CN103069029A - 铝合金及铝合金铸件 - Google Patents
铝合金及铝合金铸件 Download PDFInfo
- Publication number
- CN103069029A CN103069029A CN2011800267252A CN201180026725A CN103069029A CN 103069029 A CN103069029 A CN 103069029A CN 2011800267252 A CN2011800267252 A CN 2011800267252A CN 201180026725 A CN201180026725 A CN 201180026725A CN 103069029 A CN103069029 A CN 103069029A
- Authority
- CN
- China
- Prior art keywords
- weight
- aluminium alloy
- alloy
- content
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C30/00—Alloys containing less than 50% by weight of each constituent
- C22C30/06—Alloys containing less than 50% by weight of each constituent containing zinc
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/10—Alloys based on aluminium with zinc as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C30/00—Alloys containing less than 50% by weight of each constituent
- C22C30/02—Alloys containing less than 50% by weight of each constituent containing copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C30/00—Alloys containing less than 50% by weight of each constituent
- C22C30/04—Alloys containing less than 50% by weight of each constituent containing tin or lead
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Conductive Materials (AREA)
- Continuous Casting (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2010-0050693 | 2010-05-29 | ||
KR1020100050693A KR101124235B1 (ko) | 2010-05-29 | 2010-05-29 | 알루미늄 합금 및 알루미늄 합금 주물 |
PCT/KR2011/003521 WO2011152617A2 (ko) | 2010-05-29 | 2011-05-12 | 알루미늄 합금 및 알루미늄 합금 주물 |
Publications (1)
Publication Number | Publication Date |
---|---|
CN103069029A true CN103069029A (zh) | 2013-04-24 |
Family
ID=45067164
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN2011800267252A Pending CN103069029A (zh) | 2010-05-29 | 2011-05-12 | 铝合金及铝合金铸件 |
Country Status (6)
Country | Link |
---|---|
US (1) | US20130209311A1 (ko) |
JP (1) | JP2013529255A (ko) |
KR (1) | KR101124235B1 (ko) |
CN (1) | CN103069029A (ko) |
DE (1) | DE112011101836T5 (ko) |
WO (1) | WO2011152617A2 (ko) |
Cited By (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103526088A (zh) * | 2013-09-29 | 2014-01-22 | 苏州利达铸造有限公司 | 一种数码电子产品用压铸铝合金 |
CN103614596A (zh) * | 2013-07-16 | 2014-03-05 | 深圳市欣茂鑫精密五金制品有限公司 | 一种用于电子产品结构件的高强度铝合金及其制备方法 |
CN103695732A (zh) * | 2013-11-26 | 2014-04-02 | 宁波瑞铭机械有限公司 | 一种缝纫机连杆及其制备方法 |
CN104264020A (zh) * | 2014-10-17 | 2015-01-07 | 苏州凯宥电子科技有限公司 | 一种高强度压铸铝合金及其制备方法 |
CN104259752A (zh) * | 2014-08-07 | 2015-01-07 | 兰宝琴 | 一种烤漆铝合金板的制造方法 |
CN107686923A (zh) * | 2017-09-18 | 2018-02-13 | 太仓天润新材料科技有限公司 | 一种超合金环保电子新材料 |
CN108728703A (zh) * | 2017-04-13 | 2018-11-02 | 韩国机械研究院 | Al-Zn-Cu合金及其制备方法 |
CN109972003A (zh) * | 2019-04-03 | 2019-07-05 | 上海交通大学 | 适于重力铸造的高延伸率耐热铝合金及其制备方法 |
CN112143949A (zh) * | 2019-06-27 | 2020-12-29 | 比亚迪股份有限公司 | 一种压铸铝合金及其制备方法和应用 |
CN113046607A (zh) * | 2021-03-16 | 2021-06-29 | 郑州大学 | 一种高硬高导热多元合金及其制备方法 |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2014015600A1 (zh) * | 2012-07-23 | 2014-01-30 | 刘欣明 | 一种高强度铝合金及其生产方法 |
KR101526657B1 (ko) | 2013-05-07 | 2015-06-05 | 현대자동차주식회사 | 복합 미세조직을 갖는 내마모성 합금 |
KR101526658B1 (ko) | 2013-05-07 | 2015-06-05 | 현대자동차주식회사 | 복합 미세조직을 갖는 내마모성 합금 |
CN103409673A (zh) * | 2013-08-26 | 2013-11-27 | 深圳市天合兴五金塑胶有限公司 | 高强性压铸铝钛合金 |
CN106563919B (zh) * | 2014-06-13 | 2019-06-07 | 广东长盈精密技术有限公司 | 一种手机中框、后盖的制备方法 |
CN107923004B (zh) * | 2015-08-13 | 2021-12-14 | 美铝美国公司 | 改善的3xx铝铸造合金及其制备方法 |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6256131A (ja) * | 1985-09-06 | 1987-03-11 | 三菱マテリアル株式会社 | 防振特性のすぐれたZn−Al系合金製防振部材 |
GB2233667A (en) * | 1989-06-02 | 1991-01-16 | Daido Metal Co | A1-based alloy |
JPH03230890A (ja) * | 1990-02-07 | 1991-10-14 | Showa Alum Corp | アルミニウム合金ろう材 |
US5925315A (en) * | 1995-02-14 | 1999-07-20 | Caterpillar Inc. | Aluminum alloy with improved tribological characteristics |
JP2005281798A (ja) * | 2004-03-30 | 2005-10-13 | Denso Corp | ガソリン−エタノール混合燃料用のアルミダイキャスト合金部品 |
CN101311283A (zh) * | 2007-05-24 | 2008-11-26 | 莱茵费尔登炼铝厂有限责任公司 | 耐热铝合金 |
Family Cites Families (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS607014B2 (ja) * | 1982-12-20 | 1985-02-21 | 三菱マテリアル株式会社 | 常温および高温強度のすぐれた鋳造用防振性Zn合金 |
US4808243A (en) * | 1982-12-20 | 1989-02-28 | Mitsubishi Metal Corporation | High damping zinc alloy with good intergranular corrosion resistance and high strength at both room and elevated temperatures |
JP4055177B2 (ja) * | 1994-08-18 | 2008-03-05 | 日曹金属化学株式会社 | 機械的強度の優れたダイカスト用アルミニウム合金及びそれを用いたボールジョイント装置 |
JP2006176851A (ja) * | 2004-12-24 | 2006-07-06 | Mitsubishi Alum Co Ltd | 耐エロージョン性に優れた熱交換器用の高強度アルミニウム合金板材および熱交換器並びに高強度アルミニウム合金板材の製造方法 |
US20090263273A1 (en) * | 2008-04-18 | 2009-10-22 | United Technologies Corporation | High strength L12 aluminum alloys |
KR20100050693A (ko) | 2008-11-06 | 2010-05-14 | 이인근 | 웹 기반 온톨로지 협업 구축 시스템에서 온톨로지 추론 엔진을 이용한 온톨로지의 논리기반 검색 및 논리기반 추론방법 및 그 시스템 |
KR100961081B1 (ko) | 2009-03-03 | 2010-06-08 | 임현규 | 고강도 경량 아연-알루미늄 합금 |
KR20100102301A (ko) * | 2009-03-11 | 2010-09-24 | 현대자동차주식회사 | 차량용 내마모성 알루미늄 합금 |
KR20100134361A (ko) * | 2009-06-15 | 2010-12-23 | 현대자동차주식회사 | 저 실리콘계 알루미늄 합금 |
-
2010
- 2010-05-29 KR KR1020100050693A patent/KR101124235B1/ko not_active IP Right Cessation
-
2011
- 2011-05-12 CN CN2011800267252A patent/CN103069029A/zh active Pending
- 2011-05-12 DE DE112011101836T patent/DE112011101836T5/de not_active Withdrawn
- 2011-05-12 WO PCT/KR2011/003521 patent/WO2011152617A2/ko active Application Filing
- 2011-05-12 US US13/700,550 patent/US20130209311A1/en not_active Abandoned
- 2011-05-12 JP JP2013512523A patent/JP2013529255A/ja active Pending
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6256131A (ja) * | 1985-09-06 | 1987-03-11 | 三菱マテリアル株式会社 | 防振特性のすぐれたZn−Al系合金製防振部材 |
GB2233667A (en) * | 1989-06-02 | 1991-01-16 | Daido Metal Co | A1-based alloy |
JPH03230890A (ja) * | 1990-02-07 | 1991-10-14 | Showa Alum Corp | アルミニウム合金ろう材 |
US5925315A (en) * | 1995-02-14 | 1999-07-20 | Caterpillar Inc. | Aluminum alloy with improved tribological characteristics |
JP2005281798A (ja) * | 2004-03-30 | 2005-10-13 | Denso Corp | ガソリン−エタノール混合燃料用のアルミダイキャスト合金部品 |
CN101311283A (zh) * | 2007-05-24 | 2008-11-26 | 莱茵费尔登炼铝厂有限责任公司 | 耐热铝合金 |
Cited By (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103614596B (zh) * | 2013-07-16 | 2016-03-02 | 深圳市欣茂鑫精密五金制品有限公司 | 一种用于电子产品结构件的高强度铝合金及其制备方法 |
CN103614596A (zh) * | 2013-07-16 | 2014-03-05 | 深圳市欣茂鑫精密五金制品有限公司 | 一种用于电子产品结构件的高强度铝合金及其制备方法 |
CN103526088A (zh) * | 2013-09-29 | 2014-01-22 | 苏州利达铸造有限公司 | 一种数码电子产品用压铸铝合金 |
CN103526088B (zh) * | 2013-09-29 | 2016-03-09 | 苏州利达铸造有限公司 | 一种数码电子产品用压铸铝合金 |
CN103695732A (zh) * | 2013-11-26 | 2014-04-02 | 宁波瑞铭机械有限公司 | 一种缝纫机连杆及其制备方法 |
CN103695732B (zh) * | 2013-11-26 | 2015-11-18 | 宁波瑞铭机械有限公司 | 一种缝纫机连杆及其制备方法 |
CN104259752B (zh) * | 2014-08-07 | 2016-08-31 | 兰宝琴 | 一种烤漆铝合金板的制造方法 |
CN104259752A (zh) * | 2014-08-07 | 2015-01-07 | 兰宝琴 | 一种烤漆铝合金板的制造方法 |
CN104264020A (zh) * | 2014-10-17 | 2015-01-07 | 苏州凯宥电子科技有限公司 | 一种高强度压铸铝合金及其制备方法 |
CN104264020B (zh) * | 2014-10-17 | 2016-10-26 | 苏州凯宥电子科技有限公司 | 一种高强度压铸铝合金及其制备方法 |
CN108728703A (zh) * | 2017-04-13 | 2018-11-02 | 韩国机械研究院 | Al-Zn-Cu合金及其制备方法 |
CN108728703B (zh) * | 2017-04-13 | 2020-09-04 | 韩国机械研究院 | Al-Zn-Cu合金及其制备方法 |
CN107686923A (zh) * | 2017-09-18 | 2018-02-13 | 太仓天润新材料科技有限公司 | 一种超合金环保电子新材料 |
CN109972003A (zh) * | 2019-04-03 | 2019-07-05 | 上海交通大学 | 适于重力铸造的高延伸率耐热铝合金及其制备方法 |
CN109972003B (zh) * | 2019-04-03 | 2020-05-22 | 上海交通大学 | 适于重力铸造的高延伸率耐热铝合金及其制备方法 |
CN112143949A (zh) * | 2019-06-27 | 2020-12-29 | 比亚迪股份有限公司 | 一种压铸铝合金及其制备方法和应用 |
CN112143949B (zh) * | 2019-06-27 | 2021-12-07 | 比亚迪股份有限公司 | 一种压铸铝合金及其制备方法和应用 |
CN113046607A (zh) * | 2021-03-16 | 2021-06-29 | 郑州大学 | 一种高硬高导热多元合金及其制备方法 |
CN113046607B (zh) * | 2021-03-16 | 2022-03-04 | 郑州大学 | 一种高硬高导热多元合金及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
KR101124235B1 (ko) | 2012-03-27 |
WO2011152617A3 (ko) | 2012-04-19 |
DE112011101836T5 (de) | 2013-03-07 |
KR20110131327A (ko) | 2011-12-07 |
JP2013529255A (ja) | 2013-07-18 |
US20130209311A1 (en) | 2013-08-15 |
WO2011152617A2 (ko) | 2011-12-08 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN103069029A (zh) | 铝合金及铝合金铸件 | |
JP5355320B2 (ja) | アルミニウム合金鋳物部材及びその製造方法 | |
CN110714148A (zh) | 一种高性能半固态压铸铝合金及其制备方法 | |
CN109811206B (zh) | 铸造铝合金 | |
CN111155000A (zh) | 一种用于压铸薄壁件的急速热处理强化高强韧铝合金材料及其制备方法和应用 | |
CN112779443B (zh) | 一种铝合金及铝合金结构件 | |
CN117568671B (zh) | 一种免热处理的压铸铝合金材料及其制备方法、汽车结构件 | |
JP2022517830A (ja) | 高圧真空ダイカスト用鋳造合金 | |
CN109022940A (zh) | 一种铝合金及其制备方法和应用 | |
JP5215710B2 (ja) | 高温でのクリープ特性に優れたマグネシウム合金およびその製造方法 | |
CN113046606B (zh) | 铝合金及其制备方法和铝合金结构件 | |
CN113846255B (zh) | 铝合金及其制备方法和铝合金结构件 | |
JP6726058B2 (ja) | Al合金鋳造物の製造方法 | |
JP4996854B2 (ja) | 高温高速成形用アルミニウム合金材及びその製造方法、並びにアルミニウム合金成形品の製造方法 | |
CN115491558A (zh) | 一种压铸镁合金及其制备方法和应用 | |
CN105838937A (zh) | 一种具有高力学性能的Al-Si-Mg-Sr-Sc-Ti铸造合金及其制备方法 | |
JP6649665B2 (ja) | マグネシウム合金製造方法、マグネシウム合金圧延材、およびマグネシウム合金成形体 | |
CN110079714B (zh) | 一种非热处理强化高强高韧压铸铝镁铜合金及其制备方法 | |
CN112126835B (zh) | 一种压铸镁合金及其制备方法和应用 | |
CN114351020B (zh) | 一种镁合金铸件及其制备方法和应用 | |
CN112921219B (zh) | 一种铝合金及其制备方法和铝合金结构件 | |
CN112553508B (zh) | 铝合金及其制备方法和铝合金结构件 | |
KR101269516B1 (ko) | 스칸듐이 없는 다이캐스팅용 고강도 알루미늄 합금 | |
KR101311915B1 (ko) | 알루미늄 합금 및 알루미늄 합금 주물 | |
CN105506322A (zh) | 一种铸造Al-Si合金性能的优化方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
C02 | Deemed withdrawal of patent application after publication (patent law 2001) | ||
WD01 | Invention patent application deemed withdrawn after publication |
Application publication date: 20130424 |