CN102659681A - 用于微表处的咪唑啉类阳离子沥青乳化剂的制备方法 - Google Patents
用于微表处的咪唑啉类阳离子沥青乳化剂的制备方法 Download PDFInfo
- Publication number
- CN102659681A CN102659681A CN201210114643XA CN201210114643A CN102659681A CN 102659681 A CN102659681 A CN 102659681A CN 201210114643X A CN201210114643X A CN 201210114643XA CN 201210114643 A CN201210114643 A CN 201210114643A CN 102659681 A CN102659681 A CN 102659681A
- Authority
- CN
- China
- Prior art keywords
- imidazolines
- reaction
- preparation
- little table
- cation asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 125 | 137 | 不小于120s |
30min内聚力 | 1.2 | 1.35 | 不小于1.2Nm |
60min内聚力 | 2.15 | 2.4 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 407 | 496 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 684 | 259 | 不大于807g/m2 |
负荷车轮黏砂量 | 307 | 276 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 157 | 162 | 不小于120s |
30min内聚力 | 1.35 | 1.25 | 不小于1.2Nm |
60min内聚力 | 2.45 | 2.05 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 317 | 422 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 658 | 723 | 不大于807g/m2 |
负荷车轮黏砂量 | 182 | 263 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 147 | 137 | 不小于120s |
30min内聚力 | 1.25 | 1.3 | 不小于1.2Nm |
60min内聚力 | 2.25 | 2.1 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 364 | 289 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 468 | 372 | 不大于807g/m2 |
负荷车轮黏砂量 | 137 | 268 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 124 | 194 | 不小于120s |
30min内聚力 | 1.3 | 1.25 | 不小于1.2Nm |
60min内聚力 | 2.55 | 2.3 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 198 | 264 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 582 | 671 | 不大于807g/m2 |
负荷车轮黏砂量 | 167 | 273 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 157 | 155 | 不小于120s |
30min内聚力 | 1.3 | 1.2 | 不小于1.2Nm |
60min内聚力 | 2.35 | 2.15 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 292 | 381 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 797 | 802 | 不大于807g/m2 |
负荷车轮黏砂量 | 273 | 399 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 121 | 153 | 不小于120s |
30min内聚力 | 1.25 | 1.2 | 不小于1.2Nm |
60min内聚力 | 2.35 | 2.15 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 277 | 357 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 785 | 762 | 不大于807g/m2 |
负荷车轮黏砂量 | 181 | 297 | 不大于450g/m2 |
内容 | 自制乳化剂+A | 自制乳化剂+B | 技术要求 |
拌和时间(s) | 117 | 155 | 不小于120s |
30min内聚力 | 1.25 | 1.25 | 不小于1.2Nm |
60min内聚力 | 1.8 | 1.85 | 不小于2.0Nm |
浸水1h湿轮磨耗 | 533 | 387 | 不大于540g/m2 |
浸水6d湿轮磨耗 | 725 | 792 | 不大于807g/m2 |
负荷车轮黏砂量 | 306 | 221 | 不大于450g/m2 |
Claims (7)