CN110150768A - A kind of sheet smoke section, preparation method and use - Google Patents
A kind of sheet smoke section, preparation method and use Download PDFInfo
- Publication number
- CN110150768A CN110150768A CN201910606168.XA CN201910606168A CN110150768A CN 110150768 A CN110150768 A CN 110150768A CN 201910606168 A CN201910606168 A CN 201910606168A CN 110150768 A CN110150768 A CN 110150768A
- Authority
- CN
- China
- Prior art keywords
- smoke
- smoke section
- section
- sheet
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sheet smoke sections, length between its marginal surface two o'clock is at least five times of thickness, generally single or multi-layer structure, wherein, the number of plies of the sheet smoke section through-thickness is N, and N is the positive integer less than or equal to 3, and/or the number of plies of the sheet smoke section along its length is n, n is positive integer less than or equal to 4, and every layer all includes mixed supporting substrates, filler material, smoke agent and fragrance in the sheet smoke section, but every layer of inside is not comprising adhesive.The invention also discloses the preparation methods and purposes of the sheet smoke section.The smoke generator of smoke section of the present invention is come out from side by the direct flue-cured tobacco of smoke agent, then directly enters oral cavity by smoke path, and this usage mode can be avoided the back segment retention that conventional slices reconstituted class heats the cigarette that do not burn.The amount of smoke experienced is big when smoke section of the present invention is aspirated, and is not in exhaust gas volumn by there is the case where notable difference between mouth.
Description
Technical field
The invention belongs to heat technical field of tobacco of not burning, in particular to a kind of sheet smoke section, preparation method and
Purposes.
Background technique
With the improvement of living standards, people increasingly pay attention to the health problem of itself, in recent years about smoking health
The attention rate of problem is very high.It is traditional to develop various substitutions in order to meet the consumption demand of variation one after another for domestic and international each large enterprises
The novel tobacco product of cigarette.In these ever-increasing novel tobacco products, electronic cigarette and the heating cigarette that do not burn are them
In outstanding person.
Expansion application in tobacco business of the electronic cigarette as electronic product, it is advantageous that it is strong to inhale taste changeability, it can be with
Component by adjusting tobacco tar realizes any regulation that taste is inhaled to flue gas, but since its flue gas is mainly produced by electronic atomizer
Raw, mouthfeel, especially thermal sensation, the traditional cigarette for generating flue gas with heating still have certain difference, the receiving of old smoker
It spends poor.
Heating the cigarette that do not burn is to heat its smoke section to generate flue gas, and the acceptance for generating flue gas mouthfeel is preferable, at present
The do not burn smoke section of cigarette of the heating of the marketization is orderly or unordered filling reconstituted tobacco thin slice, and cigarette is in aspiration procedure
Exhaust gas volumn is insufficient.And exhaust gas volumn deficiency is primarily due to: (1) the reconstituted tobacco thin slice as smoke section requires in the filling process
There is certain processing intensity, also causes the amount of the fragrance added thereon and smoke agent few；(2) it adds after fragrance and smoke agent again
Making tobacco sheet also needs to cause by multiple high temp treatment process the fragrance of addition and smoke agent volatilization serious；(3) due to again
It makes tobacco sheet closely to arrange in smoke section, the flue gas that the smoke section front end far from filter segment generates can be big in rear end
Amount retention.
In addition, reconstituted tobacco is in manufacturing process since subsequent chopping, compacting etc. operate, it is desirable that reconstituted tobacco has certain
Processing intensity, inevitably need to add the exogenous adhesive of a large amount of tobacco, exogenous adhesive includes but not
It is limited to: natural gum, such as guar gum, xanthan gum, Arabic gum and locust bean gum；Cellulosic binders, such as hydroxypropyl cellulose,
Carboxymethyl cellulose, methylcellulose and ethyl cellulose；Polysaccharide, such as starch；Organic acid or its alkali salt, such as alginic acid, sea
Mosanom, agar, pectin；Or combinations thereof, etc..
In addition to this, the heating occurred currently on the market the cigarette that do not burn is all based on traditional cigarette machine manufacture, though
Right length and circumference change, but have substantially continued the moulding of cigarette, and product identification is low.
In order to solve problem above, the present invention is proposed.
Summary of the invention
To solve the above-mentioned problems, the present invention is proposed.
The present invention provides a kind of sheet smoke section, and cross section is polygonized structure, generally single or multi-layer structure,
In, the number of plies of the sheet smoke section through-thickness is N, and N is the positive integer less than or equal to 3, and/or, the sheet smoke
The section number of plies along its length is n, and n is the positive integer less than or equal to 4, in the sheet smoke section every layer all comprising the negative of mixing
Substrate, filler material, smoke agent and fragrance are carried, but every layer of inside does not include adhesive.
Preferably, described adhesive is selected from plant fiber, starch or modified starch or natural plant gum, i.e. adhesive is outside tobacco
Source property adhesive.
Preferably, the N is selected from 2,3, n and is selected from 2,3,4.
Preferably, the length of the sheet smoke section is 40-100mm, width 10-40mm, with a thickness of 2-10mm.
Preferably, in the sheet smoke section every layer the supporting substrates for including is identical or different, filler material is identical or different,
Smoke agent is identical or different, and fragrance is identical or different.
Preferably, the supporting substrates are selected from natural plants, porous material, and the filler material is selected from cellulose, calcium carbonate.
Wherein, it is based on mass percent, the supporting substrates account for the 40%-50% of the smoke section, and the filler material accounts for
The 10%-20% of the smoke section, the smoke agent account for the 20%-30% of the smoke section, and the fragrance accounts for the smoke section
10%-20%.
Preferably, the supporting substrates are tobacco leaf, offal or the vegetable material that can produce specific suction taste.
Preferably, the smoke agent is glycerol or propylene glycol.
Second aspect of the present invention provides the preparation method of sheet smoke section described in first aspect comprising following steps:
(1) supporting substrates, filler material, smoke agent and/or fragrance are mixed, obtains smoke section mixture, water is inside not added；
(2) the smoke section mixture for obtaining step (1) forms, and cutting, drying obtain single layer smoke section；
(3) the single layer smoke section for obtaining step (2) is N layers compound in thickness direction, or in the compound n-layer of length direction,
Obtain the sheet smoke section.
Preferably, the supporting substrates and filler material are powdered.
Preferably, in step (2), for the forming process using injection molding, compression moulding or pressing film method, the drying time is 2-
6h, drying temperature are lower than 85 DEG C；In step (3), the recombination process is using the viscous connection of sizing or in the case where not parching completely
The method that direct weighting is coupled.
Preferably, dry selected from air-dried or drying in step (2).
Preferably due to the contraction of drying process product, can be cut again after dry in step (2).
Third aspect present invention provides sheet smoke section described in first aspect and is heated generation cigarette in electric heating smoking set
The purposes of gas.
Preferably, the sheet smoke section is placed individually into heating cavity connects using or the sheet smoke section rear end
The suction nozzle with smoke path is connect, is inserted into smoking set and uses.
Preferably, the sheet smoke section uses side heating arrangement in electric heating smoking set.
The invention has the following advantages:
1, sheet smoke section of the present invention be mixed supporting substrates, filler material, smoke agent and/or fragrance be molded,
Compression moulding or molded smoke piece, not reconstituted tobacco thin slice, so in smoke section the additional amount of smoke agent and fragrance not by
Limitation, the smoke agent and fragrance total amount added under equivalent weight in smoke section of the present invention are 2-3 times in reconstituted tobacco thin slice, energy
Enough be solved perfectly in reconstituted tobacco thin slice due to being limited by processing intensity, caused by smoke agent and flavors and fragrances additive amount it is insufficient
The problem of.Simultaneously as the most of fragrance and smoke agent of this smoke section are all in the inside of smoke section, common process process
High temperature can not make it largely volatilize in a short time, and the loss of effective component work in-process largely reduces.
2, the smoke generator of smoke section of the present invention is come out from side by the direct flue-cured tobacco of smoke agent, is then directly led to by smog
Road enters oral cavity, and this usage mode can be avoided the back segment retention that conventional slices reconstituted class heats the cigarette that do not burn.The present invention
The amount of smoke experienced is big when smoke section is aspirated, and is not in exhaust gas volumn by there is the case where notable difference between mouth.
3, the flavoring process of smoke section of the present invention is to add smoke agent and fragrance during the preparation process, not the prior art
In, outer plus smoke agent and fragrance on the reconstituted tobacco thin slice prepared, flavoring process is more simple, uniform, can be significantly
Difficulty is reduced, design cost is reduced.
4, the present invention prepares smoke section using injection molding, compression moulding or molded method, and low, preparation is lost in manufacturing process
Method is simple；Do not burn compared with common heating cigarette product identification of obtained product is high.
5, laminated structure of the invention is highly beneficial for MULTILAYER COMPOSITE, multi-layer compound structure, and every layer may include difference
Supporting substrates, filler material, smoke agent and fragrance, different heating temperatures can be applicable in, this proposes the blending and seasoning of smog
Huge space is supplied, can also regulate and control smoking set heating schedule changes flue gas with more organoleptic qualities.
6, paper process prepares reconstituted tobacco process and a large amount of water is added, and will form azeotropic mixture with smoke agent, subsequent dried
Journey, water content could be reduced by needing to increase temperature and reaching azeotropic point.Smoke section of the invention is no during the preparation process to add water,
Be conducive to the low temperature drying of smoke section.
7, with the processing request of the preparation of reconstituted tobacco, it is necessary to add the exogenous adhesive of tobacco.Sheet of the invention
Smoke section does not include the exogenous adhesive of tobacco, avoids adhesive tape due to not needing complicated processing request, every layer of inside
The flue gas mouthfeel come changes and health problem.
Detailed description of the invention
Fig. 1 is the schematic diagram of 1 sheet smoke section of embodiment
Fig. 2 is 2 sheet smoke section cross-sectional view schematic diagram of embodiment.
Fig. 3 is 3 sheet smoke section cross-sectional view schematic diagram of embodiment.
Specific embodiment
The contents of the present invention are further illustrated below by specific embodiment.
Embodiment 1
The smoke section of the present embodiment is as shown in Figure 1, cross section is rectangle, single layer structure, length 60mm, and width is
30mm, with a thickness of 2mm.
The preparation method of the present embodiment smoke section, comprising the following steps:
(1) supporting substrates are broken into powder, obtain powdered loaded substrate；
(2) the powdered loaded substrate that step (1) obtains is mixed with filler material, smoke agent and fragrance is added, stirring is mixed
It closes, obtains smoke section mixture；
(3) the smoke section mixture for obtaining step (2) is formed by the method for injection molding, and is cut by actually required
It is dry at section, obtain smoke section.
Wherein, supporting substrates described in step (1) are tobacco leaf；Filler material described in step (2) is cellulose, the smoke
Agent is glycerol；It is dried in step (3) by air-drying, drying time 2h.
Based on mass percent, the supporting substrates account for the 40% of the smoke section, and filler material accounts for the smoke section
20%, smoke agent accounts for the 20% of the smoke section, and fragrance accounts for the 20% of the smoke section.
The smoke section of the present embodiment is known as sample 1.
Embodiment 2
The smoke section of the present embodiment is as shown in Fig. 2, cross section is square, and generally through-thickness is complex as the double-deck knot
Structure, length 40mm, width 40mm, with a thickness of 10mm.
The preparation method of the present embodiment smoke section, comprising the following steps:
(1) supporting substrates are broken into powder, obtain powdered loaded substrate；
(2) the powdered loaded substrate that step (1) obtains is mixed with filler material, smoke agent and fragrance is added, stirring is mixed
It closes, obtains smoke section mixture；
(3) the smoke section mixture for obtaining step (2) is formed by the method for injection molding, and is cut by actually required
It is dry at section, obtain smoke section.
(4) two kinds compound by the viscous connection of sizing by smoke section made from above-mentioned steps, obtains the double of desired thickness direction
Layer smoke section.
Supporting substrates described in step (1) are respectively tobacco leaf and active carbon in two layers of smoke section；Step is filled out described in (2)
Charge is cellulose, and the smoke agent is the mixture of glycerol and propylene glycol, volume ratio 2:1；It is dry by heating in step (3)
Dry, drying time 4h, temperature is 80 DEG C.
Based on mass percent, the supporting substrates account for the 50% of the smoke section, and filler material accounts for the smoke section
10%, smoke agent accounts for the 30% of the smoke section, and fragrance accounts for the 10% of the smoke section.
The smoke section of the present embodiment is known as sample 2.
Embodiment 3
Smoke section such as Fig. 3 of the present embodiment, cross section is rectangle, whole to be complex as double-layer structure along its length, long
Degree is 80mm, width 20mm, with a thickness of 5mm.
The preparation method of the present embodiment smoke section, comprising the following steps:
(1) supporting substrates are broken into powder, obtain powdered loaded substrate；
(2) the powdered loaded substrate that step (1) obtains is mixed with filler material, smoke agent and fragrance is added, stirring is mixed
It closes, obtains smoke section mixture；
(3) the smoke section mixture for obtaining step (2) is formed by the method for injection molding, and is cut by actually required
It is dry at section, obtain smoke section.
(4) two kinds compound by the viscous connection of sizing by smoke section made from above-mentioned steps, obtains the double of desired length direction
Layer smoke section.
Supporting substrates described in step (1) are respectively tobacco leaf and offal in two layers of smoke section；It is filled described in step (2)
Material is cellulose and calcium carbonate mixture, and the smoke agent is the mixture of glycerol and propylene glycol, volume ratio 3:1；Step (3)
In by heat dry, drying time 3h, temperature be 50 DEG C.
Based on mass percent, the supporting substrates account for the 45% of the smoke section, and filler material accounts for the smoke section
20%, smoke agent accounts for the 20% of the smoke section, and fragrance accounts for the 15% of the smoke section.
The smoke section of the present embodiment is known as sample 3.
Embodiment 4
The smoke section cross section of the present embodiment is rectangle, the generally three-decker of through-thickness, length 60mm,
Width is 15mm, with a thickness of 5mm.
The preparation method of the present embodiment smoke section, comprising the following steps:
(1) supporting substrates are broken into powder, obtain powdered loaded substrate；
(2) the powdered loaded substrate that step (1) obtains is mixed with filler material, smoke agent and fragrance is added, stirring is mixed
It closes, obtains smoke section mixture；
(3) the smoke section mixture for obtaining step (2) is formed by the method for injection molding, and is cut by actually required
It is dry at section, obtain smoke section.
(4) three kinds by smoke section made from above-mentioned steps by the case where not parching completely direct weighting be coupled it is multiple
It closes, obtains three layers of smoke section of desired thickness direction.
Supporting substrates described in step (1) are respectively tobacco leaf, offal and active carbon in three layers of smoke section；In step (2)
The filler material be cellulose and calcium carbonate mixture, the smoke agent be glycerol and propylene glycol mixture, volume ratio 2:
1；By heating dry, drying time 4h in step (3), temperature is 50 DEG C.
Based on mass percent, the supporting substrates account for the 45% of the smoke section, and filler material accounts for the smoke section
15%, smoke agent accounts for the 30% of the smoke section, and flavors and fragrances accounts for the 10% of the smoke section.
The smoke section of the present embodiment is known as sample 4.
Embodiment 5
The smoke section cross section of the present embodiment is hexagon, four-layer structure generally along its length, equivalent length
For 100mm, width 20mm, with a thickness of 3mm.
The preparation method of the present embodiment smoke section, comprising the following steps:
(1) supporting substrates are broken into powder, obtain powdered loaded substrate；
(2) the powdered loaded substrate that step (1) obtains is mixed with filler material, smoke agent and fragrance is added, stirring is mixed
It closes, obtains smoke section mixture；
(3) the smoke section mixture for obtaining step (2) is formed by the method for injection molding, and is cut by actually required
It is dry at section, obtain smoke section.
(4) four kinds are compound by the viscous connection of sizing by smoke section made from above-mentioned steps, obtain it is desired along its length
Four-layer structure smoke section.
Supporting substrates described in step (1) are respectively tobacco leaf, active carbon, offal and tobacco leaf in four layers of smoke section；Step
Suddenly filler material described in (2) is cellulose, and the smoke agent is the mixture of glycerol and propylene glycol, volume ratio 4:1；Step
(3) by heating dry, drying time 2h in, temperature is 60 DEG C.
Based on mass percent, the supporting substrates account for the 50% of the smoke section, and filler material accounts for the smoke section
20%, smoke agent accounts for the 15% of the smoke section, and fragrance accounts for the 15% of the smoke section.
The smoke section of the present embodiment is known as sample 5.
Embodiment 6
Above-mentioned sample 1, sample 2, sample 3, sample 4 and sample 5 are chosen, and again with 5 sample difference equal qualities
Tobacco sheet sample sample as a comparison is made, the comparison of amount of smoke and perfume quantity is carried out under same heating schedule.
Cigarette made of above-mentioned sample 1- sample 5 and respective comparative sample is filled in into size matching side heat or week therewith
It is aspirated into the smoking set of heating, heating schedule is identical.Sense organ is carried out to Cigarette by multiple sensory evaluating smoking personnel to comment
Valence, main to investigate 2 indexs of Cigarette amount of smoke and perfume quantity, the marking value of 2 quality detecting index is respectively as follows: cigarette
Mist amount 0-10 points, perfume quantity 0-10 points, wherein the higher feeling for representing the evaluation index in aspiration procedure of score is stronger.It is different
The Analyses Methods for Sensory Evaluation Results of sample is shown in Table 1.
The different sample Analyses Methods for Sensory Evaluation Results of table 1
As it can be seen from table 1 smoke section cigarette of the present invention, relative to existing reconstituted tobacco thin slice cigarette, exhaust gas volumn significantly increases
Add, satisfaction rises, and perfume quantity obviously increases.
In the embodiment of the present invention 2,3,4,5, due to the presence of multilayered structure, the regulation of smoking set heating schedule can make cigarette
Gas changes with more organoleptic qualities；And 5 smoke section samples in the embodiment of the present invention are relative to the existing of effect same
Reconstituted tobacco thin slice comparative sample, production cost reduce by 65% or more.
The above description is merely a specific embodiment, but scope of protection of the present invention is not limited thereto, any
Those familiar with the art in the technical scope disclosed by the present invention, can easily think of the change or the replacement, and should all contain
Lid is within protection scope of the present invention.Therefore, protection scope of the present invention should be subject to the protection scope in claims.
Claims (10)
1. a kind of sheet smoke section, which is characterized in that the length between its marginal surface two o'clock is at least five times of thickness, whole
For single or multi-layer structure, wherein the number of plies of the sheet smoke section through-thickness is N, and N is the positive integer less than or equal to 3,
And/or the number of plies of the sheet smoke section along its length is n, n is the positive integer less than or equal to 4；The sheet smoke section
Interior every layer all includes mixed supporting substrates, filler material, smoke agent and fragrance, but every layer of inside does not include adhesive.
2. sheet smoke section according to claim 1, which is characterized in that the length of the sheet smoke section is 40-
100mm, width 10-40mm, with a thickness of 2-10mm.
3. sheet smoke section according to claim 1, which is characterized in that the supporting substrates are selected from natural plants, porous
Material, the filler material are selected from cellulose, calcium carbonate.
4. sheet smoke section according to claim 1, which is characterized in that be based on mass percent, the supporting substrates account for
The 40%-50% of the smoke section, the filler material account for the 10%-20% of the smoke section, and the smoke agent accounts for the smoke
The 20%-30% of section, the fragrance account for the 10%-20% of the smoke section.
5. sheet smoke section according to claim 1, which is characterized in that every layer of load for including in the sheet smoke section
Substrate is identical or different, filler material is identical or different, smoke agent is identical or different, and fragrance is identical or different.
6. sheet smoke section according to claim 1, which is characterized in that described adhesive be selected from plant fiber, starch or
Modified starch or natural plant gum.
7. a kind of preparation method of sheet smoke section described in claim 1, which comprises the following steps:
(1) supporting substrates, filler material, smoke agent and fragrance are mixed, obtains smoke section mixture, water is inside not added；
(2) the smoke section mixture for obtaining step (1) forms, and cutting, drying obtain single layer smoke section；
(3) the single layer smoke section for obtaining step (2) is N layers compound in thickness direction, and/or in the compound n-layer of length direction, i.e.,
Obtain the sheet smoke section.
8. the preparation method of sheet smoke section according to claim 7, which is characterized in that described to form in step (2)
Cheng Caiyong injection molding, compression moulding or pressing film method, the drying time are 2-6h, and drying temperature is lower than 85 DEG C；It is described in step (3)
The method of recombination process direct weighting connection using the viscous connection of sizing or in the case where not parching completely.
9. sheet smoke section described in claim 1 is heated the purposes for generating flue gas in electric heating smoking set.
10. purposes according to claim 9, the sheet smoke section, which is placed individually into heating cavity, to be used or described
The connection of sheet smoke section rear end has the suction nozzle of smoke path, is inserted into smoking set and uses.