CN101260586A - Blended yarn and producing method thereof - Google Patents
Blended yarn and producing method thereof Download PDFInfo
- Publication number
- CN101260586A CN101260586A CNA2008100604241A CN200810060424A CN101260586A CN 101260586 A CN101260586 A CN 101260586A CN A2008100604241 A CNA2008100604241 A CN A2008100604241A CN 200810060424 A CN200810060424 A CN 200810060424A CN 101260586 A CN101260586 A CN 101260586A
- Authority
- CN
- China
- Prior art keywords
- speed
- fiber
- blended yarn
- yarn
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses blended yarns and a method for manufacturing the same, belonging to the spinning technique field. The blended yarn consists of the following fibers in percentage by weight: pearl viscose fiber 20-40, tencel fiber 30-50, and modal fiber 20-40; the spinning process comprises the following steps in sequence cleaning cotton, carding cotton, three passage drawing, roving, spinning, and cheese winding. The blended yarns and the manufacture method thereof are to spin the three cellulose fibers of the pearl viscose fiber, the tencel fiber and the modal fiber according to a certain content proportion; the process is simple and advantage complementation can be achieved; the blended yarns not only possess the characteristics of viscose moisture absorption, ventilation and comfortable wearing, but also has strong wet-dry intensity, bright luster, smooth hand feeling, and excellent dimension stability, so that product has excellent wearing function and good health care function, and satisfies the overall requirements of comfort and healthcare of people in new age.
Description
Technical field
The invention belongs to spinninging technical field, be specifically related to a kind of blended yarn and production method thereof.
Background technology
Along with the continuous listing of multiple functional fiber in recent years, people have also had new lifting and requirement to the pursuit of functional textile, and the key of decision functions of textile fabrics and taking is the performance of yarn.Common a kind of fiber is difficult to accomplish existing good functional, and good taking is arranged again, wherein just comprises pearl viscose fiber, day silk (Tencel) fiber and model (Modal) fiber.Pearl viscose fiber is a kind of functional fiber of the domestic and international initiative of the autonomous invention of China, it have pearl beauty care, relieve inflammation or internal heat relieve internal heat, tender white muscle skin, uvioresistant and emission infrared function, and moisture absorption is ventilative, comfortable and easy to wear, but because its moisture absorption is low especially by force, not water-fastly wash poor dimensional stability; Tencel, Modal fiber are the high-wet-modulus fibres that Austrian Lenzin company produces, and employed in process of production ammonification amine solvent is harmless fully to human body, and can reclaim fully, use repeatedly, chemical reaction does not take place in the contained cellulosic molecule of magma in the production process, and no coupling product, no discarded object are discharged outside the factory, free from environmental pollution, so be called 21st century environmental protection fiber by industry inside.This high-wet-modulus fibre not only has ventilative, the comfortable and easy to wear characteristic of viscose glue moisture absorption, and dried wet strength height, and gloss is beautiful, and feel is smooth, and DIMENSIONAL STABILITY is good, but they do not have the health care of pearl viscose fiber.
Summary of the invention
At the above-mentioned problems in the prior art, the object of the invention is to provide the technical scheme of a kind of blended yarn and production method thereof.
Described a kind of blended yarn is characterized in that fibrous by following weight proportion, pearl viscose fiber: 20-40%, tencel fiber: 30-50%, Modal fibre: 20-40%.
Described a kind of blended yarn is characterized in that fibrous by following weight proportion, pearl viscose fiber: 20-35%, tencel fiber: 35-50%, Modal fibre: 25-35%.
Described a kind of blended yarn is characterized in that fibrous by following weight proportion, pearl viscose fiber: 25-35%, tencel fiber: 35-45%, Modal fibre: 25-35%.
The production method of described a kind of blended yarn is characterized in that being undertaken by following processing step:
1) prepares burden according to described fibrous and weight proportion, and mix by griping cotton machine shredding, the shredding mixing of mixing and blowing machine and card wire opener successively, hired roughneck's speed is 720-760r/min in the griping cotton machine opening, cotton-pressing curtain speed is 1-1.5m/min in the mixing and blowing machine shredding hybrid technique, and hired roughneck's speed is 460-500r/min in the card wire opener hybrid technique;
2) it is cotton to adopt the vibration hopper feeder to give, and becomes lap by the lapper shredding, and hired roughneck's speed of setting is 780-820r/min;
3) adopt carding machine to make the carded sliver, the cylinder speed of setting is 310-335r/min, and licker-in speed is 735-765r/min;
4) the above-mentioned carded sliver carries out slubbing drafting, two road draftings, three road draftings successively;
5) adopt Speed frames to make rove behind the drafting;
6) rove made adopts the match network to spin fine spining machine and spins and meet quantitative yarn;
7) do, remove a yarn defect and a network one-tenth tube yarn by automatic winder check bar, winder speed is 950-1050r/min.
The production method of described a kind of blended yarn, it is characterized in that hired roughneck's speed is 730-750r/min in the griping cotton machine opening, cotton-pressing curtain speed is 1.15-1.35m/min in the mixing and blowing machine shredding hybrid technique, hired roughneck's speed is 470-490r/min in the card wire opener hybrid technique, hired roughneck's speed is 790-810r/min in the lapper opening, carding machine makes that cylinder speed is 315-330r/min in the carded sliver technology, licker-in speed is 745-760r/min, and winder speed is 980-1020r/min.
The production method of described a kind of blended yarn is characterized in that the carded sliver dry weight that carding machine is made is 16.0-17.0g/5m.
The production method of described a kind of blended yarn is characterized in that 4 feedings of slubbing drafting, and spinning the strip dry weight is 9.5-11.5g/5m; 8 feedings of two road draftings, spinning the strip dry weight is 9.5-11.5g/5m; 8 feedings of three road draftings, spinning the strip dry weight is 9.5-11.5g/5m.
The production method of described a kind of blended yarn is characterized in that the rove dry weight is 2.4-2.8g/10m.
The production method of described a kind of blended yarn is characterized in that the spun yarn dry weight is 1.044-1.867g/100m.
The production method of described a kind of blended yarn is characterized in that temperature is 24-32 ℃ in the spun yarn spinning process, and humidity is 50-60%; Temperature is 20-28 ℃ in the winding process, and humidity is 60-70%; Temperature in other processing step is 22-30 ℃, and humidity is 55-65%.
Above-mentioned a kind of blended yarn and production method thereof are spinned pearl viscose glue, day silk (Tencel) and three kinds of cellulose fibres of model (Modal) according to certain content proportioning, technology is simple, can accomplish to have complementary advantages, not only has ventilative, the comfortable and easy to wear characteristic of viscose glue moisture absorption, and dried wet strength height, gloss is beautiful, feel is smooth, DIMENSIONAL STABILITY is good, make product existing good wearability, the good health care function has been arranged again, satisfied the comprehensive demand of new period people the clothing comfort health-care.
The specific embodiment
The invention will be further described below in conjunction with the specific embodiment.
A kind of blended yarn is made of pearl viscose fiber following components in portion by weight: 20-40%, tencel fiber: 30-50%, Modal fibre: 20-40%; Preferred content proportioning is: pearl fiber: 20-35%, tencel fiber: 35-50%, Modal fibre: 20-35%; Preferred content proportioning is: pearl fiber: 25-35%, tencel fiber: 35-45%, Modal fibre: 25-35%.The optimum content proportioning is: pearl fiber: 30%, and tencel fiber: 40%, Modal fibre: 30%.
Concrete production technology is as follows: carry out package by said ratio content, by the griping cotton machine shredding, during shredding, hired roughneck's speed is 740r/min, and the each slippage of hired roughneck is 100m/min; Shredding mixes through the mixing and blowing machine again, this moment, cotton-pressing curtain speed was 1.25m/min, handing over spiked lattice speed is 100m/min, the first brad hired roughneck speed is 673r/min, the second brad hired roughneck speed is 799r/min, and evener roller speed is 313r/min, and brad curtain and cotton-pressing curtain spacing are 60mm, hand over spiked lattice and equal cotton hired roughneck to space and be that 40mm, dirt interrod spacing are 5mm; Adopt the card wire opener to mix then, this moment, hired roughneck's speed was 480r/min, and the hired roughneck is 11mm with spacing to cotton roller; Give cottonly in the mixed process with the vibrations hopper feeder, become lap by the lapper shredding, this moment, kirschner beater speed was 800r/min, and the hired roughneck is that 11mm, lap roller rotating speed are 12r/min with spacing to cotton roller, and it is 360g/m that lap is done quantitatively; Above step is called cotton cleaning process, and temperature requirement is 22-30 ℃, and humidity is 55-65%; Make the carded sliver by carding machine again, during the system carded sliver, cylinder speed is 323r/min, licker-in speed is 754r/min, cover plate speed is 81mm/min, doffer speed is 21r/min, feed plate and licker-in spacer are 0.38mm, licker-in and mote knife space and are 0.508mm, mote knife height+5mm, established angle is 95 °, licker-in and cylinder space and are 0.177mm, and licker-in and pre-combing plate space and be that 0.558mm, cylinder and back stationary plate space and be 0.406mm, 0.355m, cylinder and removable cover space and are 0.254mm, 0.228mm, 0.203mm, 0.203mm, 0.228mm, cylinder and preceding securing cover plate space and are 0.254mm, 0.228mm, 0.203mm cylinder and doffer are spaced and be 0.127mm, comb and parallel cotton fibers prior to spinning carded sliver dry weight is 1615g/5m; Successively by first drawing frame and close, intermediate drawing frame also closes with the carded sliver that obtains, and three road drawing frames also close; During the first drawing frame drafting, horn mouth ￠ 2.6mm, pressure bar cushion block ￠ 8.9mm, back pressure roller linear velocity is 250m/min, it is 47 * 53mm that roller grips distance, 1.77 times of back area drafts, the total draft multiple is 6.35 times, public affairs 13.0%, 4 feeding that gets damp again surely, sliver exporting speed is 250m/min, and spinning the strip dry weight is 10.8g/5m; During the intermediate drawing frame drafting, horn mouth ￠ 2.6mm, pressure bar cushion block ￠ 8.9mm, back pressure roller linear velocity is 250m/min, it is 47 * 53mm that roller grips distance, 1.30 times of back area drafts, the total draft multiple is 8.21 times, public affairs 13.0%, 8 feeding that gets damp again surely, sliver exporting speed is 250m/min, and spinning the strip dry weight is 10.8g/5m; During three road drawing frame draftings, horn mouth ￠ 2.6mm, pressure bar cushion block ￠ 8.9mm, back pressure roller linear velocity is 250m/min, it is 47 * 53mm that roller grips distance, 1.30 times of back area drafts, the total draft multiple is 8.21 times, public affairs 13.0%, 8 feeding that gets damp again surely, sliver exporting speed is 250m/min, and spinning the strip dry weight is 10.8g/5m; Make rove by Speed frames behind the drafting, jaw is 3.5mm, and it is 41 * 53.5 * 60.5mm that roller grips distance, 1.19 times of back area drafts; The total draft multiple is 8.43 times, the two ingots of reel cage pressure 120 * 200 * 150 * 150N/, and ingot speed is 850r/min, front roller speed is 213r/min, and over-end winding speed is 4.46 circle/cm, and cone drums moves apart from being 3.88mm, twist factor is 80, and public affairs get damp again 13.0% surely, spins rove dry weight 2.6g/10m; Again rove being spun fine spining machine by the match network spins and meets quantitative yarn, jaw is 2.5mm, roller grips apart from being 44 * 60mm, and 1.15 times of back area drafts, total draft multiple are 41.38 times, ingot speed is 12000r/min, front roller speed is 192r/min, and reeling to tooth Z13/Z14 is 46/48, super fastener tooth 4T/ time, twist factor is 332, and public affairs get damp again 13.0% surely; Join 6,903 10/0 shaped steel wire rings, double horn mouth centre-to-centre spacing is 5-6mm, and two rove feed same horn mouth simultaneously, and to spin the spun yarn dry weight be 1.310g/100m, and it is 24-32 ℃ that this step requires temperature, and humidity is 50-60%; Do, remove a yarn defect and a network one-tenth tube yarn by automatic winder check bar again, winder speed is 1000m/min, the N passage is 220%, the S passage is 160%, length is 1.5cm, the L passage is 40%, length is 15cm, the T passage for-30%, length is 15cm, Cp+20%, Cm-20%, C2.0m, CCp+20%, CCm-20%, CC1.0m, it is 20-28 ℃ that this step requires temperature, and humidity is 60-70%; Be that the 25kg/ bag is packed according to Condition Weights at last.
Select other technological parameter in the technique scheme scope to test equally, all can realize beneficial effect of the present invention.
Claims (10)
1. blended yarn is characterized in that fibrous by following weight proportion, pearl viscose fiber: 20-40%, tencel fiber: 30-50%, Modal fibre: 20-40%.
2. a kind of blended yarn as claimed in claim 1 is characterized in that fibrous by following weight proportion, pearl viscose fiber: 20-35%, tencel fiber: 35-50%, Modal fibre: 20-35%.
3. a kind of blended yarn as claimed in claim 1 is characterized in that fibrous by following weight proportion, pearl viscose fiber: 25-35%, tencel fiber: 35-45%, Modal fibre: 25-35%.
4. as the production method of claim 1 or 2 or 3 described a kind of blended yarns, it is characterized in that being undertaken by following processing step:
1) prepares burden according to described fibrous and weight proportion, and mix by griping cotton machine shredding, the shredding mixing of mixing and blowing machine and card wire opener successively, hired roughneck's speed is 720-760r/min in the griping cotton machine opening, cotton-pressing curtain speed is 1-1.5m/min in the mixing and blowing machine shredding hybrid technique, and hired roughneck's speed is 460-500r/min in the card wire opener hybrid technique;
2) it is cotton to adopt the vibration hopper feeder to give, and becomes lap by the lapper shredding, and hired roughneck's speed of setting is 780-820r/min;
3) adopt carding machine to make the carded sliver, the cylinder speed of setting is 310-335r/min, and licker-in speed is 735-765r/min;
4) the above-mentioned carded sliver carries out slubbing drafting, two road draftings, three road draftings successively;
5) adopt Speed frames to make rove behind the drafting;
6) rove made adopts the match network to spin fine spining machine and spins and meet quantitative yarn;
7) do, remove a yarn defect and a network one-tenth tube yarn by automatic winder check bar, winder speed is 950-1050r/min.
5. the production method of a kind of blended yarn as claimed in claim 4, it is characterized in that hired roughneck's speed is 730-750r/min in the griping cotton machine opening, cotton-pressing curtain speed is 1.15-1.35m/min in the mixing and blowing machine shredding hybrid technique, hired roughneck's speed is 470-490r/min in the card wire opener hybrid technique, hired roughneck's speed is 790-810r/min in the lapper opening, carding machine makes that cylinder speed is 315-330r/min in the carded sliver technology, licker-in speed is 745-760r/min, and winder speed is 980-1020r/min.
6. the production method of a kind of blended yarn as claimed in claim 4 is characterized in that the carded sliver dry weight that carding machine is made is 16.0-17.0g/5m.
7. the production method of a kind of blended yarn as claimed in claim 4 is characterized in that 4 feedings of slubbing drafting, and spinning the strip dry weight is 9.5-11.5g/5m; 8 feedings of two road draftings, spinning the strip dry weight is 9.5-11.5g/5m; 8 feedings of three road draftings, spinning the strip dry weight is 9.5-11.5g/5m.
8. the production method of a kind of blended yarn as claimed in claim 4 is characterized in that the rove dry weight is 2.4-2.8g/10m.
9. the production method of a kind of blended yarn as claimed in claim 4 is characterized in that the spun yarn dry weight is 1.044-1.867g/100m.
10. the production method of a kind of blended yarn as claimed in claim 4 is characterized in that temperature is 24-32 ℃ in the spun yarn spinning process, and humidity is 50-60%; Temperature is 20-28 ℃ in the winding process, and humidity is 60-70%; Temperature in other processing step is 22-30 ℃, and humidity is 55-65%.