CN102746650A - 硫酸钙晶须填充的无卤阻燃尼龙合金材料 - Google Patents
硫酸钙晶须填充的无卤阻燃尼龙合金材料 Download PDFInfo
- Publication number
- CN102746650A CN102746650A CN2012101980192A CN201210198019A CN102746650A CN 102746650 A CN102746650 A CN 102746650A CN 2012101980192 A CN2012101980192 A CN 2012101980192A CN 201210198019 A CN201210198019 A CN 201210198019A CN 102746650 A CN102746650 A CN 102746650A
- Authority
- CN
- China
- Prior art keywords
- calcium sulfate
- parts
- halogen
- alloy material
- sulfate crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种硫酸钙晶须填充的无卤阻燃的尼龙合金材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：尼龙
66
树脂
210
～
250
份；相容剂
70
～
90
份；偶联剂
3
～
5
份；硫酸钙晶须
60
～
80
份；磷酸盐
30
～
50
份；抗氧剂
0.9
～
1.8
份；短切玻璃纤维
130
～
170
份；表面改性剂
0.5
～
1.2
份。优点：不含有卤素而可体现绿色环保，具有良好的耐热性能，从而可应用于建筑、电子和汽车等领域。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种硫酸钙晶须填充的无卤阻燃尼龙合金材料。
背景技术
尼龙是一种优良的树脂，其可以与聚乙烯形成良好的合金材料。为了使这种尼龙合金材料具有阻燃性，通常添加含卤素的阻燃剂，而含有卤素的阻燃剂燃烧时容易产生有毒的烟雾，影响环保。因此，如何使尼龙合金材料体现绿色环保而藉以应用于建筑、电子和汽车等领域始终受到人们的关注。为此，本申请人作了有益的尝试，下面将要介绍的技术方案便是在这种背景下产生的。
发明内容
本发明的任务在于提供一种既具有优异的物理性能，又具有良好的环保性和耐热性而藉以适合应用于如建筑、电子和汽车领域的硫酸钙晶须填充的无卤阻燃尼龙合金材料。
本发明的任务是这样来完成的，一种硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其是由以下重量份数的原料组成：
尼龙66树脂 210～250份；
相容剂 70～90份；
偶联剂 3～5份；
硫酸钙晶须 60～80份；
磷酸盐 30～50份；
抗氧剂 0.9～1.8份；
短切玻璃纤维 130～170份；
表面改性剂 0.5～1.2份。
在本发明的一个实施例中，所述的尼龙66树脂为熔点在250℃树脂。
在本发明的另一个实施例中，所述的相容剂为马来酸酐接枝的聚乙烯树脂。
在本发明的又一个实施例中，所述的偶联剂为N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷。
在本发明的再一个实施例中，所述的硫酸钙晶须为经过表面处理的并且长径比为120～150的硫酸钙晶须。
在本发明的还有一个实施例中，所述的磷酸盐为三聚氰胺焦磷酸盐。
在本发明的更而一个实施例中，所述的抗氧剂为N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺。
在本发明的进而一个实施例中，所述的短切玻璃纤维为长度3mm的无碱短切玻璃纤维。
在本发明的又更而一个实施例中，所述的表面改性剂为双硬脂酸酰胺。
本发明提供的硫酸钙晶须填充的无卤阻燃尼龙合金材料的拉伸强度大于110MPa，弯曲强度大于240MPa,悬臂梁缺口冲击强度大于37kj/m
2
, 熔融指数大于28g/10min，阻燃性达到V-0（UL-94-1.6mm），不含有卤素而可体现绿色环保，具有良好的耐热性能，从而可应用于建筑、电子和汽车等领域。
具体实施方式
实施例1：
按重量份数，熔点在250℃的树脂即尼龙66树脂210份，相容剂即马来酸酐接枝的聚乙烯树脂90份，偶联剂即N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷5份，硫酸钙晶须即经过表面处理的并且长径比为120～150的硫酸钙晶须70份，磷酸盐即三聚氰胺焦磷酸盐30份，抗氧剂即N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺0.8份，长度3mm的无碱短切玻璃纤维150份，表面改性剂即双硬脂酸酰胺0.5份。
实施例2：
按重量份数，熔点在250℃的树脂即尼龙66树脂250份，相容剂即马来酸酐接枝的聚乙烯树脂70份，偶联剂即N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷3份，硫酸钙晶须即经过表面处理的并且长径比为120～150的硫酸钙晶须60份，磷酸盐即三聚氰胺焦磷酸盐35份，抗氧剂即N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺1.4份，长度3mm的无碱短切玻璃纤维130份，表面改性剂即双硬脂酸酰胺0.7份。
实施例3：
按重量份数，熔点在250℃的树脂即尼龙66树脂235份，相容剂即马来酸酐接枝的聚乙烯树脂65份，偶联剂即N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷3.5份，硫酸钙晶须即经过表面处理的并且长径比为120～150的硫酸钙晶须80份，磷酸盐即三聚氰胺焦磷酸盐45份，抗氧剂即N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺0.9份，长度3mm的无碱短切玻璃纤维160份，表面改性剂即双硬脂酸酰胺0.9份。
实施例4：
按重量份数，熔点在250℃的树脂即尼龙66树脂240份，相容剂即马来酸酐接枝的聚乙烯树脂60份，偶联剂即N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷4份，硫酸钙晶须即经过表面处理的并且长径比为120～150的硫酸钙晶须85份，磷酸盐即三聚氰胺焦磷酸盐50份，抗氧剂即N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺1.8份，长度3mm的无碱短切玻璃纤维170份，表面改性剂即双硬脂酸酰胺1.2份。
由上述实施例1-4提到的硫酸钙晶须填充的无卤阻燃的尼龙合金材料经测试具有下表所示的技术效果：
| 测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
| 拉伸强度MPa | 110 | 113 | 117 | 122 |
| 弯曲强度MPa | 240 | 244 | 248 | 251 |
| 悬臂梁缺口冲击强度kj/m 2 | 37.0 | 37.5 | 37.8 | 38.2 |
| 熔融指数g/10min | 28 | 28.4 | 28.9 | 29.3 |
| 阻燃性（UL-94-1.6mm） | V-0 | V-0 | V-0 | V-0 |
Claims (9)
1.一种硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于其是由以下重量份数的原料组成：
尼龙66树脂 210～250份；
相容剂 70～90份；
偶联剂 3～5份；
硫酸钙晶须 60～80份；
磷酸盐 30～50份；
抗氧剂 0.9～1.8份；
短切玻璃纤维 130～170份；
表面改性剂 0.5～1.2份。
2.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的尼龙66树脂为熔点在250℃树脂。
3.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的相容剂为马来酸酐接枝的聚乙烯树脂。
4.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的偶联剂为N-β-(氨乙基)-γ-氨丙基甲基二甲氧基硅烷。
5.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的硫酸钙晶须为经过表面处理的并且长径比为120～150的硫酸钙晶须。
6.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的磷酸盐为三聚氰胺焦磷酸盐。
7.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的抗氧剂为N，Nˊ-双-[3-（3，5-二叔丁基-4-羟基苯基）丙酰基]已二胺。
8.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的短切玻璃纤维为长度3mm的无碱短切玻璃纤维。
9.根据权利要求1所述的硫酸钙晶须填充的无卤阻燃的尼龙合金材料，其特征在于所述的表面改性剂为双硬脂酸酰胺。