CN103214815A - 浅色的无卤阻燃聚碳酸酯模塑料 - Google Patents

浅色的无卤阻燃聚碳酸酯模塑料 Download PDF

Info

Publication number
CN103214815A
CN103214815A CN2013101297203A CN201310129720A CN103214815A CN 103214815 A CN103214815 A CN 103214815A CN 2013101297203 A CN2013101297203 A CN 2013101297203A CN 201310129720 A CN201310129720 A CN 201310129720A CN 103214815 A CN103214815 A CN 103214815A
Authority
CN
China
Prior art keywords
halogen
parts
polycarbonate
light color
moulding compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101297203A
Other languages
English (en)
Inventor
陶渭清
沈兴元
颜卫峰
陶立强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Original Assignee
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd filed Critical SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority to CN2013101297203A priority Critical patent/CN103214815A/zh
Publication of CN103214815A publication Critical patent/CN103214815A/zh
Pending legal-status Critical Current

Abstract

一种浅色的无卤阻燃的聚碳酸酯模塑料，属于高分子材料技术领域。其是由以下按重量计的原料组成：聚碳酸酯树脂60~75份；氢化苯乙烯-丁二烯-苯乙烯树脂12~16份；抗氧剂0.6~1.0份；短切玻璃纤维9~14份；钛白粉5~9份；紫色母粒0.01~0.12份；磷酸盐13~21份；润滑剂0.7~1.3份。提供的浅色的无卤阻燃的聚碳酸酯模塑料具有强度高，无卤阻燃的长处，并且成型性好，成型效率高，可以用于生产消费类电子产品的外壳部件；弯曲强度112~125MPa；断裂伸长率25~46%；缺口冲击强度8~12KJ/m2(-40℃下)；阻燃性达到V-0(UL-94-3.0mm)。

Description

浅色的无卤阻燃聚碳酸酯模塑料
技术领域
本发明属于高分子材料技术领域，具体涉及一种浅色的无卤阻燃聚碳酸酯模塑料。
背景技术
聚碳酸酯是一种性能优良的热塑性树脂，其具有电性能优异，透光度高及尺寸稳定性好等特点，经常用于生产仪器仪表盘，电器的透明外壳等，特别是不少电子消费品的外壳采用聚碳酸酯模塑料生产，如手机，电视机，电脑等，这些电子产品要求外壳具有鲜艳、高贵的品质，常常选择浅色制品来制作。尽管聚碳酸酯材料具有一定阻燃性，但是用于生产薄壁制品时，仍显阻燃性不足，需要进行改性。中国专利CN10152284A中公开了一种阻燃聚碳酸酯树脂组合物，在聚碳酸酯中引入硅氧烷基团，通过新阻燃基团来体现阻燃性。尽管这种方法可以使聚碳酸酯的阻燃性提高，但是考虑到合成的成本以及实施方便性都并不理想，因此有必要加以合理改进。
发明内容
本发明的任务是提供一种浅色的无卤阻燃的聚碳酸酯模塑料，该种模塑料在生产电子消费品、薄壁制品外壳时具有实施方便和生产效率高的特点。
本发明的任务是这样来完成的，一种浅色的无卤阻燃的聚碳酸酯模塑料，其是由以下按重量计的原料组成：
在本发明的一个实施例中，所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
在本发明的另一个实施例中，所述的氢化的苯乙烯-丁二烯-苯乙烯为苯乙烯含量为30%的热塑性橡胶。
在本发明的又一个实施例中，所述的抗氧剂为2,5-二特丁基对苯二酚。
在本发明的再一个实施例中，所述的短切玻璃纤维的长度为3mm。
在本发明的还有一个实施例中，所述的钛白粉是指锐钛型二氧化钛。
在本发明的更而一个实施例中，所述的紫色母粒为紫色的无卤色母粒。
在本发明的进而一个实施例中，所述的磷酸盐为复配的磷酸盐，由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成。
本发明的又更而一个实施例中，所述的润滑剂为聚乙烯蜡。
本发明提供的浅色的无卤阻燃的聚碳酸酯模塑料具有强度高，无卤阻燃的长处，并且成型性好，成型效率高，可以用于生产消费类电子产品的外壳部件；弯曲强度112~125MPa；断裂伸长率25~46%；缺口冲击强度8~12KJ/m2(-40℃下)；阻燃性达到V-0(UL-94-3.0mm)。
具体实施方式
实施例1：
Figure BDA0000304969952
由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成的磷酸盐15份；
润滑剂1.3份。
实施例2：
Figure BDA0000304969953
由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成的磷酸盐18份；
润滑剂1份。
实施例3：
Figure BDA0000304969954
由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成的磷酸盐21份；
润滑剂0.7份。
实施例4：
Figure BDA0000304969955
由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成的磷酸盐13份；
润滑剂0.9份。
由上述实施例1至4得到的浅色的无卤阻燃聚碳酸酯模塑料经测试具有如下性能指标：
测试项目 实施例1 实施例2 实施例3 实施例4
弯曲强度MPa 112.3 115.7 120.4 124.5
断裂伸长率% 25 29 36 45
缺口冲击强度KJ/m2(40℃) 8.2 9.3 10.5 11.8
阻燃性（UL-94-3mm） V-0 V-0 V-0 V-0

Claims (9)

1.一种浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于其是由以下按重量计的原料组成：
聚碳酸酯树脂                     60~75份；
   氢化苯乙烯-丁二烯-苯乙烯树脂      12~16份；
抗氧剂                           0.6~1.0份；
短切玻璃纤维                     9~14份；
钛白粉                           5~9份；
紫色母粒                                0.01~0.12份；
磷酸盐                           13~21份；
   润滑剂                           0.7~1.3份。
2.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
3.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的氢化的苯乙烯-丁二烯-苯乙烯为苯乙烯含量为30%的热塑性橡胶。
4.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的抗氧剂为2,5-二特丁基对苯二酚。
5.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的短切玻璃纤维的长度为3mm。
6.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的钛白粉是指锐钛型二氧化钛。
7.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的紫色母粒为紫色的无卤色母粒。
8.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的磷酸盐为复配的磷酸盐，由质量百分数为70%的三聚氰氨聚磷酸盐与质量百分数为30%的三聚氰氨尿酸盐复配而成。
9.根据权利要求1所述的浅色的无卤阻燃的聚碳酸酯模塑料，其特征在于所述的润滑剂为聚乙烯蜡。
CN2013101297203A 2013-04-15 2013-04-15 浅色的无卤阻燃聚碳酸酯模塑料 Pending CN103214815A (zh)