CN103834145A - 纳米碳纤维增强的聚对苯二甲酸丁二醇酯 - Google Patents
纳米碳纤维增强的聚对苯二甲酸丁二醇酯 Download PDFInfo
- Publication number
- CN103834145A CN103834145A CN201210475835.3A CN201210475835A CN103834145A CN 103834145 A CN103834145 A CN 103834145A CN 201210475835 A CN201210475835 A CN 201210475835A CN 103834145 A CN103834145 A CN 103834145A
- Authority
- CN
- China
- Prior art keywords
- polybutylene terephthalate
- parts
- strengthens
- carbon nano
- nano fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯,属于高分子材料技术领域。其是由以下重量份数的原料组成:聚对苯二甲酸丁二醇酯54.2~58.5份;聚酰胺10.4~15.3份;相容剂6.3~8.4份;抗氧剂0.5~0.9份;阻燃剂11.4~18.6份;碳纤维8.6~17.8份;炭黑0.6~1.4份。优点:拉伸强度145~168MPa,弯曲强度213~228MPa,缺口冲击强度63~75j/m,阻燃性V-0(UL-94-V-0-3.0mm),因而能够满足制造耐火场合使用的各种部件。
Description
技术领域
本发明属于高分子材料技术领域,具体涉及一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯。
背景技术
聚对苯二甲酸丁二醇酯(PBT)是一种热塑性塑料,广泛用做民用或工业用材料,具有耐热性、耐候性、耐化学腐蚀性和光泽好等特点。中国发明专利公开号CN102311616A公开了一种碳纤维增强的聚酯材料,但是该材料并不能满足目前严格的阻燃要求,因此,在用于制造耐火部件时往往受到限制。鉴此,开发具有良好的阻燃效果和理想的强度的聚对苯二甲酸丁二醇酯具有积极意义。
发明内容
本发明的任务在于提供一种有助于显著增进阻燃效果、有利于体现优异的强度而藉以满足制造耐火部件要求的纳米碳纤维增强的聚对苯二甲酸丁二醇酯。
本发明的任务是这样来完成的,一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其是由以下重量份数的原料组成:
在本发明的一个实施例中,所述的聚对苯二甲酸丁二醇酯树脂的熔点为223℃。
在本发明的另一个实施例中,所述的聚酰胺为熔点在230℃的聚酰胺66树脂。
在本发明的又一个实施例中,所述的相容剂为马来酸酐接枝的聚酰胺6树脂。
在本发明的再一个实施例中,所述的抗氧剂为硫代二丙酸二(十八)酯。
在本发明的还有一个实施例中,所述的阻燃剂为十溴二苯乙烷。
在本发明的更而一个实施例中,所述的碳纤维为以乙烯为碳源制备的并且长度为60~110μm的纳米碳纤维。
在本发明的进而一个实施例中,所述的炭黑为槽法炭黑。
本发明提供的技术方案相对于已有技术由于具有如下优异的性能指标:拉伸强度145~168MPa,弯曲强度213~228MPa,缺口冲击强度63~75j/m,阻燃性V-0(UL-94-V-0-3.0mm),因而能够满足制造耐火场合使用的各种部件。
具体实施方式
实施例1:
实施例2:
实施例3:
实施例4:
由上述实施例1至4得到的纳米碳纤维增强的聚对苯二甲酸丁二醇酯经测试具有下表所示的技术效果。
Claims (8)
1.一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于其是由以下重量份数的原料组成:
聚对苯二甲酸丁二醇酯 54.2~58.5份;
聚酰胺 10.4~15.3份;
相容剂 6.3~8.4份;
抗氧剂 0.5~0.9份;
阻燃剂 11.4~18.6份;
碳纤维 8.6~17.8份;
炭黑 0.6~1.4份。
2.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的聚对苯二甲酸丁二醇酯树脂的熔点为223℃。
3.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的聚酰胺为熔点在230℃的聚酰胺66树脂。
4.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的相容剂为马来酸酐接枝的聚酰胺6树脂。
5.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的抗氧剂为硫代二丙酸二(十八)酯。
6.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的阻燃剂为十溴二苯乙烷。
7.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的碳纤维为以乙烯为碳源制备的并且长度为60~110μm的纳米碳纤维。
8.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯,其特征在于所述的炭黑为槽法炭黑。