CN104805554A - Spinning method for aloe yarns - Google Patents

Spinning method for aloe yarns Download PDF

Info

Publication number
CN104805554A
CN104805554A CN201510197418.0A CN201510197418A CN104805554A CN 104805554 A CN104805554 A CN 104805554A CN 201510197418 A CN201510197418 A CN 201510197418A CN 104805554 A CN104805554 A CN 104805554A
Authority
CN
China
Prior art keywords
controls
speed
aloe
cotton
spinning
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510197418.0A
Other languages
Chinese (zh)
Inventor
马顺彬
张冶
蔡永东
陈志华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Textile Vocational Technology College
Original Assignee
Nantong Textile Vocational Technology College
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Textile Vocational Technology College filed Critical Nantong Textile Vocational Technology College
Priority to CN201510197418.0A priority Critical patent/CN104805554A/en
Publication of CN104805554A publication Critical patent/CN104805554A/en
Pending legal-status Critical Current

Abstract

The invention discloses a spinning method for aloe yarns. According to the method, aloe fiber is processed through work procedures of blowing, combing, drawing, roving, spinning, spooling and the like, and the aloe yarns are formed. A tight Siro-spinning technology is adopted, through the reasonable arrangement of parameters of each work procedure, the problems that the aloe fiber is short, and the spinning is difficult are solved, and the spun aloe yarns have good properties of moisture absorption, moisture permeability, dyeing and the like.

Description

A kind of spinning method of aloe yarn
Technical field
The present invention relates to spinninging technical field, especially employing aloe fibre is the spinning method of the tight SEILE textile of raw material.
Background technology
Along with the raising day by day of socioeconomic develop rapidly and people's level of consumption, the level of consumption idea of people is also in continuous renewal, to quality of life and living environment also attention all the more, the Functional Requirement of clothes is more and more paid attention to, especially to the characteristic such as feel, quality, environmental protection of clothes.Aloe fibre has come out in this case, and aloe fibre is a kind of New Regenerated Cellulosic Fibers, and it is contained that the material such as amino acid, polysaccharide has skin care, health care, therapeutic action, and it also has the comfortableness of viscose simultaneously.
RING SPINNING belongs to traditional spinning technique, and its method is ripe, and spinning quality is stablized.In whole world spinning total amount, ring spun yarn accounts for more than 80%, is spinning form most important, most crucial during Modern Spinning Process is produced.Along with the development of science and technology, ring spinning technology also experienced by the process of constantly bringing forth new ideas, it at a high speed, efficient, energy-conservation, electromechanical integration, automatic technology are ripe, the manufacture and exploit of especially all kinds of textile equipment, greatly promoted the technological progress of ring throstle.In the face of the challenge of many Advanced Spinning Technologies, ring spinning technology is except keeping the advantage of spinning Fine count Yarn, also at expansion varietal adaptation, improve yarn texture, improve in yarn qualities etc. and also carried out a series of improvement, there is spinning method as new in SEILE textile, compact spinning etc.And the Fine count Yarn line that can obtain and meet specific instructions for use, there is brand-new effect that compact spinning is combined with Siro-spun yarn technology, people can wear type transformation from warming-type to frivolous, comfortable, four seasons requirement to the requirement of product can be met, make enterprise Development and Production can go out lower, frivolous elegant, the fabric that drapability is good of cost, to meet the need of market.Compact-siro spinning process also arises at the historic moment just on this basis, has good market prospects.The tight SEILE textile set advantage of compact spinning and SEILE textile two kinds of technology, with independent compact spinning or SEILE textile higher than its brute force, filoplume reduces further, and possess the gloss of strand, feel is more soft, can Some substitute strand, but cost obviously reduces, be applicable to high-grade fabric, there are wide market prospects.This product, towards high-grade designer clothing consumer group, is make the ideal product of top-grade fashion, for textile garment, household textiles field provide the novel fabric of high-tech, comfort property.
Shandong surmounts Textile Co., Ltd. prospectus CN102719960B and discloses a kind of cotton fiber, aloe fibre, viscose fiber blended yarn and spinning method thereof.Adopt the spinning technique of tight SEILE textile, the raw-material ratio of reasonable selection, thus both solved the short shortcoming of aloe fibre, again the maximized advantage having aloe fibre; But the raw material of three kinds of different proportions, method just has certain triviality.
Summary of the invention
The object of the invention is to the spinning method designing a kind of aloe yarn.The method overcome the short and shortcoming that cannot spin separately of aloe fibre, thus the yarn spun has the easy dyeing of aloe fibre, moisture absorption and the strong feature of permeability.
For achieving the above object, technical scheme of the present invention is: a kind of spinning method of aloe yarn, and be mainly and adopt tight SEILE textile technology spinning to form, its step comprises blowing, combing, drafting, rove, spun yarn and winder; It is characterized in that: concrete spinning stage is as follows:
(1) raw material is chosen: employing length is 30 ~ 40mm, and fineness is the aloe fibre of 1.5 ~ 1.7dtex;
(2) blowing step is specially: the bale of cotton carries out the loose operation of fiber through griping cotton machine, arranging A002C griping cotton machine Beater Speed is 845r/min, dolly speed of gyration 2.3r/min, blade stretches out rib distance 0 ~ 10mm, grabs cotton dolly and often runs decline in one week 3mm/ time; Fibre bundle after loose is sent in A006B cotton blender machine and carries out mixed cotton operation, cotton blender machine hired roughneck rotating speed is set to 430r/min, between dirt bastinade hand, import is spaced at 10 ~ 15mm, between dirt bastinade hand, outlet is spaced at 12 ~ 20mm, cotton-pressing curtain and brad curtain space 60 ~ 80mm, and brad curtain and evener roller space 40 ~ 80mm; Delivered to by aloe fibre in A036C opener and carry out shredding operation, opener speeds control is at 480r/min; Aloe fibre raw material after shredding is carried out married operation via condenser feeding A092A hopper feeder, and cotton feeder brad curtain wire velocity control is at 50 ~ 70m/min, and V-type cord speeds control is at 1.56 ~ 3.5m/min; Outputted to uniformly in A076C lapper by delivery roller by mixed aloe fibre and carry out clot and operate, the comprehensive Beater Speed 900r/min of lapper, the speeds control of rolling roller is at 11 ~ 13r/min; The aloe fibre lap length 34.2 ~ 36m formed after opening and cleaning step, dry weight is 400 grams/m, the rolling time be 3 points 55 seconds;
(3) combing step is specially: in combing operation, and use FA201 carding machine, the speed of the cylinder in carding machine is arranged on 330r/min, and the speed of licker-in is arranged on 860r/min, and the speeds control of cover plate is at 72.3 ~ 100mm/min; Doffer speed controls at 20 ~ 28r/min, and cylinder and cover plate 5 are spaced and be respectively 0.25mm, 0.23mm, 0.2mm, 0.2mm, 0.23mm from import to outlet; Aloe fibre weight of card sliver is 21.5g/5m;
(4) drafting step is specially: in mixing in doubling step, use FA311 drawing frame, and carry out three road mixing in doubling step, sliver exporting speed controls at 275 ~ 300m/min;
(5) rove step is specially: control 1.05 by FA423 Speed frames Distribution Area drafting multiple, first break draft multiple controls 1.12 ~ 1.48, and primary area drafting multiple controls 7.0 ~ 9.0, and total draft multiple is 8 ~ 12;
(6) spun yarn step is specially: adopt tight SEILE textile technology, Spinning Draft Zone is the feeding of double joint rove, and stroke wants little grasp, controls at 3.0 ~ 4.0mm, back zone drafting multiple Selecting parameter 1.30, front roller centre-to-centre spacing controls at 42 ~ 45mm, and rear roller centre-to-centre spacing controls at 50 ~ 65mm, and ingot speed control is built in 11000 ~ 13000r/min, spacing block is 2.5 ~ 3.0mm, twist factor controls 330 ~ 360, and front roller speeds control is at 150 ~ 200r/min, and total draft multiple is 50 ~ 60;
(7) winder step is specially: adopt NO.21C automatic winder, winder speed 1200 ~ 1500m/min, clearing method is arranged: cotton knot 250 ~ 300%, short slub 140 ~ 180% × 1.2 ~ 2.0cm, long slubbing 30 ~ 40% × 30 ~ 40cm, long details-30 ~-40% × 30 ~ 40cm.
Further, described raw material adopts length to be 38mm, and fineness is the aloe fibre of 1.67dtex.
Further, FA423 Speed frames Distribution Area drafting multiple controls 1.05 by described rove step, and first break draft multiple controls 1.26, and primary area drafting multiple controls 7.12, and total draft multiple is 8.97.
Further, described spun yarn step, Spinning Draft Zone stroke controls at 3.5mm, back zone drafting multiple Selecting parameter 1.30, and front roller centre-to-centre spacing controls at 43mm, rear roller centre-to-centre spacing controls at 57mm, ingot speed control is built in 12000r/min, and spacing block is 2.7mm, and twist factor controls 350, front roller speeds control is at 170r/min, and total draft multiple is 54.71.
The invention has the beneficial effects as follows:
(1) the present invention produces yarn to aloe fibre through operations such as blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, spun yarn, winders, adopt compact-siro spinning process, the method parameter of each operation reasonably improves, solve the short problem of not easily spinning separately of fiber of aloe fibre, still remain the advantage of aloe fibre.
(2) aloe fibre of the present invention is a kind of New Regenerated Cellulosic Fibers, it is contained that the material such as amino acid, polysaccharide has skin care, health care, therapeutic action, it also has the comfortableness of viscose simultaneously, under selecting the aloe fibre of length-specific and fineness that it can be made to refuse other more long stapled blending, the fabric that the yarn spun is made into has good skin-friendly, be a kind of environmental protection, callable material, can be widely used in house and spin industry.
(3) aloe fibre of the present invention, especially, employing length is 38mm, fineness is the aloe fibre of 1.67dtex, under it can be made to refuse other more long stapled blending, required qualified yarn can be spun faster, simultaneously, because length and fineness value more meet the demand of yarn own, make yam physical performance, chemical property more excellent.
(4) the present invention is in 6 operations, by setting distinctive technological parameter, just can make extremely short aloe fibre, under the blending of the fiber not needing other longer, also can purely spin.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme of the present invention is elaborated.
Embodiment 1
The method step of the tight SEILE textile of aloe:
Main flow line:
A002C(griping cotton machine) → A006B(cotton blender machine) → A036C(kirschner beater opener) → A092A(hopper feeder) → A076C(lapper)
FA201(carding machine) → FA311(drawing frame) three also → FA423(Speed frames) → A513W(fine spining machine) → NO.21C(automatic winder)
A, raw material are: employing length is 30 ~ 40mm, and fineness is the aloe fibre of 1.5 ~ 1.7dtex;
B, concrete steps:
1, blowing concrete steps are: the bale of cotton carries out the loose operation of fiber through griping cotton machine, and arranging A002C griping cotton machine Beater Speed is 845r/min, dolly speed of gyration 2.3r/min, and blade stretches out rib distance 1mm, grab cotton dolly and often run decline in one week 3mm/ time; Fibre bundle after loose is sent in A006B cotton blender machine and carries out mixed cotton operation, cotton blender machine hired roughneck rotating speed is set to 430r/min, and between dirt bastinade hand, import is spaced at 10mm, and between dirt bastinade hand, outlet is spaced at 12mm, cotton-pressing curtain and brad curtain space 60mm, and brad curtain and evener roller space 40mm; Delivered to by aloe fibre in A036C opener and carry out shredding operation, opener speeds control is at 480r/min; Aloe fibre raw material after shredding is carried out married operation via condenser feeding A092A hopper feeder, and cotton feeder brad curtain wire velocity control is at 50m/min, and V-type cord speeds control is at 1.56m/min; Outputted to uniformly in A076C lapper by delivery roller by mixed aloe fibre and carry out clot and operate, the comprehensive Beater Speed 900r/min of lapper, the speeds control of rolling roller is at 11r/min; The aloe fibre lap length 34.2m formed after opening and cleaning step, dry weight is 400 grams/m, the rolling time be 3 points 55 seconds.
2, combing concrete steps are: in combing operation, and use FA201 carding machine, the speed of the cylinder in carding machine is arranged on 330r/min, and the speed of licker-in is arranged on 860r/min, and the speeds control of cover plate is at 72.3mm/min; Doffer speed controls at 20r/min, and cylinder and cover plate 5 are spaced and be respectively 0.25mm, 0.23mm, 0.2mm, 0.2mm, 0.23mm from import to outlet; Aloe fibre weight of card sliver is 21.5g/5m.
3, drafting concrete steps are: in mixing in doubling step, use FA311 drawing frame, and carry out three road mixing in doubling step, sliver exporting speed controls at 275m/min.
4, rove concrete steps are: control 1.05 by FA423 Speed frames Distribution Area drafting multiple, first break draft multiple controls 1.12, and primary area drafting multiple controls 7.0, and total draft multiple is 8.
5, spun yarn step is specially: adopt tight SEILE textile technology, Spinning Draft Zone is the feeding of double joint rove, and stroke wants little grasp, controls at 3.0mm, back zone drafting multiple Selecting parameter 1.30, front roller centre-to-centre spacing controls at 42mm, and rear roller centre-to-centre spacing controls at 50mm, and ingot speed control is built in 11000r/min, spacing block is 2.5mm, twist factor controls 330, and front roller speeds control is at 150r/min, and total draft multiple is 50.
6, winder step is specially: adopt NO.21C automatic winder, winder speed 1200m/min, and clearing method is arranged: cotton knot 250%, short slub 140% × 1.2cm, long slubbing 30% × 30cm, long details-30% × 30cm.
The aloe yarn spun under this operation has following characteristic:
Ultimate strength/cN Extension at break/mm Elongation at break/% CV/%
431.25 61.37 12.63 9.74
Embodiment 2
The method step of the tight SEILE textile of aloe:
Main flow line:
A002C(griping cotton machine) → A006B(cotton blender machine) → A036C(kirschner beater opener) → A092A(hopper feeder) → A076C(lapper)
FA201(carding machine) → FA311(drawing frame) three also → FA423(Speed frames) → A513W(fine spining machine) → NO.21C(automatic winder)
A, raw material are: employing length is 30 ~ 40mm, and fineness is the aloe fibre of 1.5 ~ 1.7dtex;
B, concrete steps:
1, blowing step is specially: the bale of cotton carries out the loose operation of fiber through griping cotton machine, and arranging A002C griping cotton machine Beater Speed is 845r/min, dolly speed of gyration 2.3r/min, and blade stretches out rib distance 10mm, grabs cotton dolly and often runs decline in one week 3mm/ time; Fibre bundle after loose is sent in A006B cotton blender machine and carries out mixed cotton operation, cotton blender machine hired roughneck rotating speed is set to 430r/min, and between dirt bastinade hand, import is spaced at 15mm, and between dirt bastinade hand, outlet is spaced at 20mm, cotton-pressing curtain and brad curtain space 80mm, and brad curtain and evener roller space 80mm; Delivered to by aloe fibre in A036C opener and carry out shredding operation, opener speeds control is at 480r/min; Aloe fibre raw material after shredding is carried out married operation via condenser feeding A092A hopper feeder, and cotton feeder brad curtain wire velocity control is at 70m/min, and V-type cord speeds control is at 3.5m/min; Outputted to uniformly in A076C lapper by delivery roller by mixed aloe fibre and carry out clot and operate, the comprehensive Beater Speed 900r/min of lapper, the speeds control of rolling roller is at 13r/min; The aloe fibre lap length 36m formed after opening and cleaning step, dry weight is 400 grams/m, the rolling time be 3 points 55 seconds.
2, combing step is specially: in combing operation, and use FA201 carding machine, the speed of the cylinder in carding machine is arranged on 330r/min, and the speed of licker-in is arranged on 860r/min, and the speeds control of cover plate is at 100mm/min; Doffer speed controls at 28r/min, and cylinder and cover plate 5 are spaced and be respectively 0.25mm, 0.23mm, 0.2mm, 0.2mm, 0.23mm from import to outlet; Aloe fibre weight of card sliver is 21.5g/5m.
3, drafting step is specially: in mixing in doubling step, use FA311 drawing frame, and carry out three road mixing in doubling step, sliver exporting speed controls at 300m/min.
4, rove step is specially: control 1.05 by FA423 Speed frames Distribution Area drafting multiple, first break draft multiple controls 1.48, and primary area drafting multiple controls 9.0, and total draft multiple is 12.
5, spun yarn step is specially: adopt tight SEILE textile technology, Spinning Draft Zone is the feeding of double joint rove, and stroke wants little grasp, controls at 4.0mm, back zone drafting multiple Selecting parameter 1.30, front roller centre-to-centre spacing controls at 45mm, and rear roller centre-to-centre spacing controls at 65mm, and ingot speed control is built in 13000r/min, spacing block is 3.0mm, twist factor controls 360, and front roller speeds control is at 200r/min, and total draft multiple is 60.
6, winder step is specially: adopt NO.21C automatic winder, winder speed 1500m/min, and clearing method is arranged: cotton knot 300%, short slub 180% × 2.0cm, long slubbing 40% × 40cm, long details-40% × 40cm.
The aloe yarn spun under this operation has following characteristic:
Ultimate strength/cN Extension at break/mm Elongation at break/% CV/%
460.23 63.14 13.78 7.45
Embodiment 3
The method step of the tight SEILE textile of aloe:
Main flow line:
A002C(griping cotton machine) → A006B(cotton blender machine) → A036C(kirschner beater opener) → A092A(hopper feeder) → A076C(lapper)
FA201(carding machine) → FA311(drawing frame) three also → FA423(Speed frames) → A513W(fine spining machine) → NO.21C(automatic winder)
A, raw material are: employing length is 30 ~ 40mm, and fineness is the aloe fibre of 1.5 ~ 1.7dtex;
B, concrete steps:
1, blowing step is specially: the bale of cotton carries out the loose operation of fiber through griping cotton machine, and arranging A002C griping cotton machine Beater Speed is 845r/min, dolly speed of gyration 2.3r/min, and blade stretches out rib distance 5mm, grabs cotton dolly and often runs decline in one week 3mm/ time; Fibre bundle after loose is sent in A006B cotton blender machine and carries out mixed cotton operation, cotton blender machine hired roughneck rotating speed is set to 430r/min, and between dirt bastinade hand, import is spaced at 13mm, and between dirt bastinade hand, outlet is spaced at 15mm, cotton-pressing curtain and brad curtain space 70mm, and brad curtain and evener roller space 60mm; Delivered to by aloe fibre in A036C opener and carry out shredding operation, opener speeds control is at 480r/min; Aloe fibre raw material after shredding is carried out married operation via condenser feeding A092A hopper feeder, and cotton feeder brad curtain wire velocity control is at 60m/min, and V-type cord speeds control is at 2.56m/min; Outputted to uniformly in A076C lapper by delivery roller by mixed aloe fibre and carry out clot and operate, the comprehensive Beater Speed 900r/min of lapper, the speeds control of rolling roller is at 12r/min; The aloe fibre lap length 34.2m formed after opening and cleaning step, dry weight is 400 grams/m, the rolling time be 3 points 55 seconds.
(3) combing step is specially: in combing operation, and use FA201 carding machine, the speed of the cylinder in carding machine is arranged on 330r/min, and the speed of licker-in is arranged on 860r/min, and the speeds control of cover plate is at 88.4mm/min; Doffer speed controls at 24r/min, and cylinder and cover plate 5 are spaced and be respectively 0.25mm, 0.23mm, 0.2mm, 0.2mm, 0.23mm from import to outlet; Aloe fibre weight of card sliver is 21.5g/5m.
(4) drafting step is specially: in mixing in doubling step, use FA311 drawing frame, and carry out three road mixing in doubling step, sliver exporting speed controls at 275m/min.
(5) rove step is specially: control 1.05 by FA423 Speed frames Distribution Area drafting multiple, first break draft multiple controls 1. 26, and primary area drafting multiple controls 7.21, and total draft multiple is 8.97.
(6) spun yarn step is specially: adopt tight SEILE textile technology, Spinning Draft Zone is the feeding of double joint rove, and stroke wants little grasp, controls at 3.5mm, back zone drafting multiple Selecting parameter 1.30, front roller centre-to-centre spacing controls at 43mm, and rear roller centre-to-centre spacing controls at 57mm, and ingot speed control is built in 12000r/min, spacing block is 2.7mm, twist factor controls 350, and front roller speeds control is at 170r/min, and total draft multiple is 54.71.
(7) winder step is specially: adopt NO.21C automatic winder, winder speed 1400m/min, and clearing method is arranged: cotton knot 270%, short slub 160% × 1.6cm, long slubbing 35% × 35cm, long details-35% × 35cm.
The aloe yarn spun under this operation has following characteristic:
Ultimate strength/cN Extension at break/mm Elongation at break/% CV/%
440.52 62.15 13.05 8.45

Claims (4)

1. a spinning method for aloe yarn, be mainly and adopt tight SEILE textile technology spinning to form, its step comprises blowing, combing, drafting, rove, spun yarn and winder; It is characterized in that: concrete spinning stage is as follows:
(1) raw material is chosen: employing length is 30 ~ 40mm, and fineness is the aloe fibre of 1.5 ~ 1.7dtex;
(2) blowing step is specially: the bale of cotton carries out the loose operation of fiber through griping cotton machine, arranging A002C griping cotton machine Beater Speed is 845r/min, dolly speed of gyration 2.3r/min, blade stretches out rib distance 0 ~ 10mm, grabs cotton dolly and often runs decline in one week 3mm/ time; Fibre bundle after loose is sent in A006B cotton blender machine and carries out mixed cotton operation, cotton blender machine hired roughneck rotating speed is set to 430r/min, between dirt bastinade hand, import is spaced at 10 ~ 15mm, between dirt bastinade hand, outlet is spaced at 12 ~ 20mm, cotton-pressing curtain and brad curtain space 60 ~ 80mm, and brad curtain and evener roller space 40 ~ 80mm; Delivered to by aloe fibre in A036C opener and carry out shredding operation, opener speeds control is at 480r/min; Aloe fibre raw material after shredding is carried out married operation via condenser feeding A092A hopper feeder, and cotton feeder brad curtain wire velocity control is at 50 ~ 70m/min, and V-type cord speeds control is at 1.56 ~ 3.5m/min; Outputted to uniformly in A076C lapper by delivery roller by mixed aloe fibre and carry out clot and operate, the comprehensive Beater Speed 900r/min of lapper, the speeds control of rolling roller is at 11 ~ 13r/min; The aloe fibre lap length 34.2 ~ 36m formed after opening and cleaning step, dry weight is 400 grams/m, the rolling time be 3 points 55 seconds;
(3) combing step is specially: in combing operation, and use FA201 carding machine, the speed of the cylinder in carding machine is arranged on 330r/min, and the speed of licker-in is arranged on 860r/min, and the speeds control of cover plate is at 72.3 ~ 100mm/min; Doffer speed controls at 20 ~ 28r/min, and cylinder and cover plate 5 are spaced and be respectively 0.25mm, 0.23mm, 0.2mm, 0.2mm, 0.23mm from import to outlet; Aloe fibre weight of card sliver is 21.5g/5m;
(4) drafting step is specially: in mixing in doubling step, use FA311 drawing frame, and carry out three road mixing in doubling step, sliver exporting speed controls at 275 ~ 300m/min;
(5) rove step is specially: control 1.05 by FA423 Speed frames Distribution Area drafting multiple, first break draft multiple controls 1.12 ~ 1.48, and primary area drafting multiple controls 7.0 ~ 9.0, and total draft multiple is 8 ~ 12;
(6) spun yarn step is specially: adopt tight SEILE textile technology, Spinning Draft Zone is the feeding of double joint rove, and stroke wants little grasp, controls at 3.0 ~ 4.0mm, back zone drafting multiple Selecting parameter 1.30, front roller centre-to-centre spacing controls at 42 ~ 45mm, and rear roller centre-to-centre spacing controls at 50 ~ 65mm, and ingot speed control is built in 11000 ~ 13000r/min, spacing block is 2.5 ~ 3.0mm, twist factor controls 330 ~ 360, and front roller speeds control is at 150 ~ 200r/min, and total draft multiple is 50 ~ 60;
(7) winder step is specially: adopt NO.21C automatic winder, winder speed 1200 ~ 1500m/min, clearing method is arranged: cotton knot 250 ~ 300%, short slub 140 ~ 180%x1.2 ~ 2.0cm, long slubbing 30 ~ 40%x30 ~ 40cm, long details-30 ~-40%x30 ~ 40cm.
2. the spinning method of a kind of aloe yarn according to claim 1, is characterized in that: described raw material adopts length to be 38mm, and fineness is the aloe fibre of 1.67dtex.
3. the spinning method of a kind of aloe yarn according to claim 1, it is characterized in that: FA423 Speed frames Distribution Area drafting multiple controls 1.05 by described rove step, first break draft multiple controls 1.26, and primary area drafting multiple controls 7.12, and total draft multiple is 8.97.
4. the spinning method of a kind of aloe yarn according to claim 1, it is characterized in that: described spun yarn step, Spinning Draft Zone stroke controls at 3.5mm, back zone drafting multiple Selecting parameter 1.30, and front roller centre-to-centre spacing controls at 43mm, rear roller centre-to-centre spacing controls at 57mm, ingot speed control is built in 12000r/min, and spacing block is 2.7mm, and twist factor controls 350, front roller speeds control is at 170r/min, and total draft multiple is 54.71.
CN201510197418.0A 2015-04-24 2015-04-24 Spinning method for aloe yarns Pending CN104805554A (en)