CN103254585A - 芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料 - Google Patents
芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料 Download PDFInfo
- Publication number
- CN103254585A CN103254585A CN2013101691394A CN201310169139A CN103254585A CN 103254585 A CN103254585 A CN 103254585A CN 2013101691394 A CN2013101691394 A CN 2013101691394A CN 201310169139 A CN201310169139 A CN 201310169139A CN 103254585 A CN103254585 A CN 103254585A
- Authority
- CN
- China
- Prior art keywords
- aryl phosphate
- parts
- phosphate ester
- fire
- pet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚对苯二甲酸乙二醇酯37～43份；聚碳酸酯13～18份；增韧剂5~8份；芳基磷酸酯5~6.5份；填料14~21份；抗氧剂0.4~0.9份；增强纤维8~16份；炭黑0.7~1.5份。提供的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料经测试具有如下性能指标：拉伸强度105～128MPa，弯曲强度183～211MPa，缺口冲击强度58～76j/m,阻燃性达到V-0(UL-94-3.0mm)，热变形温度150～175℃。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种芳基磷酸酯阻燃的聚对苯基二甲酸乙二醇酯材料。
背景技术
聚对苯二甲酸乙二醇酯是由对苯二甲酸与乙二醇经过缩聚反应而得的基础应用树脂，聚对苯二甲酸乙二醇酯具有结晶强，熔点高，强度高的长处，广泛用于增强、增韧等场合。芳基磷酸酯是一种具有较好阻燃性的含磷阻燃剂，其对很多树脂具有增塑和增韧效果。芳基磷酸酯属于环保类阻燃剂，对人体以及环境等影响小。本发明在下面将要提出的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料具有强度高，阻燃好的特点。
发明内容
本发明的任务在于提供一种具有拔萃的强度和阻燃效果的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料。
本发明的任务是这样来完成的，一种芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其是由以下重量份数的原料组成：
在本发明的一个实施例中，所述的聚对苯二甲酸乙二醇酯树脂为熔点在260℃并且特性黏度指数为0.65dl/g 的聚对苯二甲酸乙二醇酯。
在本发明的另一个实施例中，所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
在本发明的又一个实施例中，所述的增韧剂为马来酸酐接枝的氢化的苯乙烯-丁二烯-苯乙烯共聚物。
在本发明的再一个实施例中，所述的芳基磷酸酯为对苯二酚四苯基二磷酸酯。
在本发明的还有一个实施例中，所述的填料为活性碳酸钙。
在本发明的更而一个实施例中，所述的抗氧剂为2,2亚甲基-双(4-甲基-6-叔丁基苯酚)。
在本发明的进而一个实施例中，所述的增强纤维为长度3mm的无碱玻璃纤维。
在本发明的又更而一个实施例中，所述的炭黑为槽法炭黑。
本发明提供的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料经测试具有如下性能指标：拉伸强度105～128MPa，弯曲强度183～211MPa，缺口冲击强度58～76j/m,阻燃性达到V-0(UL-94-3.0mm)，热变形温度150～175℃。
具体实施方式
实施例1：
实施例2：
实施例3：
实施例4：
由上述实施例1至4得到的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料经测试具有下表所示的技术效果：
| 测试项目 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
| 拉伸强度MPa | 105 | 112 | 119 | 127 |
| 弯曲强度MPa | 183 | 192 | 201 | 210 |
| 缺口冲击强度j/m | 58.3 | 65.4 | 70.8 | 75.6 |
| 阻燃性(UL-94-3.0mm) | V-0 | V-0 | V-0 | V-0 |
| 热变形温度℃ | 150 | 158 | 165 | 174 |
Claims (9)
1.一种芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于其是由以下重量份数的原料组成：
聚对苯二甲酸乙二醇酯 37～43份；
聚碳酸酯 13～18份；
增韧剂 5~8份；
芳基磷酸酯 5~6.5份；
填料 14~21份；
抗氧剂 0 .4~0.9份；
增强纤维 8~16份；
炭黑 0.7~1.5份。
2.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的聚对苯二甲酸乙二醇酯树脂为熔点在260℃并且特性黏度指数为0.65dl/g 的聚对苯二甲酸乙二醇酯。
3.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的聚碳酸酯树脂为双酚A型聚碳酸酯。
4.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的增韧剂为马来酸酐接枝的氢化的苯乙烯-丁二烯-苯乙烯共聚物。
5.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的芳基磷酸酯为对苯二酚四苯基二磷酸酯。
6.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的填料为活性碳酸钙。
7.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的抗氧剂为2,2亚甲基-双(4-甲基-6-叔丁基苯酚)。
8.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的增强纤维为长度3mm的无碱玻璃纤维。
9.根据权利要求1所述的芳基磷酸酯阻燃的聚对苯二甲酸乙二醇酯材料，其特征在于所述的炭黑为槽法炭黑。