CN102493065A - Regenerated cotton snowflake blended yarn and blending technology thereof - Google Patents
Regenerated cotton snowflake blended yarn and blending technology thereof Download PDFInfo
- Publication number
- CN102493065A CN102493065A CN2011104260358A CN201110426035A CN102493065A CN 102493065 A CN102493065 A CN 102493065A CN 2011104260358 A CN2011104260358 A CN 2011104260358A CN 201110426035 A CN201110426035 A CN 201110426035A CN 102493065 A CN102493065 A CN 102493065A
- Authority
- CN
- China
- Prior art keywords
- cotton
- snowflake
- blending
- regeneration
- regeneration cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the regenerated cotton spinning technical field, in particular to a regenerated cotton snowflake blended yarn and a blending technology thereof. The regenerated cotton snowflake blended yarn is prepared through the blending technology by using regenerated cotton, fine staple cotton and regenerated polyester as raw materials, the cotton blending percents of regenerated polyester, fine staple cotton and regenerated cotton are 35%, 24% and 41%; and the regenerated cotton accounting for 41% comprises the following components by weight percent: 19% of fly cotton, 4% of flat strips and 18% of comb noil. The blending technology comprises the following specific steps: 1) blending cotton; 2) blowing; 3) carding; 4) drawing; 5) roving; and 6) spinning. Compared with the prior art, deodorization cotton and fine staple cotton are used for blending and the parameters of the blending equipment are adjusted, thus the deodorization cotton blended yarn has good deodorization function, the yarn evenness and strength are increased and neps are reduced. Therefore, the moisture conductivity, air permeability and aesthetic property of the deodorization cotton blended yarn can be increased.
Description
Technical field
The present invention relates to the regeneration cotton spinninging technical field, specifically a kind of regeneration cotton snowflake melange yarn and blending technology thereof.
Background technology
The Along with people's growth in the living standard, also increasingly high, especially more and more interesting to the fashion degree requirement of dress to the second use of textile raw material.The regeneration cotton snowflake melange yarn is a kind of international and domestic popular green Eco-Fashion yarn, owing to use the outward appearance of the lining of this yarn production to present the flakes effect, so be called " snowflake melange yarn " again.But snowflake melange yarn is in spinning process, and the materials of distributing cotton are difficult to mix, thereby has caused the yarn strength of snowflake melange yarn low, problem that cotton knot is high.Therefore, a kind of regeneration cotton snowflake melange yarn and blending technology thereof that can improve yarn strength and reduce cotton knot of design is vital.
Summary of the invention
The objective of the invention is to overcome the deficiency of prior art, a kind of regeneration cotton snowflake melange yarn and blending technology thereof that can improve yarn strength and reduce cotton knot is provided.
In order to achieve the above object; Among the present invention; The regeneration cotton snowflake melange yarn adopts regeneration cotton, medium staple cotton and regenerated terylene to be raw material and to process according to blending technology; The length of regeneration cotton is that 15 millimeters, fineness are 5700, and the length of medium staple cotton is that 29mm, fineness are 7500, and the length of regenerated terylene is that 38mm, fineness are 6500; The ratio of distributing cotton is a regenerated terylene 35%, medium staple cotton 24%, and regeneration cotton 41%, described 41% regeneration cotton comprises: underfly 19%, card strips 4%, cotton noils 18%; Described blending technology concrete steps are following: 1, distribute cotton: regeneration cotton, medium staple cotton and regenerated terylene are broken into sandwich bag in proportion; 2, blowing: behind the sandwich bag of humidification, sandwich bag successively on A002 griping cotton machine, FA106 opener, A035 mixing and blowing machine and A076C lapper blending become regeneration cotton snowflake blending volume; 3, comb and parallel cotton fibers prior to spinning: the blending of regeneration cotton snowflake twists in to be carried out carding step and processes the regeneration cotton snowflake blending carded sliver on the carding machine; 4, drafting: the regeneration cotton snowflake blending carded sliver carries out mixing in doubling step and processes regeneration cotton snowflake blending bar on drawing frame; 5 rove: regeneration snowflake blending bar carries out the rove operation and processes regeneration cotton snowflake blended roving on Speed frames; 6 spun yarns: regeneration cotton snowflake blended roving carries out spinning process and processes regeneration cotton snowflake blending spun yarn on fine spining machine.
The speed of described A002 griping cotton machine is 700 r/min.
Kirschner beater speed is 550 r/min in the described FA106 opener, and the distance between kirschner beater and dirt rod is 12mm, and spacing between dirt rod and the dirt rod is 8mm.
The running speed of described A035 mixing and blowing machine is 700 * 800 r/min.
The licker-in speed of described carding machine is that 780 r/min, cylinder speed are that 340 r/min, doffer speed are 20 r/min, and the cover plate linear velocity is 160mm/min, and import is spaced and is 7mm at the bottom of the little leakage.
The drafting ratch of described drawing frame is 43 * 38mm, and front roller speed is 200 m/min, and overhead tension draft multiple is 1.0 times.
Described Speed frames adopt the enclosed type flyer, and ratch is 50 * 58.5mm, and jaw is of a size of 6mm, and overhead tension draft multiple is 1.0 times, and roving twist factor is 115.
Described fine spining machine adopts 876 Winding-proof rollers, and front roller speed is 200 r/min, and jaw is of a size of 2.3mm, and back zone drafting multiple is 1.15 times, and the spun yarn twist factor is 330.
The present invention compares with prior art; Adopt regeneration cotton, medium staple cotton and regenerated terylene to carry out blending; And the parameter of adjustment blending equipment, when making the regeneration cotton snowflake melange yarn have good environmental protection function, also improved the brute force of regeneration cotton snowflake melange yarn resultant yarn; Reduced cotton knot, thereby made that leading of regeneration cotton snowflake melange yarn is moist, gas permeability and aesthetic property all be improved.
The specific embodiment
Existing the present invention is done further describes.
Among the present invention; The regeneration cotton snowflake melange yarn adopts regeneration cotton, medium staple cotton and regenerated terylene to be raw material and to process according to blending technology; The length of regeneration cotton is that 15 millimeters, fineness are 5700; The length of medium staple cotton is that 29mm, fineness are 7500, and the length of regenerated terylene is that 38mm, fineness are 6500; The ratio of distributing cotton is a regenerated terylene 35%, medium staple cotton 24%, and regeneration cotton 41%, described 41% regeneration cotton comprises: underfly 19%, card strips 4%, cotton noils 18%.
Blending technology concrete steps are following:
1, distribute cotton: regeneration cotton, medium staple cotton and regenerated terylene are broken into sandwich bag in proportion.
2, blowing: behind the sandwich bag of humidification, sandwich bag successively on A002 griping cotton machine, FA106 opener, A035 mixing and blowing machine and A076C lapper blending become regeneration cotton snowflake blending volume.Wherein, the speed of A002 griping cotton machine is increased to 700 r/min; Kirschner beater speed is reduced to 550 r/min in the FA106 opener, and the distance between kirschner beater and dirt rod is adjusted into 12mm, and spacing between dirt rod and the dirt rod is adjusted into 8mm, and this kirschner beater has reduced the fibre damage in regeneration cotton, medium staple cotton and the regenerated terylene; The running speed of A035 mixing and blowing machine is increased to 700 * 800 r/min, and the regeneration cotton snowflake blending volume after handling through cotton cleaning process has improved the mixture homogeneity of regeneration cotton, medium staple cotton and regenerated terylene.
3, comb and parallel cotton fibers prior to spinning: the blending of regeneration cotton snowflake twists in to be carried out carding step and processes the regeneration cotton snowflake blending carded sliver on the carding machine; The licker-in speed of carding machine is reduced to that 780 r/min, cylinder speed are reduced to 340 r/min, doffer speed is reduced to 20 r/min; The cover plate linear velocity is increased to 160mm/min; Import is spaced to tighten up and is 7mm at the bottom of the little leakage; Increase noil, in 15, adjustment comb and parallel cotton fibers prior to spinning stripping form is the apron stripping with the control cotton junction grain number.
4; Drafting: the regeneration cotton snowflake blending carded sliver carries out mixing in doubling step and processes regeneration cotton snowflake blending bar on drawing frame; Because regeneration cotton, medium staple cotton are different with regenerated terylene length; Thereby caused in the regeneration cotton snowflake blending carded sliver fibre length uneven, in order to solve the uneven problem of fibre length in the regeneration cotton snowflake blending carded sliver, it is 43 * 38mm that the drafting roller central moment of drawing frame is tightened up; Front roller speed is reduced to 200 m/min, and overhead tension draft multiple is increased to 1.0 times.
5; Rove: regeneration snowflake blending bar carries out the rove operation and processes regeneration cotton snowflake blended roving on Speed frames; Speed frames adopt the enclosed type flyer, and it is 50 * 58.5mm that the ratch of Speed frames tightens up, and the jaw size is reduced to 6mm; Overhead tension force multiple is adjusted into 1.0 times, and roving twist factor increases to 115.
6; Spun yarn: regeneration cotton snowflake blended roving carries out spinning process and processes regeneration cotton snowflake blending spun yarn on fine spining machine; Fine spining machine adopts 876 Winding-proof rollers, and the front roller speed of fine spining machine is 200 r/min, and the jaw size is reduced to 2.3mm; Back zone drafting multiple is adjusted into 1.15 times, and the spun yarn twist factor increases to 330 to improve the brute force of regeneration cotton snowflake blending spun yarn.
Claims (8)
1. regeneration cotton snowflake melange yarn and blending technology thereof; It is characterized in that: the regeneration cotton snowflake melange yarn adopts regeneration cotton, medium staple cotton and regenerated terylene to be raw material and to process according to blending technology; The length of regeneration cotton is that 15 millimeters, fineness are 5700; The length of medium staple cotton is that 29mm, fineness are 7500, and the length of regenerated terylene is that 38mm, fineness are 6500; The ratio of distributing cotton is a regenerated terylene 35%, medium staple cotton 24%, and regeneration cotton 41%, described 41% regeneration cotton comprises: underfly 19%, card strips 4%, cotton noils 18%; Described blending technology concrete steps are following: 1, distribute cotton: regeneration cotton, medium staple cotton and regenerated terylene are broken into sandwich bag in proportion; 2, blowing: behind the sandwich bag of humidification, sandwich bag successively on A002 griping cotton machine, FA106 opener, A035 mixing and blowing machine and A076C lapper blending become regeneration cotton snowflake blending volume; 3, comb and parallel cotton fibers prior to spinning: the blending of regeneration cotton snowflake twists in to be carried out carding step and processes the regeneration cotton snowflake blending carded sliver on the carding machine; 4, drafting: the regeneration cotton snowflake blending carded sliver carries out mixing in doubling step and processes regeneration cotton snowflake blending bar on drawing frame; 5 rove: regeneration snowflake blending bar carries out the rove operation and processes regeneration cotton snowflake blended roving on Speed frames; 6 spun yarns: regeneration cotton snowflake blended roving carries out spinning process and processes regeneration cotton snowflake blending spun yarn on fine spining machine.
2. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof is characterized in that: the speed of described A002 griping cotton machine is 700 r/min.
3. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof; It is characterized in that: kirschner beater speed is 550 r/min in the described FA106 opener; Distance between kirschner beater and dirt rod is 12mm, and spacing between dirt rod and the dirt rod is 8mm.
4. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof is characterized in that: the running speed of described A035 mixing and blowing machine is 700 * 800 r/min.
5. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof; It is characterized in that: the licker-in speed of described carding machine is that 780 r/min, cylinder speed are that 340 r/min, doffer speed are 20 r/min; The cover plate linear velocity is 160mm/min, and import is spaced and is 7mm at the bottom of the little leakage.
6. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof is characterized in that: the drafting ratch of described drawing frame is 43 * 38mm, and front roller speed is 200 m/min, and overhead tension draft multiple is 1.0 times.
7. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof; It is characterized in that: described Speed frames adopt the enclosed type flyer, and ratch is 50 * 58.5mm, and jaw is of a size of 6mm; Overhead tension draft multiple is 1.0 times, and roving twist factor is 115.
8. a kind of regeneration cotton snowflake melange yarn according to claim 1 and blending technology thereof; It is characterized in that: described fine spining machine adopts 876 Winding-proof rollers, and front roller speed is 200 r/min, and jaw is of a size of 2.3mm; Back zone drafting multiple is 1.15 times, and the spun yarn twist factor is 330.