CN103214817A - 白色的无卤阻燃聚碳酸酯复合材料 - Google Patents

白色的无卤阻燃聚碳酸酯复合材料 Download PDF

Info

Publication number
CN103214817A
CN103214817A CN2013101298437A CN201310129843A CN103214817A CN 103214817 A CN103214817 A CN 103214817A CN 2013101298437 A CN2013101298437 A CN 2013101298437A CN 201310129843 A CN201310129843 A CN 201310129843A CN 103214817 A CN103214817 A CN 103214817A
Authority
CN
China
Prior art keywords
parts
halogen
flame
free
matrix material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101298437A
Other languages
English (en)
Inventor
陶渭清
沈兴元
颜卫峰
陶立强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Original Assignee
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd filed Critical SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority to CN2013101298437A priority Critical patent/CN103214817A/zh
Publication of CN103214817A publication Critical patent/CN103214817A/zh
Pending legal-status Critical Current

Abstract

一种白色的无卤阻燃聚碳酸酯复合材料，属于高分子材料技术领域。其是由以下按重量份计的原料组成：聚碳酸酯树脂110～140份；聚丙烯树脂30～45份；马来酸酐接枝聚丙烯11～16份；抗氧剂0.8～1.4份；阻燃剂30～45份；增强纤维14～22份；钛白粉34～42份；润滑剂2.2～3.6份。提供的白色的无卤阻燃聚碳酸酯复合材料具有无卤阻燃和白色的特点，适合生产计算机外壳，打印机外壳，汽车部件和电视机部件等；弯曲强度100～130MPa；断裂伸长率20～40%；缺口冲击强度11～13KJ/m2；热变形温度100～125℃；阻燃性达到V-0(UL-94-1.6mm)；白度大于93。

Description

白色的无卤阻燃聚碳酸酯复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种白色的无卤阻燃聚碳酸酯复合材料。
背景技术
聚碳酸酯（PC）具有优良的综合性能，广泛用于电子电器、建筑、包装、医疗器械、光学仪器、交通运输等领域。尽管聚碳酸酯具有一定阻燃性，但是仍难满足某些特殊领域的要求，如电视机、计算机、打印机、汽车部件、建筑材料等领域对聚碳酸酯阻燃性能的要求，为此，有必要对聚碳酸酯材料进行阻燃改性。特别是随着欧盟对阻燃材料要求的提高，传统的含卤素的阻燃剂由于燃烧产生有毒烟雾，已被列为限制使用，因此，有必要开发不含卤素的并且具有很好阻燃性的聚碳酸酯复合材料，使其适合于生产计算机外壳、打印机外壳、汽车部件和电视机等部件。
发明内容
本发明的任务在于提供一种具有无卤阻燃特点的白色的无卤阻燃聚碳酸酯复合材料，以便适合生产计算机外壳、打印机外壳、汽车部件和电机机部件等。
本发明的任务是这样来完成的，一种白色的无卤阻燃聚碳酸酯复合材料，其是由以下按重量份计的原料组成：
Figure BDA0000304974301
在本发明的一个实施例中，所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
在本发明的另一个实施例中，所述的聚丙烯树脂为均聚聚丙烯，熔指为2.4g/10min。
在本发明的又一个实施例中，所述的马来酸酐接枝聚丙烯树脂为马来酸酐与聚丙烯熔融接枝形成，接枝率0.8%。
在本发明的再一个实施例中，所述的抗氧剂为硫代二丙酸二（十八）酯。
在本发明的还有一个实施例中，所述的阻燃剂为微胶囊包覆的聚磷酸铵，粒径为50~100纳米。
在本发明的更而一个实施例中，所述的增强纤维为磨碎的玻璃纤维，其纤维长度为50~100微米。
在本发明的进而一个实施例中，所述的钛白粉为锐钛型二氧化钛。
在本发明的又更而一个实施例中，所述的润滑剂为硬脂酸锂。
本发明提供的白色的无卤阻燃聚碳酸酯复合材料具有无卤阻燃和白色的特点，适合生产计算机外壳，打印机外壳，汽车部件和电视机部件等；弯曲强度100~130MPa；断裂伸长率20~40%；缺口冲击强度11~13KJ/m2；热变形温度100～125℃；阻燃性达到V-0(UL-94-1.6mm)；白度大于93。
具体实施方式
实施例1：
Figure BDA0000304974302
实施例2：
Figure BDA0000304974303
实施例3：
双
Figure BDA0000304974304
实施例4：
Figure BDA0000304974305
由上述实施例1至4得到的白色的无卤阻燃聚碳酸酯复合材料权测试具有如下性能指标：
测试项目 实施例1 实施例2 实施例3 实施例4
弯曲强度MPa 100 106 114 128
断裂伸长率% 38 32 27 21
缺口冲击强度KJ/m2(40℃) 11.2 11.7 12.3 12.8
热变形温度 102 108 115 123
阻燃性（UL-94-1.6mm） V-0 V-0 V-0 V-0
白度 93.2 93.8 94.2 95.1

Claims (9)

1.一种白色的无卤阻燃聚碳酸酯复合材料，其特征在于其是由以下按重量份计的原料组成：
聚碳酸酯树脂                   110~140份；
  聚丙烯树脂                     30~45份；
马来酸酐接枝聚丙烯              11~16份；
抗氧剂                          0.8~1.4份；
阻燃剂                          30~45份；
增强纤维                                                14~22份；    
钛白粉                                                    34~42份；
润滑剂                          2.2~3.6份。
2.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
3.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的聚丙烯树脂为均聚聚丙烯，熔指为2.4g/10min。
4.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的马来酸酐接枝聚丙烯树脂为马来酸酐与聚丙烯熔融接枝形成，接枝率0.8%。
5.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的抗氧剂为硫代二丙酸二（十八）酯。
6.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的阻燃剂为微胶囊包覆的聚磷酸铵，粒径为50~100纳米。
7.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的增强纤维为磨碎的玻璃纤维，其纤维长度为50~100微米。
8.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的钛白粉为锐钛型二氧化钛。
9.根据权利要求1所述的白色的无卤阻燃聚碳酸酯复合材料，其特征在于所述的润滑剂为硬脂酸锂。
CN2013101298437A 2013-04-15 2013-04-15 白色的无卤阻燃聚碳酸酯复合材料 Pending CN103214817A (zh)