CN102731997B - 阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料 - Google Patents
阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料 Download PDFInfo
- Publication number
- CN102731997B CN102731997B CN 201210197991 CN201210197991A CN102731997B CN 102731997 B CN102731997 B CN 102731997B CN 201210197991 CN201210197991 CN 201210197991 CN 201210197991 A CN201210197991 A CN 201210197991A CN 102731997 B CN102731997 B CN 102731997B
- Authority
- CN
- China
- Prior art keywords
- parts
- refers
- silicon carbide
- nylon
- polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙6树脂290～340份；聚乙烯树脂90～120份；接枝的聚乙烯树脂40～55份；偶联剂5～7.5份；填料90～130份；阻燃剂30～50份；碳化硅70～90份；抗氧剂1.5～2份；玻璃纤维150～190份；表面改性剂1.2～2.1份。优点：其拉伸强度大于165MPa，弯曲强度大于235MPa，悬臂梁缺口冲击强度大于28.5kj/m2,熔融指数大于25g/10min，阻燃等级达到V-0，不易吸潮，能够满足制作建筑和机械的零部件要求。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料。
背景技术
尽管尼龙具有广泛的用途，但是尼龙存在抗冲击性差和易吸潮等缺点，从而在一定程度上制约了其应用领域的拓展，因此有必要以合理的技术手段对其改性，为此本申请人作了积极的尝试，形成了下面将要公开的技术方案。
发明内容
本发明的任务在于提供一种有助于保障良好的抗冲击性、有利于消除吸潮而藉以适合制作建筑和机械零部件的阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料。
本发明的任务是这样来完成的，一种阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料，其是由以下重量份数的原料组成：
尼龙6树脂 290～340份；
聚乙烯树脂 90～120份；
接枝的聚乙烯树脂 40～55份；
偶联剂 5～7.5份；
填料 90～130份；
阻燃剂 30～50份；
碳化硅 70～90份；
抗氧剂 1.5～2份；
玻璃纤维 150～190份；
表面改性剂 1.2～2.1份。
在本发明的一个实施例中，所述的尼龙6树脂是指熔点在225℃的树脂。
在本发明的另一个实施例中，所述的聚乙烯树脂是指低密度聚乙烯。
在本发明的又一个实施例中，所述的接枝聚乙烯树脂是指马来酸酐接枝的聚乙烯，其接枝率为2.3%。
在本发明的再一个实施例中，所述的偶联剂是指3-氨基丙基三乙氧基硅烷。
在本发明的还有一个实施例中，所述的填料是指经过表面处理的氢氧化镁。
在本发明的更而一个实施例中，所述的阻燃剂是指十溴二苯醚。
在本发明的进而一个实施例中，所述的碳化硅是指长径比为200～250的碳化硅晶须。
在本发明的又更而一个实施例中，所述的抗氧剂是指三[2，4二叔丁基苯基]亚磷酸酯。
在本发明的又进而一个实施例中，所述的玻璃纤维是指长度为3mm的无碱短切玻璃纤维，所述的表面改性剂是指双硬脂酸酰胺。
本发明提供的阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料的拉伸强度大于165MPa，弯曲强度大于235MPa,悬臂梁缺口冲击强度大于28.5kj/m2, 熔融指数大于25g/10min，阻燃等级达到V-0（UL-94-1.6mm），不易吸潮，能够满足制作建筑和机械的零部件要求。
具体实施方式
实施例1：
按重量份数，熔点在225℃的树脂即尼龙6树脂290份，聚乙烯树脂即低密度聚乙烯100份，马来酸酐接枝的聚乙烯（接枝率为2.3%）40份，偶联剂即3-氨基丙基三乙氧基硅烷5份，填料即经过表面处理的氢氧化镁130份，阻燃剂即十溴二苯醚30份，长径比为200～250的碳化硅晶须90份，抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1.5份，长度为3mm的无碱短切玻璃纤维190份和表面改性剂即双硬脂酸酰胺1.8份。
实施例2：
按重量份数，熔点在225℃的树脂即尼龙6树脂310份，聚乙烯树脂即低密度聚乙烯90份，马来酸酐接枝的聚乙烯（接枝率为2.3%）45份，偶联剂即3-氨基丙基三乙氧基硅烷7.5份，填料即经过表面处理的氢氧化镁90份，阻燃剂即十溴二苯醚40份，长径比为200～250的碳化硅晶须70份，抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1.8份，长度为3mm的无碱短切玻璃纤维165份和表面改性剂即双硬脂酸酰胺1.2份。
实施例3：
按重量份数，熔点在225℃的树脂即尼龙6树脂340份，聚乙烯树脂即低密度聚乙烯120份，马来酸酐接枝的聚乙烯（接枝率为2.3%）55份，偶联剂即3-氨基丙基三乙氧基硅烷6.5份，填料即经过表面处理的氢氧化镁110份，阻燃剂即十溴二苯醚45份，长径比为200～250的碳化硅晶须75份，抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯2份，长度为3mm的无碱短切玻璃纤维180份和表面改性剂即双硬脂酸酰胺1.6份。
实施例4：
按重量份数，熔点在225℃的树脂即尼龙6树脂320份，聚乙烯树脂即低密度聚乙烯110份，马来酸酐接枝的聚乙烯（接枝率为2.3%）50份，偶联剂即3-氨基丙基三乙氧基硅烷6份，填料即经过表面处理的氢氧化镁120份，阻燃剂即十溴二苯醚50份，长径比为200～250的碳化硅晶须80份，抗氧剂即三[2，4二叔丁基苯基]亚磷酸酯1.9份，长度为3mm的无碱短切玻璃纤维150份和表面改性剂即双硬脂酸酰胺2.1份。
由上述实施例1至4得到的阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料经测试具有下表所示的技术效果：
| 测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
| 拉伸强度MPa | 165 | 168 | 171 | 174 |
| 弯曲强度MPa | 235 | 239 | 244 | 248 |
| 悬臂梁缺口冲击强度kj/m2 | 28.5 | 28.9 | 29.3 | 29.7 |
| 熔融指数g/10min | 25 | 25.4 | 25.8 | 26.1 |
| 阻燃性（UL-94-1.6mm） | V-0 | V-0 | V-0 | V-0 |
Claims (1)
1.一种阻燃的碳化硅填充的尼龙6和聚乙烯合金复合材料，其特征在于其是由以下重量份数的原料组成：
尼龙6树脂 290～340份；
聚乙烯树脂 90～120份；
接枝的聚乙烯树脂 40～55份；
偶联剂 5～7.5份；
填料 90～130份；
阻燃剂 30～50份；
碳化硅 70～90份；
抗氧剂 1.5～2份；
玻璃纤维 150～190份；
表面改性剂 1.2～2.1份，所述的尼龙6树脂是指熔点在225℃的树脂，所述的聚乙烯树脂是指低密度聚乙烯，所述的接枝聚乙烯树脂是指马来酸酐接枝的聚乙烯，其接枝率为2.3%，所述的偶联剂是指3-氨基丙基三乙氧基硅烷，所述的填料是指经过表面处理的氢氧化镁，所述的阻燃剂是指十溴二苯醚，所述的碳化硅是指长径比为200～250的碳化硅晶须，所述的抗氧剂是指三[2，4二叔丁基苯基]亚磷酸酯，所述的玻璃纤维是指长度为3mm的无碱短切玻璃纤维，所述的表面改性剂是指双硬脂酸酰胺。