen that comparative example method be obtained do not fire cigarette paper after 6 mouthfuls of continuous sucking, occur serious tar stain,
The problems such as blackened appearance, is it is impossible to enough use in 350 DEG C of heating non-burning cigarette heater.Illustrate to use ammonium polyphosphate flame retardant
Although can be fire-retardant, cigarette paper has turned yellow blackening, and has serious tar stain it is impossible to practical application.
The heating non-burning cigarette paper that the inventive method is obtained, carries out adding with 350 DEG C of heating non-burning cigarette heater
Heat is simultaneously aspirated, and after 6 mouthfuls of continuous sucking, taking-up is taken pictures, and the whiteness using cigarette paper after Instrumental Analysis suction, and analysis result shows
After 6 mouthfuls of continuous sucking, the whiteness scope of cigarette paper is 80～88%, and whiteness conservation rate is 85～98%；Additionally, by illustrating
The attached Fig. 1 and 2 of book can be seen that the prepared heating non-burning cigarette paper of the inventive method after 6 mouthfuls of continuous sucking, Jiao
The problems such as oil mark, deformation.Illustrate to add at 350 DEG C and less than 350 DEG C using the heating non-burning cigarette paper of this method preparation
Successfully use in hot non-burning Medicated cigarette.
In addition, the heating non-burning cigarette paper of the present invention is in production and follow-up processing curly course, do not occur existing
The common paper phenomenon of frequently breaking of some cigarette paper.
Claims (11)
1. a kind of preparation method of heating non-burning cigarette paper, comprises the steps:
1) choose Plant fiber's making beating that length is 0.5～4mm, or the inorfil mixing proper proportion；
2) add inorganic filler during thick stock dilution after grinding, the adding proportion of inorganic filler is the 5～50% of stock quality；
3) applying glue after copy paper, improves water resistant, the grease resistance of body paper；
Quantification of 50～the 120g/ of cigarette paper.
2. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: described step 1), right
Length is 0.5～1.5mm, the beating degree of 3～4mm Plant fiber is 20～40 ° of sr, and length is beating of 1.5～3mm Plant fiber
The degree of beating is 40～90 ° of sr.
3. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: described step 1),
Inorfil is mixed, the mass mixing ratio of Plant fiber and inorfil is 0.5～4:1 in vegetable-fibre slurry.
4. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: described inorfil bag
Include alumina silicate fibre, brucite fiber or Calcium Carbonate.
5. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: described inorfil grain
Footpath requires 0.1～4mm.
6. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: step 2) described in inorganic
Filler is caco3, Pulvis Talci, caso4、al(oh)3.3h2o、al2o3、mg(oh)2One or more of mixture.
7. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: inorganic filler Particle size requirements
0.3～20 micron.
8. heating non-burning cigarette paper as claimed in claim 1 preparation method it is characterised in that: step 3) applying glue that adopts
Agent is stearic acid, calcium stearate, styrene-acrylate polymers, alkyl ketene dimer, styrene acrylic polymers, benzene
The single sizing agent such as ethenyl maleic anhydride copolymer, carboxymethyl cellulose, polyvinyl alcohol, polyacrylamide, polyurethane or
The mixture of multiple sizing agents.
9. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: before pressurized screen add increase
Strong agent, described reinforcing agent is Oxytarch, phosphate ester starch, hydroxyalkyl starch, acetate starch, cationic starch, Guar
One of glue, xanthan gum, casein, polyvinyl alcohol, polyacrylamide etc. or multiple mixture.
10. as claimed in claim 1 heating non-burning cigarette paper preparation method it is characterised in that: after pressurized screen add
Retention agent, addition is 1～5kg paper per ton.
The heating non-burning Medicated cigarette that the preparation method of the arbitrary described heating non-burning cigarette paper of 11. claim 1-10 obtains
Paper.