CN104177720A - 乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料 - Google Patents

乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料 Download PDF

Info

Publication number
CN104177720A
CN104177720A CN201310188236.8A CN201310188236A CN104177720A CN 104177720 A CN104177720 A CN 104177720A CN 201310188236 A CN201310188236 A CN 201310188236A CN 104177720 A CN104177720 A CN 104177720A
Authority
CN
China
Prior art keywords
polyvinyl chloride
ethylene
vinyl acetate
acetate copolymer
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310188236.8A
Other languages
English (en)
Inventor
金钟文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Kasimayin Kitchen Ware Co Ltd
Original Assignee
Changshu Kasimayin Kitchen Ware Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Kasimayin Kitchen Ware Co Ltd filed Critical Changshu Kasimayin Kitchen Ware Co Ltd
Priority to CN201310188236.8A priority Critical patent/CN104177720A/zh
Publication of CN104177720A publication Critical patent/CN104177720A/zh
Pending legal-status Critical Current

Abstract

一种乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚氯乙烯树脂52.3~58.7份；氯化聚乙烯7.3~11.5份；增塑剂5.1～8.9份；聚烯烃8.4～12.7份；填料8~15份；稳定剂0.6~1.6份；竹粉5~8.2份；润滑剂0.6~1.2份。经测试具有如下性能指标：弯曲强度32～47MPa,弯曲模量，1500～1900MPa，缺口冲击强度大于2.7～4.6kj/m2，热变形温度97～115℃,阻燃性V-0(UL-94-V-0-4.0mm)。

Description

乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料。
背景技术
聚氯乙烯是一种性能优异的热塑性材料，广泛用于生产管道、建筑材料、装饰材料、汽车材料等。一般建筑和管道都会选择聚氯乙烯合金材料，这种材料材料具有价廉、加工方便的长处，但是这类材料韧性差，不耐弯折和冲击，并且耐低温性能差，很容易在低温下开裂等，为了改善这种缺陷，本发明人进行大量的研究，终于形成了下面将要介绍的技术方案。
发明内容
本发明的任务在于提供一种具有强度高、耐低温性好和弯折不开裂等特点的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料。
本发明的任务是这样来完成的，一种乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其是由以下重量份数的原料组成：
在本发明的一个实施例中，所述的聚氯乙烯树脂为k值65的聚氯乙烯树脂。
在本发明的另一个实施例中，所述的氯化聚乙烯为全氯化聚乙烯。
在本发明的又一个实施例中，所述的增塑剂为邻苯二甲酸二甲酯。
在本发明的再一个实施例中，所述的聚烯烃为乙烯-醋酸乙烯共聚物。
在本发明的还有一个实施例中，所述的填料为煅烧碳酸钙。
在本发明的更而一个实施例中，所述的稳定剂为钙锌稳定剂。
在本发明的进而一个实施例中，所述的竹纤维为磨碎的竹粉。
在本发明的又更而一个实施例中，所述的润滑剂为硬脂酸锌。
本发明提供的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料经测试具有如下性能指标：弯曲强度 32～47MPa,弯曲模量，1500～1900MPa,缺口冲击强度大于2.7～4.6kj/m2，热变形温度97～115℃,阻燃性V-0(UL-94-V-0-4.0mm)。
具体实施方式
实施例1：
实施例2：
实施例3：
实施例4：
由上述实施例1至4得到的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
弯曲强度MPa 32 36 42 47
弯曲模量MPa 1550 1680 1760 1890
缺口冲击强度kj/m2 2.8 3.2 3.9 4.6
热变形温度℃ 97 102 109 115
阻燃性（UL-94-4.0mm） V-0 V-0 V-0 V-0

Claims (9)

1.一种乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于其是由以下重量份数的原料组成：
         聚氯乙烯树脂         52.3~58.7份；
          氯化聚乙烯          7.3~11.5份；
          增塑剂              5.1～8.9份；
          聚烯烃              8.4～12.7份；
          填料                8~15份；
          稳定剂              0.6~1.6份；
          竹粉                5~8.2份；
         润滑剂               0.6~1.2份。
2.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的聚氯乙烯树脂为k值65的聚氯乙烯树脂。
3.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的氯化聚乙烯为全氯化聚乙烯。
4.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的增塑剂为邻苯二甲酸二甲酯。
5.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的聚烯烃为乙烯-醋酸乙烯共聚物。
6.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的填料为煅烧碳酸钙。
7.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的稳定剂为钙锌稳定剂。
8.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的竹纤维为磨碎的竹粉。
9.根据权利要求1所述的乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料，其特征在于所述的润滑剂为硬脂酸锌。
CN201310188236.8A 2013-05-20 2013-05-20 乙烯-醋酸乙烯共聚物改性的聚氯乙烯合金材料 Pending CN104177720A (zh)