CN103497707A - 一种钢丝绳芯输送带 - Google Patents

一种钢丝绳芯输送带 Download PDF

Info

Publication number
CN103497707A
CN103497707A CN201310479564.3A CN201310479564A CN103497707A CN 103497707 A CN103497707 A CN 103497707A CN 201310479564 A CN201310479564 A CN 201310479564A CN 103497707 A CN103497707 A CN 103497707A
Authority
CN
China
Prior art keywords
conveying belt
core conveying
cable core
steel cable
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310479564.3A
Other languages
English (en)
Inventor
浦娇青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Universal Steel Rope Co Ltd
Original Assignee
Wuxi Universal Steel Rope Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Universal Steel Rope Co Ltd filed Critical Wuxi Universal Steel Rope Co Ltd
Priority to CN201310479564.3A priority Critical patent/CN103497707A/zh
Publication of CN103497707A publication Critical patent/CN103497707A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：氯丁橡胶60～75、顺丁橡胶20～35、氧化锌2～9、氧化镁0.5～2、硬脂酸0.5～2、防老剂1～4、炭黑20～50、阻燃剂40～70、硫磺0.5～2.5、促进剂0.5～4、增塑剂2～8。本发明提供的钢丝绳芯输送带具有良好的韧性和强度，且阻燃性能优异。

Description

一种钢丝绳芯输送带
技术领域
本发明涉及钢丝绳技术领域，尤其涉及一种钢丝绳芯输送带。
背景技术
煤炭是我国重要的基础能源和原料，在国民经济中具有重要的战略地位。
钢丝绳起到承受载荷的作用，其性能主要由钢丝决定。钢丝是碳素钢或合金钢通过冷拉或冷轧而成的圆形（或异形）丝材，具有很高的强度和韧性，并根据使用环境条件不同对钢丝进行表面处理。
钢丝绳芯输送带以钢绳芯衬垫覆盖橡胶制成的输送带作为带式输送机的牵引和运载构件。钢绳芯输送带具有拉伸强度大、抗冲击好、寿命长、使用伸长小、成槽性好、耐曲挠性好的特点，适于长距离、大运程、高速度输送物料。
钢绳芯输送带由芯胶、钢丝绳、覆盖层和边胶构成。
现有钢绳芯输送带的阻燃性和韧性，强度不足，本领域亟需开发一种韧性和强度好，阻燃性能优异的钢绳芯输送带。
发明内容
针对现有技术的不足，本发明的目的之一在于提供一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000011
Figure BDA0000395607260000021
优选地，所述的促进剂是促进剂ZBX、促进剂PZ中的任意1种或至少2种的组合。
优选地，所述的抗氧剂是BHT，或WingStay L抗氧剂。
优选地，所述阻燃剂选自氢氧化铝、氢氢氧化铝、氢氧化镁、磷酸一铵、磷酸二铵、氯化铵、硼酸氧化镁、磷酸一铵、磷酸二铵、氯化铵、硼酸中的任意1种。
优选地，所述增塑剂选自N-一邻苯二甲酸二异壬酯或邻苯二甲酸二乙基己酯。
优选地，粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000022
Figure BDA0000395607260000031
优选地，粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000032
优选地，所述钢丝绳芯为6×19+IWRC结构。
与现有技术相比，本发明具有如下有益效果：
本发明提供的钢丝绳芯输送带具有良好的韧性和强度，且阻燃性能优异。
具体实施方式
为便于理解本发明，本发明列举实施例如下。本领域技术人员应该明了，所述实施例仅仅是帮助理解本发明，不应视为对本发明的具体限制。
实施例1
一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000041
所述钢丝绳为6×19+IWRC结构。
实施例2
一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000042
Figure BDA0000395607260000051
所述钢丝绳为6×19+IWRC结构。
实施例3
一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000052
所述钢丝绳为6×19+IWRC结构。
实施例4
一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
所述钢丝绳为6×19+IWRC结构。
实施例4
一种钢丝绳芯输送带，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure BDA0000395607260000062
Figure BDA0000395607260000071
所述钢丝绳为6×19+IWRC结构。
申请人声明，本发明通过上述实施例来说明本发明的详细配方，但本发明并不局限于上述详细配方，即不意味着本发明必须依赖上述详细配方才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。

Claims (8)

1.一种钢丝绳芯输送带，其特征在于，所述钢丝绳芯输送带的粘合胶按重量份数包括如下组分：
Figure FDA0000395607250000011
2.如权利要求1所述的钢丝绳芯输送带，其特征在于，所述的促进剂是促进剂ZBX、促进剂PZ中的任意1种或至少2种的组合。
3.如权利要求1所述的钢丝绳芯输送带，其特征在于，所述的抗氧剂是BHT，或WingStay L抗氧剂。
4.如权利要求1所述的钢丝绳芯输送带，其特征在于，所述阻燃剂选自氢氧化铝、氢氢氧化铝、氢氧化镁、磷酸一铵、磷酸二铵、氯化铵、硼酸氧化镁、磷酸一铵、磷酸二铵、氯化铵、硼酸中的任意1种。
5.如权利要求1所述的钢丝绳芯输送带，其特征在于，所述增塑剂选自N-一邻苯二甲酸二异壬酯或邻苯二甲酸二乙基己酯。
6.如权利要求1所述的钢丝绳芯输送带，其特征在于，粘合胶按重量份数包括如下组分：
Figure FDA0000395607250000021
7.如权利要求1所述的钢丝绳芯输送带，其特征在于，粘合胶按重量份数包括如下组分：
Figure FDA0000395607250000022
Figure FDA0000395607250000031
8.如权利要求1所述的钢丝绳芯输送带，其特征在于，所述钢丝绳芯为6×19+IWRC结构。
CN201310479564.3A 2013-10-14 2013-10-14 一种钢丝绳芯输送带 Pending CN103497707A (zh)