CN103290721B - Production method of tipping base paper for flame-retardant cigarettes - Google Patents
Production method of tipping base paper for flame-retardant cigarettes Download PDFInfo
- Publication number
- CN103290721B CN103290721B CN201310188921.0A CN201310188921A CN103290721B CN 103290721 B CN103290721 B CN 103290721B CN 201310188921 A CN201310188921 A CN 201310188921A CN 103290721 B CN103290721 B CN 103290721B
- Authority
- CN
- China
- Prior art keywords
- pulp
- slurry
- mixing
- paper
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a production method of tipping base paper for flame-retardant cigarettes. The production method of tipping base paper for flame-retardant cigarettes comprises the following steps of: continuously beating softwood pulp and hardwood pulp by using a double disc refiner, wherein the beating concentration of the softwood pulp is 3.4-4.4% and the beating degree is 65-750SR, the beating concentration of the hardwood pulp is 3.8-4.2% and the beating degree is 60-700SR; mixing the pulped softwood pulp and the pulped hardwood pulp in a weight ratio of 40-65% to 35-60% as mixed pulp for future use. The raw materials, filling substances, various additives and the surface additives during producing the products are innocuous and non-poisonous products, so that the tipping base paper for flame-retardant cigarettes is low in heavy metal content, free of fluorescent whitening agent and good in flame retardant property. The tipping base paper is coiled on the cigarettes, so that the cigarettes can be automatically extinguished when the cigarettes are combusted to the position of the tipping base paper for the flame-retardant cigarettes.
Description
technical field
The present invention relates to a kind of production method of fire-retardant body paper for tobacco-use tipping paper.
background technology
People suck after cigarette, owing to there is no extinguish cigarette end timely, easily cause fire, along with the attention of country to fire safety evaluating problem, the raising of people's inherently safe consciousness, requires tobacco business to strengthen the security of cigarette product self, reduces the fire safety evaluating hidden danger of cigarette product, meet the development requirement to safety, environment-friendly products in industry, the body paper for tobacco-use tipping paper that market demand research and development can be fire-retardant.
summary of the invention
The object of the invention is to for the deficiencies in the prior art, the production method of fire-retardant body paper for tobacco-use tipping paper is provided, by the anti-flammability that has of tipping body paper self, can automatic distinguishing when reaching cigarette and being burned to stub, improved preferably the problem of security.
Fire-retardant body paper for tobacco-use tipping paper basic material mainly contains various strings and forms, and string is ground and carried out wire-dividing broom purification by double plate, makes it have certain beating degree, guarantees can reach the combination that is well interweaved between fiber, forms the basic framework of paper; Packing material improves paper printing characteristic, improves the opacity of paper as talcum powder, titanium dioxide etc. can play, make paper have high temperature resistant, heat conductivility not preferably, increases fire resistance; And each analog assistant is as improved keeping of fiber fines and filler adding of cationic starch, polyacrylamide etc., guarantee paper formation and intensity, further improve paper fire resistance simultaneously.
Fire-retardant body paper for tobacco-use tipping paper is mainly comprised of following several constituents:
Basic material: mainly contain softwood pulp, hardwood pulp, straw pulp, bamboo pulp, reed pulp (or other non-wood materials) etc., basic material accounts for the 70-95% of total composition.
Packing material: mainly comprise grinding calcium carbonate, mineral fibres, talcum powder, kaolin, titanium dioxide, magnesia, magnesium hydroxide, aluminium hydroxide etc.Packing material accounts for the 5-30% of total composition.
Each analog assistant: mainly comprise bactericide, defoamer, Polyamide-Polyamsne-Epichlorohydrin resin (or other wet strength agents), cationic starch, polymine, polyacrylamide, alkyl ketene dimer (or other neutral sizing agents) etc.Each analog assistant accounts for total composition 5%-10%.
Table is coated with auxiliary agent: fire retardant, water repellent agent, polyvinyl alcohol, alginate, carboxymethyl cellulose (or other cellulose derivatives), styrene-butadiene latex (or other adhesives), thickener, printability agent, oxidized starch (or other converted starches) etc.Each analog assistant accounts for total composition 10%-30%.
Above-mentioned object realizes by following technical scheme:
1, a production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0between SR; Hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0between SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9%, be coated with composite mixture weight at 0.3-1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9%, is coated with composite mixture weight at 0.3-1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
Described hardwood pulp replaces with hardwood pulp and mixes slurry with bamboo pulp, and wherein hardwood pulp and bamboo pulp part by weight are 2:1.
Described hardwood pulp replaces with straw pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
Described copy paper workshop section replaces with: in the mixing slurry preparing in beater floor with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3-5g/m
2, table is proceeded after being coated with to dry again,
Described talcum powder replaces with grinding calcium carbonate.
Described talcum powder replaces with and grinds ridge soil.
Described oxidized starch replaces with carboxymethyl cellulose.
Described oxidized starch replaces with polyvinyl alcohol.
Beneficial effect:
The invention belongs to fire-retardant body paper for tobacco-use tipping paper production technology, its fire resistance is mainly by attaching filler, each analog assistant and realizing by surface size press light coating in starching.Sizing material in coating be take water as dispersed emulsion, selects suspension is good, content of beary metal is low fire retardant, water repellent agent to be equipped with the table painting auxiliary agent dispersions such as oxidized starch wherein simultaneously, realizes coating good uniformity by coating method.During production, selected raw material, filler, each analog assistant and table are coated with auxiliary agent and are nontoxic product, content of beary metal is low, not containing fluorescence optical brightener, its fire resistance is good, with it, twist in cigarette, when cigarette is burned to fire-retardant body paper for tobacco-use tipping paper position, can automatic distinguishing, the rate of certainly putting out reaches 100%.
Flame-retardant tipping paper body paper is compared with common tipping paper body paper, has stronger fire resistance and not sticky lip performance.During production, selected raw material, auxiliary material, auxiliary agent and table are coated with auxiliary agent and are nontoxic product, content of beary metal is low, not containing fluorescence optical brightener, its fire resistance is good, twists in cigarette, with it when cigarette is burned to flame-retardant tipping paper position, can automatic distinguishing, from the rate of putting out, reach 100%, while effectively having prevented because of cigarette combustion to stub, do not extinguish and cause fire, greatly strengthened the security of product.In addition product has higher WATER RESISTANCE and opacity, and good bond strength can meet high-speed press requirement.
The production method of above-mentioned a kind of fire-retardant body paper for tobacco-use tipping paper all can reach fire resistance, meet the requirement of client to fire resistance, technical scheme is except hardwood pulp slurry kind of difference, it is different that main difference point is that table is coated with technique, wherein example 1-6 carries out light coating, composite mixture viscosity is low, and coating weight is at 0.3-1.0g/m
2, example 7-12 table coated joins that component of mixture is many, and viscosity is large, and coating weight is at 3-5g/m
2, the tipping paper body paper surface film-formation result of producing is splendid, has heat-resisting, airtight, heat conductivility not preferably, and on flame retardant effect, outline is better than example 1-6.
the specific embodiment
embodiment 1
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0sR; Hardwood pulp beating consistency is 3.8%, beating degree guarantees 60
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40%:60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 40% of slurry gross weight, titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, cationic starch dosage is for mixing 1.0% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 7% of oxidized starch and fire retardant, be coated with composite mixture weight at 0.3g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 7% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 0.3g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 2
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0sR; Hardwood pulp beating consistency is 4.2%, beating degree guarantees 70
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 65%:35% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 80% of slurry gross weight, titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, cationic starch dosage is for mixing 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 9% of oxidized starch and fire retardant, be coated with composite mixture weight at 1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 9% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 3
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 4%, beating degree guarantees 70
0sR; Hardwood pulp beating consistency is 4%, beating degree guarantees 65
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 50%:50% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 60% of slurry gross weight, titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, cationic starch dosage is for mixing 1.1% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 8% of oxidized starch and fire retardant, be coated with composite mixture weight at 0.8g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 8% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 0.8g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 4
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 3.8%, beating degree guarantees 60
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 40%:60%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 40% of slurry gross weight, titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, cationic starch dosage is for mixing 1.0% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 7% of oxidized starch and fire retardant, be coated with composite mixture weight at 0.3g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 7% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 0.3g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 5
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 4.2%, beating degree guarantees 70
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 65%:35%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 80% of slurry gross weight, titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, cationic starch dosage is for mixing 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 9% of oxidized starch and fire retardant, be coated with composite mixture weight at 1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 9% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 6
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 4%, beating degree guarantees 70
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 4%, beating degree guarantees 65
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 50%:50%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing 60% of slurry gross weight, titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, cationic starch dosage is for mixing 1.1% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration 8% of oxidized starch and fire retardant, be coated with composite mixture weight at 0.8g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration 8% of water, oxidized starch and water repellent agent, is coated with composite mixture weight at 0.8g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 7
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0sR; Hardwood pulp beating consistency is 3.8%, beating degree guarantees 60
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40%:60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing 40% of slurry gross weight, titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, cationic starch dosage is for mixing 1.0% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 8
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0sR; Hardwood pulp beating consistency is 4.2%, beating degree guarantees 70
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 65%:35% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing 80% of slurry gross weight, titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, cationic starch dosage is for mixing 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 5g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 9
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 4%, beating degree guarantees 70
0sR; Hardwood pulp beating consistency is 4%, beating degree guarantees 65
0sR; The softwood pulp of slurry and the hardwood pulp ratio with weight 50%:50% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing 60% of slurry gross weight, titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, cationic starch dosage is for mixing 1.1% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 4g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp can replace with straw pulp, bamboo pulp or reed pulp.
embodiment 10
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 3.4%, beating degree guarantees 65
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 3.8%, beating degree guarantees 60
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 40%:60%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder, titanium dioxide is filler, and wherein talcum powder dosage is for mixing 40% of slurry gross weight, titanium dioxide dosage is for mixing 3% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13% of slurry gross weight, cationic starch dosage is for mixing 1.0% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.
Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 11
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 4.4%, beating degree guarantees 75
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 4.2%, beating degree guarantees 70
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 65%:35%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder, titanium dioxide is filler, and wherein talcum powder dosage is for mixing 80% of slurry gross weight, titanium dioxide dosage is for mixing 5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.15% of slurry gross weight, cationic starch dosage is for mixing 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 5g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 12
A production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 4%, beating degree guarantees 70
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 4%, beating degree guarantees 65
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 50%:50%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder, titanium dioxide is filler, and wherein talcum powder dosage is for mixing 60% of slurry gross weight, titanium dioxide dosage is for mixing 4% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.4% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.14% of slurry gross weight, cationic starch dosage is for mixing 1.1% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 4g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp mixes slurry and replaces with straw pulp and mix slurry with reed pulp with bamboo pulp, wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 13
1, a production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0between SR; Hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0between SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9%, be coated with composite mixture weight at 0.3-1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9%, is coated with composite mixture weight at 0.3-1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
embodiment 14
1, a production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 40～65%:35～60%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9%, be coated with composite mixture weight at 0.3-1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9%, is coated with composite mixture weight at 0.3-1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp with bamboo pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
embodiment 15
1, a production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0between SR; Hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0between SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3-5g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
embodiment 16
1, a production method for fire-retardant body paper for tobacco-use tipping paper, comprises the steps:
(1), beater floor, hardwood pulp is mixed to slurry, softwood pulp with bamboo pulp and adopts two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0sR; The 2:1 making beating that is mixed by weight proportion of hardwood pulp and bamboo pulp, beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0sR; By accomplishing fluently the softwood pulp of slurry and hardwood pulp, mix slurry with bamboo pulp and with the ratio of weight 40～65%:35～60%, be made into that to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3-5g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
Described talcum powder can replace with grinding calcium carbonate or grind ridge soil.Described oxidized starch can replace with carboxymethyl cellulose or polyvinyl alcohol.Described hardwood pulp replaces with straw pulp with bamboo pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
Claims (9)
1. a production method for fire-retardant body paper for tobacco-use tipping paper, is characterized in that comprising the steps:
(1), beater floor, softwood pulp and hardwood pulp are adopted to two disc grinder continuous beatings, softwood pulp beating consistency is 3.4～4.4%, beating degree guarantees 65～75
0between SR; Hardwood pulp beating consistency is 3.8～4.2%, beating degree guarantees 60～70
0between SR; The softwood pulp of slurry and the hardwood pulp ratio with weight 40～65%:35～60% of accomplishing fluently is made into to mix slurry stand-by;
(2), copy paper workshop section, in the mixing preparing in beater floor slurry with talcum powder
,titanium dioxide is filler, wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, through executing agent machine, front page one side surface after dry show to painting water, the mixture that oxidized starch and fire retardant are composite, wherein oxidized starch and fire retardant interpolation part by weight are 1:0.5, water, the composite mixture total concentration of oxidized starch and fire retardant 7-9%, be coated with composite mixture weight at 0.3-1.0g/m
2, opposite side table is coated with water, oxidized starch and the composite mixture of water repellent agent, and wherein oxidized starch and water repellent agent interpolation part by weight are 1:3, and the composite mixture total concentration of water, oxidized starch and water repellent agent 7-9%, is coated with composite mixture weight at 0.3-1.0g/m
2, table is proceeded after being coated with to dry again,
(3), press polish workshop section, adopt calender to carry out press polish to the page after drying, make product there is the characteristic that glossiness is good, can make tipping paper obtain splendid levelling effect, make paper there is certain smoothness, produce and meet printing performance requirement, and there is the body paper for tobacco-use tipping paper of fire resistance.
2. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1, is characterized in that described hardwood pulp replaces with straw pulp, bamboo pulp or reed pulp.
3. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1, is characterized in that: described hardwood pulp replaces with hardwood pulp and mixes slurry with bamboo pulp, and wherein hardwood pulp and bamboo pulp part by weight are 2:1.
4. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 1, is characterized in that: described hardwood pulp replaces with straw pulp and mixes slurry with reed pulp, and wherein straw pulp and reed pulp part by weight are 2:1.
5. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as described in claim 1-4 any one, is characterized in that: described copy paper workshop section replaces with: in the mixing slurry preparing in beater floor with talcum powder
,titanium dioxide is filler, and wherein talcum powder dosage is for mixing the 40-80% of slurry gross weight, titanium dioxide dosage is for mixing the 3-5% of slurry gross weight, and adopt the mode attaching continuously to attach neutral sizing agent alkyl ketene dimer, dosage is for mixing 0.2 ~ 0.5% of slurry gross weight, in the mixing slurry preparing, attach the double base retention agent forming with cationic polyacrylamide and cationic starch again, make body paper there is certain anti-current body permeance property, improve into dimensional stability, cationic polyacrylamide dosage is for mixing 0.13～0.15% of slurry gross weight, cationic starch dosage is for mixing 1.0 ~ 1.2% of slurry gross weight, then make to mix slurry after wet end and press section drainage and formation, l Water Paper page enters the front dry stage dries, and through executing agent machine, front page both side surface after dry show to painting water, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, the composite mixture that aluminium hydroxide forms, water in composite mixture, oxidized starch, styrene-butadiene latex, thickener, fire retardant, water repellent agent, magnesium hydroxide, aluminium hydroxide part by weight is 30%:25%:15%:5%:5%:10%:5%:5%, is coated with composite mixture weight at 3-5g/m
2, table is proceeded after being coated with to dry again.
6. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 5, is characterized in that: described talcum powder replaces with grinding calcium carbonate or grinds ridge soil.
7. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as claimed in claim 5, is characterized in that: described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.
8. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as described in claim 1-4 any one, is characterized in that: described talcum powder replaces with grinding calcium carbonate or grinds ridge soil.
9. the production method of a kind of fire-retardant body paper for tobacco-use tipping paper as described in claim 1-4 any one, is characterized in that: described oxidized starch replaces with carboxymethyl cellulose or polyvinyl alcohol.