CN102732009A - 阻燃的导电尼龙复合材料 - Google Patents

阻燃的导电尼龙复合材料 Download PDF

Info

Publication number
CN102732009A
CN102732009A CN2012101975620A CN201210197562A CN102732009A CN 102732009 A CN102732009 A CN 102732009A CN 2012101975620 A CN2012101975620 A CN 2012101975620A CN 201210197562 A CN201210197562 A CN 201210197562A CN 102732009 A CN102732009 A CN 102732009A
Authority
CN
China
Prior art keywords
parts
fire
composite materials
nylon composite
retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101975620A
Other languages
English (en)
Other versions
CN102732009B (zh
Inventor
陶渭清
沈兴元
颜卫峰
陶立强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Original Assignee
SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd filed Critical SUZHOU YUDU MEDICAL INSTRUMENT CO Ltd
Priority to CN201210197562.0A priority Critical patent/CN102732009B/zh
Publication of CN102732009A publication Critical patent/CN102732009A/zh
Application granted granted Critical
Publication of CN102732009B publication Critical patent/CN102732009B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种阻燃的导电尼龙复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙 66 树脂 200 ～ 230 份；尼龙 12 树脂 60 ～ 90 份；偶联剂 3 ～ 5 份；填料 60 ～ 100 份；阻燃剂 50 ～ 90 份；抗氧剂 1.0 ～ 2.0 份；导电剂 30 ～ 45 份；增强纤维 90 ～ 120 份；表面改性剂 1.1 ～ 2.3 份。本发明提供的阻燃的导电尼龙复合材料的拉伸强度大于 170MPa ，弯曲强度大于 240MPa, 悬臂梁缺口冲击强度大于 23kj/m 2 , 熔融指数大于 27g/10min, 阻燃等级达到 V-0(UL-94-1.6mm) 级并且由于加入了导电剂因而得以消除静电。

Description

阻燃的导电尼龙复合材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种阻燃的导电尼龙复合材料。
背景技术
由于尼龙材料存在阻燃性和抗静电性差的欠缺而被限制于在防火要求严格的场合之外，从而制约其应用领域的拓展。鉴此开发具有优异的阻燃和防静电效果的导电尼龙复合材料具有积极意义，下面将要介绍的技术方案便是基于该前提下产生的。
发明内容
本发明的任务在于提供一种有助于保障优异的强度、有利于体现优异的阻燃性和抗静电性的阻燃的导电尼龙复合材料。
本发明的任务是这样来完成的，一种阻燃的导电尼龙复合材料，其是由以下重量份数的原料组成：
Figure BDA0000177018661
在本发明的一个实施例中，所述的尼龙66树脂为熔点在240℃的树脂。
在本发明的另一个实施例中，所述的尼龙12树脂为熔点在180℃的树脂。
在本发明的又一个实施例中，所述的偶联剂为异丙基三乙氧基硅烷。
在本发明的再一个实施例中，所述的填料为经过活化处理的碳酸钙。
在本发明的还有一个实施例中，所述的阻燃剂为十溴二苯乙烷。
在本发明的更而一个实施例中，所述的抗氧剂为三[2，4二叔丁基苯基]亚磷酸酯。
在本发明进而一个实施例中，所述的导电剂为石墨。
在本发明的又更而一个实施例中，所述的增强纤维为长度为3mm的无碱短切玻璃纤维。
在本发明的又进而一个实施例中，所述的表面改性剂为双硬脂酸酰胺。
本发明提供的阻燃的导电尼龙复合材料的拉伸强度大于170MPa，弯曲强度大于240MPa,悬臂梁缺口冲击强度大于23kj/m2, 熔融指数大于27g/10min,阻燃等级达到V-0(UL-94-1.6mm)级并且由于加入了导电剂因而得以消除静电。
具体实施方式
实施例1：
按重量份数，熔点在240℃的树脂即尼龙66树脂200份、熔点在180℃的树脂即尼龙12树脂90份、偶联剂即异丙基三乙氧基硅烷3份、填料即经过活化处理的碳酸钙60份、阻燃剂即十溴二苯乙烷60份、抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1.5份，导电剂即石墨40份、增强纤维即长度为3mm的无碱短切玻璃纤维90份和表面改性剂即双硬脂酸酰胺1.1份。
实施例2：
按重量份数，熔点在240℃的树脂即尼龙66树脂210份、熔点在180℃的树脂即尼龙12树脂70份、偶联剂即异丙基三乙氧基硅烷4份、填料即经过活化处理的碳酸钙100份、阻燃剂即十溴二苯乙烷50份、抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1份，导电剂即石墨45份、增强纤维即长度为3mm的无碱短切玻璃纤维100份和表面改性剂即双硬脂酸酰胺1.5份。
实施例3：
按重量份数，熔点在240℃的树脂即尼龙66树脂230份、熔点在180℃的树脂即尼龙12树脂80份、偶联剂即异丙基三乙氧基硅烷3份、填料即经过活化处理的碳酸钙75份、阻燃剂即十溴二苯乙烷70份、抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1.6份，导电剂即石墨30份、增强纤维即长度为3mm的无碱短切玻璃纤维120份和表面改性剂即双硬脂酸酰胺2份。
实施例4：
按重量份数，熔点在240℃的树脂即尼龙66树脂220份、熔点在180℃的树脂即尼龙12树脂85份、偶联剂即异丙基三乙氧基硅烷5份、填料即经过活化处理的碳酸钙90份、阻燃剂即十溴二苯乙烷90份、抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯2份，导电剂即石墨35份、增强纤维即长度为3mm的无碱短切纤维110份和表面改性剂即双硬脂酸酰胺2.3份。
由上述实施例1至4得到的阻燃的导电尼龙复合材料经测试具下表所示的技术效果：

Claims (10)

1.一种阻燃的导电尼龙复合材料，其特征在于其是由以下重量份数的原料组成：
尼龙66树脂    200～230份；
尼龙12树脂    60～90份；
偶联剂                     3～5份；
填料                   60～100份；
阻燃剂                     50～90份；
抗氧剂                     1.0～2.0份；
导电剂                     30～45份；
增强纤维          90～120份；
表面改性剂      1.1～2.3份。
2.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的尼龙66树脂为熔点在240℃的树脂。
3.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的尼龙12树脂为熔点在180℃的树脂。
4.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的偶联剂为异丙基三乙氧基硅烷。
5.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的填料为经过活化处理的碳酸钙。
6.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的阻燃剂为十溴二苯乙烷。
7.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的抗氧剂为三[2，4二叔丁基苯基]亚磷酸酯。
8.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的导电剂为石墨。
9.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的增强纤维为长度为3mm的无碱短切玻璃纤维。
10.根据权利要求1所述的阻燃的导电尼龙复合材料，其特征在于所述的表面改性剂为双硬脂酸酰胺。
CN201210197562.0A 2012-06-15 2012-06-15 阻燃的导电尼龙复合材料 Active CN102732009B (zh)