CN103072982A - 一种低成本沥青基石墨烯片及其制备方法 - Google Patents

一种低成本沥青基石墨烯片及其制备方法 Download PDF

Info

Publication number
CN103072982A
CN103072982A CN2013100625982A CN201310062598A CN103072982A CN 103072982 A CN103072982 A CN 103072982A CN 2013100625982 A CN2013100625982 A CN 2013100625982A CN 201310062598 A CN201310062598 A CN 201310062598A CN 103072982 A CN103072982 A CN 103072982A
Authority
CN
China
Prior art keywords
low
ball
temperature
pitch
graphene film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100625982A
Other languages
English (en)
Other versions
CN103072982B (zh
Inventor
林起浪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuzhou University
Original Assignee
Fuzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuzhou University filed Critical Fuzhou University
Priority to CN201310062598.2A priority Critical patent/CN103072982B/zh
Publication of CN103072982A publication Critical patent/CN103072982A/zh
Application granted granted Critical
Publication of CN103072982B publication Critical patent/CN103072982B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种低成本沥青基石墨烯片及其制备方法，属于碳素材料领域。本发明以沥青和添加剂为原料，经过混合、炭化、酸洗、球磨等工艺制备石墨烯片。本发明的产品纯度高，结构缺陷少、制备成本低、操作简单、易实现产业化。

Description

一种低成本沥青基石墨烯片及其制备方法
技术领域
本发明属于碳素材料领域，具体涉及一种低成本沥青基石墨烯片及其制备方法。
背景技术
石墨烯片是一种只有单层或几层原子厚度的纯碳原子结构，其C-C键以sp2结合，形成一个密集的蜂窝状晶格结构。由于它具有的独特的二维碳纳米微观结构以及优异的物理属性，因而其在物理学、材料学以及凝聚态物理等领域引起了人们的广泛兴趣。目前以石墨烯片为基础的材料有着广泛的工业应用范围，如可用作吸附剂、药物输送、催化剂载体，热传输媒体，可制成具有精细结构的电子元件。特别地，随着碳材料性能的不断改进，使其逐渐成为能源领域的主导，如在对存储设备要求高的氢储存、燃料电池、太阳能电池以及锂离子电池、电容器等方面应用广泛。
虽然石墨烯片的应用广泛，但它的许多应用亟需实现大规模、可重复地制备结构规整、厚度和尺寸可控的高质量石墨烯材料。目前用来制备石墨烯片的原料主要有两大类：鳞片石墨和富碳材料。制备石墨烯片的方法主要有机械方法以及化学方法两大类型，如微机械分离法，取向附生法、SiC或金属基板上外延生长、化学还原法与化学解理法、化学气相沉积法等。然而，上述方法制备石墨烯片存在工艺复杂、成本高、环境污染等问题，并且难以大量制备出石墨烯片，这极大阻碍石墨烯片的推广和应用。
发明内容
本发明的目的在于提供一种低成本沥青基石墨烯片及其制备方法，本发明的产品纯度高，结构缺陷少、制备成本低、操作简单、易实现产业化。
为实现上述目的，本发明采用如下技术方案：
一种低成本沥青基石墨烯片的制备方法包括原料的混合、炭化、酸洗、球磨工艺，包括以下步骤：
（1）原料的混合
将沥青与添加剂按一定比例称取，充分研磨后过筛；所用沥青为煤沥青、石油沥青、渣油沥青、合成沥青或中间相沥青，所用添加剂为铁粉、铜粉、硅粉、铝粉、氧化铝、氧化镁、氧化铁、二茂铁、氧化钙或氧化铜；混合工艺参数为：
原料粒度：60-300目
沥青与添加剂的质量比为100:1～100:100
添加剂的纯度：大于99％；
（2）低温炭化
将步骤（1）混合好的原料放入气氛炉中，然后以一定的升温速率升温至预定温度后保持一段时间，冷却至室温取出；低温炭化工艺参数为：
升温速率：2℃/min–100℃/min
预定温度：400℃–1000℃
保温时间：0.1h–10h
保护气氛：N2或者Ar
气体流量：50 mL/min–200 mL/min；      
（3）高温炭化
将步骤（2）所得到的产物放入真空炉中，然后以一定的升温速率升温至预定温度后保持一段时间，冷却至室温取出；高温炭化工艺参数为：
升温速率：2℃/min–50℃/min
温度：1200℃–2000℃
保温时间：0.1 h–10 h
真空度：1.0×10-1 Pa–1.0×103 Pa；
（4）酸洗
将步骤（3）所得炭化产物置于一定pH值的酸液中并搅拌一段时间，经过滤分离后用去离子水充分洗涤至无Cl－或者F－检测出，然后放入120℃烘箱中进行干燥5 h；酸洗工艺参数为：
酸液：盐酸或氢氟酸
pH值：1–5
炭化产物与酸液的质量比：1:3～1:10
搅拌时间：1–5h
搅拌速度：50–500转/分；
（5）球磨
将步骤（4）所得产物放入球磨机中进行球磨处理；球磨工艺参数为：
球磨时间：0.5–10h
球磨转速：50–500转/分。
本发明的显著优点在于：本发明的产品纯度高，结构缺陷少、制备成本低、操作简单、易实现产业化。
附图说明
图1为采用实施例1工艺制备的石墨烯片的场发射扫描电镜图片。
图2为采用实施例2工艺制备的石墨烯片的场发射扫描电镜图片。
图3为采用实施例3工艺制备的石墨烯片的场发射扫描电镜图片。
图4为采用实施例4工艺制备的石墨烯片的场发射扫描电镜图片。
图5为采用实施例5工艺制备的石墨烯片的场发射扫描电镜图片。
具体实施方式
实施例1
将煤沥青与二茂铁按100：1（质量比）称取，研磨至60目后放入气氛炉中，并通入N2（N2流量为100mL/min），以2℃/min升温至700℃后保温5h，冷却至室温取出低温炭化产物。将低温炭化产物放入真空炉中（真空度1.0×103Pa），以50℃/min升温至1900℃后保温2h，冷却至室温取出高温炭化产物。将高温炭化产物置于pH值为1的盐酸中（炭化产物与盐酸的质量比1:3），搅拌1h（搅拌速度50转/分），经过滤分离后用去离子水充分洗涤至无Cl－检测出，置于120℃烘箱中进行干燥5 h，然后放入球磨机中球磨5h（球磨转速200转/分），即获得石墨烯片。所制备的石墨烯片具有如下性能：层数为10～20、含碳量98.5％、比表面积26m2/g。
实施例2
将中间相沥青与氧化铝按100：100（质量比）称取，研磨至100目后放入气氛炉中，并通入Ar（Ar流量为50mL/min），以5℃/min升温至1000℃后保温0.1h，冷却至室温取出低温炭化产物。将低温炭化产物放入真空炉中（真空度1.0×10-1Pa），以20℃/min升温至2000℃后保温0.1h，冷却至室温取出高温炭化产物。将高温炭化产物置于pH值为3的盐酸中（炭化产物与盐酸的质量比1:5），搅拌4h（搅拌速度200转/分），经过滤分离后用去离子水充分洗涤至无Cl－检测出，置于120℃烘箱中进行干燥5 h，然后放入球磨机中球磨2h（球磨转速400转/分），即获得石墨烯片。所制备的石墨烯片具有如下性能：层数为10～15、含碳量99.5％、比表面积120m2/g。
实施例3
将石油沥青与铝粉按100：10（质量比）称取，研磨至300目后放入气氛炉中，并通入Ar（Ar流量为200mL/min），以100℃/min升温至800℃后保温5h，冷却至室温取出低温炭化产物。将低温炭化产物放入真空炉中（真空度1.0×10-1 Pa），以2℃/min升温至1800℃后保温1h，冷却至室温取出高温炭化产物。将高温炭化产物置于pH值为2的盐酸中（炭化产物与盐酸的质量比1:3），搅拌4h（搅拌速度150转/分），经过滤分离后用去离子水充分洗涤至无Cl－检测出，置于120℃烘箱中进行干燥5 h，然后放入球磨机中球磨10h（球磨转速500转/分），即获得石墨烯片。所制备的石墨烯片具有如下性能：层数为5～10、含碳量99.0％、比表面积192m2/g。
实施例4
将渣油沥青与氧化镁按100：80（质量比）称取，研磨至80目后放入气氛炉中，并通入N2（N2流量为200mL/min），以2℃/min升温至400℃后保温10h，冷却至室温取出低温炭化产物。将低温炭化产物放入真空炉中（真空度1.0×102Pa），以10℃/min升温至1500℃后保温5h，冷却至室温取出高温炭化产物。将高温炭化产物置于pH值为4的盐酸中（炭化产物与盐酸的质量比1:5），并搅拌5h（转速300转/分），经过滤分离后用去离子水充分洗涤至无Cl－检测出，置于120℃烘箱中进行干燥5 h，然后放入球磨机中球磨5h（球磨转速500转/分），即获得石墨烯片。所制备的石墨烯片具有如下性能：层数为8～12、含碳量99.0％、比表面积156m2/g。
实施例5
将合成沥青与硅粉按100：50（质量比）称取，研磨至300目后放入气氛炉中，并通入N2（N2流量为100mL/min），以5℃/min升温至800℃后保温1h，冷却至室温取出低温炭化产物。将低温炭化产物放入真空炉中（真空度1.0×10－1Pa），以5℃/min升温至1800℃后保温4h，冷却至室温取出高温炭化产物。将高温炭化产物置于pH值为1的氢氟酸中（炭化产物与氢氟酸的质量比1:5），并搅拌1h（搅拌速度500转/分），经过滤分离后用去离子水充分洗涤至无F－检测出，置于120℃烘箱中进行干燥5h，然后放入球磨机中球磨5h（球磨转速250转/分），即获得石墨烯片。所制备的石墨烯片具有如下性能：层数为5～10、含碳量95％、比表面积260m2/g。
以上所述仅为本发明的较佳实施例，凡依本发明申请专利范围所做的均等变化与修饰，皆应属本发明的涵盖范围。

Claims (3)

1.一种低成本沥青基石墨烯片的制备方法，其特征在于：包括原料的混合、炭化、酸洗、球磨工艺。
2.根据权利要求1所述的低成本沥青基石墨烯片的制备方法，其特征在于：包括以下步骤：
（1）原料的混合
将沥青与添加剂按一定比例称取，充分研磨后过筛；所用沥青为煤沥青、石油沥青、渣油沥青、合成沥青或中间相沥青，所用添加剂为铁粉、铜粉、硅粉、铝粉、氧化铝、氧化镁、氧化铁、二茂铁、氧化钙或氧化铜；混合工艺参数为：
原料粒度：60-300目
沥青与添加剂的质量比为100:1～100:100
添加剂的纯度：大于99％；
（2）低温炭化
将步骤（1）混合好的原料放入气氛炉中，然后以一定的升温速率升温至预定温度后保持一段时间，冷却至室温取出；低温炭化工艺参数为：
升温速率：2℃/min–100℃/min
预定温度：400℃–1000℃
保温时间：0.1h–10h
保护气氛：N2或者Ar
气体流量：50 mL/min–200 mL/min；  
（3）高温炭化
将步骤（2）所得到的产物放入真空炉中，然后以一定的升温速率升温至预定温度后保持一段时间，冷却至室温取出；高温炭化工艺参数为：
升温速率：2℃/min–50℃/min
温度：1200℃–2000℃
保温时间：0.1 h–10 h
真空度：1.0×10-1 Pa–1.0×103 Pa；
（4）酸洗
将步骤（3）所得炭化产物置于一定pH值的酸液中并搅拌一段时间，经过滤分离后用去离子水充分洗涤至无Cl－或者F－检测出，然后放入120℃烘箱中进行干燥5 h；酸洗工艺参数为：
酸液：盐酸或氢氟酸
pH值：1–5
炭化产物与酸液的质量比：1:3～1:10
搅拌时间：1–5h
搅拌速度：50–500转/分；
（5）球磨
将步骤（4）所得产物放入球磨机中进行球磨处理；球磨工艺参数为：
球磨时间：0.5–10h
球磨转速：50–500转/分。
3.一种如权利要求1所述的方法制得的低成本沥青基石墨烯片。
CN201310062598.2A 2013-02-28 2013-02-28 一种低成本沥青基石墨烯片及其制备方法 Expired - Fee Related CN103072982B (zh)