CN102976033A - 一种阻燃钢丝绳芯输送带 - Google Patents
一种阻燃钢丝绳芯输送带 Download PDFInfo
- Publication number
- CN102976033A CN102976033A CN 201210529590 CN201210529590A CN102976033A CN 102976033 A CN102976033 A CN 102976033A CN 201210529590 CN201210529590 CN 201210529590 CN 201210529590 A CN201210529590 A CN 201210529590A CN 102976033 A CN102976033 A CN 102976033A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- rope core
- micron
- steel wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种阻燃钢丝绳芯输送带。包括钢丝绳芯、与钢丝绳芯结合的中间胶层、以及附着在中间胶层上下两端面的上覆盖胶层和下覆盖胶层,其特征在于,所述中间胶和覆盖胶的重量比组成是:20-40份的三元乙丙橡胶、20-50份的聚烯烃合金热塑性弹性体、50-80份的微米级复合型阻燃剂、2-3.5份的硫化剂、10-20份的导电炭黑、2.5-4.5份的防老剂、5-10份的粘合剂及6-10份的氧化镁;所述微米级复合型阻燃剂是微米级三氧化二锑、微米级氢氧化铝和微米级氢氧化镁,其重量比为2-4:3-5:4-7。本发明的有益效果是:通过微米级复合阻燃材料的加入,可更好地对输送带起到阻燃的效用。
Description
技术领域
本发明涉及一种钢丝绳芯输送带,尤其涉及一种阻燃钢丝绳芯输送带。
背景技术
钢丝绳芯输送带由于其良好的性能,被广泛应用于矿山、冶金及化工等领域输送物料。其特点是抗冲击性小,使用伸长小,适于长距离输送物料。但如煤矿等领域对于钢丝绳芯输送带具有特殊要求,要求其阻燃性能要好,这就导致了目前生产的一般钢丝绳芯输送带已经无法满足其特殊要求了。
发明内容
本发明针对上述现有技术的不足,提供一种阻燃钢丝绳芯输送带。能很好地输送物料同时阻燃效果良好。
本发明解决上述技术问题的技术方案如下:一种阻燃钢丝绳芯输送带,包括钢丝绳芯、与钢丝绳芯结合的中间胶层、以及附着在中间胶层上下两端面的上覆盖胶层和下覆盖胶层,其特征在于,所述中间胶和覆盖胶的重量比组成是:20-40份的三元乙丙橡胶、20-50份的聚烯烃合金热塑性弹性体、50-80份的微米级复合型阻燃剂、2-3.5份的硫化剂、10-20份的导电炭黑、2.5-4.5份的防老剂、5-10份的粘合剂及6-10份的氧化镁;
所述微米级复合型阻燃剂是微米级三氧化二锑、微米级氢氧化铝和微米级氢氧化镁,其重量比为2-4:3-5:4-7。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,所述硫化剂是硫磺。
本发明的有益效果是:通过微米级复合阻燃材料的加入,可更好地对输送带起到阻燃的效用。
具体实施方式
以下结合本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
一种阻燃钢丝绳芯输送带,包括钢丝绳芯、与钢丝绳芯结合的中间胶层、以及附着在中间胶层上下两端面的上覆盖胶层和下覆盖胶层,其特征在于,所述中间胶和覆盖胶的重量比组成是:40份的三元乙丙橡胶、30份的聚烯烃合金热塑性弹性体、50份的微米级复合型阻燃剂、3份的硫化剂、15份的导电炭黑、2.5份的防老剂、8份的粘合剂及6份的氧化镁;
所述微米级复合型阻燃剂是微米级三氧化二锑、微米级氢氧化铝和微米级氢氧化镁,其重量比为4:3:4。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,所述硫化剂是硫磺。
实施例2
一种阻燃钢丝绳芯输送带,包括钢丝绳芯、与钢丝绳芯结合的中间胶层、以及附着在中间胶层上下两端面的上覆盖胶层和下覆盖胶层,其特征在于,所述中间胶和覆盖胶的重量比组成是:20份的三元乙丙橡胶、50份的聚烯烃合金热塑性弹性体、70份的微米级复合型阻燃剂、2份的硫化剂、10份的导电炭黑、4份的防老剂、5份的粘合剂及9份的氧化镁;
所述微米级复合型阻燃剂是微米级三氧化二锑、微米级氢氧化铝和微米级氢氧化镁,其重量比为3:3:6。
在上述技术方案的基础上,本发明还可以做如下改进。
进一步,所述硫化剂是硫磺。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种阻燃钢丝绳芯输送带,包括钢丝绳芯、与钢丝绳芯结合的中间胶层、以及附着在中间胶层上下两端面的上覆盖胶层和下覆盖胶层,其特征在于,所述中间胶和覆盖胶的重量比组成是:20-40份的三元乙丙橡胶、20-50份的聚烯烃合金热塑性弹性体、50-80份的微米级复合型阻燃剂、2-3.5份的硫化剂、10-20份的导电炭黑、2.5-4.5份的防老剂、5-10份的粘合剂及6-10份的氧化镁;
所述微米级复合型阻燃剂是微米级三氧化二锑、微米级氢氧化铝和微米级氢氧化镁,其重量比为2-4:3-5:4-7。
2.根据权利要求1所述的阻燃钢丝绳芯输送带,其特征在于,所述硫化剂是硫磺。