CN103254594A - 环保的聚对苯二甲酸乙二醇酯模塑料 - Google Patents

环保的聚对苯二甲酸乙二醇酯模塑料 Download PDF

Info

Publication number
CN103254594A
CN103254594A CN2013102143039A CN201310214303A CN103254594A CN 103254594 A CN103254594 A CN 103254594A CN 2013102143039 A CN2013102143039 A CN 2013102143039A CN 201310214303 A CN201310214303 A CN 201310214303A CN 103254594 A CN103254594 A CN 103254594A
Authority
CN
China
Prior art keywords
parts
polyethylene terephthalate
moulding compound
environmental protection
protection according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102143039A
Other languages
English (en)
Inventor
李梅新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Original Assignee
CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd filed Critical CHANGSHU HONGJI NON-WOVEN PRODUCTION Co Ltd
Priority to CN2013102143039A priority Critical patent/CN103254594A/zh
Publication of CN103254594A publication Critical patent/CN103254594A/zh
Pending legal-status Critical Current

Abstract

一种环保的聚对苯二甲酸乙二醇酯模塑料，属于高分子材料技术领域。其特征在于其是由以下重量份数的原料组成：聚对苯二甲酸乙二醇酯35～43份；聚丙烯树脂5～10份；增韧剂6~12份；磷酸盐8~14份；抗氧剂0.2~0.6份；增强纤维7.5~15份；润滑剂0.6~1.1份；炭黑0.8~1.4份。提供的环保的聚对苯二甲酸乙二醇酯复合材料经测试具有如下的性能指标：拉伸强度125～147MPa，弯曲强度210～225MPa，缺口冲击强度63～76j/m,阻燃性达到V-0(UL-94-1.5mm)，热变形温度207～223℃，燃烧时无有毒有害气体释放。

Description

环保的聚对苯二甲酸乙二醇酯模塑料
技术领域
本发明属于高分子材料技术领域，具体涉及一种环保的聚对苯二甲酸乙二醇酯模塑料。
背景技术
聚对苯二甲酸乙二醇酯是由对苯二甲酸与乙二醇经过缩聚反应而制成，其具有分子排列有序，结晶性强的特点。经过改性后，聚对苯二甲酸乙二醇酯具有较高的耐热变形温度，具有很强的实际应用意义，但是聚酯属于易燃物，在日常使用中容易造成火灾，并且很多材料使用了卤素阻燃剂，这类阻燃剂燃烧时容易释放有毒的气体HX,造成环境污染，危害人类健康。因此，对于开发既具有优异的强度，又具有良好的阻燃性，并且燃烧时不释放有毒气体的模塑料具有积极意义。
发明内容
本发明的任务在于提供一种环保的聚对苯二甲酸乙二醇酯模塑料，其具有强度高，阻燃性能理想，并且在燃烧时不会释放有毒有害气体的特点。
本发明的任务是这样来完成的，一种环保的聚对苯二甲酸乙二醇酯模塑料，其是由以下重量份数的原料组成：
Figure BDA0000328230151
在本发明的一个实施例中，所述的聚对苯二甲酸乙二醇酯树脂为熔点在255℃，特性黏度指数为0.55dl/g 的聚对苯二甲酸乙二醇酯。
在本发明的另一个实施例中，所述的聚丙烯树脂为熔点为170℃的共聚聚丙烯树脂。
在本发明的又一个实施例中，所述的增韧剂为聚酯-聚醚共聚物，其中聚酯段为聚对苯二甲酸乙二醇酯，聚醚段为聚四亚甲基醚。
在本发明的再一个实施例中，所述的磷酸盐为次磷酸铝。
在本发明的还有一个实施例中，所述的抗氧剂为亚磷酸三（2·4-二叔丁基苯基）酯。
在本发明的更而一个实施例中，所述的增强纤维为长度3mm的无碱玻璃纤维。
在本发明的进而一个实施例中，所述的润滑剂为硬脂酸钙。
在本发明的又更而一个实施例中，所述的炭黑为槽法炭黑。
本发明提供的环保的聚对苯二甲酸乙二醇酯复合材料经测试具有如下的性能指标：拉伸强度125～147MPa，弯曲强度210～225MPa，缺口冲击强度63～76j/m,阻燃性达到V-0(UL-94-1.5mm)，热变形温度207～223℃，燃烧时无有毒有害气体释放。
具体实施方式
实施例1：
Figure BDA0000328230152
实施例2：
Figure BDA0000328230153
实施例3：
Figure BDA0000328230154
实施例4：
Figure BDA0000328230155
由上述实施例1至4得到的环保的聚对苯二甲酸乙二醇酯模塑料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 126 132 139 146
弯曲强度MPa 212 216 220 225
缺口冲击强度j/m 63.5 67.6 71.2 75.8
阻燃性(UL-94-1.5mm) V-0 V-0 V-0 V-0
热变形温度℃ 208 214 219 222

Claims (9)

1.一种环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于其是由以下重量份数的原料组成：
                  聚对苯二甲酸乙二醇酯         35～43份；
          聚丙烯树脂                  5～10份；
          增韧剂                      6~12份；
          磷酸盐                      8~14份；
          抗氧剂                      0.2~0.6份；
          增强纤维                    7.5~15份；
          润滑剂                      0.6~1.1份；
          炭黑                        0.8~1.4份。
2.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的聚对苯二甲酸乙二醇酯树脂为熔点在255℃，特性黏度指数为0.55dl/g 的聚对苯二甲酸乙二醇酯。
3.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的聚丙烯树脂为熔点为170℃的共聚聚丙烯树脂。
4.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的增韧剂为聚酯-聚醚共聚物，其中聚酯段为聚对苯二甲酸乙二醇酯，聚醚段为聚四亚甲基醚。
5.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的磷酸盐为次磷酸铝。
6.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的抗氧剂为亚磷酸三（2·4-二叔丁基苯基）酯。
7.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的增强纤维为长度3mm的无碱玻璃纤维。
8.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的润滑剂为硬脂酸钙。
9.根据权利要求1所述的环保的聚对苯二甲酸乙二醇酯模塑料，其特征在于所述的炭黑为槽法炭黑。
CN2013102143039A 2013-05-31 2013-05-31 环保的聚对苯二甲酸乙二醇酯模塑料 Pending CN103254594A (zh)