CN110318131A - A kind of processing method and resulting product of high resiliency tear-proof CVC mixed yarn - Google Patents
A kind of processing method and resulting product of high resiliency tear-proof CVC mixed yarn Download PDFInfo
- Publication number
- CN110318131A CN110318131A CN201910299330.8A CN201910299330A CN110318131A CN 110318131 A CN110318131 A CN 110318131A CN 201910299330 A CN201910299330 A CN 201910299330A CN 110318131 A CN110318131 A CN 110318131A
- Authority
- CN
- China
- Prior art keywords
- cvc
- mixed yarn
- tear
- proof
- high resiliency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing methods and resulting product of a kind of high resiliency tear-proof CVC mixed yarn, a kind of processing method of high resiliency tear-proof CVC mixed yarn, specific steps are as follows: 1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber；2) it prewets；3) onion and red cabbage are extracted, obtains extract liquor；4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；5) dehydration.Product produced by the present invention has high resiliency, high-flexibility, and tear-resistant effect is good, and CVC mixed yarn falls that flora number is few, the processing method high production efficiency of high resiliency tear-proof CVC mixed yarn of the present invention.
Description
Technical field
The invention belongs to field of textiles, and in particular to a kind of processing method and gained of high resiliency tear-proof CVC mixed yarn
Product.
Background technique
CVC fabric (chief value of cotton) be only wash in the fabric of two kinds of ingredients of cotton, when cotton ingredient contains
Amount equals or exceeds fabric when 50%, it has good wearability and wrinkle resistance.With the improvement of living standards, consumer
It is also higher and higher to the quality requirements of CVC fabric.Existing CVC fabric also needs to carry out subsequent arrangement, such as dyeing work
Sequence.Repeatedly through water process, the elasticity of CVC fabric, pliability can be made to be affected, while also will increase the flora of CVC fabric.
How in the case where guaranteeing high resiliency, pliability, reduction falls flora amount, improves production efficiency, be the present invention urgently can to
Problem.
Summary of the invention
Goal of the invention: the purpose of the present invention is to solve deficiencies in the prior art, provide a kind of high resiliency tear-proof
The processing method and resulting product of CVC mixed yarn, production obtained by the processing method by high resiliency tear-proof CVC mixed yarn
Product in the case where guaranteeing high resiliency, pliability, CVC mixed yarn to fall flora number few, and greatly improve production efficiency.
Technical solution: a kind of processing method of high resiliency tear-proof CVC mixed yarn, specific steps are as follows:
1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber；
2) it prewets；
3) onion and red cabbage are extracted, obtains extract liquor；
4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；
5) dehydration.
A further improvement of the present invention is that:
In step 3), onion and red cabbage are extracted respectively；
The method of onion extraction are as follows: a) weigh suitable onion-skin, red cabbage, shredded after cleaning；B) it is added and boils,
And keep the temperature a period of time；C) it is filtered, obtains filtrate and filter residue；D) filtrate and filter residue are merged, add water and is boiled,
Filtering repeats this step 2-3 times, finally obtains filtrate.
A further improvement of the present invention is that:
In step b), heat preservation when it is 0.5-1 hours a length of.
A further improvement of the present invention is that:
Onion-skin, red cabbage weight ratio be 1:1 or 2:1 or 1:2.
A further improvement of the present invention is that:
In step 4), the ratio of extract liquor and alum is 3:1.
A further improvement of the present invention is that:
In step 4), the spray liquid fallen is continued to be fed into spray equipment by circulating pump.
A further improvement of the present invention is that:
Step 5), the specific steps of dehydration are as follows: CVC mixed yarn is sent in heating device, passes through vacuum dehydration
Afterwards, CVC mixed yarn is heated using heating roller.
A kind of product of high resiliency tear-proof CVC mixed yarn: the CVC mixed yarn of preparation, it is anti-tear by a kind of above-mentioned high resiliency
Split the processing method preparation gained of CVC mixed yarn.
Compared with prior art, the processing method and gained of a kind of high resiliency tear-proof CVC mixed yarn provided by the invention
Product, at least realize it is following the utility model has the advantages that
Based on the above embodiment, the step of adding onion and red cabbage, reducing subsequent dyeing, good color fastness, dye-uptake
Height improves production efficiency, high-efficiency environment friendly, while also improving the pliability and elasticity of CVC mixed yarn.Utilize heating roller pair
CVC mixed yarn is heated, further such that the drying of CVC mixed yarn is more thorough, is improved color fastness, is also ensured simultaneously
Elasticity, the pliability of spun lacing CVC mixed yarn, but also the tear resistance of CVC mixed yarn increases.Meanwhile the CVC being prepared into
Mixed yarn, full color, dress safety will not damage or cause allergic reaction to human body, can be applied to high-cleanness, high
The field of high sanitary standard.
Certainly, not specific needs are implemented any of the products of the present invention while reaching all the above technical effect.
Specific embodiment
The existing various exemplary embodiments of detailed description of the present invention.It should also be noted that unless specifically stated otherwise, otherwise at this
Component described in a little embodiments and the positioned opposite of step, numerical expression and numerical value do not limit the scope of the invention.
Be to the description only actually of at least one exemplary embodiment below it is illustrative, never as to the present invention
And its application or any restrictions used.
Technology, method and apparatus known to person of ordinary skill in the relevant may be not discussed in detail, but suitable
In the case of, the technology, method and apparatus should be considered as part of specification.
It is shown here and discuss all examples in, any occurrence should be construed as merely illustratively, without
It is as limitation.Therefore, other examples of exemplary embodiment can have different values.
Embodiment 1, a kind of processing method of high resiliency tear-proof CVC mixed yarn, specific steps are as follows:
1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber；
2) it prewets；
3) onion and red cabbage are extracted, obtains extract liquor；
4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；
5) dehydration.
A further improvement of the present invention is that:
In step 3), onion and red cabbage are extracted respectively；
The method of onion extraction are as follows: a) weigh suitable onion-skin, red cabbage, shredded after cleaning；B) it is added and boils,
And keep the temperature a period of time；C) it is filtered, obtains filtrate and filter residue；D) filtrate and filter residue are merged, add water and is boiled,
Filtering repeats this step 2-3 times, finally obtains filtrate.
In order to which the present embodiment is explained further, it should be understood that
In step b), heat preservation when it is 0.5-1 hours a length of.
In order to which the present embodiment is explained further, it should be understood that
Onion-skin, red cabbage weight ratio be 1:1.
In order to which the present embodiment is explained further, it should be understood that
In step 4), the ratio of extract liquor and alum is 3:1.
In order to which the present embodiment is explained further, it should be understood that
In step 4), the spray liquid fallen is continued to be fed into spray equipment by circulating pump.
In order to which the present embodiment is explained further, it should be understood that
Step 5), the specific steps of dehydration are as follows: CVC mixed yarn is sent in heating device, passes through vacuum dehydration
Afterwards, CVC mixed yarn is heated using heating roller.
Based on the above embodiment, the step of adding onion and red cabbage, reducing subsequent dyeing, good color fastness, dye-uptake
Height improves production efficiency, high-efficiency environment friendly, while also improving the pliability and elasticity of CVC mixed yarn.Utilize heating roller pair
CVC mixed yarn is heated, further such that the drying of CVC mixed yarn is more thorough, is improved color fastness, is also ensured simultaneously
Elasticity, the pliability of spun lacing CVC mixed yarn, but also the tear resistance of CVC mixed yarn increases.Meanwhile the CVC being prepared into
Mixed yarn, full color, dress safety will not be damaged or be caused allergic reaction to human body.
Embodiment 2, a kind of processing method of high resiliency tear-proof CVC mixed yarn, specific steps are as follows:
1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber, wherein terylene regeneration is short
The allocation ratio of fiber, cotton yarn and cotton fiber is 50:40:30.
2) it prewets；
3) onion and red cabbage are extracted, obtains extract liquor；
4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；
5) dehydration.
In order to which the present embodiment is explained further, it should be understood that
In step 3), onion and red cabbage are extracted respectively；
The method of onion extraction are as follows: a) weigh suitable onion-skin, red cabbage, shredded after cleaning；B) it is added and boils,
And keep the temperature a period of time；C) it is filtered, obtains filtrate and filter residue；D) filtrate and filter residue are merged, add water and is boiled,
Filtering repeats this step 2-3 times, finally obtains filtrate.
In order to which the present embodiment is explained further, it should be understood that
In step b), heat preservation when it is 0.5-1 hours a length of.
A further improvement of the present invention is that:
Onion-skin, red cabbage weight ratio be 2:1.
A further improvement of the present invention is that:
In step 4), the ratio of extract liquor and alum is 3:1.
In order to which the present embodiment is explained further, it should be understood that
In step 4), the spray liquid fallen is continued to be fed into spray equipment by circulating pump.
In order to which the present embodiment is explained further, it should be understood that
Step 5), the specific steps of dehydration are as follows: CVC mixed yarn is sent in heating device, passes through vacuum dehydration
Afterwards, CVC mixed yarn is heated using heating roller.
Based on the above embodiment, the prepared CVC mixed yarn obtained, full color, dress safety will not cause human body
It injures or causes allergic reaction.
Embodiment 3, a kind of processing method of high resiliency tear-proof CVC mixed yarn, specific steps are as follows:
1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber, wherein terylene regeneration is short
The allocation ratio of fiber, cotton yarn and cotton fiber is 50:40:30.
2) it prewets；
3) onion and red cabbage are extracted, obtains extract liquor；
4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；
5) dehydration.
In order to which the present embodiment is explained further, it should be understood that
In step 3), onion and red cabbage are extracted respectively；
The method of onion extraction are as follows: a) weigh suitable onion-skin, red cabbage, shredded after cleaning；B) it is added and boils,
And keep the temperature a period of time；C) it is filtered, obtains filtrate and filter residue；D) filtrate and filter residue are merged, add water and is boiled,
Filtering repeats this step 2-3 times, finally obtains filtrate.
In order to which the present embodiment is explained further, it should be understood that
In step b), heat preservation when it is 0.5-1 hours a length of.
In order to which the present embodiment is explained further, it should be understood that
The weight ratio 1:2 of onion-skin, red cabbage.
In order to which the present embodiment is explained further, it should be understood that
In step 4), the ratio of extract liquor and alum is 3:1.
In order to which the present embodiment is explained further, it should be understood that
In step 4), the spray liquid fallen is continued to be fed into spray equipment by circulating pump.
In order to which the present embodiment is explained further, it should be understood that
Step 5), the specific steps of dehydration are as follows: CVC mixed yarn is sent in heating device, passes through vacuum dehydration
Afterwards, CVC mixed yarn is heated using heating roller.
The CVC mixed yarn that above-described embodiment is prepared into, full color, dress safety, human body will not be damaged or
It causes allergic reaction.
Embodiment 4,
A kind of product of high resiliency tear-proof CVC mixed yarn: the CVC mixed yarn of preparation, by any one in embodiment 1-3
The processing method of high resiliency tear-proof CVC mixed yarn in embodiment prepares gained.The CVC mixed yarn being prepared into is through measuring, often
The grammes per square metre of volume is in 30/g/m2Left and right.
In embodiment 1-3 it is obtained can not portion tested, detected, crack conditions and extensibility are shown in Table 1, health detection
Situation is shown in Table 2.
Table 1
| Ultimate strength/N | Elongation/% | |
| It is longitudinal | 30 | 98 |
| Laterally | 9 | 195 |
Table 2
Through the foregoing embodiment it is found that a kind of processing method of high resiliency tear-proof CVC mixed yarn provided by the invention and
Resulting product, at least realize it is following the utility model has the advantages that
Based on the above embodiment, the step of adding onion and red cabbage, reducing subsequent dyeing, good color fastness, dye-uptake
Height improves production efficiency, high-efficiency environment friendly, while also improving the pliability and elasticity of CVC mixed yarn.Utilize heating roller pair
CVC mixed yarn is heated, further such that the drying of CVC mixed yarn is more thorough, is improved color fastness, is also ensured simultaneously
Elasticity, the pliability of spun lacing CVC mixed yarn, but also the tear resistance of CVC mixed yarn increases.Meanwhile the CVC being prepared into
Mixed yarn, full color, dress safety will not damage or cause allergic reaction to human body, can be applied to high-cleanness, high
The field of high sanitary standard.
Although some specific embodiments of the invention are described in detail by example, the skill of this field
Art personnel it should be understood that example above merely to being illustrated, the range being not intended to be limiting of the invention.The skill of this field
Art personnel are it should be understood that can without departing from the scope and spirit of the present invention modify to above embodiments.This hair
Bright range is defined by the following claims.
Claims (8)
1. a kind of processing method of high resiliency tear-proof CVC mixed yarn, which is characterized in that specific steps are as follows:
1) pass through terylene regeneration staple, cotton yarn and the blended preparation CVC mixed yarn of cotton fiber；
2) it prewets；
3) onion and red cabbage are extracted, obtains extract liquor；
4) after being sufficiently mixed extract liquor and alum, CVC mixed yarn is sprayed；
5) dehydration.
2. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 1, which is characterized in that
In the step 3), onion and red cabbage are extracted respectively；
The method of onion extraction are as follows: a) weigh suitable onion-skin, red cabbage, shredded after cleaning；B) it is added and boils, and protect
Warm a period of time；C) it is filtered, obtains filtrate and filter residue；D) filtrate and filter residue are merged, adds water and is boiled, mistake
Filter repeats this step 2-3 times, finally obtains filtrate.
3. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 2, which is characterized in that
In the step b), heat preservation when it is 0.5-1 hours a length of.
4. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 1, which is characterized in that
The onion-skin, red cabbage weight ratio be 1:1 or 2:1 or 1:2.
5. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 1, which is characterized in that
In the step 4), the ratio of extract liquor and alum is 3:1.
6. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 1, which is characterized in that
In the step 4), the spray liquid fallen is continued to be fed into spray equipment by circulating pump.
7. a kind of processing method of high resiliency tear-proof CVC mixed yarn according to claim 1, which is characterized in that
The step 5), the specific steps of dehydration are as follows: CVC mixed yarn is sent in heating device, passes through vacuum dehydration
Afterwards, CVC mixed yarn is heated using heating roller.
8. a kind of product of high resiliency tear-proof CVC mixed yarn, it is characterised in that: the CVC mixed yarn of the preparation is wanted by right
A kind of processing method preparation gained of high resiliency tear-proof CVC mixed yarn described in asking 1-7 any one.