CN108914295A - A kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process - Google Patents

A kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process Download PDF

Info

Publication number
CN108914295A
CN108914295A CN201810883627.4A CN201810883627A CN108914295A CN 108914295 A CN108914295 A CN 108914295A CN 201810883627 A CN201810883627 A CN 201810883627A CN 108914295 A CN108914295 A CN 108914295A
Authority
CN
China
Prior art keywords
speed
cotton
spinning process
scribbled
tussah silk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810883627.4A
Other languages
Chinese (zh)
Inventor
厉红英
付晓娟
郑印
陈康
杨俊鹏
赵明剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Textile (group) Dafeng Textile Co Ltd
Original Assignee
Shanghai Textile (group) Dafeng Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Textile (group) Dafeng Textile Co Ltd filed Critical Shanghai Textile (group) Dafeng Textile Co Ltd
Priority to CN201810883627.4A priority Critical patent/CN108914295A/en
Publication of CN108914295A publication Critical patent/CN108914295A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process, the scribbled is formed with Modal fibre, combed cotton, tussah silk blend, and each component accounts in the scribbled:Modal fibre 65%;Combed cotton 25%;Tussah silk 10%;The spinning process includes blow room system, carding process, drawing process, coarse sand technique, spinning process, winding process.The scribbled that the present invention obtains integrates the advantages of Modal fibre, combed cotton, tussah silk, with good quality, can be used for preparing high-grade fabric, especially can be used as the fabric of underwear.

Description

A kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process
Technical field
The present invention relates to a kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process, belong to weaving skill Art field.
Background technique
The raw material of Modal fibre (Modal) fiber, can be with natural degradation after use from the timber of the Nature, not generation Your fiber softening, bright and clean, beautiful in colour, fabric feeling is especially smooth, and cloth cover gloss is beautiful, drapability than existing cotton, wash It is good, there are the gloss and feel as silk, is a kind of natural mercerising fabric, there is excellent stainability and bright color after being dyed The characteristics of.
Combed cotton removes shorter fiber in cotton fiber with combing machine, and the longer and neat fiber left.Combing The spun yarn quality of cotton is more preferable.Cloth made of combed cotton yarn has higher quality level in texture, washable and durability.
Tussah silk is one of distinctive natural textile raw material in China, and silk has unique jewelry gloss, natural luxurious, cunning It is refreshing comfortable;And ramie is known as green natural textile fabric, because of strength height, moisture absorption rapid heat dissipation, rough elegant, antibacterial anti-corrosion, guarantor The functions such as strong, the always raw material as top grade textile garment.
Summary of the invention
One aspect of the present invention provides a kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process, Have both Modal fibre, combed cotton, tussah silk excellent performance, have good quality, can be used for preparing high-grade fabric.
The detailed technology scheme of the scribbled of the invention is as follows:
A kind of Modal fibre, combed cotton, tussah silk scribbled, it is characterised in that:The scribbled is with not generation That fiber, combed cotton, tussah silk blend form, and each component accounts in the scribbled:Modal is fine Dimension 65%;Combed cotton 25%;Tussah silk 10%.
A kind of spinning process producing Modal fibre, combed cotton, tussah silk scribbled, it is characterised in that:It includes Blow room system, carding process, drawing process, coarse sand technique, spinning process, winding process.
In a specific embodiment, the blow room system successively use automatic plucker, mixed cotton slitter, opener, The technological parameter of cotton feeder, lapper, the blow room system is:Automatic plucker Beater Speed is 730r/min, and blade is stretched The distance of rib is 2mm out, and trolley rotational speed 1.66r/min, the U-shaped Beater Speed of mixed cotton slitter is 450r/min, porcupine The speed of hired roughneck is 850r/min, and the Beater Speed of opener is 500r/min, and the Beater Speed of lapper is 850r/min, at The speed for rolling up roller is 10r/min, and feeding hopper is vibration-type feeding hopper, and the speed of brad curtain is 40m/min, the speed of cotton transport curtain 8.4m/min, the air quantity of cotton blender machine are 5200m3/ h, pressure 100pa, hybrid mode be mainly air-flow mixing, intensive mixing, Lamination mixing.
In a specific embodiment, the technological parameter of the carding process is:The quantitative 380g/m of cotton layer, cylinder speed are 30r/min, licker-in speed 780r/min, cover plate speed 92r/min, doffer speed 18r/min, cylinder and cover board are from import Gauge to outlet is respectively 8mm, 7mm, 6mm, 6mm, 7mm, and the gauge between cylinder and doffer is 5mm, cylinder and licker-in it Between gauge be 7mm, the angle of mote knife be 85 ° of positions be it is flat, the sliver exporting speed of carding machine is 39m/min, carding step Total draft multiple is 105 times, weight of card sliver 18.5g/m.
In a specific embodiment, the drawing process is using three and the process of sum, and drawing process is to improve fiber Degree of stretching reduces weight inhomogeneities and attaches most importance to, and Process configuration is used along drawing-off, head and to pull multiple be 6 times, and two and and three simultaneously Drawing multiple be respectively 6.34 times and 6.77 times.
In a specific embodiment, the technological parameter of the coarse sand technique is:Roller gauge be 12mm × 28mm × 38mm, twist factor 90, ingot speed 950r/min design quantification of 4g/m, total draft multiple 8.16, and back zone drawing multiple is 1.22, nip gauge 5mm.
In a specific embodiment, the technological parameter of the spinning process is:Front and back roller gauge be respectively 18mm × 40mm, ingot speed 12500r/min, drafting multiple be 47.8 times, back zone pull 1.17 times of multiple, twist factor 380, jaw every Away from 2.5mm.
By adopting the above-described technical solution, scribbled collection Modal fibre, combed cotton, tussah silk that the present invention obtains The advantages of, with good quality, can be used for preparing high-grade fabric.
Specific embodiment
To make above objects, features, and advantages of the present invention, can be more obvious and easy to understand, below to preferable implementation of the invention Example is described in detail, so as to make a clearer definition of the protection scope of the present invention.
The present invention has obtained optimum proportion scheme by studying, testing repeatedly according to the characteristic of above two fiber, thus Obtain a kind of Modal fibre, combed cotton, tussah silk scribbled.
The scribbled is formed with Modal fibre, combed cotton, tussah silk blend, each component in the scribbled It accounts for:Modal fibre 65%;Combed cotton 25%;Tussah silk 10%.
In addition, the present invention is according to the technological difficulties in the characteristic and blending process of above-mentioned three kinds of fibers, by studying repeatedly, Test obtains the spinning process of optimal production Modal fibre, combed cotton, tussah silk scribbled.The spinning process includes opening Scutching cotton technique, carding process, drawing process, coarse sand technique, spinning process and winding process.
In a specific embodiment, blow room system of the present invention, carding process, drawing process, coarse sand technique, spun yarn work Skill, winding process are specific as follows:
1, blow room system
The blow room system successively use A002 automatic plucker, A035 mixed cotton slitter, FA106 opener, A092 to Cotton machine, A076 lapper, the technological parameter of the blow room system are:Automatic plucker Beater Speed is 730r/min, blade The distance for stretching out rib is 2mm, and trolley rotational speed 1.66r/min, the U-shaped Beater Speed of mixed cotton slitter is 450r/min, person of outstanding talent The speed of pig hired roughneck is 850r/min, and the Beater Speed of opener is 500r/min, and the Beater Speed of lapper is 850r/min, The speed of coiled roller is 10r/min, and feeding hopper is vibration-type feeding hopper, and the speed of brad curtain is 40m/min, the speed of cotton transport curtain 8.4m/min is spent, the air quantity of cotton blender machine is 5200m3/h, and pressure 100pa, hybrid mode is mainly that air-flow mixes, is intensive mixed It closes, lamination mixing.
2, carding process
The technological parameter of the carding process is:Quantitatively 380g/m, cylinder speed 30r/min, licker-in speed are cotton layer 780r/min, cover plate speed 92r/min, doffer speed 18r/min, the gauge of cylinder and cover board from import to outlet are respectively 8mm, 7mm, 6mm, 6mm, 7mm, the gauge between cylinder and doffer are 5mm, and the gauge between cylinder and licker-in is 7mm, dedusting The angle of knife be 85 ° of positions be it is flat, the sliver exporting speed of carding machine is 39m/min, and the total draft multiple of carding step is 105 times, Weight of card sliver 18.5g/m.
3, drawing process
The drawing process is using three and the process of sum, and drawing process is to improve Fiber Straightness, reduce weight unevenness Even property is attached most importance to, and Process configuration is used along drawing-off, head and to pull multiple be 6 times, two and and three and drawing multiple be respectively 6.34 times and 6.77 times.
4, coarse sand technique
The technological parameter of the coarse sand technique is:Roller gauge is 12mm × 28mm × 38mm, and twist factor 90, ingot speed is 950r/min designs quantification of 4g/m, total draft multiple 8.16, and it is 1.22 that back zone, which pulls multiple, nip gauge 5mm.
5, spinning process
The technological parameter of the spinning process is:Front and back roller gauge is respectively 18mm × 40mm, ingot speed 12500r/ Min, drafting multiple are 47.8 times, 1.17 times of multiple of back zone drawing, twist factor 380, nip gauge 2.5mm.
6, winding process
The revolving speed of winder is set as 800~1000r/min, to ensure cylinder yarn quality.
After the present invention carries out opening picking, cotton carding to tencel fiber and cashmere first, then to the two carry out item it is mixed to So that blending rate is accurate.
The scribbled that the present invention obtains integrates the advantages of Modal fibre, combed cotton, tussah silk, can be used for making Standby high-grade fabric, is particularly suitable as the fabric of underwear.
The description with certain particularity detailed enough has been carried out to the present invention above.Ordinary skill in fields Personnel are it should be understood that the description in embodiment is only exemplary, before without departing from true spirit and scope of the present invention Put make it is all change all should belong to protection scope of the present invention.Scope of the present invention is by the power What sharp claim was defined, rather than limited by the foregoing description in embodiment.

Claims (7)

1. a kind of Modal fibre, combed cotton, tussah silk scribbled, it is characterised in that:The scribbled is with Modal Fiber, combed cotton, tussah silk blend form, and each component accounts in the scribbled:Modal fibre 65%;Combed cotton 25%;Tussah silk 10%.
2. a kind of spinning process for producing Modal fibre as described in claim 1, combed cotton, tussah silk scribbled, It is characterized in that:It includes blow room system, carding process, drawing process, coarse sand technique, spinning process, winding process.
3. spinning process as claimed in claim 2, which is characterized in that the blow room system successively use automatic plucker, The technological parameter of mixed cotton slitter, opener, cotton feeder, lapper, the blow room system is:Automatic plucker Beater Speed is 730r/min, the distance that blade stretches out rib is 2mm, trolley rotational speed 1.66r/min, the U-shaped Beater Speed of mixed cotton slitter For 450r/min, the speed of porcupine hired roughneck is 850r/min, and the Beater Speed of opener is 500r/min, hired roughneck's speed of lapper Degree is 850r/min, and the speed of coiled roller is 10r/min, and feeding hopper is vibration-type feeding hopper, and the speed of brad curtain is 40m/ Min, the speed 8.4m/min of cotton transport curtain, the air quantity of cotton blender machine are 5200m3/ h, pressure 100pa, hybrid mode are mainly gas Stream mixing, intensive mixing, lamination mixing.
4. spinning process as claimed in claim 2, which is characterized in that the technological parameter of the carding process is:Cotton layer is quantitative 380g/m, cylinder speed 30r/min, licker-in speed 780r/min, cover plate speed 92r/min, doffer speed 18r/ The gauge of min, cylinder and cover board from import to outlet is respectively 8mm, 7mm, 6mm, 6mm, 7mm, between cylinder and doffer every Away from for 5mm, the gauge between cylinder and licker-in is 7mm, and the angle of mote knife is 85 °, and the sliver exporting speed of carding machine is 39m/ Min, the total draft multiple of carding step are 105 times, weight of card sliver 18.5g/m.
5. spinning process as claimed in claim 2, which is characterized in that the process that the drawing process uses three and sum, and Technique is attached most importance to improving Fiber Straightness, reducing weight inhomogeneities, and Process configuration is used along drawing-off, and head simultaneously pulls multiple It is 6 times, two be respectively simultaneously 6.34 times and 6.77 times with three drawing multiples simultaneously.
6. spinning process as claimed in claim 2, which is characterized in that the technological parameter of the coarse sand technique is:Roller gauge For 12mm × 28mm × 38mm, twist factor 90, ingot speed 950r/min designs quantification of 4g/m, total draft multiple 8.16, after It is 1.22 that area, which pulls multiple, nip gauge 5mm.
7. spinning process as claimed in claim 2, which is characterized in that the technological parameter of the spinning process is:Front and back roller Gauge is respectively 18mm × 40mm, and ingot speed 12500r/min, drafting multiple is 47.8 times, and back zone pulls 1.17 times of multiple, twists Coefficient is 380, nip gauge 2.5mm.
CN201810883627.4A 2018-08-03 2018-08-03 A kind of Modal fibre, combed cotton, tussah silk scribbled and its spinning process Withdrawn CN108914295A (en)