CN102701792A - 一种制备陶瓷用的黑釉 - Google Patents

一种制备陶瓷用的黑釉 Download PDF

Info

Publication number
CN102701792A
CN102701792A CN2012102014122A CN201210201412A CN102701792A CN 102701792 A CN102701792 A CN 102701792A CN 2012102014122 A CN2012102014122 A CN 2012102014122A CN 201210201412 A CN201210201412 A CN 201210201412A CN 102701792 A CN102701792 A CN 102701792A
Authority
CN
China
Prior art keywords
parts
black glaze
glaze
black
silicate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102014122A
Other languages
English (en)
Other versions
CN102701792B (zh
Inventor
赵白弟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CARLOBBIA GLAZE (KUNSHAN) Co Ltd
Original Assignee
CARLOBBIA GLAZE (KUNSHAN) Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CARLOBBIA GLAZE (KUNSHAN) Co Ltd filed Critical CARLOBBIA GLAZE (KUNSHAN) Co Ltd
Priority to CN201210201412.2A priority Critical patent/CN102701792B/zh
Publication of CN102701792A publication Critical patent/CN102701792A/zh
Application granted granted Critical
Publication of CN102701792B publication Critical patent/CN102701792B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：硅酸盐20~40份、Al(OH)35~15份、FeO5~15份、SeCl25~15份、ZrO5~15份、MnO21至5份、PbO5至10份、TiO25至15份、Na2CO35至15份。本发明提供的制备陶瓷用的黑釉，各组份配比科学合理，制备得到的黑釉具有很好的亮度、色泽均匀，颜色烧制范围宽、能作为多种颜色的衬底，能制备得到高雅美观的彩色釉，具有很好的应用价值。

Description

一种制备陶瓷用的黑釉
 
技术领域
本发明涉及一种陶瓷釉，具体涉及一种化学性能稳定、耐酸、耐碱的黑釉。
背景技术
陶瓷因其外表具有很好的光滑度、致密性等诸多优点广泛应用于各个领域，在陶瓷器制备过程中，经常在纯净的黑釉上施以各种低温色彩，黑釉成为各种美丽颜色的衬托， 可以得到高调典雅的陶瓷釉，但是现有技术的黑釉其釉面不够光亮。色泽不够均匀，因此很有必要再现有技术的基础之上，设计一种釉面滋润、光亮，色黑如漆的陶瓷黑釉。
发明内容
发明目的：本发明所要解决的技术问题是克服现有技术的不足，提供一种釉面滋润、光亮，色黑如漆，能作为彩釉衬底，易烧制的制备陶瓷用的黑釉。
技术方案：为解决以上技术问题，本发明采取如下技术方案：
一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸盐20~40份、Al(OH)3 5~15份、FeO5~15份、SeCl25~15份、ZrO5~15份、MnO21至5份、PbO5至10份、TiO2 5至15份、Na2CO3 5至15份。
作为优选方案，以上所述的制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸盐20~30份、Al(OH)3 5~10份、FeO 5~10份、SeCl25~10份、ZrO5~10份、MnO2 3至5份、PbO5至8份、TiO2 5至10份、Na2CO3 5至10份。
作为优选方案，以上所述的制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸盐30份、Al(OH)3 10份、FeO10份、SeCl210份、ZrO10份、MnO2 3份、PbO8份、TiO2 10份、Na2CO3 10份。
作为优选方案，以上述的制备陶瓷用的黑釉，所述的硅酸盐为硅酸钠或硅酸钾。。
本发明针对现有技术制备陶瓷用黑釉亮度低、光泽性差等的不足，通过大量实验确定制备陶瓷用的黑釉的组成和各组份的比例。
有益效果：本发明提供的制备陶瓷用的黑釉和现有技术相比具有如下优点：
本发明提供的制备陶瓷用的黑釉，根据大量实验优选熔块的最佳组成和配比，具有易分散、着色力强、颜色鲜艳、亮度高、色泽均匀，低温黑釉着色力强，色彩明快、装饰性强的优点。  
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实施例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1
一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸钠 40份、Al(OH)3 15份、FeO 15份、SeCl2 15份、ZrO 15份、MnO2 5份、PbO 10份、TiO2  15份、Na2CO3  15份。
实施例2
一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸钾20份、Al(OH)3 5份、FeO5份、SeCl25份、ZrO5份、MnO21份、PbO5份、TiO2 5份、Na2CO3 5份。
实施例3
一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸钾30份、Al(OH)310份、FeO 10份、SeCl210份、ZrO10份、MnO2 5份、PbO5至8份、TiO2 10份、Na2CO3 10份。
实施例4
一种制备陶瓷用的黑釉，它由下列重量份数的原料制成：
硅酸钠30份、Al(OH)3 10份、FeO10份、SeCl210份、ZrO10份、MnO2 3份、PbO8份、TiO2 10份、Na2CO3 10份。
用本发明提供的原料制备得到的黑釉可广泛用于强化瓷、骨质瓷、软质瓷、硬质瓷或建筑瓷等瓷种的釉上装饰，颜色烧制范围宽。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (4)

1.一种制备陶瓷用的黑釉，其特征在于，它由下列重量份数的原料制成：
硅酸盐20~40份、Al(OH)3 5~15份、FeO5~15份、SeCl25~15份、ZrO5~15份、MnO21至5份、PbO5至10份、TiO2 5至15份、Na2CO3 5至15份。
2.根据权利要求1所述的制备陶瓷用的黑釉，其特征在于，它由下列重量份数的原料制成：
硅酸盐20~30份、Al(OH)3 5~10份、FeO 5~10份、SeCl25~10份、ZrO5~10份、MnO2 3至5份、PbO5至8份、TiO2 5至10份、Na2CO3 5至10份。
3.根据权利要求1所述的制备陶瓷用的黑釉，其特征在于，它由下列重量份数的原料制成：
硅酸盐30份、Al(OH)3 10份、FeO10份、SeCl210份、ZrO10份、MnO2 3份、PbO8份、TiO2 10份、Na2CO3 10份。
4.根据权利要求1至3任一项所述的制备陶瓷用的黑釉，其特征在于，所述的硅酸盐为硅酸钠或硅酸钾。
CN201210201412.2A 2012-06-19 2012-06-19 一种制备陶瓷用的黑釉 Expired - Fee Related CN102701792B (zh)