CN102719117A - 一种用于pvc型材的改性硅酸铝的制备方法 - Google Patents

一种用于pvc型材的改性硅酸铝的制备方法 Download PDF

Info

Publication number
CN102719117A
CN102719117A CN2011104629555A CN201110462955A CN102719117A CN 102719117 A CN102719117 A CN 102719117A CN 2011104629555 A CN2011104629555 A CN 2011104629555A CN 201110462955 A CN201110462955 A CN 201110462955A CN 102719117 A CN102719117 A CN 102719117A
Authority
CN
China
Prior art keywords
aluminium silicate
aluminum silicate
pvc
preparation
coupling agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104629555A
Other languages
English (en)
Other versions
CN102719117B (zh
Inventor
赵向军
周永东
孙殿举
胡海波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia Huasheng Kaolin Co Ltd
Original Assignee
Inner Mongolia Huasheng Kaolin Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia Huasheng Kaolin Co Ltd filed Critical Inner Mongolia Huasheng Kaolin Co Ltd
Priority to CN2011104629555A priority Critical patent/CN102719117B/zh
Publication of CN102719117A publication Critical patent/CN102719117A/zh
Application granted granted Critical
Publication of CN102719117B publication Critical patent/CN102719117B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于PVC型材的改性硅酸铝的制备方法，主要工艺过程是先将硅烷偶联剂A151、硫酸、盐酸、乙酸以上各组份按比例依次加入专用反应器中，室温下搅拌混合制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热混合搅拌后制备成改性硅酸铝。本改性硅酸铝用于PVC型材中，可使PVC型材产品的成本在原基础上降低4％～6％，耐老化性能提高1.5倍。

Description

一种用于PVC型材的改性硅酸铝的制备方法
技术领域
本发明涉及一种用于PVC型材的改性硅酸铝的制备方法；特别指用于PVC型材生产过程中，做为PVC型材填料使用的改性硅酸铝的制备方法。
背景技术
目前国内外用于PVC型材的硅酸铝无机改性材料，多数是以水或酒精稀释后的硅烷偶联剂做为改性剂，改性温度一般控制在80℃以上，这一方法虽然在原基础上降低了PVC型材产品的成本，并提高了PVC型材的耐老化性，但进一步改进提高的余地仍然很大。
发明内容
本发明要解决的技术问题是提供一种用于PVC型材的改性硅酸铝的制备方法，这种改性硅酸铝由6000目硅酸铝粉、铝酸酯偶联剂DL-481、硅烷偶联剂A151、硫酸、盐酸、乙酸，经加热搅拌混合制备而成。
本发明要解决的技术问题由如下方案来实现：一种用于PVC型材的改性硅酸铝的制备方法，其特征是：组成改性硅酸铝的各种组份按重量百分比为：6000目硅酸铝粉93％～95％，铝酸酯偶联剂DL-4811％～2％，硅烷偶联剂A151 1％～2％，硫酸1％～2％，盐酸0.5％～1％、乙酸0.5％～1％，制备过程如下：按比例定量称取硅烷偶联剂A151、硫酸、盐酸、乙酸于专用反应器中，室温下搅拌混合40分钟～60分钟配制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热至60℃～70℃，搅拌混合40分钟～60分钟，完成后降温至室温，通过打散机打散后包装即为用于PVC型材的改性硅酸铝。
本发明的优点是：以酸为稀释剂的硅烷偶联剂A151和铝酸酯偶联剂DL-481的复合使用，可使PVC型材产品的成本在原基础上降低4％～6％，耐老化性能提高1.5倍。
附图说明
图1是用于PVC型材的改性硅酸铝制备工艺流程示意图
具体实施方式
实施例1：以制备100kg用于PVC型材的改性硅酸铝为例，称取6000目硅酸铝粉95kg，铝酸酯偶联剂DL-481 2kg，硅烷偶联剂A151 1kg，硫酸1kg，盐酸0.5kg，乙酸0.5kg，制备过程如下：先按比例定量称取硅烷偶联剂A151、硫酸、盐酸、乙酸于专用反应器中，室温下搅拌混合40分钟配制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热至60℃，搅拌混合40分钟，完成后降温至室温，通过打散机打散后包装即为用于PVC型材的改性硅酸铝。
实施例2：以制备100kg用于PVC型材的改性硅酸铝为例，称取6000目硅酸铝粉94kg，铝酸酯偶联剂DL-481 1.5kg，硅烷偶联剂A151 1.5kg，硫酸1.5kg，盐酸0.75kg，乙酸0.75kg，制备过程如下：先按比例定量称取硅烷偶联剂A151、硫酸、盐酸、乙酸于专用反应器中，室温下搅拌混合50分钟配制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热至65℃，高速混合50分钟，完成后降温至室温，通过打散机打散后包装即为用于PVC型材的改性硅酸铝。
实施例3：以制备100kg用于PVC型材的改性硅酸铝为例，称取6000目硅酸铝粉93kg，铝酸酯偶联剂DL-481 1kg，硅烷偶联剂A151 2kg，硫酸2kg，盐酸1kg，乙酸1kg，制备过程如下：先按比例定量称取硅烷偶联剂A151、硫酸、盐酸、乙酸于专用反应器中，室温下搅拌混合60分钟配制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热至70℃，高速混合60分钟，完成后降温至室温，通过打散机打散后包装即为用于PVC型材的改性硅酸铝。

Claims (1)

1.一种用于PVC型材的改性硅酸铝的制备方法，其特征是：用于PVC型材的改性硅酸铝的各种组份按重量百分比为：6000目硅酸铝粉93％～95％，铝酸酯偶联剂DL-481 1％～2％，硅烷偶联剂A151 1％～2％，硫酸1％～2％，盐酸0.5％～1％、乙酸0.5％～1％，先将硅烷偶联剂A151、硫酸、盐酸、乙酸依次加入专用反应器中，室温下搅拌混合40分钟～60分钟配制成混合液，再将此混合液与按比例定量称取的铝酸酯偶联剂DL-481，6000目硅酸铝粉依次加入高速混合机中，加热至60℃～70℃，搅拌混合40分钟～60分钟，完成后降温至室温，通过打散机打散后包装即为用于PVC型材的改性硅酸铝。
CN2011104629555A 2011-12-14 2011-12-14 一种用于pvc型材的改性硅酸铝的制备方法 Expired - Fee Related CN102719117B (zh)