CN104130571A - 一种增强增韧尼龙pa6改性工程塑料的制备方法 - Google Patents

一种增强增韧尼龙pa6改性工程塑料的制备方法 Download PDF

Info

Publication number
CN104130571A
CN104130571A CN201410407772.7A CN201410407772A CN104130571A CN 104130571 A CN104130571 A CN 104130571A CN 201410407772 A CN201410407772 A CN 201410407772A CN 104130571 A CN104130571 A CN 104130571A
Authority
CN
China
Prior art keywords
weight part
preparation
parts
nylon
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410407772.7A
Other languages
English (en)
Inventor
王进
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG RUILONG NEW MATERIAL CO Ltd
Original Assignee
NANTONG RUILONG NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG RUILONG NEW MATERIAL CO Ltd filed Critical NANTONG RUILONG NEW MATERIAL CO Ltd
Priority to CN201410407772.7A priority Critical patent/CN104130571A/zh
Publication of CN104130571A publication Critical patent/CN104130571A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种增强增韧尼龙PA6改性工程塑料的制备方法，包括以下步骤：1）按照下列配比准备原料：尼龙切片PA650-60重量份，无碱玻璃纤维短切丝30-40重量份,硅酸石25-35重量份，马来酸酐熔融接枝EPDM 10-20重量份，偶联剂0.5-1重量份，抗氧剂0.5-1重量份，润滑剂0.5-1重量份，加入高速混合机中混合均匀；2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。本发明具有如下技术效果：制备的增强增韧PA6是经增韧改性的一种刚性兼备、性能均衡的工程塑料，除具有高冲击性很好的溶接强度外，还具有热稳定性、耐磨性，良好的自润性，成型加工性能好等特点。

Description

一种增强增韧尼龙PA6改性工程塑料的制备方法
技术领域
    本发明涉及一种增强增韧尼龙PA6改性工程塑料的制备方法，属于改性工程塑料技术领域。
背景技术
工程塑料是指拉伸强度在50MPa以上，弯曲模量在2GPa以上，冲击强度在60J/m以上，长期使用温度在100摄氏度以上，用于汽车、机械、电子电器等行业的塑料。
改性工程塑料，是指在通用塑料和工程塑料的基础上，经过填充、共混、增强等方法加工，提高了阻燃性、强度、抗冲击性、韧性等方面的性能的塑料制品。 普通的塑料往往会有它自身的特性和缺陷，改性塑料就是给塑料改变一下性质，基本的技术包括：1、增强：将玻璃纤维等与塑料共混以增加塑料的机械强度。2、填充：将矿物等填充物与塑料共混，使塑料的收缩率、硬度、强度等性质得到改变。3、增韧：通过给普通塑料加入增韧剂共混以提高塑料的韧性，增韧改性后的产品：铁轨垫片。4、阻燃：给普通塑料树脂里面添加阻燃剂，即可使塑料具有阻燃特性，阻燃剂可以是一种或者是几种阻燃剂的复合体系，如溴+锑系，磷系，氮系，硅系，以及其他无机阻燃体系。5、耐寒：增加塑料在低温下的强度和韧性，一般塑料在低温下固有的低温脆性，使得在低温环境中应用受限，需要添加一些耐低温增韧剂改变塑料在低温下的脆性，例如汽车保险杠等塑件，一般要求耐寒。
PA作为工程塑料中最大最重要的品种，具有很强的生命力，主要在于它改性后实现高性能化，其次是汽车、电器、电讯、电子、机械等产业自身对产品高性能的要求越来越强烈，相关产业飞速发展，促进了工程塑料高性能化的进程，使其扮演着越来越重要的角色。随着国内汽车电气电子等工业的蓬勃发展，人们对材料的要求越来越高，改性工程塑料的需求将大幅上升，对改性工程塑料的强度和阻燃等性能要求越来越高。
发明内容
本发明的目的是克服现有技术的不足之处，提供一种增强增韧尼龙PA6改性工程塑料的制备方法。
本发明的增强增韧尼龙PA6改性工程塑料的制备方法，包括以下步骤：
1）按照下列配比准备原料：尼龙切片PA6 50-60重量份，无碱玻璃纤维短切丝30-40重量份,硅酸石25-35重量份，马来酸酐熔融接枝EPDM  10-20重量份，偶联剂0.5-1重量份，抗氧剂0.5-1重量份，润滑剂0.5-1重量份，加入高速混合机中混合均匀；
2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。
优选地，
所述的原料包括下列成分：尼龙切片PA6 55重量份，无碱玻璃纤维短切丝35重量份,硅酸石30重量份，马来酸酐熔融接枝EPDM  15重量份，偶联剂0.8重量份，抗氧剂0.8重量份，润滑剂0.8重量份。
本发明具有如下技术效果：制备的增强增韧PA6是经增韧改性的一种刚性兼备、性能均衡的工程塑料，除具有高冲击性很好的溶接强度外，还具有热稳定性、耐磨性，良好的自润性，成型加工性能好等特点。可用于生产汽车零部件，运动器材，纺织机械配件，油管，齿轮，童车，高档轿车保险杠，轴承保持架，扎带，轮罩，接插件，医疗器械配件等可替代部分进口产品。
具体实施方式
实施例1  制备增强增韧尼龙PA6改性工程塑料
本实施例的增强增韧尼龙PA6改性工程塑料的制备方法，包括以下步骤：
1）按照下列配比准备原料：尼龙切片PA6 60重量份，无碱玻璃纤维短切丝40重量份,硅酸石35重量份，马来酸酐熔融接枝EPDM  10重量份，偶联剂1重量份，抗氧剂1重量份，润滑剂1重量份，加入高速混合机中混合均匀；
2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。
 
实施例2  制备增强增韧尼龙PA6改性工程塑料
本实施例的增强增韧尼龙PA6改性工程塑料的制备方法，包括以下步骤：
1）按照下列配比准备原料：尼龙切片PA6 50重量份，无碱玻璃纤维短切丝30重量份,硅酸石25重量份，马来酸酐熔融接枝EPDM  20重量份，偶联剂0.5重量份，抗氧剂0.5重量份，润滑剂0.5重量份，加入高速混合机中混合均匀；
2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。
 
实施例3  制备增强增韧尼龙PA6改性工程塑料
本实施例的增强增韧尼龙PA6改性工程塑料的制备方法，包括以下步骤：
1）按照下列配比准备原料：尼龙切片PA6 55重量份，无碱玻璃纤维短切丝35重量份,硅酸石30重量份，马来酸酐熔融接枝EPDM  15重量份，偶联剂0.8重量份，抗氧剂0.8重量份，润滑剂0.8重量份，加入高速混合机中混合均匀；
2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。

Claims (2)

1.一种增强增韧尼龙PA6改性工程塑料的制备方法，其特征在于，包括以下步骤：
1）按照下列配比准备原料：尼龙切片PA6 50-60重量份，无碱玻璃纤维短切丝30-40重量份,硅酸石25-35重量份，马来酸酐熔融接枝EPDM  10-20重量份，偶联剂0.5-1重量份，抗氧剂0.5-1重量份，润滑剂0.5-1重量份，加入高速混合机中混合均匀；
2）熔融挤出：将混合料送入双螺杆挤出机进行熔融共混挤出、拉条、水冷、切粒、干燥，即得成品。
2.根据权利要求1所述的增强增韧尼龙PA6改性工程塑料的制备方法，其特征在于，所述的原料包括下列成分：尼龙切片PA6 55重量份，无碱玻璃纤维短切丝35重量份,硅酸石30重量份，马来酸酐熔融接枝EPDM  15重量份，偶联剂0.8重量份，抗氧剂0.8重量份，润滑剂0.8重量份。
 
CN201410407772.7A 2014-08-19 2014-08-19 一种增强增韧尼龙pa6改性工程塑料的制备方法 Pending CN104130571A (zh)