CN103254587A - 增韧的聚对苯二甲酸丁二醇酯合金复合材料 - Google Patents

增韧的聚对苯二甲酸丁二醇酯合金复合材料 Download PDF

Info

Publication number
CN103254587A
CN103254587A CN201310173213XA CN201310173213A CN103254587A CN 103254587 A CN103254587 A CN 103254587A CN 201310173213X A CN201310173213X A CN 201310173213XA CN 201310173213 A CN201310173213 A CN 201310173213A CN 103254587 A CN103254587 A CN 103254587A
Authority
CN
China
Prior art keywords
polybutylene terephthalate
parts
alloy composite
composite materials
toughness reinforcing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310173213XA
Other languages
English (en)
Inventor
沈国俭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XIEXIN METALLURG MATERIAL Co Ltd
Original Assignee
CHANGSHU XIEXIN METALLURG MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XIEXIN METALLURG MATERIAL Co Ltd filed Critical CHANGSHU XIEXIN METALLURG MATERIAL Co Ltd
Priority to CN201310173213XA priority Critical patent/CN103254587A/zh
Publication of CN103254587A publication Critical patent/CN103254587A/zh
Pending legal-status Critical Current

Abstract

一种增韧的聚对苯二甲酸丁二醇酯合金复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚对苯二甲酸丁二醇酯67～75份；烯烃树脂5～11份；增韧剂10～15份；相容剂3～7份；抗氧剂0.5～1.0份；增强纤维15～28份；炭黑0.8～1.5份。提供的增韧的聚对苯二甲酸丁二醇酯合金复合材料经测试具有如下性能指标：拉伸强度115～128MPa，弯曲强度222～235MPa，弯曲模量8500～11000MPa，缺口冲击强度20～38kj/m2，热变形温度215～228℃；所有原料易得而有利于工业化放大生产。

Description

增韧的聚对苯二甲酸丁二醇酯合金复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种增韧的聚对苯二甲酸丁二醇酯合金复合材料。
背景技术
聚对苯二甲酸丁二醇酯具有机械强度高、尺寸稳定好和电气性能优异的特点，但是由于聚对苯二甲酸丁二醇酯结晶性强，因而使聚对苯二甲酸丁二醇酯制品的耐冲击性能差，从而限制了在一些韧性部件的应用。中国专利公开号CN1580122A中提到了使用乙丙橡胶与甲基丙烯的甘油酯的接枝共聚物作为聚对苯二甲酸丁二醇酯的增韧剂，由于这种特殊原料不属于基本树脂类，因此存在原材料来源限制，工业化应用比较困难的缺憾。
发明内容
本发明的任务在于提供一种原料易得并且强度和耐温性能优异的增韧的聚对苯二甲酸丁二醇酯合金复合材料。
本发明的任务是这样来完成的，一种增韧的聚对苯二甲酸丁二醇酯合金复合材料，其是由以下重量份数的原料组成：
Figure BDA0000317196501
在本发明的一个实施例中，所述的聚对苯二甲酸丁二醇酯树脂为熔点在220℃的聚对苯二甲酸丁二醇酯。
在本发明的另一个实施例中，所述的烯烃树脂为熔点在160℃的共聚聚丙烯树脂。
在本发明的又一个实施例中，所述的增韧剂为丙烯腈-丁二烯-苯乙烯共聚物。
在本发明的再一个实施例中，所述的相容剂为马来酸酐接枝的聚丙烯树脂。
在本发明的还有一个实施例中，所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
在本发明的更而一个实施例中，所述的增强纤维为长度3mm的无碱玻璃纤维。
在本发明的进而一个实施例中，所述的炭黑为乙炔黑。
本发明提供的增韧的聚对苯二甲酸丁二醇酯合金复合材料经测试具有如下性能指标：拉伸强度115～128MPa，弯曲强度222～235MPa，弯曲模量8500～11000MPa,缺口冲击强度20～38kj/m2,热变形温度215～228℃；所有原料易得而有利于工业化放大生产。
具体实施方式
实施例1：
Figure BDA0000317196502
实施例2：
Figure BDA0000317196503
实施例3：
Figure BDA0000317196504
实施例4：
Figure BDA0000317196505
由上述实施例1至4得到的增韧的聚对苯二甲酸丁二醇酯合金复合材料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 115 119 123 128
弯曲强度MPa 222 227 231 235
弯曲模量MPa 8550 9270 10050 10970
缺口冲击强度kj/m2 20.3 25.3 32.6 38.7
热变形温度℃ 215 219 225 228

Claims (8)

1.一种增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于其是由以下重量份数的原料组成：
                  聚对苯二甲酸丁二醇酯         67～75份；
            烯烃树脂                  5～11份；
           增韧剂                     10～15份；
           相容剂                     3~7份；
           抗氧剂                     0.5~1.0份；
          增强纤维                    15~28份；
             炭黑                     0.8~1.5份。
2.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的聚对苯二甲酸丁二醇酯树脂为熔点在220℃的聚对苯二甲酸丁二醇酯。
3.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的烯烃树脂为熔点在160℃的共聚聚丙烯树脂。
4.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的增韧剂为丙烯腈-丁二烯-苯乙烯共聚物。
5.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的相容剂为马来酸酐接枝的聚丙烯树脂。
6.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
7.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的增强纤维为长度3mm的无碱玻璃纤维。
8.根据权利要求1所述的增韧的聚对苯二甲酸丁二醇酯合金复合材料，其特征在于所述的炭黑为乙炔黑。
CN201310173213XA 2013-05-10 2013-05-10 增韧的聚对苯二甲酸丁二醇酯合金复合材料 Pending CN103254587A (zh)