CN102864546A - 一种同向异捻双层二元复合纱及其制作方法及其面料 - Google Patents
一种同向异捻双层二元复合纱及其制作方法及其面料 Download PDFInfo
- Publication number
- CN102864546A CN102864546A CN2012103772298A CN201210377229A CN102864546A CN 102864546 A CN102864546 A CN 102864546A CN 2012103772298 A CN2012103772298 A CN 2012103772298A CN 201210377229 A CN201210377229 A CN 201210377229A CN 102864546 A CN102864546 A CN 102864546A
- Authority
- CN
- China
- Prior art keywords
- yarn
- twist
- binary composite
- composite yarn
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种同向异捻双层二元复合纱及其面料,由内外两层纤维加捻而成的复合纱,分别将内层纤维和外层纤维加捻,通过内层纤维的捻系数与外层纤维的捻系数的改变制得纱线并形成独特风格的面料。本发明纺制的同向异捻双层二元复合纱整体捻度较少,柔软度好。同时因为复合纱中内层纤维和外层纤维均有捻度,所以保证了该复合纱强力,使该复合纱具有不容易断,耐磨性好等特点,并且制得的面料具有丝绸的风格,表面光泽度好,布面柔软度好,可替代丝绸。
Description
技术领域
本发明涉及一种复合纱线及面料,具体涉及一种同向异捻双层二元复合纱。
背景技术
当纱线的号数一定时,纱线的强度与纱线的捻度由小到大呈正态分布,捻度小,纱线强度也小,柔软性好;捻度大,纱线强度也大,柔软性差。当捻度大到一定的值时,纱线强度达到最大,若捻度再增加,会导致纱线强度减小,易断。所以如何控制纱线的捻度对纱线的性能具有重要的作用。
单纤维的纱线很难满足既柔软又不易断的功能,所以出现了很多复合纱线,现有的复合纱线有很多种,对于纱线的选料上还有很多限制,否则会导致复合出来的纱线不够光洁,也不能达到柔软性和强度综合最佳的效果。
发明内容
发明目的:本发明的目的是为了解决现有技术的不足,提供一种柔软性好且强力高的同向异捻双层二元复合纱。
一种同向异捻双层二元复合纱,其创新点在于:将作为二元复合纱线的主体成分的皮纱与芯纱进行复合制成二元复合纱成品。
作为优化地,所述二元复合纱线为S捻向,捻系数为260——420,芯纱和皮纱的捻度比为1.2——1.4:1。
作为优化地,所述二元复合纱为高支数纱线复合而成。
作为优化地,所述二元复合纱中的二元纱线可一种或多种混合纱线。
本发明的另一个目的是提供该异捻双层二元复合纱的加工方法。
技术方案:一种同向异捻双层二元复合纱,步骤如下:
a、所述芯纱:为依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、捻线工艺得到的纱线,捻系数为260-420,捻向为S
b、所述皮纱:依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、捻线工艺得到的纱线,捻系数为260-420,捻向为S
c、将上述具有相同捻向和不同捻系数的芯纱和皮纱按芯纱与皮纱捻系数的比值为1.2-1.4:1进行加捻复合形成二元复合纱制品,捻系数为300-330,捻向为S。
作为优化地,芯纱的捻度是皮纱的1.2-1.4倍。
作为优化地,所述芯纱为人造纤维或合成纤维或聚酯纤维中的一种或者多种短纤纯纺纱或混合纱,其捻向为S捻向,捻系数为330。
作为优化地,所述皮纱为人造短纤或者棉纤维中的一种或者多种纯纺或混合短纤纱,其捻向为S捻,捻系数为300。
作为优化地,所述二元复合纱的捻系数为300,捻向为S捻。
当芯纱与皮纱捻方向相同,捻系数不同的时候,复合后,捻系数小的芯纱可以将捻系数大的皮纱的捻度降下来。
本发明还提供了一种采用本反向异捻二元复合纱制作的面料,其创新点在于:所述面料可作为丝绸面料替代产品。
有益效果:本发明纺制的同向异捻双层二元复合纱因为皮纱捻度较小,柔软度好,但是芯纱做为单纱强度大,不容易断;在芯纱外面包覆捻度较小的皮纱进行复合,在梳棉、并条复合的过程中因为皮纱和复合纱的捻向相同,使得纱线芯纱捻度加大,皮纱捻度可以降低,实现柔软,同时又皮纱对芯纱还具有保护作用,所以使得该复合纱的整体捻度较少,但强力高 柔软度好。同时因为复合纱中内层纤维和外层纤维均有捻度,所以保证了该复合纱强力,使该复合纱不容易断,耐磨性好。用该纱线制作的面料,能有效替代丝绸面料,且部分性能指标高于丝绸在产。
具体实施方式
下面结合具体实施例对本发明作进一步说明:
实施例1
本发明相对于传统双层二元复合纱,相同支数的情况下,具有单纱强力更高,总体捻系数较小,手感更加柔软,毛羽少,CV值小,成纱质量高的特点,具有很高的实用价值和很高的经济性。
设备改造:首先在普通细纱机上加装芯丝喂入机构和预牵伸机构。然后改装粗纱架,以增加容纳增加的芯纱吊锭。其次,对普通的细纱机上进行长丝加弱捻机构的改造。
用料:70%的棉和30%的粘胶)混纺粗纱作包覆纱,依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、加Z捻作皮纱,捻系数为330;用6.4tex的涤纶丝依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱,加弱S捻作芯纱,芯纱和皮纱按芯纱与皮纱捻度的比值为1.2-1.4:1,将芯纱和皮纱分别在上述改装过的FA 506S型细纱机上生产进行了110支的异捻(S捻)双层二元复合包芯纱,捻系数为380。芯纱细纱机采用的纺纱工艺是:预牵伸倍数为1.08倍,前罗拉转速为180 r/min,锭子转速为13000r/min。二元复合纱的工艺是:后区牵伸倍数为1.456,前区罗拉隔距19 mm,后区罗拉隔距35mm前、中、后罗拉加压分别为22、14、捻系数为380,前罗拉转速为182 r/min、锭子转速为13800 r/min,芯丝预牵伸倍数为1.02,芯纱的喂入粗纱定量为3.8 g/10 m。取里外两层不同的捻系数。异捻双层二元复合纱的性能如下:纱密度:110支,断裂强度:23.6cN/tex,断裂伸长裂28.4%,条干不匀率6.2%,重量不匀率0.78%,包覆率99.3%,毛羽897(+2mm/根/100m)。
同向异捻双层二元复合纱是分别在加装了包芯纱装置和预牵伸加弱捻的细纱机上纺制而成的,外包纤维密集度比较均匀,外表光滑 有光泽。纤维的抱合力高 ,成纱断裂强度增加,但总体成纱的捻系数较小 伸长度增大,其条干均匀度也优于传统包芯纱。
该实施例中皮纱和芯纱的捻向相同,捻系数不同,皮纱和芯纱复合时减小了皮纱的捻度,纱线手感柔软,毛羽少,耐磨性能好,改善了传统包芯纱的包覆效果。
本实施例中主要是采用了涤纶等长纤维,在使用长纤维时,一定要对该长纤维进行加捻处理,要不不能达到效果。
实施例2
用料:芯纱和皮纱采用腈纶短纤和精梳棉。
皮纱制作工艺:依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、加Z捻作皮纱,捻系数为360;芯纱细纱机采用的纺纱工艺是:预牵伸倍数为1.13倍,前罗拉转速为203 r/min,锭定转速为14100r/min。
芯纱制作工艺:依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱,加弱S捻作芯纱,捻系数200;芯纱细纱机采用的纺纱工艺是:预牵伸倍数为1.08倍,前罗拉转速为188 r/min,锭定转速为13100转。
芯纱和皮纱进行复合的工艺:芯纱与皮纱捻度的比值为1.2-1.4:1,将芯纱和皮纱分别在上述改装过的FA 506S型细纱机上生产进行了100支规格的异捻(S捻)双层二元复合包芯纱,捻系数为300。
二元复合纱的工艺是:后区牵伸倍数为1.62,前区罗拉隔距19 mm,后区罗拉隔距35 mm前、中、后罗拉加压分别为21、11、捻系数为330,前罗拉转速为203 r/min、锭子转速为14100 r/min,芯丝预牵伸倍数为1.1,芯纱的喂入粗纱定量为3.68 g/10 m。取里外两层不同的捻系数。
异捻双层二元复合纱的性能如下:纱密度:100支,断裂强度:20.3cN/tex,断裂伸长率27.4%,条干不匀率6.8%,重量不匀率0.78%,包覆率99.7%,毛羽870(+2mm/根/100m)。
特点:本实施例采用的是短纤制作,与实施例1相比,在制作过程中增加芯纱的生产捻的步骤。一般建议使用长丝原料。
实施例3
用料:用实施例1制成的110支同向异捻双层二元复合纱
面料工艺:
1.该混纺棉织物经密度为173根/英寸,纬密度为124根/英寸,幅宽为160CM;该混纺棉织物的组织结构为1/1平纹;
2.该混纺棉织物经纬纱均采用110支同向异捻双层二元复合纱;
3.上述纱线经过整经 浆纱 穿经 织造制成的混纺棉织物。
面料织造工艺:
1. 设备:丰田JAT710-190型;
2. 工艺参数:上机经纱张力采1.1系数,上机张力120公斤,开口量 28-30度,平稳量6格,平稳时间290度,车速680转/分钟,开口时间280-300度,主喷气压180kpa,辅喷气压240kpa,入纬时间90度,到纬时间240度。
本发明利用110支同向异捻双层二元复合纱 混纺棉纱线织成的纺织面料,外观光泽幽雅柔和,具有珍珠的光泽;手感柔软光滑,富有弹性,但不易起皱。具有天然纤维良好的服用性能,和丝绸织物滑爽 飘逸 光泽鲜丽的外观特性。是理想的丝绸面料的替代产品。具有很高的经济效益和社会效益。
Claims (9)
1.一种同向异捻双层二元复合纱,其特征在于:将作为二元复合纱线的主体成分的皮纱与芯纱进行复合制成二元复合纱成品。
2.根据权利要求1所述的一种同向异捻双层二元复合纱,其特征在于:所述二元复合纱线为S捻向,纱线的捻系数为260——420,芯纱和皮纱的捻系数比为1.2——1.4:1。
3.根据权利要求1所述的一种同向异捻双层二元复合纱,其特征在于:所述二元复合纱为高支数纱线复合而成。
4.根据权利要求1所述的一种同向异捻双层二元复合纱,其特征在于:所述二元复合纱中的二元纱线可一种或多种混合纱线。
5.一种如权利要求1所述的一种同向异捻双层二元复合纱的生产方法,其特征在于:步骤如下:
a、所述芯纱:为依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、捻线工艺得到的纱,捻系数为260-420,捻向为S;
b、所述皮纱:依次经清棉、梳棉、并条、精梳、并条、粗纱、细纱、络纱、并纱、捻线工艺得到的纱,捻系数为260-420,捻向为S;
c、将上述具有各自捻向和捻度的芯纱和皮纱,按芯纱与皮纱捻度的比值为1.2-1.4:1进行加捻复合形成二元复合纱制品,捻系数为300-330,捻向为S。
6.根据权利要求5所述同向异捻双层二元复合纱的生产方法,其特征在于:所述芯纱为天然纤维或合成纤维的一种或者多种纱,捻系数为370。
7.根据权利要求5所述的同向异捻双层二元复合纱的生产方法,其特征在于:所述皮纱捻系数为300。
8.根据权利要求5所述的同向异捻双层二元复合纱的生产方法,其特征在于:所述二元复合纱的捻系数为300。
9.根据权利要求1制得的面料,该面料可作为丝绸面料替代产品。