CN102863764A - Sebs改性的聚碳酸酯合金材料 - Google Patents

Sebs改性的聚碳酸酯合金材料 Download PDF

Info

Publication number
CN102863764A
CN102863764A CN2012103515706A CN201210351570A CN102863764A CN 102863764 A CN102863764 A CN 102863764A CN 2012103515706 A CN2012103515706 A CN 2012103515706A CN 201210351570 A CN201210351570 A CN 201210351570A CN 102863764 A CN102863764 A CN 102863764A
Authority
CN
China
Prior art keywords
sebs
alloy material
styrene
polycarbonate alloy
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103515706A
Other languages
English (en)
Inventor
方云祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Kailida Honeycomb Package Material Co Ltd
Original Assignee
Changshu Kailida Honeycomb Package Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Kailida Honeycomb Package Material Co Ltd filed Critical Changshu Kailida Honeycomb Package Material Co Ltd
Priority to CN2012103515706A priority Critical patent/CN102863764A/zh
Publication of CN102863764A publication Critical patent/CN102863764A/zh
Pending legal-status Critical Current

Abstract

一种SEBS改性的聚碳酸酯合金材料，属于高分子材料技术领域。其是由以下组份的原料组成：聚碳酸酯树脂280~310份；SEBS45~53份；相容剂15~20份；抗氧剂0.5~0.9份；润滑剂2.3~2.8份。除具有优异的机械物理性能外，还具有耐低温开裂性。弯曲强度68~75MPa，断裂伸长率60~80%，冲击强度60~67kJ/m2，-40℃下，放置4小时，不开裂。

Description

SEBS改性的聚碳酸酯合金材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种SEBS改性的聚碳酸酯合金材料。
背景技术
由于SEBS（苯乙烯-乙烯/丁二烯-苯乙烯）的分子结构呈饱和结构，具有很好的稳定性，因而在室外具有优异的耐候性。SEBS可以提高材料耐低温性，可以消除材料内应力等。聚碳酸酯材料残余内应力高，容易开裂，并且不耐低温。因此，使用SEBS对聚碳酸酯改性具有积极作用。
发明内容
本发明的任务在于提供一种具有良好的耐低温性和理想的机械物理性能的SEBS改性的聚碳酸酯合金材料。
本发明的任务是这样来完成的，一种SEBS改性的聚碳酸酯合金材料，其是由以下组份的原料组成：
Figure BDA0000216684071
在本发明的一个具体的实施例中，所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
在本发明的另一个具体的实施例中，所述的相容剂为马来酸酐接枝的SEBS,其接枝率为1.2%。
在本发明的又一个具体的实施例中，所述的抗氧剂为四[β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
在本发明的再一个具体的实施例中，所述的润滑剂为聚乙烯蜡。
由本发明提供的SEBS改性的聚碳酸酯合金材料除具有优异的机械物理性能外，还具有耐低温开裂性。弯曲强度68~75MPa,断裂伸长率60~80%， 冲击强度60~67KJ/m2,-40℃下，放置4小时，不开裂。
具体实施方式
实施例1：
Figure BDA0000216684072
Figure BDA0000216684073
实施例2：
Figure BDA0000216684074
实施例3：
Figure BDA0000216684075
实施例4：
Figure BDA0000216684076
由上述实施例1-4得的SEBS改性的聚碳酸酯合金材料经测试具有下表所示的技术指标：
测试项目 实施例1 实施例2 实施例3 实施例4
弯曲强度MPa 68.3 70.6 72.8 74.7
断裂伸长率% 61 68 73 78
冲击强度KJ/m2 60.2 63.5 65.1 66.8
-40℃放置4小时 不开裂 不开裂 不开裂 不开裂

Claims (5)

1.一种SEBS改性的聚碳酸酯合金材料，其特征在于其是由以下组份的原料组成：
聚碳酸酯树脂   280~310份；
   SEBS          45~53份；
   相容剂         15~20份；
抗氧剂         0.5~0.9份；
   润滑剂         2.3~2.8份。
2.根据权利要求1所述的SEBS改性的聚碳酸酯合金材料，其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯树脂。
3.根据权利要求1所述的SEBS改性的聚碳酸酯合金材料，其特征在于所述的相容剂为马来酸酐接枝的SEBS,其接枝率为1.2%。
4.根据权利要求1所述的SEBS改性的聚碳酸酯合金材料，其特征在于所述的抗氧剂为四[β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
5.根据权利要求1所述的SEBS改性的聚碳酸酯合金材料，其特征在于所述的润滑剂为聚乙烯蜡。
CN2012103515706A 2012-09-20 2012-09-20 Sebs改性的聚碳酸酯合金材料 Pending CN102863764A (zh)