CN110172868A - A kind of composite cigarette paper for magnetic grain soaking tobacco product - Google Patents
A kind of composite cigarette paper for magnetic grain soaking tobacco product Download PDFInfo
- Publication number
- CN110172868A CN110172868A CN201910358730.1A CN201910358730A CN110172868A CN 110172868 A CN110172868 A CN 110172868A CN 201910358730 A CN201910358730 A CN 201910358730A CN 110172868 A CN110172868 A CN 110172868A
- Authority
- CN
- China
- Prior art keywords
- cigarette
- cigarette paper
- paper
- composite
- filmogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of composite cigarette papers for magnetic grain soaking tobacco product, it is made of cigarette fibrous paper, filmogen and the adhesive layer between fiber cigarette paper and filmogen.Composite cigarette paper of the present invention not only solves the basic problems such as magnetic grain soaking tobacco product cigarette paper heatproof, heat preservation, constant temperature, while cigarette is sucked rear fibrous paper surface and shown without discoloration, carbonization etc., cigarette good appearance.It is excessive that composite cigarette paper of the present invention not only avoids the equal thermal process smokeless of cigarette, while effectively improving suction relaxation and flue gas organoleptic quality.
Description
[technical field]
The invention belongs to technical field of cigarette production.More particularly it relates to which a kind of be used for magnetic grain soaking tobacco system
The composite cigarette paper of product.
[background technique]
In recent years, with tobacco control situation be more becoming tight and consumer steps up health concerns degree, various countries pair
Public place smoking control is further stringent.It is not burnt with heating, the soaking of magnetic grain, the categories such as electronic cigarette and smoke-free tobacco product
New tobacco products gradually by the favor of the majority of consumers.The new tobacco products research and development of current each category, design and
The great attention by domestic and international tobacco business is manufactured, and becomes the hot subject of tobacco research.
As the new category of new tobacco products-magnetic grain soaking tobacco product, with common cigarette appearance without essential difference, by filtering
Mouth, cigarette paper and soaking tobacco matrix composition, wherein there is special strict demand for cigarette paper, such as: insulation is reduced
Thermal loss；It is resistant to certain temperature, cigarette paper is prevented to be carbonized, influences consumption experience；Steady temperature guarantees that flue gas is uniformly released
It puts；With certain solvent barrier effect, guarantee that cigarette paper appearance does not occur solvent spot.Common cigarette paper is not possible to meet
The requirement of magnetic grain soaking tobacco product, cigarette paper used in other category new tobacco productses (as low temperature does not burn tobacco product)
It is unable to satisfy requirement, if CN 104452479B is related to a kind of composite cigarette paper with aluminium foil layer, passes through outer layer wood pulp cellulose
Paper burning heat supply, heats the pipe tobacco wrapped up by aluminium foil, which will lead to cigarette burning since outer layer fiber paper is inflammable
Or appearance carbonization blacks, and is not suitable for magnetic grain soaking tobacco product, is taking out further, since being easily led to using laser or mechanical punching
There is the excessive phenomenon of flue gas during inhaling, causes punch position solvent spot occur, influence consumption experience；CN 104452418B,CN
There is similar technical application problem in 201510624220 and CN 201420653193 etc..Therefore, it needs to develop at present suitable
Special cigarette paper for New Magnetic Field Controlled grain soaking tobacco product.
[summary of the invention]
[technical problems to be solved]
The object of the present invention is to provide a kind of composite cigarette papers for magnetic grain soaking tobacco product.
[technical solution]
The present invention is achieved through the following technical solutions.
The present invention relates to a kind of composite cigarette papers for magnetic grain soaking tobacco product.
This composite cigarette paper is by cigarette fibrous paper, filmogen and between fiber cigarette paper and filmogen
Adhesive layer composition.
A preferred embodiment of the invention, the cigarette fibrous paper are fine selected from wood pulp by one or more
Dimension, ramie pulp fiber or other sponges plant fiber, pearl filler and auxiliary agent according to 60~80:20 of weight ratio~
What 35:2~4 was formed.
According to another preferred method of implementation of the present invention, quantifying for the cigarette fibrous paper is 10~50g/m2, anti-tensile
Energy absorption index is 150mJ/g or more.
According to another preferred method of implementation of the present invention, the auxiliary agent is one or more selected from sodium metasilicate, phosphoric acid
The auxiliary agent of hydrogen diammonium, silica or ammonium polyphosphate.
According to another preferred method of implementation of the present invention, the filmogen is the aluminium with a thickness of 0.004~0.2mm
The ferroaluminium that content is by weight 6~16%.
According to another preferred method of implementation of the present invention, quantifying for the filmogen is 10~40g/m2, anti-tensile energy
Measuring absorption index is 150~600mJ/g.
According to another preferred method of implementation of the present invention, the adhesive is one or more selected from vinyl acetate-
Ethylene copolymer, vinyl acetate homopolymer or vinyl acetate-butyl acrylate copolymer adhesive, it contains by weight 5
~20% aerosil.
According to another preferred method of implementation of the present invention, the temperature resistant range of the adhesive is 200~600 DEG C；Viscosity
It is 125~450mpa.s；Resin added is 0.5~1.5g/m2。
According to another preferred method of implementation of the present invention, the air permeability of the composite cigarette paper is 10~60CU；It is quantitative
It is 25~95g/m2；Opacity is greater than 70%.
According to another preferred method of implementation of the present invention, the thickness ratio of cigarette fibrous paper, filmogen and adhesive layer
1:0.06~0.50:0.02~0.10.
The present invention is described in more detail below.
The present invention relates to a kind of composite cigarette papers for magnetic grain soaking tobacco product.
In the present invention, the magnetic grain soaking tobacco product is it should be understood that a kind of be evenly heated utensil for electromagnetic induction
The tobacco product used.
This composite cigarette paper is by cigarette fibrous paper, filmogen and between fiber cigarette paper and filmogen
Adhesive layer composition.
According to the present invention, the cigarette fibrous paper is by one or more selected from wood pulp cellulose, ramie pulp fiber or other
Plant fiber, pearl filler and the auxiliary agent of sponge are formed according to 60~80:20 of weight ratio~35:2~4.
In the present invention, basic role of the plant fiber in cigarette fibrous paper is to provide the skeleton of cigarette paper.
The present invention is 10~50g/m using quantifying for cigarette fibrous paper2；If the fibrous paper is quantitatively more than the range, i.e.,
Lower than 10g/m2Or it is higher than 50g/m2It is all worthless, this is because this is quantitative too low, cigarette appearance has fold and is difficult to multiple
Processing is closed, and this is quantitative excessively high, is difficult to compound or cigarette and is not easy to roll.
The present invention is 150mJ/g or more using the tensile energy absorption index of cigarette fibrous paper.If the tensile energy is inhaled
It receives index and is lower than 150mJ/g, then the fracture of paper compound tense fibre paper easily occur.
The plant fiber that the present invention uses is wood pulp cellulose, ramie pulp fiber or other sponges, their length
Usually 0.62~0.85mm, and width is usually 20~35 μm.The plant fiber that the present invention uses all is to sell currently on the market
The product sold, for example, sold by Qingdao Zhong Yi Trade Development Co., Ltd with trade name Chile Venus wood pulp cellulose, by Shanghai
Ramie pulp fiber that Pu Lai Ma International Trading Company Ltd is sold with trade name Spain Sai Laisha, by the limited public affairs of Dalian Yang Run trade
Take charge of other plant fibers such as the straw pulp fiber sold with Trade Name Chemical straw pulp.
In the present invention, main function of the pearl filler in cigarette fibrous paper be adjust paper air permeability and
Opacity.Certainly, all that there is this effect, and other filled out to what magnetic grain soaking tobacco product will not have a negative impact
Material matter may be used to the present invention, they are also within protection scope of the present invention.
The pearl filler that the present invention uses is precipitated calcium carbonate, powdered whiting or calcene filler, preferably
It is precipitated calcium carbonate.The pearl filler that the present invention uses all is current market sales of product, such as auspicious greatly by Jiangxi Province
Chemical Co., Ltd. with trade name greatly the precipitated calcium carbonate of auspicious precipitated calcium carbonate sale, by Guangzhou Bang You Chemical Industry Science Co., Ltd
With trade name powdered whiting sale powdered whiting, by great Rui Chemical Co., Ltd., Jiangxi Province with trade name nano active carbon
The calcene of sour calcium sale.
In the present invention, the auxiliary agent is it should be understood that a kind of substance with catalytic flame retardancy performance, it is in cigarette fibre
Basic role in dimension paper is to reduce cigarette paper carbonization, promote appearance of the cigarette after suction.Certainly, all that there is this work
With, and the other auxiliary materials that will not be had a negative impact to magnetic grain soaking tobacco product may be used to the present invention, they
Also within protection scope of the present invention.
According to the present invention, the auxiliary agent is one or more selected from sodium metasilicate, diammonium hydrogen phosphate, silica or poly
The auxiliary agent of ammonium phosphate.The auxiliary agent that the present invention uses all is current market sales of product, such as is had by the Jinan source Xin Sen chemical industry
Sodium metasilicate that limit company is sold with trade name quick dissolved sodium silicate is sold by Shandong Shi An Chemical Co., Ltd. with trade name APP
Ammonium polyphosphate.
In the present invention, the weight ratio of plant fiber, pearl filler and auxiliary agent is 60~80:20~35:2~4.
In the present invention, when the dosage of pearl filler and auxiliary agent is in the range, if the dosage of plant fiber
Lower than 60, then paper tensile strength reduces；If the dosage of plant fiber is higher than 80, paper opacity is insufficient；Therefore, it plants
It is suitable that the dosage of fibres, which is 60~80,；Preferably 65~72.
Similarly, when the dosage of plant fiber and auxiliary agent is in the range, if the dosage of pearl filler is lower than 20,
Then paper opacity is insufficient；If the dosage of pearl filler is higher than 35, air permeability is higher, the easy permeability of cigarette；Therefore, carbon
It is feasible that the dosage of sour calcium filler, which is 20~35,；Preferably 25~30.
When the dosage of plant fiber and pearl filler is in the range, if the dosage of auxiliary agent is lower than 2, aspirating
Cigarette paper is easily carbonized discoloration afterwards；If the dosage of auxiliary agent is higher than 4, paper tensile strength is reduced；Therefore, the dosage of auxiliary agent is 2
~4 be feasible；Preferably 2.6~3.5.
In the present invention, the filmogen is it should be understood that a kind of material with heat production heat preservation and barrier property,
Its basic role in composite cigarette paper of the present invention is heat preservation and antiseep.Certainly, all that there is this effect, and to magnetic
Other filmogens that grain soaking tobacco product will not have a negative impact may be used to the present invention, they are also of the invention
Within protection scope.
According to the present invention, the filmogen be with a thickness of 0.004~0.2mm aluminium content be by weight 6~
16% ferroaluminium, it is current market sales of product, such as by upper sea blue eastern Industrial Co., Ltd. with trade name
The product of 1j12 sale.
It is measured according to 451.2 standard method of GB/T, the present invention is 10~40g/m using quantifying for filmogen2；If
The filmogen is quantitatively more than the range, that is, is lower than 10g/m2Or it is higher than 40g/m2It is all worthless, this is because
Its quantitative too low cigarette appearance has fold, and its quantitative excessively high cigarette is not easy to roll.
It is measured according to GB/T 12655-2007 standard method of analysis, the present invention uses the tensile energy absorption of filmogen
Index is 150~600mJ/g；If the filmogen is quantitatively more than the range, that is, it is lower than 150mJ/g or is higher than
600mJ/g is worthless, this is because tensile energy absorption index is too low or excessively high upper machine adaptability is poor.
According to the present invention, the adhesive is it should be understood that a kind of have bonding and heat-proof quality containing aeroge
Material, its main function in composite cigarette paper of the present invention is bondable fibers paper and filmogen and the loss for reducing thermal energy.
Certainly, all that there is this effect, and the other adhesives that will not be had a negative impact to magnetic grain soaking tobacco product all may be used
With for the present invention, they are also within protection scope of the present invention.
The adhesive that the present invention uses is one or more selected from vinyl acetate-ethylene copolymer, vinyl acetate homopolymer
Or vinyl acetate-butyl acrylate copolymer adhesive, it contains by weight 5~20% aerosil.?
The main purpose that aeroge is added in the adhesive is to improve the high temperature resistance of adhesive and reduce heat-energy losses.This hair
It is bright to use aerosil；It is current market sales of product, such as by Nanuo Technology Co., Ltd. with trade name
The aerosil of aerogel powder particle sale.
The adhesive that the present invention uses all is current market sales of product, such as by Henkel adhesive technology (Guangdong)
Vinyl acetate-ethylene copolymer that Co., Ltd is sold with trade name T3880, by company, Bangbu Cigarette Material Plant with trade name
The vinyl acetate homopolymer of J9021 sale, the vinyl acetate-the third sold by company, Bangbu Cigarette Material Plant with trade name J4023
Olefin(e) acid acrylate copolymer.
According to the present invention, the temperature resistant range of the adhesive is 200~600 DEG C；The temperature resistant range of the adhesive is root
It is measured according to the test method standard method of GB/T 32368-2015 adhesive tape high-temp resisting high-humidity resisting aging.
The viscosity of the adhesive is 125~450mpa.s；The viscosity of the adhesive is according to GB/T 2794-1995
Adhesive viscosity measures standard method measurement.In the present invention, if the viscosity of the adhesive is less than 125mpa.s, nothing
Method reaches target resin added；If the viscosity of the adhesive is greater than 450mpa.s, glue-line uniformity is poor；Therefore, described
The viscosity of adhesive is that 125~450mpa.s is appropriate；
The resin added of the adhesive is 0.5~1.5g/m2.The resin added of the adhesive is according to GB_T 460-
What the measurement standard method of 2008_ paper degree of sizing obtained.In the present invention, if the resin added of the adhesive is small then
0.5g/m2, then it is pasted not strongly；If the resin added of the adhesive is greater than 1.5g/m2, then the blocked up cigarette of glue-line is not easy to roll；Cause
This, the resin added of the adhesive is 0.5~1.5g/m2It is suitable.
According to the present invention, the fiber air permeance for cigarette paper it should be understood that unit volume or section in the unit time and
The size of Air permenbility under specified pressure.The air permeability of fiber cigarette paper of the present invention is 10~60CU；The fiber cigarette paper it is saturating
Manner is measured according to the measuring method of ISO2965 air permeance for cigarette paper.In the present invention, if fiber cigarette paper is breathed freely
Degree is less than 10CU, then it is poor to aspirate relaxation；If the air permeability of fiber cigarette paper is greater than 60CU, the easy sepage of cigarette paper；Cause
This, fiber air permeance for cigarette paper is that 10~60CU is reasonable, preferably 20~45CU；
In the present invention, quantifying for the composite cigarette paper is 25~95g/m2；If the composite cigarette paper quantifies
Less than 25g/m2, then the anti-tensile of composite cigarette paper is too small, opacity is small；If composite cigarette paper is quantitatively greater than 95g/m2, then
Cigarette is difficult to roll；Therefore, quantification of 25~95g/m of composite cigarette paper2It is suitable, preferably 35~65g/m2；
In the present invention, composite cigarette paper opacity it should be understood that single layer reflectivity and its internal reflection factor it
Than.The opacity of composite cigarette paper of the present invention is greater than 70%.The opacity of composite cigarette paper of the present invention is according to GB/T
Measurement (diffusing reflection method) the standard method measurement of 1543-2005 paper and cardboard opacity (paper backing).In the present invention, such as
The opacity of fruit composite cigarette paper is lower than 70g/m2, then the appearance of the transparent influence of paper, color evenness are poor；
According to the present invention, thickness ratio 1:0.06~0.50:0.02 of cigarette fibrous paper, filmogen and adhesive layer~
0.10。
In the present invention, when the thickness of cigarette fibrous paper and adhesive layer is in the range, if filmogen
Thickness is less than 0.06, then filmogen and fibrous paper are difficult to compound；If the thickness of filmogen is greater than 0.50, composite cigarette
Paper is difficult to roll into cigarette；Therefore, filmogen is appropriate with a thickness of 0.06~0.50；
When the thickness of cigarette fibrous paper and filmogen is in the range, if the thickness of adhesive layer is less than
0.02, then it is pasted not strongly；If the thickness of adhesive layer is greater than 0.10, uniformity of size application is poor；Therefore, the thickness of adhesive layer
It is appropriate for 0.02~0.10；
Preferably, thickness ratio 1:0.16~0.40:0.04~0.08 of cigarette fibrous paper, filmogen and adhesive layer.
Composite cigarette paper preparation step of the present invention for magnetic grain soaking tobacco product is as follows:
The plant fiber, pearl filler and auxiliary agent are made according to 60~80:20 of weight ratio~35:2~4 described
Cigarette fibrous paper；It is a kind of conventional papermaking process that the present invention, which makes method used by cigarette fibrous paper, referring specifically to text
Offer " papermaking principle and engineering (third edition) ".
Then, the adhesive that temperature resistant range is 200-600 DEG C is uniformly coated on roll surfaces using roller coating sizing applicator,
The adhesive on roll surfaces is transferred in cigarette fibrous paper surface again, filmogen is then compounded in adhesive layer
On, obtain the composite cigarette paper that air permeability is 10-60CU.
Rolling for cigarette is carried out using conventional high-speed cigarette machine.
Referring to YC/T 497-2014 cigarette Chinese-style cigarette style sensory evaluation method and GB 5606.4-2005 cigarette the 4th
Part: sense organ technical requirements, tissue are commented by the group of smokeing panel test that seven experts that smoke panel test form according to the appraising standard that table 1 is listed
It inhales, smoking result is listed in Table 2 below.
[beneficial effect]
The beneficial effects of the present invention are:
Composite cigarette paper of the present invention for magnetic grain soaking tobacco product has good upper machine adaptability, is suitable for tradition
High-speed cigarette machine rolls requirement, and the cigarette appearance looks elegant rolled, no sepage and fold.
Composite cigarette paper of the present invention not only solves the bases such as magnetic grain soaking tobacco product cigarette paper heatproof, heat preservation, constant temperature
This problem, while cigarette is sucked rear fibrous paper surface and is shown without discoloration, carbonization etc., cigarette good appearance.
It is excessive that composite cigarette paper of the present invention not only avoids the equal thermal process smokeless of cigarette, while it is light to effectively improve suction
The flue gases organoleptic qualities such as pine sense, comfort level and perfume quantity.
[specific embodiment]
It will be better understood that the present invention by following embodiments.
Embodiment 1: the composite cigarette paper for magnetic grain soaking tobacco product
The embodiment of the embodiment is as follows:
The composite cigarette paper is by cigarette fibrous paper, filmogen and to be located at fiber cigarette paper and filmogen
Between adhesive layer form according to thickness ratio 1:0.2:0.06.
Wherein, the cigarette fibrous paper is by Qingdao Zhong Yi Trade Development Co., Ltd with the sale of trade name Chile Venus
Wood pulp cellulose plant fiber, by great Rui Chemical Co., Ltd., Jiangxi Province with the lightweight carbon of trade name auspicious precipitated calcium carbonate sale greatly
Sour calcium filler and the sodium metasilicate auxiliary agent sold by Jinan Xin Senyuan Chemical Co., Ltd. with trade name quick dissolved sodium silicate are according to weight
Than 62:20:3 composition.
The filmogen is the ferroaluminium filmogen for being by weight 12% with a thickness of the aluminium content of 0.1mm,
Using the measuring method measurement of this specification description, quantifying for it is 40g/m2, tensile energy absorption index be 400mJ/g.
The adhesive layer is to sell acetic acid second by Henkel adhesive technology (Guangdong) Co., Ltd with trade name T3880
Alkene-ethylene copolymer layer, wherein being sold containing by weight 5% by Nanuo Technology Co., Ltd. with trade name aerogel powder particle
Aerosil.Using the measuring method measurement of this specification description, its temperature resistant range is 250 DEG C；Viscosity is
125mpa.s；Resin added is 0.8g/m2。
According to the measuring method measurement of this specification description, the Combined roll for magnetic grain soaking tobacco product of the embodiment
The air permeability of cigarette paper is 35CU；Quantitative 55g/m2；Opacity 82%.
It is using the composite cigarette paper of cigarette machine and the embodiment, conventional smoke section, temperature adjustment section and fillter section is successively compound,
A kind of heating is obtained not burn cigarette.The method (Judging index is shown in Table 1) described according to this specification is non-ignitable to the heating
It burns cigarette to smoke panel test, smoking result is listed in Table 2 below.
Embodiment 2: the composite cigarette paper for magnetic grain soaking tobacco product
The embodiment of the embodiment is as follows:
The composite cigarette paper is by cigarette fibrous paper, filmogen and to be located at fiber cigarette paper and filmogen
Between adhesive layer form according to thickness ratio 1:0.06:0.02.
Wherein, the cigarette fibrous paper is to match Lay by Shanghai Pu Laima International Trading Company Ltd with trade name Spain
The ramie pulp fiber plant fiber of Sha's sale, the weight sold by Guangzhou Bang You Chemical Industry Science Co., Ltd with trade name powdered whiting
Matter pearl filler and the phosphoric acid sold by the more food ingredient Co., Ltds in Jiangsu Cologne with trade name food grade phosphoric acid hydrogen diammonium
Hydrogen diammonium auxiliary agent is formed according to weight ratio 74:34:2.
The filmogen is the ferroaluminium filmogen for being by weight 6% with a thickness of the aluminium content of 0.006mm,
Using the measuring method measurement of this specification description, quantifying for it is 18g/m2, tensile energy absorption index be 200mJ/g.
The adhesive layer is to sell vinyl acetate homopolymer layer by Bangbu Cigarette Material Plant with trade name J9021,
In containing by weight 12% the titanium dioxide sold by Guangdong Alison High-technology Co., Ltd. with trade name aerogel particle
Silica aerogel.Using the measuring method measurement of this specification description, its temperature resistant range is 200 DEG C；Viscosity is 325mpa.s；It applies
Glue amount is 0.5g/m2。
According to the measuring method measurement of this specification description, the Combined roll for magnetic grain soaking tobacco product of the embodiment
The air permeability of cigarette paper is 15CU；Quantitative 35g/m2；Opacity 75%.
It is using the composite cigarette paper of cigarette machine and the embodiment, conventional smoke section, temperature adjustment section and fillter section is successively compound,
A kind of heating is obtained not burn cigarette.It is smoked panel test according to the method for this specification description to the heating cigarette that do not burn,
Its smoking result is listed in Table 2 below.
Embodiment 3: the composite cigarette paper for magnetic grain soaking tobacco product
The embodiment of the embodiment is as follows:
The composite cigarette paper is by cigarette fibrous paper, filmogen and to be located at fiber cigarette paper and filmogen
Between adhesive layer according to thickness ratio 1:0.5:0.1 form.
Wherein, the cigarette fibrous paper is the grass sold by Dalian Yang Run trade Co., Ltd with Trade Name Chemical straw pulp
Pulp fibres plant fiber, the calcene sold by great Rui Chemical Co., Ltd., Jiangxi Province with trade name nm-class active calcium carbonate
Filler and the silica auxiliary agent sold by Guangzhou Zhong Qigui industry Co., Ltd with trade name silica are according to weight ratio 80:
28:3 composition.
The filmogen is the ferroaluminium filmogen for being by weight 6% with a thickness of the aluminium content of 0.008mm,
Using the measuring method measurement of this specification description, quantifying for it is 22g/m2, tensile energy absorption index be 600mJ/g.
The adhesive layer is to sell acetic acid second by Henkel adhesive technology (Guangdong) Co., Ltd with trade name T3880
Alkene-butyl acrylate copolymer layer, wherein containing by weight 20% by Guangdong Alison High-technology Co., Ltd. with commodity
The aerosil of name aerogel particle sale, is measured, its temperature resistant range using the measuring method of this specification description
850℃；Viscosity is 450mpa.s；Resin added is 1.5g/ square metres.
According to the measuring method measurement of this specification description, the Combined roll for magnetic grain soaking tobacco product of the embodiment
The air permeability of cigarette paper is 60CU；Quantitative 51g/m2；Opacity 85%.
It is using the composite cigarette paper of cigarette machine and the embodiment, conventional smoke section, temperature adjustment section and fillter section is successively compound,
A kind of heating is obtained not burn cigarette.It is smoked panel test according to the method for this specification description to the heating cigarette that do not burn,
Its smoking result is listed in Table 2 below.
Embodiment 4: the composite cigarette paper for magnetic grain soaking tobacco product
The embodiment of the embodiment is as follows:
The composite cigarette paper is by cigarette fibrous paper, filmogen and to be located at fiber cigarette paper and filmogen
Between adhesive layer according to thickness ratio 1:0.3:0.08 form.
Wherein, the cigarette fibrous paper is by Qingdao Zhong Yi Trade Development Co., Ltd with the sale of trade name Chile Venus
Wood pulp cellulose and ramie pulp fiber mixture (weight ratio 1:1) plant fiber, by great Rui Chemical Co., Ltd., Jiangxi Province with commodity
The precipitated calcium carbonate filler of the big auspicious precipitated calcium carbonate sale of name with sold by Shandong Shi An Chemical Co., Ltd. with trade name APP
Ammonium polyphosphate auxiliary agent is formed according to weight ratio 76:24:4.
The filmogen is the ferroaluminium filmogen for being by weight 9% with a thickness of the aluminium content of 0.2mm, is adopted
The measuring method measurement described with this specification, quantifying for it is 30g/m2, tensile energy absorption index be 300mJ/g.
The adhesive layer is to sell acetic acid second by Henkel adhesive technology (Guangdong) Co., Ltd with trade name T3880
Alkene-ethylene copolymer layer, wherein containing by weight 8% by Nanuo Technology Co., Ltd. with trade name aerogel powder particle pin
The aerosil sold.Using the measuring method measurement of this specification description, its temperature resistant range is 500 DEG C；Viscosity is
225mpa.s；Resin added is 1.2g/m2。
According to the measuring method measurement of this specification description, the Combined roll for magnetic grain soaking tobacco product of the embodiment
The air permeability of cigarette paper is 42CU；Quantitative 32g/m2；Opacity 78%.
It is using the composite cigarette paper of cigarette machine and the embodiment, conventional smoke section, temperature adjustment section and fillter section is successively compound,
A kind of heating is obtained not burn cigarette.It is smoked panel test according to the method for this specification description to the heating cigarette that do not burn,
Its smoking result is listed in Table 2 below.
Comparative example 1
It, will using cigarette machine and the cigarette paper sold by Anhui Jing Feng Paper Co., Ltd with trade name JF27.5A60WT
Conventional smoke section, temperature adjustment section and fillter section are successively compound, obtain a kind of heating and do not burn cigarette.The side described according to this specification
Method smokes panel test to the heating cigarette that do not burn, and smoking result is listed in Table 2 below.
Comparative example 2
It, will be conventional using cigarette machine and the cigarette paper sold by Minfeng Special Paper Co., Ltd. with trade name MFU60
Smoke section, temperature adjustment section and fillter section are successively compound, obtain a kind of heating and do not burn cigarette.The method pair described according to this specification
The heating cigarette that do not burn is smoked panel test, and smoking result is listed in Table 2 below.
The cigarette made it can be seen from the result that table 2 is listed using composite cigarette paper of the present invention is dense in amount of smoke, flue gas
Degree, perfume quantity, comfort level, relaxation, physiological strength, suction uniformity and cigarette appearance etc. be all substantially better than it is existing often
It advises cigarette paper (comparative example 1 and 2), especially in terms of smoke amount, flue gas concentration and perfume quantity；Utilize Combined roll of the present invention
Tobacco Roll tobacco curing branch is not in upper machine bad adaptability, cigarette permeability, cigarette paper pleat Zou as caused by high fog agent additive amount
Phenomena such as with discoloration, cigarette appearance looks elegant, consumption embodies；Significantly more is that composite cigarette paper of the present invention has resistance to mild guarantor
Temperature effect, sucks rear composite cigarette paper surface without high temperature cabonization phenomenon；It is sucked using the cigarette that composite cigarette paper of the present invention rolls
The problems such as process smokeless is excessive, and fibrous paper surface changes colour without permeability after sucking, sucks rear cigarette good appearance.
Claims (10)
1. a kind of composite cigarette paper for magnetic grain soaking tobacco product, it is characterised in that it is by cigarette fibrous paper, at membrane material
What material and the adhesive layer between fiber cigarette paper and filmogen formed.
2. composite cigarette paper according to claim 1, it is characterised in that the cigarette fibrous paper is by one or more
Selected from wood pulp cellulose, the plant fiber of ramie pulp fiber or other sponges, pearl filler and auxiliary agent according to weight ratio
What 60~80:20~35:2~4 was formed.
3. composite cigarette paper according to claim 1, it is characterised in that quantifying for the cigarette fibrous paper is 10~50g/
m2, tensile energy absorption index is 150mJ/g or more.
4. composite cigarette paper according to claim 2, it is characterised in that the auxiliary agent is one or more selected from silicic acid
Sodium, diammonium hydrogen phosphate, silica or ammonium polyphosphate auxiliary agent.
5. composite cigarette paper according to claim 1, it is characterised in that the filmogen be with a thickness of 0.004~
The ferroaluminium that the aluminium content of 0.2mm is by weight 6~16%.
6. composite cigarette paper according to claim 1 or 5, it is characterised in that quantifying for the filmogen is 10~40g/
m2, tensile energy absorption index is 150~600mJ/g.
7. composite cigarette paper according to claim 1 or 5, it is characterised in that the adhesive is one or more is selected from
Vinyl acetate-ethylene copolymer, vinyl acetate homopolymer or vinyl acetate-butyl acrylate copolymer adhesive, it contains
5~20% aerosil by weight.
8. cigarette paper according to claim 1, it is characterised in that the temperature resistant range of the adhesive is 200~600 DEG C；Viscosity
It is 125~450mpa.s；Resin added is 0.5~1.5g/m2。
9. cigarette paper according to claim 1, it is characterised in that the air permeability of the composite cigarette paper is 10~60CU；It is quantitative
It is 25~95g/m2；Opacity is greater than 70%.
10. cigarette paper according to claim 1, it is characterised in that the thickness of cigarette fibrous paper, filmogen and adhesive layer
Than 1:0.06~0.50:0.02~0.10.