CN102731864B - 一种丁腈再生橡胶密封圈材料 - Google Patents

一种丁腈再生橡胶密封圈材料 Download PDF

Info

Publication number
CN102731864B
CN102731864B CN 201210173212 CN201210173212A CN102731864B CN 102731864 B CN102731864 B CN 102731864B CN 201210173212 CN201210173212 CN 201210173212 CN 201210173212 A CN201210173212 A CN 201210173212A CN 102731864 B CN102731864 B CN 102731864B
Authority
CN
China
Prior art keywords
sealing ring
butyronitrile
ring material
rubber sealing
nitrile rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201210173212
Other languages
English (en)
Other versions
CN102731864A (zh
Inventor
邵仁杰
王建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CGP Wuhu Sealing Co Ltd
Original Assignee
CGP Wuhu Sealing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CGP Wuhu Sealing Co Ltd filed Critical CGP Wuhu Sealing Co Ltd
Priority to CN 201210173212 priority Critical patent/CN102731864B/zh
Publication of CN102731864A publication Critical patent/CN102731864A/zh
Application granted granted Critical
Publication of CN102731864B publication Critical patent/CN102731864B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种丁腈再生橡胶密封圈材料，其是由丁腈橡胶3345 ，丁腈再生橡胶，防老剂SP，防老剂MB，硬脂酸，硫磺粉，棕榈蜡，氧化锌，加工助剂WB16，碳黑N550，碳黑N330，五氯硬脂酸甲酯，促进剂TMTD，促进剂TETD ，促进剂DM,纳米碳酸钙，改性丙烯酸酯，烷基间苯二酚甲醛树脂，顺丁烯二酸酐，增塑剂等制成。本发明利用再生丁腈橡胶作为原料，优化配方原料，制备出性能优良、耐高温性能好，硬度高的丁腈再生橡胶密封圈材料，节约成本。

Description

一种丁腈再生橡胶密封圈材料
技术领域
本发明涉及密封圈材料领域，确切地说是一种丁腈再生橡胶密封圈材料。
背景技术
丁腈橡胶又称丁二烯一丙烯腈橡胶，简称NBR，平均分子量70万左右。灰白色至浅黄色块状或粉状固体，相对密度0.95～1.0。丙烯腈含量为26%的丁腈橡胶玻璃化温度Tg=一52℃，脆化温度Tb=一47℃，而丙烯腈含量为40%的丁腈橡胶玻璃化温度Tg=一22℃。溶解度参数δ=8.9～9.9，溶于醋酸乙酯、醋酸丁酯、氯苯、甲乙酮等。丁腈橡胶具有优良的耐油性,其耐油性仅次于聚硫橡胶和氟橡胶，并且具有的耐磨性和气密性。丁晴橡胶的缺点是不耐臭氧及芳香族、卤代烃、酮及酯类溶剂，不宜做绝缘材料。耐热性优于丁苯橡胶、氯丁橡胶，可在120℃长期工作。气密性仅次于丁基橡胶。丁腈橡胶的性能受丙烯腈含量影响，随着丙烯腈含量增加拉伸强度、耐热性、耐油性、气密性、硬度提高，但弹性、耐寒性降低。丁腈橡胶耐臭氧性能和电绝缘性能不佳。
发明内容
本发明的目的提供一种变废为宝，利用再生丁腈橡胶生产的的密封圈材料。
上述目的通过以下方案实现：
一种丁腈再生橡胶密封圈材料，其特征在于：
其是由下述重量份的原料制成的：
丁腈橡胶3345  48-52，丁腈再生橡胶 20-25，防老剂SP 1.5-2，防老剂BLE 0.8-1，硬脂酸0.8-1，硫磺粉0.5-0.8，棕榈蜡1-1.2，氧化锌5-6，加工助剂WB16   1-1.2，碳黑N550  60-65，碳黑N330  30-35，五氯硬脂酸甲酯35-40，促进剂TMTD  1-1.5，促进剂TETD  1-1.5，促进剂DM 1.5-2, 纳米碳酸钙 2-4，烷基间苯二酚甲醛树脂2-3，顺丁烯二酸酐2-3，增塑剂 2-4。
所述的一种丁腈再生橡胶密封圈材料，其特征在于：所述的增塑剂采用柠檬酸三丁酯，或采用以下重量份的原料制备改性而得：
柠檬酸三丁酯  10-12
正丁醇    3-4
聚乙二醇  5-8
氯化石蜡  20-25
纳米二氧化硅  0.2-0.5
纳米氧化钡  0.2-0.5
丙三醇三甘油酸酯   18-23；其制备方法为将上述组分加温、乳化，包装即得。
所述的一种丁腈再生橡胶密封圈材料，其特征在于：其采用混炼工艺制备而得。
所述的一种丁腈再生橡胶密封圈材料，其特征在于：制备工艺为：按重量份取丁腈橡胶、丁腈再生橡胶充分混炼后，再按照重量份加入其他原料充分混炼取得混炼胶经过硫化后，再加工成型即得产品。
本发明的有益效果为：
本发明利用再生丁腈橡胶作为原料，优化配方原料，制备出性能优良、耐高温性能好，硬度高的丁腈再生橡胶密封圈材料，节约成本。
具体实施方式
实施例1：
一种丁腈再生橡胶密封圈材料，
其是由下述重量份的原料制成的：
丁腈橡胶3345  50，丁腈再生橡胶 20，防老剂SP   2，防老剂BLE 1，硬脂酸 1，硫磺粉 0.8，棕榈蜡 1.2，氧化锌 6，加工助剂WB16    1.2，碳黑N550  60 ，碳黑N330   35，五氯硬脂酸甲酯 40，促进剂TMTD  1 ，促进剂TETD  1 ，促进剂DM 2, 纳米碳酸钙  4，烷基间苯二酚甲醛树脂 3，顺丁烯二酸酐 3，增塑剂  4。
所述的增塑剂采用以下重量份的原料制备改性而得：
柠檬酸三丁酯  10
正丁醇    3
聚乙二醇  5
氯化石蜡  20
纳米二氧化硅  0.2
纳米氧化钡  0.2
丙三醇三甘油酸酯   18；其制备方法为将上述组分加温、乳化，包装即得。
制备工艺为：按重量份取丁腈橡胶、丁腈再生橡胶充分混炼后，再按照重量份加入其他原料充分混炼取得混炼胶经过硫化后，再加工成型即得产品。
本实施例的绍尔硬度A平均值为84，硬度高，扯断伸长率≥270，弹性好。压缩永久变形低、平均值为8.47%。
耐高温测试：120°C*168h，外观无变形、收缩、裂纹、发粘及析出现象。
实施例2：
一种丁腈再生橡胶密封圈材料，其是由下述重量份的原料制成的：
丁腈橡胶3345  50，丁腈再生橡胶 20，防老剂SP   2，防老剂BLE 1，硬脂酸 1，硫磺粉 0.8，棕榈蜡 1.2，氧化锌 6，加工助剂WB16    1.2，碳黑N550  60 ，碳黑N330   35，五氯硬脂酸甲酯 40，促进剂TMTD  1 ，促进剂TETD  1 ，促进剂DM 2, 纳米碳酸钙  4，烷基间苯二酚甲醛树脂 3，顺丁烯二酸酐 3，增塑剂  4。
所述的增塑剂为柠檬酸三丁酯；其制备方法为将上述组分加温、乳化，包装即得。
制备工艺为：按重量份取丁腈橡胶、丁腈再生橡胶充分混炼后，再按照重量份加入其他原料充分混炼取得混炼胶经过硫化后，再加工成型即得产品。
本实施例的绍尔硬度A平均值为80，硬度高，扯断伸长率≥270，弹性好。压缩永久变形低、平均值为7.98%。
耐高温测试：120°C*168h，外观无变形、收缩、裂纹、发粘及析出现象。

Claims (4)

1.一种丁腈再生橡胶密封圈材料，其特征在于：
其是由下述重量份的原料制成的：
丁腈橡胶3345  48-52，丁腈再生橡胶 20-25，防老剂SP 1.5-2，防老剂BLE 0.8-1，硬脂酸0.8-1，硫磺粉0.5-0.8，棕榈蜡1-1.2，氧化锌5-6，加工助剂WB16   1-1.2，碳黑N550  60-65，碳黑N330  30-35，五氯硬脂酸甲酯35-40，促进剂TMTD  1-1.5，促进剂TETD  1-1.5，促进剂DM 1.5-2, 纳米碳酸钙 2-4，烷基间苯二酚甲醛树脂2-3，顺丁烯二酸酐2-3，增塑剂 2-4。
2.根据权利要求1所述的一种丁腈再生橡胶密封圈材料，其特征在于：所述的增塑剂采用柠檬酸三丁酯，或采用以下重量份的原料制备改性而得：
柠檬酸三丁酯  10-12
正丁醇    3-4
聚乙二醇  5-8
氯化石蜡  20-25
纳米二氧化硅  0.2-0.5
纳米氧化钡  0.2-0.5
丙三醇三甘油酸酯   18-23；其制备方法为将上述组分加温、乳化，包装即得。
3.根据权利要求1所述的一种丁腈再生橡胶密封圈材料，其特征在于：其采用混炼工艺制备而得。
4.根据权利要求1所述的一种丁腈再生橡胶密封圈材料，其特征在于：制备工艺为：按重量份取丁腈橡胶、丁腈再生橡胶充分混炼后，再按照重量份加入其他原料充分混炼取得混炼胶经过硫化后，再加工成型即得产品。
CN 201210173212 2012-05-30 2012-05-30 一种丁腈再生橡胶密封圈材料 Expired - Fee Related CN102731864B (zh)