CN102732013A - 阻燃的碳化硅填充的尼龙复合材料 - Google Patents
阻燃的碳化硅填充的尼龙复合材料 Download PDFInfo
- Publication number
- CN102732013A CN102732013A CN2012101979994A CN201210197999A CN102732013A CN 102732013 A CN102732013 A CN 102732013A CN 2012101979994 A CN2012101979994 A CN 2012101979994A CN 201210197999 A CN201210197999 A CN 201210197999A CN 102732013 A CN102732013 A CN 102732013A
- Authority
- CN
- China
- Prior art keywords
- parts
- nylon
- fire
- retardant
- silit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种阻燃的碳化硅填充的尼龙复合材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙
1010
树脂
60
～
67
份；尼龙
6
树脂
19
～
25
份；硅烷助剂
0.7
～
1.3
份；阻燃剂
8
～
17
份；碳化硅
11
～
18
份；间苯二酚四苯基二磷酸酯
6
～
11
份；抗氧剂
0.3
～
0.6
份；玻璃纤维
30
～
38
份；芥酸酰胺
0.3
～
0.8
份。具有良好的机械性能和热变形稳定性，从而能满足制造汽车、机械和建筑用的零部件要求。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种阻燃的碳化硅填充的尼龙复合材料。
背景技术
碳化硅作为一种耐热性和耐磨性均较佳的填充材料，广泛用于高端复合材料中。尼龙作为一类工程塑料，具有高强、耐磨、耐油和耐化学腐蚀的特点，被广泛用于汽车制造、电子电器、机械设备、航空航天、体育机械等领域。将碳化硅填充在尼龙材料中，可以改善尼龙材料的耐热和冲击性能而藉以应用于建筑、机械、汽车等领域。下面将要介绍的技术方案便是基于该前提下产生的。
发明内容
本发明的任务在于提供一种既具有良好的机械性能又具有优异的耐热和冲击性而适合于制作汽车、机械、建筑等部件的阻燃的碳化硅填充的尼龙复合材料。
本发明的任务是这样来完成的，一种阻燃的碳化硅填充的尼龙复合材料，其是由以下重量份数的原料组成：
尼龙1010树脂 60～67份；
尼龙6树脂 19～25份；
硅烷助剂 0.7～1.3份；
阻燃剂 8～17份；
碳化硅 11～18份；
间苯二酚四苯基二磷酸酯 6～11份；
抗氧剂 0.3～0.6份；
玻璃纤维 30～38份；
芥酸酰胺 0.3～0.8份。
在本发明的一个实施例中，所述的尼龙1010树脂是指熔点在200℃的树脂。
在本发明的另一个实施例中，所述的尼龙6树脂是指熔点在225℃的树脂。
在本发明的又一个实施例中，所述的硅烷助剂是指N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷。
在本发明的再一个实施例中，所述的阻燃剂是指十溴二苯乙烷。
在本发明的还有一个实施例中，所述的碳化硅是指长径比为150～180的碳化硅晶须。
在本发明的更而一个实施例中，所述的抗氧剂是指四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
在本发明的进而一个实施例中，所述的玻璃纤维是指长度为3mm的无碱短切玻璃纤维。
本发明提供的阻燃的碳化硅增强的尼龙复合材料的拉伸强度大于180MPa，弯曲强度大于263MPa,悬臂梁缺口冲击强度大于28kj/m
2
, 熔融指数大于19g/10min，热变形温度达到230℃，阻燃性达到V-0（UL-94-0.8mm），因此由于具有良好的机械性能和热变形稳定性，从而能满足制造汽车、机械和建筑用的零部件要求。
具体实施方式
实施例1：
按重量份数，熔点在200℃的树脂即尼龙1010树脂60份，熔点在225℃的树脂即尼龙6树脂22份，硅烷助剂即N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷0.7份，阻燃剂即十溴二苯乙烷12份，长径比为150～180的碳化硅晶须11份，间苯二酚四苯基二磷酸酯7份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.4份，长度为3mm的无碱短切玻璃纤维38份，芥酸酰胺0.3份。
实施例2：
按重量份数，熔点在200℃的树脂即尼龙1010树脂62份，熔点在225℃的树脂即尼龙6树脂19份，硅烷助剂即N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷0.9份，阻燃剂即十溴二苯乙烷8份，长径比为150～180的碳化硅晶须14份，间苯二酚四苯基二磷酸酯6份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.6份，长度为3mm的无碱短切玻璃纤维30份，芥酸酰胺0.4份。
实施例3：
按重量份数，熔点在200℃的树脂即尼龙1010树脂67份，熔点在225℃的树脂即尼龙6树脂25份，硅烷助剂即N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷1.3份，阻燃剂即十溴二苯乙烷14份，长径比为150～180的碳化硅晶须16份，间苯二酚四苯基二磷酸酯9份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.5份，长度为3mm的无碱短切玻璃纤维33份，芥酸酰胺0.8份。
实施例4：
按重量份数，熔点在200℃的树脂即尼龙1010树脂64份，熔点在225℃的树脂即尼龙6树脂23份，硅烷助剂即N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷1.1份，阻燃剂即十溴二苯乙烷17份，长径比为150～180的碳化硅晶须18份，间苯二酚四苯基二磷酸酯11份，抗氧剂即四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯0.3份，长度为3mm的无碱短切玻璃纤维36份，芥酸酰胺0.6份。
由上述实施例得到的阻燃的碳化硅填充的尼龙复合材料经测试具有下表所示的技术效果：
| 测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
| 拉伸强度MPa | 180 | 184 | 186 | 189 |
| 弯曲强度MPa | 263 | 267 | 269 | 272 |
| 悬臂梁缺口冲击强度kj/m 2 | 28.0 | 28.4 | 28.6 | 28.9 |
| 熔融指数g/10min | 19 | 19.4 | 19.7 | 20.1 |
| 热变形温度℃ | 230 | 234 | 237 | 241 |
| 阻燃性（UL-94-0.8mm） | V-0 | V-0 | V-0 | V-0 |
Claims (8)
1.一种阻燃的碳化硅填充的尼龙复合材料，其特征在于其是由以下重量份数的原料组成：
尼龙1010树脂 60～67份；
尼龙6树脂 19～25份；
硅烷助剂 0.7～1.3份；
阻燃剂 8～17份；
碳化硅 11～18份；
间苯二酚四苯基二磷酸酯 6～11份；
抗氧剂 0.3～0.6份；
玻璃纤维 30～38份；
芥酸酰胺 0.3～0.8份。
2.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的尼龙1010树脂是指熔点在200℃的树脂。
3.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的尼龙6树脂是指熔点在225℃的树脂。
4.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的硅烷助剂是指N-β-（氨乙基）-γ-氨丙基三甲氧基硅烷。
5.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的阻燃剂是指十溴二苯乙烷。
6.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的碳化硅是指长径比为150～180的碳化硅晶须。
7.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的抗氧剂是指四[甲基-β-（3，5-二叔丁基-4-羟基苯基）丙酸酯]季戊四醇酯。
8.根据权利要求1所述的阻燃的碳化硅填充的尼龙复合材料，其特征在于所述的玻璃纤维是指长度为3mm的无碱短切玻璃纤维。