CN101157841A - 服装人造革用环境友好型水性聚氨酯热溶胶的制备方法 - Google Patents

服装人造革用环境友好型水性聚氨酯热溶胶的制备方法 Download PDF

Info

Publication number
CN101157841A
CN101157841A CNA200710133168XA CN200710133168A CN101157841A CN 101157841 A CN101157841 A CN 101157841A CN A200710133168X A CNA200710133168X A CN A200710133168XA CN 200710133168 A CN200710133168 A CN 200710133168A CN 101157841 A CN101157841 A CN 101157841A
Authority
CN
China
Prior art keywords
artificial leather
environment
aqueous polyurethane
friendly type
polyurethane hot
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200710133168XA
Other languages
English (en)
Inventor
华明扬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA200710133168XA priority Critical patent/CN101157841A/zh
Publication of CN101157841A publication Critical patent/CN101157841A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种服装人造革用环境友好型水性聚氨酯热溶胶的制备方法，该法生产的热溶胶主要用于纺织织物与服装类合成人造革材料的粘合。是用二异氰酸酯和二元醇类化合物生成端基为－NCO的预聚体，然后用二羟甲基丙酸和1、4丁二醇扩链反应，最后用胺调节pH值至中性后，加入去离子水搅拌，即得到服装人造革用环境友好型水性聚氨酯热溶胶。本发明方法生产的水性聚氨酯热溶胶粘合牢度大，强度高，粘结织物的手感柔软，有优异的耐水性能和防水性能。

Description

服装人造革用环境友好型水性聚氨酯热溶胶的制备方法
技术领域
本发明涉及一种服装人造革用环境友好型水性聚氨酯热溶胶的制备方法，该法生产的热溶胶主要用于纺织织物与服装类合成人造革材料的粘合。属纺织助剂技术领域。
技术背景
在本发明作出以前，目前用于箱包类人造革的热溶涂层胶是溶剂型PU胶或丙烯酸酯类黏合剂。它主要存在以下不足：如制作成本比较高，且含有大量的如甲苯、二甲基甲酰胺等毒性大的溶剂，在使用时其排放的大量溶剂严重污染环境。随着世界各国对环保要求的越来越关注，环保法规的日益严格，高污染的溶剂类产品逐渐被水性清洁产品所替代，丙烯酸酯类黏合剂强度不高，软度不够，制备出的服装人造革偏硬。而一般传统方法制备的水性聚氨酯粘合牢度低，很少有商品化的水性聚氨酯的热溶胶。
发明内容
本发明的目的在于克服上述不足，提供一种粘合牢度大，强度高，粘结织物的手感柔软，有优异的耐水性能和防水性能的服装人造革用环境友好型水性聚氨酯热溶胶。
本发明的目的是这样实现的：一种服装人造革用环境友好型水性聚氨酯热溶胶的制备方法，其特征在于：用二异氰酸酯和二元醇类化合物生成端基为-NCO的预聚体，然后用亲水单体二羟甲基丙酸和1、4丁二醇扩链反应，最后用胺调节pH值至中性后，加入去离子水搅拌，即得到服装人造革用环境友好型水性聚氨酯热溶胶，具体方法为：在反应容器内加入二元醇类化合物和二异氰酸酯，在85℃±5℃下反应1.5小时±0.5小时，降温至70-75℃，加入二羟甲基丙酸(DMPA)和1、4丁二醇，保温搅拌30-40min，滴加占二异氰酸酯重量0.08-0.12％的二丁基二月桂酸锡，加入占热溶胶成品总重量0.8-1.2％的乙酸乙酯或丙酮降低体系粘度，保温4.5小时±0.5小时，降至室温，加入三乙胺中和，加去离子水，搅拌，脱去乙酸乙酯或丙酮，即得到服装人造革用环境友好型水性聚氨酯热溶胶。
各物料是按照以下配比进行反应：
所述-NCO∶-OH＝1.5-3∶1(摩尔比)，其中-NCO表示异氰酸酯基，-OH表示大分子二元醇类化合物的羟基。
所述亲水单体二羟甲基丙酸与二元醇类化合物的摩尔比为0.5-1∶1。
所述1、4丁二醇与二元醇类化合物的摩尔比为1-1.8∶1。
所述二异氰酸酯可以为IPDI、HDI、TDI或改性二亚胺MDI。
所述二元醇类化合物可以为分子量为1000-2000的聚丙二醇或聚醚220。
本发明的特点在于该热溶胶的粘合牢度大，强度高，粘结织物的手感柔软，有优异的耐水性能和防水性能。本发明的另一特点是所述热溶胶是一种环保型单组分水性聚氨酯，是以水为溶剂，可以根本上消除涂层中的有害物质。在辊涂和刮涂固化过程无有害溶剂挥发，完全符合纺织环保技术要求。制得的热溶胶的涂膜不黄变，外观半透明，固含量30-40％，数均分子量为30000-50000(waters公司的凝胶色谱仪检测)，粘度为300-1000cps(埃米拉粘度计检测)。
具体实施方式
实施例1：
在烧瓶内加入80克分子量为1000的聚丙二醇，36克MDI，在85℃下反应1.5小时，降温至70℃，加入6克DMPA，8.6克1、4丁二醇，保温搅拌30min，滴加5滴二丁基二月桂酸锡，加入70克丙酮降低体系粘度，保温4.5小时，降至室温，加入4克三乙胺中和，加去510克离子水，搅拌，脱去丙酮，即得到本发明服装人造革用环境友好型水性聚氨酯热溶胶。
实施例2：在烧瓶内加入117克聚醚220，40克IPDI、HDI或TDI，在85℃下反应1.5小时，降温至75℃，加入6克DMPA，7.5克1、4丁二醇，保温搅拌30min，滴加5滴二丁基二月桂酸锡，加入80克乙酸乙酯降低体系粘度，保温4.5小时，降至室温，加入4克三乙胺中和，加500克去离子水，搅拌，脱去乙酸乙酯，即得到本发明服装人造革用环境友好型水性聚氨酯热溶胶。
实施例3：
用以上服装人造革用环境友好型水性聚氨酯热溶胶50克，刮涂在PET基材布上，在压延机上与PVC粘合，得到的复合材料粘合强度高，测试的剥离强度可达10N/15mm，且复合材料手感柔软。

Claims (3)

1.一种服装人造革用环境友好型水性聚氨酯热溶胶的制备方法，其特征在于：用二异氰酸酯和二元醇类化合物生成端基为-NCO的预聚体，然后用亲水单体二羟甲基丙酸和1、4丁二醇扩链反应，最后用胺调节pH值至中性后，加入去离子水搅拌，即得到服装人造革用环境友好型水性聚氨酯热溶胶，具体方法为：在反应容器内加入二元醇类化合物和二异氰酸酯，在85℃±5℃下反应1.5小时±0.5小时，降温至70-75℃，加入二羟甲基丙酸和1、4丁二醇，保温搅拌30-40min，滴加占二异氰酸酯重量0.08-0.12％的二丁基二月桂酸锡，加入占热溶胶成品总重量0.8-1.2％的乙酸乙酯或丙酮，保温4.5小时±0.5小时，降至室温，加入三乙胺中和，加去离子水，搅拌，脱去乙酸乙酯或丙酮，即得到服装人造革用环境友好型水性聚氨酯热溶胶，各物料是按照以下配比进行反应：
所述-NCO∶-OH＝1.5-3∶1摩尔比，其中-NCO表示异氰酸酯基，-OH表示大分子二元醇类化合物的羟基，
所述亲水单体二羟甲基丙酸与二元醇类化合物的摩尔比为0.5-1∶1，
所述1、4丁二醇与二元醇类化合物的摩尔比为1-1.8∶1。
2.根据权利要求1所述的一种服装人造革用环境友好型水性聚氨酯热溶胶的制备方法，其特征在于：所述二异氰酸酯为IPDI、HDI、TDI或改性二亚胺MDI。
3.根据权利要求1所述的一种服装人造革用环境友好型水性聚氨酯热熔胶的制备方法，其特征在于：所述二元醇类化合物为分子量为1000-2000的聚丙二醇或聚醚220。
CNA200710133168XA 2007-09-20 2007-09-20 服装人造革用环境友好型水性聚氨酯热溶胶的制备方法 Pending CN101157841A (zh)