CN102977764A - 一种耐候性皮革涂饰剂 - Google Patents

一种耐候性皮革涂饰剂 Download PDF

Info

Publication number
CN102977764A
CN102977764A CN2012104733996A CN201210473399A CN102977764A CN 102977764 A CN102977764 A CN 102977764A CN 2012104733996 A CN2012104733996 A CN 2012104733996A CN 201210473399 A CN201210473399 A CN 201210473399A CN 102977764 A CN102977764 A CN 102977764A
Authority
CN
China
Prior art keywords
performed polymer
weathering resistance
hide finishes
bdo
dmpa
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104733996A
Other languages
English (en)
Inventor
苏建丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Wenchuang Technology Co Ltd
Original Assignee
Qingdao Wenchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Wenchuang Technology Co Ltd filed Critical Qingdao Wenchuang Technology Co Ltd
Priority to CN2012104733996A priority Critical patent/CN102977764A/zh
Publication of CN102977764A publication Critical patent/CN102977764A/zh
Pending legal-status Critical Current

Abstract

一种耐候性皮革涂饰剂，包含水性聚氨酯乳液，是以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG3000)、1,4-丁二醇(BDO)、二羟甲基丙酸(DMPA)为原料制备预聚体，经封端及中和反应后，加入二缩三丙二醇二丙烯酸酯(TPGDA)和水进行乳化，加入适量的引发剂，得到丙烯酸酯改性水性聚氨酯乳液。本发明采用光稳定性好的脂肪族异佛尔酮二异氰酸酯(IPDI)为原料制备聚氨酯，再以丙烯酸酯对其改性，从根本上解决易黄变问题，大大提高了皮革涂饰剂的耐候性。

Description

一种耐候性皮革涂饰剂
技术领域
本发明涉及一种耐候性皮革涂饰剂，属化工领域。
技术背景        
涂饰是皮革制造过程中的一个重环节，涂饰可增加皮革美观和耐用性能，提高皮革档次，增加花色品种和扩大使用范围。常用皮革涂饰剂有酪素涂饰剂、丙烯酸涂饰剂、硝化纤维涂饰剂和聚氨酯涂饰剂，其中水性聚氨酯涂饰剂以水为溶剂，消除了溶剂型聚氨酯生产、储运和使用过程中易燃易爆等危险，满足定全、健康及环保的要求，具有成膜性能好，遮盖力强，粘结牢固，涂层光亮，易于清洁保养，涂饰后的成革手感丰满、舒适，能大大提高成革的等级。
目前国产水性聚氨酯皮革涂饰剂多以芳香族水性聚氨酯为原料，易黄变，耐候性差，限制了水性聚氨酯在皮革涂饰剂中的应用。若采用添加少量抗氧剂和紫外光吸收剂等防老剂的方法，只能延缓产品变黄，而不能从根本上解决问题。本专利采用光稳定性好的脂肪族异佛尔酮二异氰酸酯(IPDI)为原料制备聚氨酯，从聚氨酯结构中消除了易发色的共轭基团，再以二缩三丙二醇二丙烯酸酯(TPGDA)对水性聚氨酯进行改性，得到的乳液兼具聚氨酯的高耐磨性及丙烯酸良好的耐候性和耐水性，使水性聚氨酯的性能得到明显改善，更加符合制备皮革涂饰剂的要求。
发明内容
本发明的目的是提供一种强耐候性、耐水性的皮革涂饰剂。
为实现以上目的，本发明的皮革涂饰剂，包含水性聚氨酯乳液，是以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG3000)、1,4-丁二醇(BDO)、二羟甲基丙酸(DMPA)为原料制备预聚体，经封端及中和反应后，加入二缩三丙二醇二丙烯酸酯(TPGDA)和水进行乳化，乳化时间为60min，加入适量的引发剂，得到丙烯酸酯改性水性聚氨酯乳液。
其中预聚体的配比为：IPDI与PEG3000、DMPA、BDO的摩尔比为1.4:1-1.5:1，BDO占预聚体质量的2%-3%，DMPA占预聚体质量的4%-6%。
其中二缩三丙二醇二丙烯酸酯(TPGDA) 用量为预聚体总质量的20%-30%，水的用量为预聚体总质量的1.5-2倍。
本发明的皮革涂饰剂还需加入稳定剂0.1%、流平剂0.1%，均为重量百分含量。
本发明产生的有益效果为，本专利采用脂肪族异佛尔酮二异氰酸酯(IPDI)为原料制备水性聚氨酯，再以二缩三丙二醇二丙烯酸酯(TPGDA) 对其改性，得到的丙烯酸酯改性脂肪族水性聚氨酯乳液作为皮革涂饰剂的主要成分，一方面消除了聚氨酯结构中易发色的共轭基团，从根本上解决了聚氨酯易黄变的缺陷，另一方面该乳液集合了水性聚氨酯的高耐磨性以及丙烯酸良好的耐候性和耐水性，大大提高了成革等级，扩大了皮革涂饰剂的应用范围。
实施例
实施例1：
以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG3000)、1,4-丁二醇(BDO)、二羟甲基丙酸(DMPA)为原料制备预聚体。其配比为：IPDI与PEG3000、DMPA、BDO的摩尔比为1.4:1，BDO占预聚体质量的2%，DMPA占预聚体质量的5%。然后经封端及中和反应后，加入预聚体总质量20%的二缩三丙二醇二丙烯酸酯(TPGDA)和预聚体总质量1.8倍的水进行乳化，乳化时间为60min，加入适量的引发剂，得到丙烯酸酯与水性聚氨酯共聚改性的乳液。
在乳液中加入稳定剂0.1%、流平剂0.1%（均为重量百分含量），搅拌均匀后，静置，过滤后得到耐候性皮革涂饰剂。
实施例2：
以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG3000)、1,4-丁二醇(BDO)、二羟甲基丙酸(DMPA)为原料制备。其配比为：IPDI与PEG3000、DMPA、BDO的摩尔比为1.5:1，BDO占预聚体质量的2%，DMPA占预聚体质量的5%。然后经封端及中和反应后，加入预聚体总质量20%的二缩三丙二醇二丙烯酸酯(TPGDA)和预聚体总质量2倍的水进行乳化，乳化时间为60min，加入适量的引发剂，得到丙烯酸酯与水性聚氨酯共聚改性的乳液。
在乳液中加入稳定剂0.1%、流平剂0.1%（均为重量百分含量），搅拌均匀后，静置，过滤后得到耐候性皮革涂饰剂。

Claims (6)

1.一种耐候性皮革涂饰剂，包含水性聚氨酯乳液，其特征在于：以异佛尔酮二异氰酸酯(IPDI)、聚乙二醇(PEG3000)、1,4-丁二醇(BDO)、二羟甲基丙酸(DMPA)为原料制备预聚体，经封端及中和反应后，加入二缩三丙二醇二丙烯酸酯(TPGDA)和水进行乳化，加入适量的引发剂，得到丙烯酸酯改性水性聚氨酯乳液。
2.如权利要求1所述的一种耐候性皮革涂饰剂，其特征在于：所述的预聚体其配比为：IPDI与PEG3000、DMPA、BDO的摩尔比为1.4:1-1.5:1，BDO占预聚体质量的2%-3%，DMPA占预聚体质量的4%-6%。
3.如权利要求1所述的一种耐候性皮革涂饰剂，其特征在于：所述的二缩三丙二醇二丙烯酸酯(TPGDA) 的用量为预聚体总质量的20%-30%。
4.如权利要求1所述的一种耐候性皮革涂饰剂，其特征在于：所述的水的用量为预聚体总质量的1.5-2倍。
5.如权利要求1所述的一种耐候性皮革涂饰剂，其特征在于：所述的乳化时间为60min。
6.如权利要求1所述的一种耐候性皮革涂饰剂，其特征在于：还需加入稳定剂0.1%、流平剂0.1%，均为重量百分含量。
CN2012104733996A 2012-11-21 2012-11-21 一种耐候性皮革涂饰剂 Pending CN102977764A (zh)