CN103254593A - 聚对苯二甲酸乙二醇酯模塑料 - Google Patents

聚对苯二甲酸乙二醇酯模塑料 Download PDF

Info

Publication number
CN103254593A
CN103254593A CN2013102140204A CN201310214020A CN103254593A CN 103254593 A CN103254593 A CN 103254593A CN 2013102140204 A CN2013102140204 A CN 2013102140204A CN 201310214020 A CN201310214020 A CN 201310214020A CN 103254593 A CN103254593 A CN 103254593A
Authority
CN
China
Prior art keywords
parts
moulding compound
polyethylene terephthalate
compound according
terephthalate moulding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102140204A
Other languages
English (en)
Inventor
李梅新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Original Assignee
CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd filed Critical CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Priority to CN2013102140204A priority Critical patent/CN103254593A/zh
Publication of CN103254593A publication Critical patent/CN103254593A/zh
Pending legal-status Critical Current

Abstract

一种聚对苯二甲酸乙二醇酯模塑料，属于高分子材料技术领域。其特征在于其是由以下重量份数的原料组成：聚对苯二甲酸乙二醇酯25～31份；非结晶性聚酯树脂5～9份；增韧剂3~7份；阻燃剂6~11份；填料20~29份；抗氧剂0.3~0.7份；增强纤维6~15份；炭黑0.8~1.4份。提供的聚对苯二甲酸乙二醇酯模塑料经测试具有如下的性能指标：拉伸强度135～158MPa，弯曲强度200～220MPa，缺口冲击强度60～80j/m,阻燃性达到V-0(UL-94-3.0mm)，热变形温度210～230℃；具有低收缩的技术效果。

Description

聚对苯二甲酸乙二醇酯模塑料
技术领域
本发明属于高分子材料技术领域，具体涉及一种聚对苯二甲酸乙二醇酯模塑料。
背景技术
聚对苯二甲酸乙二醇酯是由对苯二甲酸与乙二醇经过缩聚反应而得的基础应用树脂，聚对苯二甲酸乙二醇酯具有结晶强，熔点高的特点，但是因其强度欠缺而达不到工业应用要求。CN102161817A中公开了由碳纤维增强聚酯树脂的方法，通过引入碳纤维，提高制品的强度，达到应用要求，但是，强度仍不足以满足业界的使用要求，并且收缩系数大。
发明内容
本发明的任务在于提供一种具有优异的强度并且收缩小的聚对苯二甲酸乙二醇酯模塑料。
本发明的任务是这样来完成的，一种聚对苯二甲酸乙二醇酯模塑料，其是由以下重量份数的原料组成：
Figure BDA0000328188121
在本发明的一个实施例中，所述的聚对苯二甲酸乙二醇酯树脂为熔点在250℃，特性黏度指数为0.65dl/g 的聚对苯二甲酸乙二醇酯。
在本发明的另一个实施例中，所述的非结晶性聚酯树脂为软化点在120℃的饱和聚酯树脂。
在本发明的又一个实施例中，所述的增韧剂为聚酯-聚醚热塑性弹性体，其中聚酯段为聚对苯二甲酸乙二醇酯，聚醚段为聚四亚甲基醚。
在本发明的再一个实施例中，所述的阻燃剂为十溴二苯乙烷。
在本发明的还有一个实施例中，所述的填料为碳酸钙。
在本发明的更而一个实施例中，所述的抗氧剂为硫代二丙酸双十二烷酯。
在本发明的进而一个实施例中，所述的增强纤维为长度6mm的无碱玻璃纤维。
在本发明的又更而一个实施例中，所述的炭黑为槽法炭黑。
本发明提供的聚对苯二甲酸乙二醇酯模塑料经测试具有如下的性能指标：拉伸强度135～158MPa，弯曲强度200～220MPa，缺口冲击强度60～80j/m,阻燃性达到V-0(UL-94-3.0mm)，热变形温度210～230℃；具有低收缩的技术效果。
具体实施方式
实施例1：
Figure BDA0000328188122
实施例2：
Figure BDA0000328188123
实施例3：
Figure BDA0000328188124
Figure BDA0000328188125
实施例4：
Figure BDA0000328188126
由上述实施例1至4得到的聚对苯二甲酸乙二醇酯模塑料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 136 143 149 157
弯曲强度MPa 201 209 215 220
缺口冲击强度j/m 60.2 65.8 70.4 78.4
阻燃性(UL-94-3.0mm) V-0 V-0 V-0 V-0
热变形温度℃ 212 217 224 228

Claims (9)

1.一种聚对苯二甲酸乙二醇酯模塑料，其特征在于其是由以下重量份数的原料组成：
                  聚对苯二甲酸乙二醇酯         25～31份；
         非结晶性聚酯树脂             5～9份；
          增韧剂                      3~7份；
          阻燃剂                      6~11份；
          填料                        20~29份；
          抗氧剂                      0.3~0.7份；
          增强纤维                    6~15份；
          炭黑                        0.8~1.4份。
2.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的聚对苯二甲酸乙二醇酯树脂为熔点在250℃，特性黏度指数为0.65dl/g 的聚对苯二甲酸乙二醇酯。
3.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的非结晶性聚酯树脂为软化点在120℃的饱和聚酯树脂。
4.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的增韧剂为聚酯-聚醚热塑性弹性体，其中聚酯段为聚对苯二甲酸乙二醇酯，聚醚段为聚四亚甲基醚。
5.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的阻燃剂为十溴二苯乙烷。
6.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的填料为碳酸钙。
7.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的抗氧剂为硫代二丙酸双十二烷酯。
8.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的增强纤维为长度6mm的无碱玻璃纤维。
9.根据权利要求1所述的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的炭黑为槽法炭黑。
CN2013102140204A 2013-05-31 2013-05-31 聚对苯二甲酸乙二醇酯模塑料 Pending CN103254593A (zh)