CN103863757A - 一种用于煤矿的无卤阻燃型钢丝绳芯输送带 - Google Patents
一种用于煤矿的无卤阻燃型钢丝绳芯输送带 Download PDFInfo
- Publication number
- CN103863757A CN103863757A CN201210531242.4A CN201210531242A CN103863757A CN 103863757 A CN103863757 A CN 103863757A CN 201210531242 A CN201210531242 A CN 201210531242A CN 103863757 A CN103863757 A CN 103863757A
- Authority
- CN
- China
- Prior art keywords
- halogen
- free flame
- parts
- conveyor belt
- steel wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于煤矿的无卤阻燃型钢丝绳芯输送带。包括钢丝绳芯、中间胶层以及覆盖胶,其特征在于,所述粘合胶和覆盖胶的重量比组成是:30-60份的三元乙丙橡胶、30-60份的聚烯烃合金热塑性弹性体、50-70份的无卤阻燃剂、2-3.5份的硫化剂、10-20份的炭黑、1.5-4.5份的防老剂、3-7份的粘合剂及6-10份的锌;所述无卤阻燃剂是由纳米级改性氢氧化镁,硼酸锌以及蒙脱土组成,其重量比为2-6:3-8:2-5。所述纳米级改性氢氧化镁是由硬脂酸表面包覆纳米级氢氧化镁制得。本发明的有益效果是:通过纳米级、改性后的阻燃剂的加入,可更好地对输送带起到阻燃的效用,并且无害。
Description
技术领域
本发明涉及一种输送带,尤其涉及一种用于煤矿的无卤阻燃型钢丝绳芯输送带。
背景技术
输送带应用广泛,如矿山、冶金及化工等领域。但如煤矿等领域对输送带具有特殊要求,要求其阻燃性能要好,这就导致了生产的一般输送带已经无法满足其特殊要求了;目前现有的阻燃型的输送带大多含有卤素,严重威胁健康。
发明内容
本发明针对上述现有技术的不足,提供一种用于煤矿的无卤阻燃型钢丝绳芯输送带。此输送带能安全无毒的起到良好阻燃效果。
本发明解决上述技术问题的技术方案如下:一种用于煤矿的无卤阻燃型钢丝绳芯输送带,包括钢丝绳芯、中间胶层以及覆盖胶,其特征在于,所述粘合胶和覆盖胶的重量比组成是:30-60份的三元乙丙橡胶、30-60份的聚烯烃合金热塑性弹性体、50-70份的无卤阻燃剂、2-3.5份的硫化剂、10-20份的炭黑、1.5-4.5份的防老剂、3-7份的粘合剂及6-10份的锌;
所述无卤阻燃剂是由纳米级改性氢氧化镁,硼酸锌以及蒙脱土组成,其重量比为2-6:3-8:2-5。
所述纳米级改性氢氧化镁是由硬脂酸表面包覆纳米级氢氧化镁制得。
本发明的有益效果是:通过纳米级、改性后的阻燃剂的加入,可更好地对输送带起到阻燃的效用,并且无害。
具体实施方式
以下结合本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
一种用于煤矿的无卤阻燃型钢丝绳芯输送带,包括钢丝绳芯、中间胶层以及覆盖胶,其特征在于,所述粘合胶和覆盖胶的重量比组成是:30份的三元乙丙橡胶、50份的聚烯烃合金热塑性弹性体、50-70份的无卤阻燃剂、2份的硫化剂、10份的炭黑、1.5份的防老剂、7份的粘合剂及10份的锌;
所述无卤阻燃剂是由纳米级改性氢氧化镁,硼酸锌以及蒙脱土组成,其重量比为2:3:5。
所述纳米级改性氢氧化镁是由硬脂酸表面包覆纳米级氢氧化镁制得。
本发明的有益效果是:通过纳米级、改性后的阻燃剂的加入,可更好地对输送带起到阻燃的效用,并且无害。
实施例2
一种用于煤矿的无卤阻燃型钢丝绳芯输送带,包括钢丝绳芯、中间胶层以及覆盖胶,其特征在于,所述粘合胶和覆盖胶的重量比组成是: 60份的三元乙丙橡胶、40份的聚烯烃合金热塑性弹性体、50份的无卤阻燃剂、2-3.5份的硫化剂、20份的炭黑、4.5份的防老剂、3份的粘合剂及710份的锌;
所述无卤阻燃剂是由纳米级改性氢氧化镁,硼酸锌以及蒙脱土组成,其重量比为6:3:2。
所述纳米级改性氢氧化镁是由硬脂酸表面包覆纳米级氢氧化镁制得。
本发明的有益效果是:通过纳米级、改性后的阻燃剂的加入,可更好地对输送带起到阻燃的效用,并且无害。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种用于煤矿的无卤阻燃型钢丝绳芯输送带,包括钢丝绳芯、中间胶层以及覆盖胶,其特征在于,所述粘合胶和覆盖胶的重量比组成是:30-60份的三元乙丙橡胶、30-60份的聚烯烃合金热塑性弹性体、50-70份的无卤阻燃剂、2-3.5份的硫化剂、10-20份的炭黑、1.5-4.5份的防老剂、3-7份的粘合剂及6-10份的锌;
所述无卤阻燃剂是由纳米级改性氢氧化镁,硼酸锌以及蒙脱土组成,其重量比为2-6:3-8:2-5。
2.根据权利要求1所述的用于煤矿的无卤阻燃型钢丝绳芯输送带,其特征在于,所述纳米级改性氢氧化镁是由硬脂酸表面包覆纳米级氢氧化镁制得。