CN103834146A - 纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料 - Google Patents

纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料 Download PDF

Info

Publication number
CN103834146A
CN103834146A CN201210476360.XA CN201210476360A CN103834146A CN 103834146 A CN103834146 A CN 103834146A CN 201210476360 A CN201210476360 A CN 201210476360A CN 103834146 A CN103834146 A CN 103834146A
Authority
CN
China
Prior art keywords
polybutylene terephthalate
parts
strengthens
carbon nano
nano fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210476360.XA
Other languages
English (en)
Inventor
陈丽刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU CITY YURUN RUBBER PRODUCTS Co Ltd
Original Assignee
CHANGSHU CITY YURUN RUBBER PRODUCTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU CITY YURUN RUBBER PRODUCTS Co Ltd filed Critical CHANGSHU CITY YURUN RUBBER PRODUCTS Co Ltd
Priority to CN201210476360.XA priority Critical patent/CN103834146A/zh
Publication of CN103834146A publication Critical patent/CN103834146A/zh
Pending legal-status Critical Current

Abstract

一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚对苯二甲酸丁二醇酯树脂50～58.5份；增韧剂8.5～15.6份；烯烃树脂5.3～13.4份；相容剂5.2~8.5份；磷酸盐15.2~23.4份；抗氧剂0.5~1.1份；玻璃微珠2~3份；碳纤维12.3~19.6份；炭黑0.8~1.4份。优点：拉伸强度122～136MPa，弯曲强度207～228MPa，缺口冲击强度61～76j/m，阻燃性V-0(UL-94-V-0-3.0mm)。

Description

纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料。
背景技术
聚对苯二甲酸丁二醇酯（PBT）是一种热塑性塑料，广泛用做民用或工业用材料。中国发明专利申请公开号CN102311616A公开了一种碳纤维增强的聚酯材料，但是专利申请方案所涉材料并不能阻燃。又，公开号CN1060189A公开了一种阻燃的聚酯材料，该方案虽然具有阻燃效果，但是，由于其使用了卤素类阻燃剂和金属三氧化锑等，这些阻燃剂燃烧时会产生有害气体，并且制品废弃后，这些有害的物质会扩散至土壤，水体等，从而造成对环境污染，由于此类材料不是环境友好材料，属于遭人们冷遇乃至被淘汰的材料。因此开发强度理想、无毒环保并且阻燃性能优异的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料具有积极的现实意义。
发明内容
本发明的任务是要提供一种具有优异的强度、无毒并且环保阻燃的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料。
本发明的任务是这样来完成的，一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其是由以下重量份数的原料组成：
Figure BDA0000244327641
在本发明的一个实施例中，所述的聚对苯二甲酸丁二醇酯树脂的熔点为210℃。
在本发明的另一个实施例中，所述的增韧剂为粉末丁腈橡胶。
在本发明的又一个实施例中，所述的烯烃树脂为熔点160℃的共聚聚丙烯树脂。
在本发明的再一个实施例中，所述的相容剂为马来酸酐接枝的聚丙烯树脂。
在本发明的还有一个实施例中，所述的磷酸盐为次磷酸铝。
在本发明的更而一个实施例中，所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
在本发明的进而一个实施例中，所述的玻璃微珠为空心玻璃微珠。
在本发明的又更而一个实施例中，所述的碳纤维为以甲烷为碳源合成的并且长度为40-80μm的纳米碳纤维。
在本发明的又进而一个实施例中，所述的炭黑为槽法炭黑。
本发明的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，经过测试具有如下的性能指标：拉伸强度122～136MPa，弯曲强度207～228MPa,缺口冲击强度61～76j/m，阻燃性V-0(UL-94-V-0-3.0mm)。
具体实施方式
实施例1：
Figure BDA0000244327642
实施例2：
Figure BDA0000244327643
Figure BDA0000244327644
实施例3：
Figure BDA0000244327645
实施例4：
Figure BDA0000244327646
由上述实施例1至4得到的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料经测试具有下表所示的技术效果：
Figure BDA0000244327647

Claims (10)

1.一种纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于其是由以下重量份数的原料组成：
                  聚对苯二甲酸丁二醇酯树脂     50～58.5份；
         增韧剂                                 8.5～15.6份；
         烯烃树脂                    5.3～13.4份；
        相容剂                       5.2~8.5份；
        磷酸盐                       15.2~23.4份；
         抗氧剂                       0.5~1.1份；
         玻璃微珠                     2~3份；
         碳纤维                       12.3~19.6份；
         炭黑                         0.8~1.4份。
2.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的聚对苯二甲酸丁二醇酯树脂的熔点为210℃。
3.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的增韧剂为粉末丁腈橡胶。
4.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的烯烃树脂为熔点160℃的共聚聚丙烯树脂。
5.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的相容剂为马来酸酐接枝的聚丙烯树脂。
6.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的磷酸盐为次磷酸铝。
7.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
8.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的玻璃微珠为空心玻璃微珠。
9.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的碳纤维为以甲烷为碳源合成的并且长度为40-80μm的纳米碳纤维。
10.根据权利要求1所述的纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料，其特征在于所述的炭黑为槽法炭黑。
CN201210476360.XA 2012-11-21 2012-11-21 纳米碳纤维增强的聚对苯二甲酸丁二醇酯复合材料 Pending CN103834146A (zh)